CN107935472A - A kind of high-strength glue for tile - Google Patents
A kind of high-strength glue for tile Download PDFInfo
- Publication number
- CN107935472A CN107935472A CN201711223327.5A CN201711223327A CN107935472A CN 107935472 A CN107935472 A CN 107935472A CN 201711223327 A CN201711223327 A CN 201711223327A CN 107935472 A CN107935472 A CN 107935472A
- Authority
- CN
- China
- Prior art keywords
- parts
- tile
- strength glue
- glue
- reinforcing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building material technical field, specifically discloses a kind of high-strength glue for tile.The high-strength glue for tile includes the raw material components of following parts by weight:30~50 parts of cement;80~120 parts of quartz sand;15~25 parts of dry powder;3~8 parts of hydroxypropyl methyl cellulose;5~10 parts of reinforcing agent.The high-strength glue for tile has very excellent intensity, the intensity data measured after immersion, Frozen-thawed cycled, thermal aging test is still more excellent, this illustrates that high-strength glue for tile of the present invention can resist various rugged environments under immersion, freezing and high temperature, remains to retain good intensity.
Description
Technical field
The present invention relates to building material technical field, and in particular to a kind of high-strength glue for tile.
Background technology
Glue for tile is also known as Ceramic Tiles adhesive, is mainly used for pasting the ornament materials such as ceramic tile, face brick, floor tile, generally applicable
In the facing decoration places of the buildings such as inside and outside metope, ground, bathroom, kitchen.Existing glue for tile is by cement, mineral collection mostly
The pulverulent mixture of material, organic admixture composition, but existing many glues for tile cause between ceramic tile and base material because of environment reason
Adhesive strength reduce, the phenomenon for causing ceramic tile to come off.And the intensity of glue for tile is to evaluate a factor of glue for tile quality, especially
It is the ceramic tile for large-size, to the intensity requirement higher of glue for tile.
The content of the invention
The technical problem to be solved by the invention is to provide a kind of high-strength glue for tile.The glue for tile intensity is high, energy
Enough ceramic tiles for firmly clinging large-size.
Above-mentioned technical problem to be solved by this invention is achieved by the following technical programs:
A kind of high-strength glue for tile, it includes the raw material components of following parts by weight:
30~50 parts of cement;80~120 parts of quartz sand;15~25 parts of dry powder;3~8 parts of hydroxypropyl methyl cellulose;Increase
Strong 5~10 parts of agent.
Preferably, the high-strength glue for tile, it includes the raw material components of following parts by weight:
40~50 parts of cement;80~100 parts of quartz sand;20~25 parts of dry powder;5~8 parts of hydroxypropyl methyl cellulose;Increase
Strong 8~10 parts of agent.
Most preferably, the high-strength glue for tile, it includes the raw material components of following parts by weight:
40 parts of cement;100 parts of quartz sand;20 parts of dry powder;5 parts of hydroxypropyl methyl cellulose;8 parts of reinforcing agent.
Preferably, the quartz sand is the quartz sand of 100~200 mesh.
Most preferably, the quartz sand is the quartz sand of 200 mesh.
Preferably, the reinforcing agent is made of the material composition of following parts by weight:
15~20 parts of ethylene-vinyl acetate copolymer;10~20 parts of farina;5~10 parts of modified starch ether.
It is further preferred that the reinforcing agent is made of the material composition of following parts by weight:
18~20 parts of ethylene-vinyl acetate copolymer;15~18 parts of farina;8~10 parts of modified starch ether.
Most preferably, the reinforcing agent is made of the material composition of following parts by weight:
18 parts of ethylene-vinyl acetate copolymer;15 parts of farina;8 parts of modified starch ether.
The preparation method of above-mentioned high-strength glue for tile, it includes following steps:
Cement, quartz sand, dry powder, hydroxypropyl methyl cellulose are uniformly mixed up to described with the reinforcing agent
High-strength glue for tile.
Beneficial effect:The present invention provides a kind of high-strength glue for tile completely newly formed;The high-strength glue for tile tool
There is very excellent intensity, the intensity data measured after immersion, Frozen-thawed cycled, thermal aging test is still more excellent, this explanation
High-strength glue for tile of the present invention can resist various rugged environments under immersion, freezing and high temperature, still retain very well
Intensity.
Embodiment
The present invention is explained further below in conjunction with specific embodiment, but embodiment does not do any type of limit to the present invention
It is fixed.
The preparation of 1 high-strength glue for tile of embodiment
Raw material proportioning:40 parts of cement;100 parts of the quartz sand of 200 mesh;20 parts of dry powder;5 parts of hydroxypropyl methyl cellulose;
8 parts of reinforcing agent;
The reinforcing agent is mixed by 18 parts of ethylene-vinyl acetate copolymer, 15 parts of farina, 8 parts of modified starch ether
Conjunction forms.
Preparation method:Cement, quartz sand, dry powder, hydroxypropyl methyl cellulose are uniformly mixed i.e. with the reinforcing agent
Obtain the high-strength glue for tile.
The preparation of 2 high-strength glue for tile of embodiment
Raw material proportioning:40 parts of cement;100 parts of the quartz sand of 200 mesh;20 parts of dry powder;5 parts of hydroxypropyl methyl cellulose;
8 parts of reinforcing agent;
The reinforcing agent is mixed by 15 parts of ethylene-vinyl acetate copolymer, 10 parts of farina, 10 parts of modified starch ether
Conjunction forms.
Preparation method:Cement, quartz sand, dry powder, hydroxypropyl methyl cellulose are uniformly mixed i.e. with the reinforcing agent
Obtain the high-strength glue for tile.
The preparation of 3 high-strength glue for tile of embodiment
Raw material proportioning:40 parts of cement;100 parts of the quartz sand of 200 mesh;20 parts of dry powder;5 parts of hydroxypropyl methyl cellulose;
8 parts of reinforcing agent;
The reinforcing agent is mixed by 20 parts of ethylene-vinyl acetate copolymer, 20 parts of farina, 5 parts of modified starch ether
Conjunction forms.
Preparation method:Cement, quartz sand, dry powder, hydroxypropyl methyl cellulose are uniformly mixed i.e. with the reinforcing agent
Obtain the high-strength glue for tile.
The preparation of 4 high-strength glue for tile of embodiment
Raw material proportioning:30 parts of cement;80 parts of the quartz sand of 200 mesh;25 parts of dry powder;8 parts of hydroxypropyl methyl cellulose;Increase
Strong 10 parts of agent;
The reinforcing agent is mixed by 18 parts of ethylene-vinyl acetate copolymer, 15 parts of farina, 8 parts of modified starch ether
Conjunction forms.
Preparation method:Cement, quartz sand, dry powder, hydroxypropyl methyl cellulose are uniformly mixed i.e. with the reinforcing agent
Obtain the high-strength glue for tile.
The preparation of 5 high-strength glue for tile of embodiment
Raw material proportioning:50 parts of cement;120 parts of the quartz sand of 200 mesh;15 parts of dry powder;3 parts of hydroxypropyl methyl cellulose;
5 parts of reinforcing agent;
The reinforcing agent is mixed by 18 parts of ethylene-vinyl acetate copolymer, 15 parts of farina, 8 parts of modified starch ether
Conjunction forms.
Preparation method:Cement, quartz sand, dry powder, hydroxypropyl methyl cellulose are uniformly mixed i.e. with the reinforcing agent
Obtain the high-strength glue for tile.
The preparation of 1 glue for tile of comparative example
Raw material is formed and matched and preparation method is with embodiment 1, and difference is, reinforcing agent is by ethyl vinyl acetate second
18 parts of alkene copolymer, 15 parts of compositions of farina, and do not contain modified starch ether.
The preparation of 2 glue for tile of comparative example
Raw material is formed and matched and preparation method is with embodiment 1, and difference is, reinforcing agent is by ethyl vinyl acetate second
18 parts of alkene copolymer, 8 parts of modified starch ether, and do not contain farina.
The preparation of 3 glue for tile of comparative example
Raw material is formed and matched and preparation method is with embodiment 1, and difference is, reinforcing agent is by ethyl vinyl acetate second
Alkene forms, and does not contain farina and modified starch ether.
The glue for tile product that embodiment and comparative example are prepared is according to JC/T 547-2005《Ceramic wall and floor bricks glue
Stick》Middle pertinent regulations are tested, and the results are shown in Table 1:
1. product strength the performance test results of table
The high-strength glue for tile that embodiment 1~5 is prepared it can be seen from 1 test data of table its be respectively provided with it is very excellent
Different intensity, the intensity data measured after immersion, Frozen-thawed cycled, heat ageing is still more excellent, illustrates height of the present invention
Strong type glue for tile still retains good intensity under immersion, freezing and high temperature.
Secondly, it is gluing former strong that the stretching after the heat ageing of the glue for tile in each embodiment is can be seen that from experimental data
Degree is little relative to gluing former Strength Changes are stretched, and the preparation-obtained glue for tile of this explanation present invention has the excellent heat resistanceheat resistant old
Change performance.
Again, as can be seen that the intensity for the glue for tile being prepared under 1 raw material proportioning of embodiment will from experimental data
Higher than the 20%~50% of other embodiment, this explanation 1 raw material proportioning of embodiment is optimal raw material proportioning, in the institute of embodiment 1
The optimal glue for tile of strength character can be prepared under the raw material proportioning stated.
Finally, the intensity that the glue for tile that comparative example 1~3 is prepared is can be seen that from comparative example test data will be much
The glue for tile being prepared less than embodiment 1.This explanation is by ethylene-vinyl acetate copolymer, farina, modified starch ether
Reinforcing agent is used as after three's mixing, the intensity of glue for tile can be greatly improved, it is particularly possible to improve the resistance to heat aging of glue for tile
Energy.
Claims (9)
1. a kind of high-strength glue for tile, it is characterised in that include the raw material components of following parts by weight:
30~50 parts of cement;80~120 parts of quartz sand;15~25 parts of dry powder;3~8 parts of hydroxypropyl methyl cellulose;Reinforcing agent
5~10 parts.
2. high-strength glue for tile according to claim 1, it is characterised in that include the raw material components of following parts by weight:
40~50 parts of cement;80~100 parts of quartz sand;20~25 parts of dry powder;5~8 parts of hydroxypropyl methyl cellulose;Reinforcing agent
8~10 parts.
3. high-strength glue for tile according to claim 1, it is characterised in that include the raw material components of following parts by weight:
40 parts of cement;100 parts of quartz sand;20 parts of dry powder;5 parts of hydroxypropyl methyl cellulose;8 parts of reinforcing agent.
4. the high-strength glue for tile described in claim 1, it is characterised in that the quartz sand is the quartz of 100~200 mesh
Sand.
5. claim 4 any one of them high-strength glue for tile, it is characterised in that the quartz sand is the quartz of 200 mesh
Sand.
6. the high-strength glue for tile described in claim 1, it is characterised in that the reinforcing agent by following parts by weight raw material into
It is grouped into:
15~20 parts of ethylene-vinyl acetate copolymer;10~20 parts of farina;5~10 parts of modified starch ether.
7. high-strength glue for tile according to claim 6, it is characterised in that the reinforcing agent by following parts by weight original
Expect component composition:
18~20 parts of ethylene-vinyl acetate copolymer;15~18 parts of farina;8~10 parts of modified starch ether.
8. high-strength glue for tile according to claim 7, it is characterised in that the reinforcing agent by following parts by weight original
Expect component composition:
18 parts of ethylene-vinyl acetate copolymer;15 parts of farina;8 parts of modified starch ether.
9. the preparation method of claim 1~8 any one of them high-strength glue for tile, it is characterised in that comprise the following steps:
Cement, quartz sand, dry powder, hydroxypropyl methyl cellulose are uniformly mixed with the reinforcing agent up to described high-strength
Type glue for tile.