CN102492959B - 一种电解铜阳极的生产方法 - Google Patents
一种电解铜阳极的生产方法 Download PDFInfo
- Publication number
- CN102492959B CN102492959B CN201110446610.0A CN201110446610A CN102492959B CN 102492959 B CN102492959 B CN 102492959B CN 201110446610 A CN201110446610 A CN 201110446610A CN 102492959 B CN102492959 B CN 102492959B
- Authority
- CN
- China
- Prior art keywords
- copper
- production method
- content
- anode
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种电解铜阳极的生产方法,将杂铜或粗铜加热熔化成为铜水,在加热熔化过程通入空气将铜氧化形成氧化亚铜,氧化亚铜作为氧化剂将杂质氧化去除,最后加入固体还原剂除去铜水中的氧,将所述铜水中氧化亚铜的含量控制在3.5~4.5%(以质量百分含量计),优选控制在4%;所述通入空气的压力控制在1.5~2个大气压,优选控制在1.8个大气压。将铜水中的氧化亚铜控制在上述含量就能很好地去除杂质,氧化精炼后的铜经测定其铜含量在99.0~99.3%(以质量百分含量计)、且表面平整、光洁,非常适合作为电解铜阳极;同时本发明电解铜阳极生产方法的冶炼时间大大缩短、还原剂消耗下降了30~50%,带来显著的经济效益。
Description
技术领域
本发明涉及铜精炼的方法,具体涉及一种杂铜或粗铜氧化精炼的方法。
背景技术
电解铜阳极是采用粗铜或杂铜(铜含量在90%~94%,以质量百分含量计)通过精炼制得。铜氧化精炼是指将粗铜或杂铜经氧化除杂、再还原熔炼精炼铜的方法;由于杂铜、粗铜中含有S、Fe、 Pb、 Zn 、Ni、 As、 Sb、 Sn、 Bi等易氧化的杂质,这些氧化物比氧化亚铜稳定;在对杂铜或粗铜的加热熔化过程中,先鼓入压缩空气或富氧空气,将杂质以氧化物的形态在铜液表面形成炉渣,另一些少量杂质存在于铜水中,鼓入空气中的氧是先将铜氧化形成的氧化亚铜,并作为一种氧化剂再将杂质氧化去除,最后加入固体还原剂除去铜水中的氧,作为电铜阳极板供下道工序使用。在氧化精炼过程中,现有技术要求铜液含8%(以质量百分含量计)的氧化亚铜,在此状态下,杂质虽然除去完全,但下一步脱氧还原需要大量还原剂去除铜水中的氧,冶炼时间延长。
发明内容
本发明的目的在于提供一种效率高、生产成本低的电解铜阳极的生产方法。
本发明目的通过如下技术措施实现:
一种电解铜阳极的生产方法,将杂铜或粗铜加热熔化成为铜水,在加热熔化过程通入空气将铜氧化形成氧化亚铜,氧化亚铜作为氧化剂将杂质氧化去除,最后加入固体还原剂除去铜水中的氧,其特征在于:将所述铜水中氧化亚铜的含量控制在3.5~4.5%(以质量百分含量计),优选控制在4%;所述通入空气的压力控制在1.5~2个大气压,优选控制在1.8个大气压。
发明人通过长期生产实践偶然发现,对粗铜或杂铜氧化精炼过程中通入空气后,将铜水中的氧化亚铜控制在上述含量就能很好地去除杂质,氧化精炼后的铜经测定其铜含量在99.0~99.3%(以质量百分含量计)、且表面平整、光洁,非常适合作为电解铜阳极;同时本发明电解铜阳极生产方法的冶炼时间大大缩短、还原剂消耗下降了30~50%,带来显著的经济效益。
具体实施方式
以下结合实施例对本发明作进一步描述。
实施例1
一种电解铜阳极的生产方法,将杂铜或粗铜加热熔化成为铜水,在加热熔化过程通入空气将铜氧化形成氧化亚铜,氧化亚铜作为氧化剂将杂质氧化去除,最后加入固体还原剂除去铜水中的氧,将所述铜水中氧化亚铜的含量控制在4%(以质量百分含量计);所述通入空气的压力控制在1.8个大气压。
通过上述氧化精炼后的铜经测定其铜含量在99.3%(以质量百分含量计),且表面平整、光洁,非常适合作为电解铜阳极;同时冶炼时间与传统工艺相比得到了大大缩短、还原剂消耗下降了45%,带来显著的经济效益。
实施例2
一种电解铜阳极的生产方法,将杂铜或粗铜加热熔化成为铜水,在加热熔化过程通入空气将铜氧化形成氧化亚铜,氧化亚铜作为氧化剂将杂质氧化去除,最后加入固体还原剂除去铜水中的氧,将所述铜水中氧化亚铜的含量控制在3.5%(以质量百分含量计);所述通入空气的压力控制在2个大气压。
通过上述氧化精炼后的铜经测定其铜含量在99.0%(以质量百分含量计),且表面平整、光洁,非常适合作为电解铜阳极;同时冶炼时间与传统工艺相比得到了大大缩短、还原剂消耗下降了50%,带来显著的经济效益。
实施例3
一种电解铜阳极的生产方法,将杂铜或粗铜加热熔化成为铜水,在加热熔化过程通入空气将铜氧化形成氧化亚铜,氧化亚铜作为氧化剂将杂质氧化去除,最后加入固体还原剂除去铜水中的氧,将所述铜水中氧化亚铜的含量控制在4.5%(以质量百分含量计);所述通入空气的压力控制在1.5个大气压。
通过上述氧化精炼后的铜经测定其铜含量在99.2%(以质量百分含量计),且表面平整、光洁,非常适合作为电解铜阳极;同时冶炼时间与传统工艺相比得到了大大缩短、还原剂消耗下降了30%,带来显著的经济效益。
Claims (3)
1.一种电解铜阳极的生产方法,将杂铜或粗铜加热熔化成铜水,在加热熔化过程通入空气将铜氧化成氧化亚铜,氧化亚铜作为氧化剂将杂质氧化去除,最后加入固体还原剂除去铜水中的氧,其特征在于:将所述铜水中氧化亚铜的含量控制在3.5~4.5%,以质量百分含量计;所述通入空气的压力控制在1.5~2个大气压。
2.如权利要求1所述的电解铜阳极的生产方法,其特征在于:所述铜水中氧化亚铜的含量控制在4%,以质量百分含量计。
3.如权利要求1所述的电解铜阳极的生产方法,其特征在于:所述通入空气的压力控制在1.8个大气压。