CN102492959A - 一种电解铜阳极的生产方法 - Google Patents

一种电解铜阳极的生产方法 Download PDF

Info

Publication number
CN102492959A
CN102492959A CN2011104466100A CN201110446610A CN102492959A CN 102492959 A CN102492959 A CN 102492959A CN 2011104466100 A CN2011104466100 A CN 2011104466100A CN 201110446610 A CN201110446610 A CN 201110446610A CN 102492959 A CN102492959 A CN 102492959A
Authority
CN
China
Prior art keywords
copper
production method
content
controlled
cuprous oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011104466100A
Other languages
English (en)
Other versions
CN102492959B (zh
Inventor
冉隆志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Heavy Metallurgy Copper Industry Co Ltd
Original Assignee
Chongqing Heavy Metallurgy Copper Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Heavy Metallurgy Copper Industry Co Ltd filed Critical Chongqing Heavy Metallurgy Copper Industry Co Ltd
Priority to CN201110446610.0A priority Critical patent/CN102492959B/zh
Publication of CN102492959A publication Critical patent/CN102492959A/zh
Application granted granted Critical
Publication of CN102492959B publication Critical patent/CN102492959B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种电解铜阳极的生产方法，将杂铜或粗铜加热熔化成为铜水，在加热熔化过程通入空气将铜氧化形成氧化亚铜，氧化亚铜作为氧化剂将杂质氧化去除，最后加入固体还原剂除去铜水中的氧，将所述铜水中氧化亚铜的含量控制在3.5～4.5%（以质量百分含量计），优选控制在4%；所述通入空气的压力控制在1.5～2个大气压，优选控制在1.8个大气压。将铜水中的氧化亚铜控制在上述含量就能很好地去除杂质，氧化精炼后的铜经测定其铜含量在99.0～99.3%（以质量百分含量计）、且表面平整、光洁，非常适合作为电解铜阳极；同时本发明电解铜阳极生产方法的冶炼时间大大缩短、还原剂消耗下降了30～50%，带来显著的经济效益。

Description

一种电解铜阳极的生产方法
技术领域
本发明涉及铜精炼的方法，具体涉及一种杂铜或粗铜氧化精炼的方法。
背景技术
电解铜阳极是采用粗铜或杂铜（铜含量在90%～94%，以质量百分含量计）通过精炼制得。铜氧化精炼是指将粗铜或杂铜经氧化除杂、再还原熔炼精炼铜的方法；由于杂铜、粗铜中含有S、Fe、 Pb、 Zn 、Ni、 As、 Sb、 Sn、 Bi等易氧化的杂质，这些氧化物比氧化亚铜稳定；在对杂铜或粗铜的加热熔化过程中，先鼓入压缩空气或富氧空气，将杂质以氧化物的形态在铜液表面形成炉渣，另一些少量杂质存在于铜水中，鼓入空气中的氧是先将铜氧化形成的氧化亚铜，并作为一种氧化剂再将杂质氧化去除，最后加入固体还原剂除去铜水中的氧，作为电铜阳极板供下道工序使用。在氧化精炼过程中，现有技术要求铜液含8%（以质量百分含量计）的氧化亚铜，在此状态下，杂质虽然除去完全，但下一步脱氧还原需要大量还原剂去除铜水中的氧，冶炼时间延长。
发明内容     
本发明的目的在于提供一种效率高、生产成本低的电解铜阳极的生产方法。
本发明目的通过如下技术措施实现：
一种电解铜阳极的生产方法，将杂铜或粗铜加热熔化成为铜水，在加热熔化过程通入空气将铜氧化形成氧化亚铜，氧化亚铜作为氧化剂将杂质氧化去除，最后加入固体还原剂除去铜水中的氧，其特征在于：将所述铜水中氧化亚铜的含量控制在3.5～4.5%（以质量百分含量计），优选控制在4%；所述通入空气的压力控制在1.5～2个大气压，优选控制在1.8个大气压。
发明人通过长期生产实践偶然发现，对粗铜或杂铜氧化精炼过程中通入空气后，将铜水中的氧化亚铜控制在上述含量就能很好地去除杂质，氧化精炼后的铜经测定其铜含量在99.0～99.3%（以质量百分含量计）、且表面平整、光洁，非常适合作为电解铜阳极；同时本发明电解铜阳极生产方法的冶炼时间大大缩短、还原剂消耗下降了30～50%，带来显著的经济效益。
具体实施方式
以下结合实施例对本发明作进一步描述。
实施例1
一种电解铜阳极的生产方法，将杂铜或粗铜加热熔化成为铜水，在加热熔化过程通入空气将铜氧化形成氧化亚铜，氧化亚铜作为氧化剂将杂质氧化去除，最后加入固体还原剂除去铜水中的氧，将所述铜水中氧化亚铜的含量控制在4%（以质量百分含量计）；所述通入空气的压力控制在1.8个大气压。
通过上述氧化精炼后的铜经测定其铜含量在99.3%（以质量百分含量计），且表面平整、光洁，非常适合作为电解铜阳极；同时冶炼时间与传统工艺相比得到了大大缩短、还原剂消耗下降了45%，带来显著的经济效益。
实施例2
一种电解铜阳极的生产方法，将杂铜或粗铜加热熔化成为铜水，在加热熔化过程通入空气将铜氧化形成氧化亚铜，氧化亚铜作为氧化剂将杂质氧化去除，最后加入固体还原剂除去铜水中的氧，将所述铜水中氧化亚铜的含量控制在3.5%（以质量百分含量计）；所述通入空气的压力控制在2个大气压。
通过上述氧化精炼后的铜经测定其铜含量在99.0%（以质量百分含量计），且表面平整、光洁，非常适合作为电解铜阳极；同时冶炼时间与传统工艺相比得到了大大缩短、还原剂消耗下降了50%，带来显著的经济效益。
实施例3
一种电解铜阳极的生产方法，将杂铜或粗铜加热熔化成为铜水，在加热熔化过程通入空气将铜氧化形成氧化亚铜，氧化亚铜作为氧化剂将杂质氧化去除，最后加入固体还原剂除去铜水中的氧，将所述铜水中氧化亚铜的含量控制在4.5%（以质量百分含量计）；所述通入空气的压力控制在1.5个大气压。
通过上述氧化精炼后的铜经测定其铜含量在99.2%（以质量百分含量计），且表面平整、光洁，非常适合作为电解铜阳极；同时冶炼时间与传统工艺相比得到了大大缩短、还原剂消耗下降了30%，带来显著的经济效益。

Claims (2)

1.一种电解铜阳极的生产方法，将杂铜或粗铜加热熔化成为铜水，在加热熔化过程通入空气将铜氧化形成氧化亚铜，氧化亚铜作为氧化剂将杂质氧化去除，最后加入固体还原剂除去铜水中的氧，其特征在于：将所述铜水中氧化亚铜的含量控制在3.5～4.5%（以质量百分含量计），优选控制在4%；所述通入空气的压力控制在1.5～2个大气压。
2.如权利要求1所述电解铜阳极的生产方法，其特征在于：所述通入空气的压力控制在1.8个大气压。
CN201110446610.0A 2011-12-28 2011-12-28 一种电解铜阳极的生产方法 Expired - Fee Related CN102492959B (zh)