CN102432405B - 一种低密度炸药及其制备方法 - Google Patents
一种低密度炸药及其制备方法 Download PDFInfo
- Publication number
- CN102432405B CN102432405B CN 201110210789 CN201110210789A CN102432405B CN 102432405 B CN102432405 B CN 102432405B CN 201110210789 CN201110210789 CN 201110210789 CN 201110210789 A CN201110210789 A CN 201110210789A CN 102432405 B CN102432405 B CN 102432405B
- Authority
- CN
- China
- Prior art keywords
- low density
- explosive
- preparation
- density explosive
- tackiness agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种低密度炸药,属于炸药材料技术领域。所述低密度炸药由下述重量百分比的成分组成:聚黑-14传爆药55%~65%,端羟基聚丁二烯20.07%~25.81%,癸二酸二异辛酯10.33%~13.28%,甲苯二异氰酸酯1.56%~2.01%,三-(2-甲基氮丙啶)氧化膦0.38%~0.49%,二月桂酸二丁基锡0.03%,二氧化硅中空微球(HD-3)2.63%~3.38%。该低密度炸药,安全性好、强度较高,同时爆轰能力较高,爆轰性能稳定。
Description
技术领域
本发明属于炸药材料技术领域,特别涉及一种低密度炸药及其制备方法。
背景技术
低密度炸药是一种密度低、爆速低,密度一般在(0.1~1.2)g/cm3,爆速为(1500~4500)m/s的炸药。这类炸药安全性好、强度较高,常用民用采矿等方面。但同时低密度炸药的爆轰能力低,爆轰性能不稳定。
发明内容
本发明的目的是解决上述问题而提供了一种低密度炸药及其制备方法。利用该制备方法制备得到的低密度炸药,安全性好、强度较高,同时爆轰能力较高,爆轰性能稳定。
本发明所采用的技术方案是:
根据本发明的一方面,提供一种低密度炸药,由高能炸药和胶粘剂组成,所述高能炸药为聚黑-14传爆药;所述胶粘剂包括端羟基聚丁二烯、癸二酸二异辛酯、甲苯二异氰酸酯、三-(2-甲基氮丙啶)氧化膦、二月桂酸二丁基锡和二氧化硅中空微球(HD-3);所述低密度炸药由下述重量百分比的成分组成:聚黑-14传爆药55%~65%,端羟基聚丁二烯20.07%~25.81%,癸二酸二异辛酯10.33%~13.28%,甲苯二异氰酸酯1.56%~2.01%,三-(2-甲基氮丙啶)氧化膦0.38%~0.49%,二月桂酸二丁基锡0.03%,二氧化硅中空微球(HD-3)2.63%~3.38%。
聚黑-14传爆药为聚黑类传爆药,作为低密度炸药的高能炸药,不仅可以提高生产过程中的安全性,也有利于提高炸药的爆轰稳定性,同时也是国内首次将聚黑类传爆药作炸药高能炸药的应用。
二氧化硅中空微球(HD-3)为自由流动白色粉末,其堆积密度为(0.09-0.11)g/cm3,粒径十到一百微米,为内部充斥CO2等气体的封闭微型球体,具有低密度、高强度等性能,该材料的应用使炸药的密度可调。
根据本发明的另一个方面,提供一种低密度炸药的制备方法,包括以下步骤:
1)依次将端羟基聚丁二烯、癸二酸二异辛酯、甲苯二异氰酸酯、三-(2-甲基氮丙啶)氧化膦、二月桂酸二丁基锡、二氧化硅中空微球(HD-3)均匀混合,得到胶粘剂;
2)将聚黑-14传爆药加入到上述胶粘剂中,机械混合搅拌,得到混合物;
3)将上述混合物进行浇注,最后进行固化,得到所述低密度炸药。
优选地,所述机械混合搅拌在混合机中进行。
优选地,所述混合机的转速为15~20rpm,搅拌时间为15~20min。
优选地,所述固化的温度为18~30℃、湿度为40~70%,时间为48~60h。
本发明具有以下优点:
利用本发明制备得到的低密度炸药,其ρ=(1.1±0.1)g/cm3,v=(5500±500)m/s,不但具有低密度性、高安全性、较高的强度和优良的物化性能等优点外,其爆速较高,爆轰性能稳定,可同时应用于军用领域和民用采矿等方面。
具体实施方式
实施例1
本实施例提供一种低密度炸药的制备方法,包括以下步骤:1)依次将端羟基聚丁二烯、癸二酸二异辛酯、甲苯二异氰酸酯、三-(2-甲基氮丙啶)氧化膦、二月桂酸二丁基锡、二氧化硅中空微球(HD-3)均匀混合,得到胶粘剂;2)将聚黑-14传爆药加入到胶粘剂中,在混合机中进行混合搅拌,混合机的转速为15~20rpm,搅拌时间为15~20min,得到混合物;3)将混合物进行浇注,最后进行固化,固化的温度为18~30℃、湿度为40~70%,时间为48~60h。
利用制备方法制备得到实施例1的低密度炸药,该炸药中的各成分的重量百分比见表1中的炸药1。
实施例2
利用制备方法制备得到实施例2的低密度炸药,该炸药中的各成分的重量百分比见表1中的炸药2。
实施例3
利用制备方法制备得到实施例3的低密度炸药,该炸药中的各成分的重量百分比见表1中的炸药3。
实施例4
利用制备方法制备得到实施例4的低密度炸药,该炸药中的各成分的重量百分比见表1中的炸药4。
表1实施例中低密度炸药的各成分的重量百分比
通过以上实施例制备得到的低密度炸药,其ρ=(1.1+0.1)g/cm3,v=(5500±500)m/s,不但具有低密度性、高安全性、较高的强度和优良的物化性能等优点外,其爆速较高,爆轰性能稳定。
以上实施例仅用以说明本发明的技术方案而非限制,尽管参照较佳实施例对本发明进行了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的精神和范围,其均应涵盖在本发明的权利要求范围当中。
Claims (5)
1.一种低密度炸药,其特征在于,由高能炸药和胶粘剂组成,所述高能炸药为聚黑-14炸药;所述胶粘剂包括端羟基聚丁二烯、癸二酸二异辛酯、甲苯二异氰酸酯、三-(2-甲基氮丙啶)氧化膦、二月桂酸二丁基锡和二氧化硅中空微球;所述低密度炸药由下述重量百分比的成分组成:聚黑-14炸药55%~65%,端羟基聚丁二烯20.07%~25.81%,癸二酸二异辛酯10.33%~13.28%,甲苯二异氰酸酯1.56%~2.01%,三-(2-甲基氮丙啶)氧化膦0.38%~0.49%,二月桂酸二丁基锡0.03%,二氧化硅中空微球2.63%~3.38%。
2.一种权利要求1所述的低密度炸药的制备方法,其特征在于,包括以下步骤:
依次将端羟基聚丁二烯、癸二酸二异辛酯、甲苯二异氰酸酯、三-(2-甲基氮丙啶)氧化膦、二月桂酸二丁基锡、二氧化硅中空微球均匀混合,得到胶粘剂;
将聚黑-14炸药加入到上述胶粘剂中,机械混合搅拌,得到混合物;
将上述混合物进行浇注,最后进行固化,得到所述低密度炸药。
3.根据权利要求2所述的低密度炸药的制备方法,其特征在于,所述机械混合搅拌在混合机中进行。
4.根据权利要求3所述的低密度炸药的制备方法,其特征在于,所述混合机的转速为15~20rpm,搅拌时间为15~20min。
5.根据权利要求2所述低密度炸药的制备方法,其特征在于,所述固化的温度为18~30℃、湿度为40~70%,时间为48~60h。