CN102408782A - 聚丙烯塑胶用移印油墨及其制备方法和应用 - Google Patents

聚丙烯塑胶用移印油墨及其制备方法和应用 Download PDF

Info

Publication number
CN102408782A
CN102408782A CN2011102688525A CN201110268852A CN102408782A CN 102408782 A CN102408782 A CN 102408782A CN 2011102688525 A CN2011102688525 A CN 2011102688525A CN 201110268852 A CN201110268852 A CN 201110268852A CN 102408782 A CN102408782 A CN 102408782A
Authority
CN
China
Prior art keywords
transfer printing
printing ink
polypropylene plastic
pad
polypropylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102688525A
Other languages
English (en)
Other versions
CN102408782B (zh
Inventor
贺开花
吴晓斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Paint Manufacturing (shenzhen) Ltd
Original Assignee
China Paint Manufacturing (shenzhen) Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Paint Manufacturing (shenzhen) Ltd filed Critical China Paint Manufacturing (shenzhen) Ltd
Priority to CN201110268852.5A priority Critical patent/CN102408782B/zh
Publication of CN102408782A publication Critical patent/CN102408782A/zh
Application granted granted Critical
Publication of CN102408782B publication Critical patent/CN102408782B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚丙烯塑胶用移印油墨及其制备方法和应用,所述聚丙烯塑胶用移印油墨由以下组分组成:氯化聚丙烯树脂15~35%;热塑性丙烯酸树脂20~30%;聚酮树脂5~15%;填料1~2%;颜料4~20%;助剂5~10%;溶剂20~40%。该移印油墨具有干燥速度快而且稳定,色浓度高,胶体性质稳定的特点,在用于聚丙烯塑胶表面直接移印时效果较好,不需进行前处理,连续印性好,不拉丝,便于清洗,印品图案清晰,立体感强,附着力好。

Description

聚丙烯塑胶用移印油墨及其制备方法和应用
技术领域
本发明涉及一种移用油墨,尤其涉及一种聚丙烯塑胶用移印油墨及其制备方法和应用。
背景技术
目前,国内还不能在聚丙烯塑胶上直接进行移印,其原因是聚丙烯立体规则性高,易于结晶,表面极性低,采用一般油墨移印,其附着力极差。因此通常需采用络酸混合液蚀刻,表面电晕或火焰处理及等离子处理后再移印,这些前处理需大型机器设备,处理方法不安全,污染环境。
因此,现有的技术还需要进一步发展。
发明内容
本发明的目的在于提供一种连接料为氯化聚丙烯树脂及其制备方法和应用,旨在解决现有的移印油墨不能直接在聚丙烯塑胶表面上进行移印的问题。
本发明的技术方案如下:
一种聚丙烯塑胶用移印油墨,其中,所述聚丙烯塑胶用移印油墨,按重量百分比计,由以下组分组成:
氯化聚丙烯树脂15~35%;
热塑性丙烯酸树脂20~30%;
聚酮树脂5~15%;
填料1~2%;
颜料4~20%;
助剂5~10%;
溶剂20~40%。 
所述的聚丙烯塑胶用移印油墨,其中,所述氯化聚丙烯树脂含氯量为15~45%。
所述的聚丙烯塑胶用移印油墨,其中,所述填料是高硬度聚乙烯和聚四氟乙烯共聚物微细粉末蜡。
所述的聚丙烯塑胶用移印油墨,其中,所述助剂是附着力促进剂、分散剂和催干剂。
所述的聚丙烯塑胶用移印油墨,其中,所述附着力促进剂由氯化聚烯烃中的一种或多种组成;
所述分散剂由低分子量不饱和多元羧酸聚合物和聚硅氧烷共聚体的一种或多种组成;
所述催干剂由环烷酸类金属盐的一种或多种组成。
所述的聚丙烯塑胶用移印油墨,其中,所述溶剂是有机溶剂。
所述的聚丙烯塑胶用移印油墨,其中,所述溶剂是环己酮、异佛尔酮、丙二醇甲醚醋酸酯、二价酸酯、乙二醇丁醚、二甲苯等中的一种或多种组成。
上述的聚丙烯塑胶用移印油墨的制备方法,其中,所述聚丙烯塑胶用移印油墨的制备方法为:
将氯化聚丙烯树脂、热塑性丙烯酸树脂和聚酮树脂先溶解于溶剂中,再添加填料、助剂和颜料搅拌使之充分湿润,混合均匀后,研磨。
上述的聚丙烯塑胶用移印油墨的应用,其中,将所述聚丙烯塑胶用移印油墨用于聚丙烯塑胶制品的表面移印。
有益效果:本发明的聚丙烯塑胶用移印油墨具有干燥速度快而且稳定、色浓度高、胶体性质稳定的特点,用于聚丙烯塑胶制品的表面直接移印时效果较好,不需进行前处理,连续印性好,不拉丝,便于清洗,印品图案清晰,立体感强,附着力好。
具体实施方式
本发明提供一种聚丙烯塑胶用移印油墨,为使本发明的目的、技术方案及效果更加清楚、明确,以下对本发明进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
本发明所提供的聚丙烯塑胶用移印油墨,是一种以氯化聚丙烯树、热塑性丙烯酸树脂和聚酮树脂为连接料的、不需表面处理就可直接在聚丙烯塑胶表面移印的油墨。所述聚丙烯塑胶用移印油墨按重量百分比计,由以下组分组成:
氯化聚丙烯树脂15~35%;
热塑性丙烯酸树脂20~30%;
聚酮树脂5~15%;
填料1~2%;
颜料4~20%;
助剂5~10%;
溶剂20~40%。
所述氯化聚丙烯树脂含氯量为15~45%。所述填料为高硬度聚乙烯和聚四氟乙烯共聚物微细粉末蜡,细度一般为9~10微米,其作用是提高油墨的表面滑爽性,使印品表面光滑。
所述颜料是由一种或多种的无机颜料或有机颜料组成,如钛白粉、炭黑、酞青蓝、酞青绿、联苯胺黄等。
    所述助剂为附着力促进剂、分散剂和催干剂。催干剂可以是环烷酸类金属盐中的一种或多种组成,例如环烷酸钴。附着力促进剂可以是氯化聚烯烃中的一种或多种组成。分散剂可以是低分子量不饱和多元羧酸聚合物和聚硅氧烷共聚体的溶液中的一种或多种组成。
所述溶剂为有机溶剂,主要是用于溶解氯化聚丙烯树脂、热塑性丙烯酸树脂及聚酮树脂,所述溶剂可以是环己酮、异佛尔酮、丙二醇甲醚醋酸酯、二价酸酯、乙二醇丁醚、二甲苯等中的一种或多种组成。
本发明还提供所述聚丙烯塑胶移印油墨的制备方法:
将氯化聚丙烯树脂、热塑性丙烯酸树脂和聚酮树脂先溶解于溶剂中,再依次添加填料、催干剂、附着力促进剂、颜料和分散剂搅拌使之充分湿润,混合均匀后上三辊机研磨至细度合格,即制成聚丙烯塑胶移印油墨。
本发明的聚丙烯塑胶用移印油墨干燥速度快而且稳定、色浓度高、胶体性质稳定,满足了移印油墨所要具备的要求,适合用于移印。本发明聚丙烯塑胶移印油墨可广泛用于聚丙烯塑胶制品的表面直接移印,而不需进行前处理,连续印性好,不拉丝,便于清洗,印品图案清晰,立体感强,附着力好。
实施例1:
            氯化聚丙烯树脂                    15KG
            热塑性丙烯酸树脂                  15KG
            聚酮树脂                           5KG
            微细粉末蜡                        1.5KG
            环烷酸钴                         0.05KG
            氯化聚烯烃                        8.5KG
            钛白粉                             32KG
            环己酮                             12KG
            二价酸酯                           5KG
            乙二醇丁醚                       5.75KG
            多元羧酸聚合物                    0.2KG
将氯化聚丙烯树脂、热塑性丙烯酸树脂和聚酮树脂先溶解于环己酮、,二价酸酯和乙二醇丁醚中,再依次添加微细粉末蜡、环烷酸钴、氯化聚烯烃、钛白粉和多元羧酸聚合物搅拌使之充分湿润,混合均匀后上三辊机研磨至细度合格,即制成聚丙烯塑胶移印油墨,其印品性能如表1所述。
实施例2:
         氯化聚丙烯树脂                    20KG
         热塑性丙烯酸树脂                  20KG
         聚酮树脂                           7KG
         微细粉末蜡                        1.5KG
         环烷酸钴                         0.05KG
         氯化聚烯烃                        8.5KG
         炭黑                              7.5KG
         环己酮                            20KG
         二价酸酯                          10KG
         乙二醇丁醚                       4.65KG
         多元羧酸聚合物                    0.8KG
其制备方法同实施例1,印品性能如表1所述。
表1印品性能测试结果:
项目 实施例1 实施例2
1.光泽 >85(60度光泽器) >85(60度光泽器)
2.附着力(划百格) ≤0 ≤0
3.遮盖力 良好 良好
4.耐磨性 良好 良好
5.耐洗涤性 良好 良好
6.硬度 F-H(三菱铅笔) F-H(三菱铅笔)
7.环境测试 良好 良好
注:1.用光泽计测试。
2.参照BS3900:E6测试标准。
3.目视判定能否遮盖细微的划痕等。
4.压强1KG/CM,距离50CM,白纱布擦拭30次
5. 2%洗衣粉溶液浸渍24小时。
6.参照ASTMD3363测试标准。
7.耐高温70℃,2小时,耐低温-20℃,2小时,耐潮湿50℃,湿度95%,48小时(电子工业部)。

Claims (9)

1.一种聚丙烯塑胶用移印油墨,其特征在于,所述聚丙烯塑胶用移印油墨,按重量百分比计,由以下组分组成:
氯化聚丙烯树脂15~35%;
热塑性丙烯酸树脂20~30%;
聚酮树脂5~15%;
填料1~2%;
颜料4~20%;
助剂5~10%;
溶剂20~40%。
2.根据权利要求1所述的聚丙烯塑胶用移印油墨,其特征在于,所述氯化聚丙烯树脂含氯量为15~45%。
3.根据权利要求1所述的聚丙烯塑胶用移印油墨,其特征在于,所述填料是高硬度聚乙烯和聚四氟乙烯共聚物微细粉末蜡。
4.根据权利要求1所述的聚丙烯塑胶用移印油墨,其特征在于,所述助剂是附着力促进剂、分散剂和催干剂。
5.根据权利要求4所述的聚丙烯塑胶用移印油墨,其特征在于,所述附着力促进剂由氯化聚烯烃中的一种或多种组成;
所述分散剂由低分子量不饱和多元羧酸聚合物和聚硅氧烷共聚体的一种或多种组成;
所述催干剂由环烷酸类金属盐的一种或多种组成。
6.根据权利要求1所述的聚丙烯塑胶用移印油墨,其特征在于,所述溶剂是有机溶剂。
7.根据权利要求1所述的聚丙烯塑胶用移印油墨,其特征在于,所述溶剂是环己酮、异佛尔酮、丙二醇甲醚醋酸酯、二价酸酯、乙二醇丁醚、二甲苯等中的一种或多种组成。
8.一种如权利要求1所述的聚丙烯塑胶用移印油墨的制备方法,其特征在于,所述聚丙烯塑胶用移印油墨的制备方法为:
将氯化聚丙烯树脂、热塑性丙烯酸树脂和聚酮树脂先溶解于溶剂中,再添加填料、助剂和颜料搅拌使之充分湿润,混合均匀后,研磨。
9.一种如权利要求1所述的聚丙烯塑胶用移印油墨的应用,其特征在于,将所述聚丙烯塑胶用移印油墨用于聚丙烯塑胶制品的表面移印。
CN201110268852.5A 2011-09-13 2011-09-13 聚丙烯塑胶用移印油墨及其制备方法和应用 Active CN102408782B (zh)