CN102382477B - 电容器灌封蜡 - Google Patents
电容器灌封蜡 Download PDFInfo
- Publication number
- CN102382477B CN102382477B CN2011103297162A CN201110329716A CN102382477B CN 102382477 B CN102382477 B CN 102382477B CN 2011103297162 A CN2011103297162 A CN 2011103297162A CN 201110329716 A CN201110329716 A CN 201110329716A CN 102382477 B CN102382477 B CN 102382477B
- Authority
- CN
- China
- Prior art keywords
- wax
- parts
- embedding
- film capacitor
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供了一种金属化膜电容器灌封蜡,由下列组分组成，各组分的重量份为：石油蜡40-60、聚异丁烯10-15、凡士林20-30、硫磺10-15、秸秆灰烬3-5、凹凸棒土10-15。本发明的金属化膜电容器灌封蜡具有良好的韧塑性、优良的电性能、适宜的运动粘度，方便填充金属化膜电容器间隙。
Description
技术领域
本发明涉及电容器灌封材料领域，具体涉及一种防金属化膜电容器灌封蜡。
背景技术
金属化膜电容器生产中，主介质以及极板与主介质之间的孔隙通常是用一种材料进行灌封，以提高电容量和绝缘性能，并改善局部放电和耐热性能。单纯使用商品石蜡或微晶蜡，存在韧塑性差低温下易脆裂并且有较大收缩等缺陷，使用油类存在损耗大并易于渗漏，不适应当前生产厂的要求。现有专利介绍金属化膜电容器灌封材料均以油类为主要成分，如JP03035513专利介绍采用聚丁烯—烷基苯—棉籽油混合物灌封，US 6,280,659用植物油灌封电容器。
发明内容
针对现有技术的不足，本发明提供了一种适用于金属化膜电容器灌封蜡组合物。本发明的灌封蜡组合物具有韧塑性能好，低温下不会断裂，收缩不明显。
为实现上述目的本发明采用的技术方案如下：
一种金属化膜电容器灌封蜡,其特征在于，由下列组分组成，各组分的重量份为：
石油蜡， 40-60
聚异丁烯 10-15
凡士林 20-30
硫磺 10-15
秸秆灰烬 3-5
凹凸棒土 10-15。
所述的金属化膜电容器灌封蜡,其特征在于，由下列组分组成，各组分的重量份为：
石油蜡 50
聚异丁烯 13
凡士林 25
硫磺 13
秸秆灰烬 4
凹凸棒土 13。
所述的金属化膜电容器灌封蜡,其特征在于：所述的石油蜡的滴点为70-80℃。
制备方法：
本发明的灌封蜡是在约100℃～110℃的温度下，加入各种原料并混合熔融成均匀的液体，经过滤后成型。
本发明的有益效果：
本发明的灌封蜡具有电性能优良，防潮性、流动牲、耐热性和耐寒性好，无毒、无腐蚀、无杂质，具有良好的使用性能。
a)具有优良的绝缘性和防潮性，保证了金属化膜电容器电性能的稳定；
b)具有良好的液态流动性，可以充填金属化膜电容器间隙；
c)具有良好耐热性和耐寒性，在工作温度下不流淌，冷却时不脱壳；
d)无腐蚀、无杂质，不会对金属化膜电容器产生不良影响：
e)无毒，不会对生产员工的身体健康造成损害。
具体实施方式
所有实施例中用到的石油蜡，滴点均在70-80℃范围内。
实施例1：
一种金属化膜电容器灌封蜡, 由下列组分组成，各组分的重量份为：
石油蜡 40
聚异丁烯 10
凡士林 20
硫磺 10
200目秸秆灰烬 4
凹凸棒土 10 。
实施例2：
一种金属化膜电容器灌封蜡, 由下列组分组成，各组分的重量份为：
石油蜡 60
聚异丁烯 15
凡士林 30
硫磺 15
秸秆灰烬 5
凹凸棒土 15。
实施例3：
一种金属化膜电容器灌封蜡, 由下列组分组成，各组分的重量份为：
石油蜡 50
聚异丁烯 13
凡士林 25
硫磺 13
秸秆灰烬 4
凹凸棒土 13。
以上各实施例的制备方法为，在100℃～110℃的温度下，将各种原料混合熔融成均匀的液体，经过滤后成型，即可。
各实施例所制得灌封蜡的实验数据如下表：
| 实施例 | 1 | 2 | 3 |
| 体积电阻率（50°C），Ωcm | 3.41*1015 | 4.33*1015 | 5.46*1015 |
| 水分 | 无 | 无 | 无 |
| 机械杂质 | 无 | 无 | 无 |
本发明的灌封蜡滴熔点均较高，说明本发明的灌封蜡具有良好的韧塑性能，具有优良的电性能，运动粘度适宜，说明本发明的灌封蜡液态流动性能较好，便于灌封时填充金属化膜电容器间隙。
Claims (2)
1.一种金属化膜电容器灌封蜡,其特征在于，由下列组分组成，各组分的重量份为：
石油蜡，滴点为70-80℃ 40-60
聚异丁烯 10-15
凡士林 20-30
硫磺 10-15
凹凸棒土 10-15
秸秆灰烬 3-5。
2.根据权利要求1所述的金属化膜电容器灌封蜡,其特征在于，由下列组分组成，各组分的重量份为：
石油蜡 50
聚异丁烯 13
凡士林 25
硫磺 13
秸秆灰烬 4
凹凸棒土 13。