CN104292855A - 金属化膜电容器灌封料用改性剂 - Google Patents
金属化膜电容器灌封料用改性剂 Download PDFInfo
- Publication number
- CN104292855A CN104292855A CN201410494958.0A CN201410494958A CN104292855A CN 104292855 A CN104292855 A CN 104292855A CN 201410494958 A CN201410494958 A CN 201410494958A CN 104292855 A CN104292855 A CN 104292855A
- Authority
- CN
- China
- Prior art keywords
- parts
- modifying agent
- mixing
- tert
- send
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种金属化膜电容器灌封料用改性剂，涉及电容器技术领域，由以下重量份数的组分构成：再生橡胶35-45份、沥青45-55份、硅凝胶10-20份、次氯酸钙2-4份、橄榄油2-4份、叔胺2-4份、硬脂酸2-4份、聚酯胶粉2-4份、羟丙甲基纤维素2-4份、叔丁酚醛硫化树脂2-4份、氨基树脂2-4份、阳离子淀粉2-4份；本发明组分简单，成本低，无毒、无腐蚀、无杂质，具有良好的使用性能，保证了金属化膜电容器电性能的稳定，在生产过程中不会对生产员工的身体健康造成损害。
Description
技术领域
本发明涉及电容器技术领域，尤其涉及一种金属化膜电容器灌封料用改性剂。
背景技术
金属化膜电容器生产中，主介质以及极板与主介质之间的孔隙通常是用一种材料进行灌封，以提高电容量和绝缘性能，并改善局部放电和耐热性能。单纯使用商品石蜡或微晶蜡，存在韧塑性差低温下易脆裂并且有较大收缩等缺陷，使用油类存在损耗大并易于渗漏，不适应当前生产厂的要求。鉴于此，本申请提供一种加入到石蜡或微晶蜡中的改性剂，以此提高石蜡或微晶蜡的性能。
发明内容
本发明所要解决的技术问题在于提供一种成本低，性能稳定的金属化膜电容器灌封料用改性剂。
本发明所要解决的技术问题采用以下技术方案来实现：
一种金属化膜电容器灌封料用改性剂，由以下重量份数的组分构成：再生橡胶35-45份、沥青45-55份、硅凝胶10-20份、次氯酸钙2-4份、橄榄油2-4份、叔胺2-4份、硬脂酸2-4份、聚酯胶粉2-4份、羟丙甲基纤维素2-4份、叔丁酚醛硫化树脂2-4份、氨基树脂2-4份、阳离子淀粉2-4份；
各组分的较佳重量份数为：再生橡胶40份、沥青50份、硅凝胶15份、次氯酸钙3份、橄榄油3份、叔胺2份、硬脂酸3份、聚酯胶粉2份、羟丙甲基纤维素2份、叔丁酚醛硫化树脂2份、氨基树脂2份、阳离子淀粉2份；
制备方法如下：
1)将再生橡胶放入粉碎机中粉碎成颗粒，粒径小于3mm，放入熔炉与沥青混炼，在100-120℃温度下混炼30-40分钟，混炼完成后加入硅凝胶搅拌均匀，冷却后制成块状，送入冷冻设备中在零下25℃环境下冷冻40-50分钟，改变沥青性能，提高其稳定性；
2)将步骤1)中冷冻完成后的沥青块送入粉碎设备中粉碎呈颗粒，粒径小于0.1mm，然后与次氯酸钙、橄榄油、叔胺、硬脂酸、聚酯胶粉、羟丙甲基纤维素、叔丁酚醛硫化树脂、氨基树脂及阳离子淀粉混匀，送入捏合机中混炼，在80-85℃温度下热处理1小时；
3)待步骤3)中热处理后的物料再次送入熔炼，熔炼成液态，即得改性剂。
本发明的有益效果是：本发明组分简单，成本低，无毒、无腐蚀、无杂质，具有良好的使用性能，保证了金属化膜电容器电性能的稳定，在生产过程中不会对生产员工的身体健康造成损害。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
一种金属化膜电容器灌封料用改性剂，由以下重量份数的组分构成：再生橡胶35-45份、沥青45-55份、硅凝胶10-20份、次氯酸钙2-4份、橄榄油2-4份、叔胺2-4份、硬脂酸2-4份、聚酯胶粉2-4份、羟丙甲基纤维素2-4份、叔丁酚醛硫化树脂2-4份、氨基树脂2-4份、阳离子淀粉2-4份；
各组分的较佳重量份数为：再生橡胶40份、沥青50份、硅凝胶15份、次氯酸钙3份、橄榄油3份、叔胺2份、硬脂酸3份、聚酯胶粉2份、羟丙甲基纤维素2份、叔丁酚醛硫化树脂2份、氨基树脂2份、阳离子淀粉2份；
制备方法如下：
1)将再生橡胶放入粉碎机中粉碎成颗粒，粒径小于3mm，放入熔炉与沥青混炼，在100-120℃温度下混炼30-40分钟，混炼完成后加入硅凝胶搅拌均匀，冷却后制成块状，送入冷冻设备中在零下25℃环境下冷冻40-50分钟，改变沥青性能，提高其稳定性；
2)将步骤1)中冷冻完成后的沥青块送入粉碎设备中粉碎呈颗粒，粒径小于0.1mm，然后与次氯酸钙、橄榄油、叔胺、硬脂酸、聚酯胶粉、羟丙甲基纤维素、叔丁酚醛硫化树脂、氨基树脂及阳离子淀粉混匀，送入捏合机中混炼，在80-85℃温度下热处理1小时；
3)待步骤3)中热处理后的物料再次送入熔炼，熔炼成液态，即得改性剂。
本发明改性剂与石蜡或微晶蜡按体积比1:5的比例进行配置，用于电容器的灌封。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种金属化膜电容器灌封料用改性剂，其特征在于，由以下重量份数的组分构成：再生橡胶35-45份、沥青45-55份、硅凝胶10-20份、次氯酸钙2-4份、橄榄油2-4份、叔胺2-4份、硬脂酸2-4份、聚酯胶粉2-4份、羟丙甲基纤维素2-4份、叔丁酚醛硫化树脂2-4份、氨基树脂2-4份、阳离子淀粉2-4份；制备方法如下：
1)将再生橡胶放入粉碎机中粉碎成颗粒，粒径小于3mm，放入熔炉与沥青混炼，在100-120℃温度下混炼30-40分钟，混炼完成后加入硅凝胶搅拌均匀，冷却后制成块状，送入冷冻设备中在零下25℃环境下冷冻40-50分钟，改变沥青性能，提高其稳定性；
2)将步骤1)中冷冻完成后的沥青块送入粉碎设备中粉碎呈颗粒，粒径小于0.1mm，然后与次氯酸钙、橄榄油、叔胺、硬脂酸、聚酯胶粉、羟丙甲基纤维素、叔丁酚醛硫化树脂、氨基树脂及阳离子淀粉混匀，送入捏合机中混炼，在80-85℃温度下热处理1小时；
3)待步骤3)中热处理后的物料再次送入熔炼，熔炼成液态，即得改性剂。
2.根据权利要求1所述的金属化膜电容器灌封料用改性剂，其特征在于，由以下重量份数的组分构成：再生橡胶40份、沥青50份、硅凝胶15份、次氯酸钙3份、橄榄油3份、叔胺2份、硬脂酸3份、聚酯胶粉2份、羟丙甲基纤维素2份、叔丁酚醛硫化树脂2份、氨基树脂2份、阳离子淀粉2份。