CN104292750A - Igbt吸收保护电容器环氧树脂灌封剂 - Google Patents
Igbt吸收保护电容器环氧树脂灌封剂 Download PDFInfo
- Publication number
- CN104292750A CN104292750A CN201410493723.XA CN201410493723A CN104292750A CN 104292750 A CN104292750 A CN 104292750A CN 201410493723 A CN201410493723 A CN 201410493723A CN 104292750 A CN104292750 A CN 104292750A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- powder
- castor oil
- potting agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种IGBT吸收保护电容器环氧树脂灌封剂,由以下重量份数的组分构成:环氧树脂40份、氯化石蜡15份、改性蓖麻油10份、海泡石粉5份、陶瓷粉5份、石英砂5份、硅藻土5份、线性聚乙烯2份、气相法白炭黑2份、甲基硅油2份、碳酸钙2份、聚有机硅氧烷2份、硅醇盐2份、滑石粉2份;本发明组分简单,成本低,改变传统单一灌封原料,且通过对蓖麻油进行改性,使得其灌封剂具有防潮性、耐热性和耐寒性好等优点,无毒、无腐蚀,具有良好的使用性能,证了电容器电性能的稳定,在生产过程中不会对生产员工的身体健康造成损害。
Description
技术领域
本发明涉及电容器技术领域,尤其涉及一种IGBT吸收保护电容器环氧树脂灌封剂。
背景技术
电容器在电气领域应用已十分广泛,在一些大容量电力电器中所使用的电容器均为厂家的专用产品,其结构是外面为一个铝质密封壳,外壳内装有电容器芯,电容器芯为多层电介质和绝缘材料叠成,然后在每极以导线引出,在外壳和芯包之间通过环氧树脂进行灌封,以提高电容量和绝缘性能,并改善局部放电和耐热性能。单纯使用商品石蜡或微晶蜡,存在韧塑性差低温下易脆裂并且有较大收缩等缺陷,使用油类存在损耗大并易于渗漏,不适应当前生产厂的要求。
发明内容
本发明所要解决的技术问题在于提供一种成本低,性能稳定的IGBT吸收保护电容器环氧树脂灌封剂。
本发明所要解决的技术问题采用以下技术方案来实现:
一种IGBT吸收保护电容器环氧树脂灌封剂,由以下重量份数的组分构成:环氧树脂40份、氯化石蜡15份、改性蓖麻油10份、海泡石粉5份、陶瓷粉5份、石英砂5份、硅藻土5份、线性聚乙烯2份、气相法白炭黑2份、甲基硅油2份、碳酸钙2份、聚有机硅氧烷2份、硅醇盐2份、滑石粉2份;制备方法如下:
1)按上述重量比称取各组分,将海泡石粉、陶瓷粉、碳酸钙、石英砂、硅藻土及滑石粉置于研磨机中连续研磨4小时,得研磨料;
2)将步骤1)中的研磨料与环氧树脂、氯化石蜡、改性蓖麻油、线性聚乙烯、气相法白炭黑、甲基硅油、聚有机硅氧烷及硅醇盐一同置于搅拌机中,在130-200℃的温度下搅拌30分钟,让其混合均匀,制得灌封剂。
上述改性蓖麻油是由以下重量份数的组分构成:蓖麻油60份、棕榈油5份、氧化聚乙烯5份、硬脂酸2份、秸秆灰烬5份、抗氧剂2份、叔丁酚醛硫化树脂2份、大豆卵磷脂2份、印楝素2份、硫磺0.5份、阳离子淀粉5份、氯铂酸0.5份、烟草纤维素1.5份;制备方法如下:
1)按上述重量比称取各组分,将蓖麻油及棕榈油放入坩埚中加温至沸腾状态,在搅拌状态下氧化聚乙烯、硬脂酸、秸秆灰烬、抗氧剂、叔丁酚醛硫化树脂、大豆卵磷脂、印楝素、硫磺、阳离子淀粉、氯铂酸及烟草纤维素熬煮30-40分钟,呈粘稠状,然后冷却至块状;
2)将步骤1)中的块状物料送入研磨机中,在转速为150转/分的条件下,连续球磨4小时,过80目筛制得粉料;
3)取出步骤2)中研磨后的粉料,在零下3℃的环境下冷冻30分钟,进行改性处理,冷冻完成后真空包装即可。
本发明的有益效果是:本发明组分简单,成本低,改变传统单一灌封原料,且通过对蓖麻油进行改性,使得其灌封剂具有防潮性、耐热性和耐寒性好等优点,无毒、无腐蚀,具有良好的使用性能,证了电容器电性能的稳定,在生产过程中不会对生产员工的身体健康造成损害。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种IGBT吸收保护电容器环氧树脂灌封剂,由以下重量份数的组分构成:环氧树脂40份、氯化石蜡15份、改性蓖麻油10份、海泡石粉5份、陶瓷粉5份、石英砂5份、硅藻土5份、线性聚乙烯2份、气相法白炭黑2份、甲基硅油2份、碳酸钙2份、聚有机硅氧烷2份、硅醇盐2份、滑石粉2份;制备方法如下:
1)按上述重量比称取各组分,将海泡石粉、陶瓷粉、碳酸钙、石英砂、硅藻土及滑石粉置于研磨机中连续研磨4小时,得研磨料;
2)将步骤1)中的研磨料与环氧树脂、氯化石蜡、改性蓖麻油、线性聚乙烯、气相法白炭黑、甲基硅油、聚有机硅氧烷及硅醇盐一同置于搅拌机中,在130-200℃的温度下搅拌30分钟,让其混合均匀,制得灌封剂。
上述改性蓖麻油是由以下重量份数的组分构成:蓖麻油60份、棕榈油5份、氧化聚乙烯5份、硬脂酸2份、秸秆灰烬5份、抗氧剂2份、叔丁酚醛硫化树脂2份、大豆卵磷脂2份、印楝素2份、硫磺0.5份、阳离子淀粉5份、氯铂酸0.5份、烟草纤维素1.5份;制备方法如下:
1)按上述重量比称取各组分,将蓖麻油及棕榈油放入坩埚中加温至沸腾状态,在搅拌状态下氧化聚乙烯、硬脂酸、秸秆灰烬、抗氧剂、叔丁酚醛硫化树脂、大豆卵磷脂、印楝素、硫磺、阳离子淀粉、氯铂酸及烟草纤维素熬煮30-40分钟,呈粘稠状,然后冷却至块状;
2)将步骤1)中的块状物料送入研磨机中,在转速为150转/分的条件下,连续球磨4小时,过80目筛制得粉料;
3)取出步骤2)中研磨后的粉料,在零下3℃的环境下冷冻30分钟,进行改性处理,冷冻完成后真空包装即可。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种IGBT吸收保护电容器环氧树脂灌封剂,其特征在于,由以下重量份数的组分构成:环氧树脂40份、氯化石蜡15份、改性蓖麻油10份、海泡石粉5份、陶瓷粉5份、石英砂5份、硅藻土5份、线性聚乙烯2份、气相法白炭黑2份、甲基硅油2份、碳酸钙2份、聚有机硅氧烷2份、硅醇盐2份、滑石粉2份;
上述改性蓖麻油是由以下重量份数的组分构成:蓖麻油60份、棕榈油5份、氧化聚乙烯5份、硬脂酸2份、秸秆灰烬5份、抗氧剂2份、叔丁酚醛硫化树脂2份、大豆卵磷脂2份、印楝素2份、硫磺0.5份、阳离子淀粉5份、氯铂酸0.5份、烟草纤维素1.5份。
2.根据权利要求1所述的IGBT吸收保护电容器环氧树脂灌封剂,其特征在于,上述改性蓖麻油的制备方法如下:
1)按上述重量比称取各组分,将蓖麻油及棕榈油放入坩埚中加温至沸腾状态,在搅拌状态下氧化聚乙烯、硬脂酸、秸秆灰烬、抗氧剂、叔丁酚醛硫化树脂、大豆卵磷脂、印楝素、硫磺、阳离子淀粉、氯铂酸及烟草纤维素熬煮30-40分钟,呈粘稠状,然后冷却至块状;
2)将步骤1)中的块状物料送入研磨机中,在转速为150转/分的条件下,连续球磨4小时,过80目筛制得粉料;
3)取出步骤2)中研磨后的粉料,在零下3℃的环境下冷冻30分钟,进行改性处理,冷冻完成后真空包装即可。