CN102382475A - 金属化膜电容器灌封蜡 - Google Patents

金属化膜电容器灌封蜡 Download PDF

Info

Publication number
CN102382475A
CN102382475A CN201110276556XA CN201110276556A CN102382475A CN 102382475 A CN102382475 A CN 102382475A CN 201110276556X A CN201110276556X A CN 201110276556XA CN 201110276556 A CN201110276556 A CN 201110276556A CN 102382475 A CN102382475 A CN 102382475A
Authority
CN
China
Prior art keywords
wax
parts
film capacitor
metalized film
embedding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110276556XA
Other languages
English (en)
Other versions
CN102382475B (zh
Inventor
骆方旭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jiangwei Precision Manufacturing Co Ltd
Original Assignee
Anhui Jiangwei Precision Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jiangwei Precision Manufacturing Co Ltd filed Critical Anhui Jiangwei Precision Manufacturing Co Ltd
Priority to CN 201110276556 priority Critical patent/CN102382475B/zh
Publication of CN102382475A publication Critical patent/CN102382475A/zh
Application granted granted Critical
Publication of CN102382475B publication Critical patent/CN102382475B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种金属化膜电容器灌封蜡,由下列组分组成,各组分的重量份为:石油蜡40-60、聚异丁烯10-15、凡士林20-30、硫磺10-15、云母粉10-15、蛭石粉10-15。本发明的金属化膜电容器灌封蜡具有良好的韧塑性、优良的电性能、适宜的运动粘度,方便填充金属化膜电容器间隙。

Description

金属化膜电容器灌封蜡
技术领域
本发明涉及电容器灌封材料领域,具体涉及一种防金属化膜电容器灌封蜡
背景技术
金属化膜电容器生产中,主介质以及极板与主介质之间的孔隙通常是用一种材料进行灌封,以提高电容量和绝缘性能,并改善局部放电和耐热性能。单纯使用商品石蜡或微晶蜡,存在韧塑性差低温下易脆裂并且有较大收缩等缺陷,使用油类存在损耗大并易于渗漏,不适应当前生产厂的要求。现有专利介绍金属化膜电容器灌封材料均以油类为主要成分,如JP03035513专利介绍采用聚丁烯-烷基苯-棉籽油混合物灌封,US6,280,659用植物油灌封电容器。
发明内容
针对现有技术的不足,本发明提供了一种适用于金属化膜电容器灌封蜡组合物。本发明的灌封蜡组合物具有韧塑性能好,低温下不会断裂,收缩不明显。
为实现上述目的本发明采用的技术方案如下:
一种金属化膜电容器灌封蜡,其特征在于,由下列组分组成,各组分的重量份为:
Figure BDA0000092110160000011
所述的金属化膜电容器灌封蜡,其特征在于,由下列组分组成,各组分的重量份为:
Figure BDA0000092110160000012
所述的金属化膜电容器灌封蜡,其特征在于:所述的石油蜡的滴点为70-80℃。
制备方法:
本发明的灌封蜡是在约100℃~110℃的温度下,加入各种原料并混合熔融成均匀的液体,经过滤后成型。
本发明的有益效果:
本发明的灌封蜡具有电性能优良,防潮性、流动牲、耐热性和耐寒性好,无毒、无腐蚀、无杂质,具有良好的使用性能。
a)具有优良的绝缘性和防潮性,保证了金属化膜电容器电性能的稳定;
b)具有良好的液态流动性,可以充填金属化膜电容器间隙;
c)具有良好耐热性和耐寒性,在工作温度下不流淌,冷却时不脱壳;
d)无腐蚀、无杂质,不会对金属化膜电容器产生不良影响:
e)无毒,不会对生产员工的身体健康造成损害。
具体实施方式
所有实施例中用到的石油蜡,滴点均在70-80℃范围内。
实施例1:
一种金属化膜电容器灌封蜡,由下列组分组成,各组分的重量份为:
Figure BDA0000092110160000021
实施例2:
一种金属化膜电容器灌封蜡,由下列组分组成,各组分的重量份为:
Figure BDA0000092110160000031
实施例3:
一种金属化膜电容器灌封蜡,由下列组分组成,各组分的重量份为:
Figure BDA0000092110160000032
以上各实施例的制备方法为,在100℃~110℃的温度下,将各种原料混合熔融成均匀的液体,经过滤后成型,即可。
各实施例所制得灌封蜡的实验数据如下表:
本发明的灌封蜡滴熔点均较高,具有良好的韧塑性能,体积电阻率均不小于1×1015Ωcm,说明本发明的灌封蜡具有优良的电性能,运动粘度适宜,说明本发明的灌封蜡液态流动性能较好,便于灌封时填充金属化膜电容器间隙。

Claims (2)

1.一种金属化膜电容器灌封蜡,其特征在于,由下列组分组成,各组分的重量份为:
石油蜡,滴点为70-80℃  40-60
聚异丁烯  10-15
凡士林   20-30
硫磺    10-15
云母粉  10-15
蛭石粉  10-15。
2.根据权利要求1所述的金属化膜电容器灌封蜡,其特征在于,由下列组分组成,各组分的重量份为:
石油蜡    50
聚异丁烯  13
凡士林    25
硫磺      13
云母粉    13
蛭石粉    13。
CN 201110276556 2011-09-17 2011-09-17 金属化膜电容器灌封蜡 Expired - Fee Related CN102382475B (zh)