CN102341514B - 铝合金 - Google Patents
铝合金 Download PDFInfo
- Publication number
- CN102341514B CN102341514B CN201080010815.8A CN201080010815A CN102341514B CN 102341514 B CN102341514 B CN 102341514B CN 201080010815 A CN201080010815 A CN 201080010815A CN 102341514 B CN102341514 B CN 102341514B
- Authority
- CN
- China
- Prior art keywords
- weight
- highest
- max
- alloy
- aluminium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及具有良好导电性和良好热传导性,用于制造压铸件的铝合金,所述铝合金包含:8.0至9.0重量%的硅,0.5至0.7重量%的铁,最高0.010重量%的铜,最高0.010重量%的镁,最高0.010重量%的锰,最高0.001重量%的铬,最高0.020重量%的钛,最高0.020重量%的钒,最高0.05重量%的锌,0.010至0.030重量%的锶,剩余部分是铝,还有其它元素和制造条件下产生的杂质每种最高0.05重量%,共计最高0.2重量%。所述合金特别适用于在压铸方法中制造具有良好导电性和良好热传导性的部件。
Description
本发明涉及一种具有良好导电性和良好热传导性的用于制造压铸件的铝合金。
本发明的目的在于,提供一种适用于压铸的铝合金,它相对于现有技术中公知的合金来说具有改善的导电性和热传导性。
为了实现根据本发明的目的,所述合金包含:
8.0至9.0重量%的硅,
0.5至0.7重量%的铁,
最高0.010重量%的铜,
最高0.010重量%的镁,
最高0.010重量%的锰,
最高0.001重量%的铬,
最高0.020重量%的钛,
最高0.020重量%的钒,
最高0.05重量%的锌,
0.010至0.030重量%的锶,
余量为铝,以及每种最高0.05重量%、共计最高0.2重量%的其它元素和制造条件下产生的杂质。
根据本发明的合金的一个优选方案,元素锰、钛、钒和铬的总和≤0.02重量%。
根据本发明的合金的一个优选应用领域是在压铸方法中制造具有良好导电性和良好热传导性的部件,例如电子元件的散热体(冷却件)。
由下面对优选实施例的描述和根据两个比较实施例给出本发明的其它优点、技术特征和细节。
根据本发明的合金A和两个比较合金B和C具有表1中给出的组成,以660℃的熔化温度开始在压铸方法中在150℃的成型温度中浇铸成重量为2.2kg的用于电子元件的散热体。在取出压铸模之后将试样在平静的空气(ruhiger Luft)中冷却。
在两个不同的测量点M1和M2上测量压铸件的导电性。表2中总结的结果表明,根据本发明的合金A相对于比较合金B和登记的标准合金C(根据BS 1490的合金LM6,AC 47000,AlSi12(Cu))具有优越性。比较合金B与根据本发明的合金A主要通过增加的硅含量来区分。
表3中总结了根据本发明的合金A和比较合金C制成的压铸件的热传导性测量结果。根据本发明的合金A相对于比较合金C显示出高30%至40%的热传导性。
表1:合金的化学组成(重量%)
合金 | Si | Fe | Cu | Mg | Mn | Cr | Ti | V | Sr |
A | 8.66 | 0.60 | 0.006 | 0.001 | 0.005 | 0.001 | 0.008 | 0.006 | 0.012 |
B | 9.40 | 0.63 | 0.008 | 0.001 | 0.006 | 0.001 | 0.008 | 0.006 | 0.008 |
C | 10.0-13.0 | 0.6 | 0.1 | 0.10 | 0.5 | - | 0.2 | - | - |
表2:导电性
表3:热传导性
Claims (5)
1.一种具有良好导电性和良好热传导性的用于制造压铸件的铝合金,其特征在于,所述合金由如下成分组成:
8.0至9.0重量%的硅,
0.5至0.7重量%的铁,
最高0.010重量%的铜,
最高0.010重量%的镁,
最高0.010重量%的锰,
最高0.001重量%的铬,
最高0.020重量%的钛,
最高0.020重量%的钒,
0.010至0.030重量%的锶,
余量为铝,以及每种最高0.05重量%、共计最高0.2重量%的其它元素和制造条件下产生的杂质。
2.根据权利要求1的铝合金,其特征在于,元素锰、钛、钒和铬的总和≤0.02重量%。
3.根据权利要求1或2的铝合金的用途,用于通过压铸制造具有良好导电性和良好热传导性的部件。
4.根据权利要求1或2的铝合金的用途,用于电子元件的散热体。
5.由根据权利要求1或2的具有良好导电性和良好热传导性的铝合金制成的压铸件。