CN102337676A - 一种环保粘性除尘布的制备方法 - Google Patents
一种环保粘性除尘布的制备方法 Download PDFInfo
- Publication number
- CN102337676A CN102337676A CN2010102285981A CN201010228598A CN102337676A CN 102337676 A CN102337676 A CN 102337676A CN 2010102285981 A CN2010102285981 A CN 2010102285981A CN 201010228598 A CN201010228598 A CN 201010228598A CN 102337676 A CN102337676 A CN 102337676A
- Authority
- CN
- China
- Prior art keywords
- preparation
- impregnating agent
- dust removing
- glue
- removing cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环保粘性除尘布的制备方法,包括如下步骤:(1)称量物质;(2)将水置入容器内,再在室温下将胶、稀释剂、防固化剂,加湿剂混装入容器经均匀搅拌,制成浸渍剂;(3)将脱脂精漂纯棉纱布置入压力机内,再把浸渍剂均匀的泼洒入压力机,通过压辊压去多余浸渍剂,最后将浸有浸渍剂的纱布均匀的摊开置于晾晒间进行自然挥发晾晒,进而制成粘性除尘布。由于本发明所述的一种环保粘性除尘布的制备方法中所用的浸渍剂的主要成分为聚异丁烯,其对物体表面灰尘的吸附力强,除尘效果好,且没有异味对人身体无害。因此用本发明制备方法所生产的除尘布对物体、尤其是如汽车一类的金属物体表面进行处理后再喷漆,可大大提高物体的表面外观质量。
Description
技术领域
本发明涉及一种环保粘性除尘布的制备方法。
背景技术
在中国专利CN1120922A和CN2157735Y中分别公开了两种清洁用洁净巾,前者是用一定配比的化学物质配置成浸渍剂浸渍在无纺布上而制成;后者则是用一定配比的化学物质配制成药水,在将这些药水喷在绒布一类载体上而制成。在中国专利CN1118681中还公开了一种“强效重油污一擦净布的制造工艺”,它也是用一定配比的化学物质浸渍在无纺布上而制成。在中国专利CN1083963C中还公开了一种“喷漆用除尘布”,它也是把纱布浸泡在用一定配比的化学物质配制而成的化合物中,上述四个专利申请所使用的浸渍剂都是有清洗剂一类的化学物质混合而成的。用这些浸渍剂浸渍在无纺布上,对物体表面的污垢、灰尘有一定的清除作用,但是由于其不含树脂,对物体便面的灰尘无吸附作用,除尘效果差而且含苯有异味对人体伤害较大,长时间使用会导致人体不孕不育。尤其对于像汽车等有高光洁度要求的金属表面喷漆前的情节处理,起不到彻底去除灰尘的作用,致使喷漆后的金属表面仍留有灰尘痕迹,严重影响了产品的质量和美观。
发明内容
本发明的目的在于提供一种环保粘性除尘布的制备方法,用该方法制成的粘性除尘布,对物体表面的灰尘有吸附作用,并且能彻底清除物体表面的灰尘,喷漆后的产品表面光滑、无灰尘痕迹,产品质量好,尤其此发明无异味,不含有毒化学物质,对人体无害。
本发明的目的是通过以下技术方案来实现的。
一种环保粘性除尘布的制备方法,包括如下步骤:
(1)称量物质,按比例称取下列物质:
胶和稀释剂总重为1,其中胶的比例为0.4-0.6
防固化剂 0.002 加湿剂 0.002
(2)将水置入容器内,再在室温下按上述比例将胶、稀释剂、防固化剂,加湿剂混装入容器经均匀搅拌,制成浸渍剂;
(3)将脱脂精漂纯棉纱布置入压力机内,再把浸渍剂均匀的泼洒入压力机,通过压辊压去多余浸渍剂,最后将浸有浸渍剂的纱布均匀的摊开置于晾晒间进行自然挥发晾晒,进而制成粘性除尘布。
所述的胶位低分子量为6000~12000,外观为无色、无味透明胶状。
所述的溶剂是6#溶剂油或200#或120#汽油。
所述的加湿剂是二缩三乙二醇。
所述的防固化剂是三氯甲烷。
由于本发明所述的一种环保粘性除尘布的制备方法中所用的浸渍剂的主要成分为聚异丁烯,其对物体表面灰尘的吸附力强,除尘效果好,且没有异味对人身体无害。因此用本发明制备方法所生产的除尘布对物体、尤其是如汽车一类的金属物体表面进行处理后再喷漆,可大大提高物体的表面外观质量。
本发明是根据汽车生产涂装工艺要求量身定做的,我们采用和吸取美国福特汽车公司的粘性除尘布技术,并结合我国汽车生产涂装工艺的特点,经上百次的实践及配方技术的改良,研制成功多功能粘性除尘布,适用范围广,具有多功能性,可用于汽车生产涂装工艺过程中的除尘,高档家具的木面的处理,金属板面的除垢等,能缓解漆面的橘皮、缩孔等现象,增加漆面的光洁度和剥离强度,使漆面光洁、牢固,提高产品的外观质量,从而使本产品无论是除尘效果还是环保洁净方面均已达到用户满意,并且本发明所有原料均为食品级原料。
具体实施方式
在本发明中,若非特指,所有的份、量均为以总重量为基础的重量单位。
例1
先按下述配比选材料:
胶总量的0.6,加湿剂0.002,稀释剂0.4,防固化剂0.002。
然后按以上比例将胶置入容器内,再在室温下加入上述比例的稀释剂、防固化剂,加湿剂经均匀搅拌,制成浸渍剂;然后,将裁好的脱脂精漂纯棉纱布逐层置入压力机内,再把浸渍剂均匀的逐层浇淋入压力机,通过压辊根据要求压去多余浸渍剂,最后将浸有浸渍剂的纱布均匀的摊开至于晾晒间进行自然挥发晾晒,一定时间后经打包制成粘性除尘布。
在本实施例子中,胶是由聚异丁烯制成。
例2
先按下述配比选配料:
胶总量的0.4,加湿剂0.002,稀释剂0.6,防固化剂0.002。
然后按以上比例将胶置入容器内,再在室温下加入上述比例的稀释剂、防固化剂,加湿剂经均匀搅拌,制成浸渍剂;然后,将裁好的脱脂精漂纯棉纱布逐层置入压力机内,再把浸渍剂均匀的逐层浇淋入压力机,通过压辊根据要求压去多余浸渍剂,最后将浸有浸渍剂的纱布均匀的摊开置于晾晒间进行自然挥发晾晒,一定时间后经打包制成粘性除尘布。
在本实施例中,胶是由聚异丁烯制成。
例3
先按下述配比选材料:
胶总量的0.4,加湿剂0.002,稀释剂0.6,防固化剂0.002。
按以上比例将胶置入容器内,再在室温下加入上述比例的稀释剂、防固化剂,加湿剂经均匀搅拌,制成浸渍剂;然后,将裁好的脱脂精漂纯棉纱布逐层置入压力机内,再把浸渍剂均匀的逐层浇淋入压力机,通过压辊根据要求压去多余浸渍剂,最后将浸有浸渍剂的纱布均匀的摊开置于晾晒间进行自然挥发晾晒,一定时间后经打包制成粘性除尘布。
在本实施例中,胶是由聚异丁烯制成。
在实施例1、2、3中,使用的稀释剂是6#溶剂,加湿剂是二缩三乙二醇,防固化剂是三氯甲烷。
用本发明所述的制备方法制成的喷漆用除尘布,经福田汽车股份有限公司北京蒙派克汽车厂、福田汽车股份有限公司北京欧曼重卡汽车厂、福田欧V汽车有限公司、山东奥铃汽车有限公司、福田南海汽车厂等大型汽车制造厂适用,证明对灰尘的吸附力强,除尘效果明显,可大大提高产品的表面光洁度和产品质量。
本技术领域中的相关技术人员应当熟悉到,以上所述实施例仅是用来说明本发明的目的,而并非用作对本发明的限定,只要在本发明的实质范围内,对上述实施例所做的的变化、变型都将落在本发明的权利要求范围内。
Claims (5)
1.一种环保粘性除尘布的制备方法,包括如下步骤:
(1)称量物质,按比例称取下列物质:
胶和稀释剂总重为1,其中胶的比例为0.4-0.6
防固化剂0.002 加湿剂0.002
(2)将水置入容器内,再在室温下按上述比例将胶、稀释剂、防固化剂,加湿剂混装入容器经均匀搅拌,制成浸渍剂;
(3)将脱脂精漂纯棉纱布置入压力机内,在把浸渍剂均匀的泼洒入压力机,通过压辊压去多余浸渍剂,最后将浸有浸渍剂的纱布均匀的摊开置于晾晒间进行自然挥发晾晒,进而制成粘性除尘布。
2.根据权利要求1所述的一种环保粘性除尘布的制备方法,其特征在于:所述的胶位低分子量为6000~12000,外观为无色、无味透明胶状。
3.根据权利要求1所述的一种环保粘性除尘布的制备方法,其特征在于:所述的溶剂是6#溶剂油或200#或120#汽油。
4.根据权利要求1所述的一种环保粘性除尘布的制备方法,其特征在于:所述的加湿剂是二缩三乙二醇。
5.根据权利要求1所述的一种环保粘性除尘布的制备方法,其特征在于:所述的防固化剂是三氯甲烷。