CN102312243A - 一种钛及钛合金带卷酸洗方法 - Google Patents

一种钛及钛合金带卷酸洗方法 Download PDF

Info

Publication number
CN102312243A
CN102312243A CN201110183790A CN201110183790A CN102312243A CN 102312243 A CN102312243 A CN 102312243A CN 201110183790 A CN201110183790 A CN 201110183790A CN 201110183790 A CN201110183790 A CN 201110183790A CN 102312243 A CN102312243 A CN 102312243A
Authority
CN
China
Prior art keywords
titanium
acid
strip
temperature
coil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110183790A
Other languages
English (en)
Inventor
曹占元
苏鹤洲
史亚鸣
范勇斌
李志敏
张彦民
赵之华
晏合彪
施汝洪
刘昆
朱发金
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yunnan Titanium Industry Co Ltd
Original Assignee
Yunnan Titanium Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yunnan Titanium Industry Co Ltd filed Critical Yunnan Titanium Industry Co Ltd
Priority to CN201110183790A priority Critical patent/CN102312243A/zh
Publication of CN102312243A publication Critical patent/CN102312243A/zh
Pending legal-status Critical Current

Abstract

一种钛及钛合金带卷酸洗方法，本发明将钛带卷打开后引导进入清洗槽用水清洗，再引入到两个以上不同浓度的酸液槽的酸洗工艺，采用控制钛带在1m/min～20m/min的运行速度以及酸液在80～300g/L的浓度、温度在30℃～100℃来控制酸液与钛带的反应程度；钛带从最后一个酸液槽出来后，进入漂洗槽，通过向运行的钛带上表面、下表面喷淋温度40℃～80℃的水，钛带从漂洗槽出来后，采用向运行的钛带上表面、下表面喷吹温度40℃～80℃的热风，把钛带表面残留的水液烘干后收裹成卷。本发明可实现对打开长度达数百米、收裹成圆环状的钛及钛合金带卷表面的处理，而且能有效地去除钛板表面的氧化层、富氧层，减少金属损耗，能够消除了对环境的污染。

Description

一种钛及钛合金带卷酸洗方法
技术领域
本发明属于钛及钛合金带卷酸洗处理方法的技术领域。
背景技术
现有的钛及钛合金板材是以单板轧制的形式生产。其中，钛板表面氧化层和富氧层的去除是采用酸液浸泡法，即把钛及钛合金平板浸入一定浓度的酸液中，使TiO2与HF发生反应，从而去除钛板表面的氧化层、富氧层。酸液浸泡法去除氧化层、富氧层，一是不能实现打开长度数百米、收裹成圆环状的钛及钛合金带卷的处理；二是酸液与钛带的反应程度难以控制，金属损耗大；三是无法实现反应过程的全密封，环境污染严重。
发明内容
本发明的目的就是为了解决酸液浸泡法不能处理钛及钛合金带卷表面氧化层、富氧层的问题，提供一种高效、环境友好、金属损耗小的钛及钛合金带卷酸洗法。
本发明的目的是通过如下技术方案实现的：
一种钛及钛合金带卷酸洗方法，本发明将钛带卷打开后被引导进入清洗槽用水清洗，然后从清洗槽出来的钛带在运行中引入到设置的酸洗工艺环节；该酸洗工艺环节包括两个以上不同浓度的酸液槽，将钛带依次通过所有的酸液槽，通过控制钛带的运行速度以及酸液的浓度、温度来控制酸液与钛带的反应程度；钛带的运行速度在1m/min～20m/min范围内调节、混合酸液的浓度在80～300g/L范围内调节、温度在30℃～100℃范围内调节；钛带从最后一个酸液槽出来后进入漂洗槽，采用设置的喷淋装置向运行的钛带上表面、下表面喷淋温度30℃～80℃的水，把钛带表面残留的酸液清洗干净；钛带从漂洗槽出来后，通过设置的喷吹装置向运行的钛带上表面、下表面喷吹温度40℃～80℃的热风，把钛带表面残留的水液烘干后收裹成卷。
本发明的有益效果是,采用本发明的方法处理钛及钛合金带卷表面氧化层、富氧层，不仅可以实现对打开长度达数百米、收裹成圆环状的钛及钛合金带卷表面的处理，而且能更准确地控制钛带与酸液的反应程度，有效地去除钛板表面的氧化层、富氧层，减少金属损耗，基本消除了对环境的污染。
具体实施方式
一种钛及钛合金带卷酸洗方法，本发明将钛带卷打开后被引导进入清洗槽用水清洗，然后从清洗槽出来的钛带在运行中被引入到设置的酸洗工艺环节；该酸洗工艺环节包括两个以上不同浓度的酸液槽，将钛带依次通过所有的酸液槽，通过控制钛带的运行速度以及酸液的浓度、温度来控制酸液与钛带的反应程度；钛带的运行速度在1m/min～20m/min范围内调节、混合酸液的浓度在80～300g/L范围内调节、温度在30℃～100℃范围内调节；钛带从最后一个酸液槽出来后进入漂洗槽，通过设置的喷淋装置向运行的钛带上表面、下表面喷淋温度40℃～80℃的水，把钛带表面残留的酸液清洗干净；钛带从漂洗槽出来后，采用设置的喷吹装置向运行的钛带上表面、下表面喷吹温度40℃～80℃的热风，把钛带表面残留的水液烘干后进入到下一工序。
实施例1：本发明将钛带卷打开后被引导进入清洗槽用水清洗，然后从清洗槽出来的钛带在运行中被引入到设置的酸洗工艺环节；该酸洗工艺环节包括两个以上不同浓度的酸液槽，将钛带依次通过所有的酸液槽，通过控制钛带的运行速度以及酸液的浓度、温度来控制酸液与钛带的反应程度；钛带的运行速度在1m/min范围内调节、混合酸液的浓度在80g/L范围内调节、温度在30℃范围内调节；钛带从最后一个酸液槽出来后进入漂洗槽，通过设置的喷淋装置向运行的钛带上表面、下表面喷淋温度40℃的水，把钛带表面残留的酸液清洗干净；钛带从漂洗槽出来后，采用设置的喷吹装置向运行的钛带上表面、下表面喷吹温度40℃的热风，把钛带表面残留的水液烘干后进入到下一工序。
实施例2：一种钛及钛合金带卷酸洗方法，本发明将钛带卷打开后被引导进入清洗槽用水清洗，然后从清洗槽出来的钛带在运行中被引入到设置的酸洗工艺环节；该酸洗工艺环节包括两个以上不同浓度的酸液槽，将钛带依次通过所有的酸液槽，通过控制钛带的运行速度以及酸液的浓度、温度来控制酸液与钛带的反应程度；钛带的运行速度在20m/min范围内调节、混合酸液的浓度在300g/L范围内调节、温度在100℃范围内调节；钛带从最后一个酸液槽出来后进入漂洗槽，通过设置的喷淋装置向运行的钛带上表面、下表面喷淋温度80℃的水，把钛带表面残留的酸液清洗干净；钛带从漂洗槽出来后，采用设置的喷吹装置向运行的钛带上表面、下表面喷吹温度80℃的热风，把钛带表面残留的水液烘干后进入到下一工序。
实施例3：一种钛及钛合金带卷酸洗方法，本发明将钛带卷打开后被引导进入清洗槽用水清洗，然后从清洗槽出来的钛带在运行中被引入到设置的酸洗工艺环节；该酸洗工艺环节包括两个以上不同浓度的酸液槽，将钛带依次通过所有的酸液槽，通过控制钛带的运行速度以及酸液的浓度、温度来控制酸液与钛带的反应程度；钛带的运行速度在10m/min范围内调节、混合酸液的浓度在190g/L范围内调节、温度在65℃范围内调节；钛带从最后一个酸液槽出来后进入漂洗槽，通过设置的喷淋装置向运行的钛带上表面、下表面喷淋温度60℃的水，把钛带表面残留的酸液清洗干净；钛带从漂洗槽出来后，采用设置的喷吹装置向运行的钛带上表面、下表面喷吹温度60℃的热风，把钛带表面残留的水液烘干后进入到下一工序。

Claims (1)

1.一种钛及钛合金带卷酸洗方法，其特征是，将钛带卷打开后引导进入清洗槽用水清洗，再将从清洗槽出来的钛带在运行中引入到设置的酸洗工艺环节，该酸洗工艺环节包括两个以上不同浓度的酸液槽，将钛带依次通过所有的酸液槽，采用控制钛带的运行速度以及酸液的浓度、温度来控制酸液与钛带的反应程度；钛带的运行速度在1m/min～20m/min范围内调节、混合酸液的浓度在80～300g/L范围内调节、温度在30℃～100℃范围内调节；钛带从最后一个酸液槽出来后，进入漂洗槽，通过设置的喷淋装置向运行的钛带上表面、下表面喷淋温度40℃～80℃的水，把钛带表面残留的酸液清洗干净；钛带从漂洗槽出来后，采用设置的喷吹装置向运行的钛带上表面、下表面喷吹温度40℃～80℃的热风，把钛带表面残留的水液烘干后收裹成卷。
CN201110183790A 2011-07-01 2011-07-01 一种钛及钛合金带卷酸洗方法 Pending CN102312243A (zh)