CN102560513A - 一种钢丝表面处理工艺 - Google Patents

一种钢丝表面处理工艺 Download PDF

Info

Publication number
CN102560513A
CN102560513A CN201210030823XA CN201210030823A CN102560513A CN 102560513 A CN102560513 A CN 102560513A CN 201210030823X A CN201210030823X A CN 201210030823XA CN 201210030823 A CN201210030823 A CN 201210030823A CN 102560513 A CN102560513 A CN 102560513A
Authority
CN
China
Prior art keywords
steel wire
pickling
surface treatment
carried out
treatment process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210030823XA
Other languages
English (en)
Inventor
玛琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzuki Garphyttan Wire Suzhou Co Ltd
Original Assignee
Suzuki Garphyttan Wire Suzhou Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzuki Garphyttan Wire Suzhou Co Ltd filed Critical Suzuki Garphyttan Wire Suzhou Co Ltd
Priority to CN201210030823XA priority Critical patent/CN102560513A/zh
Publication of CN102560513A publication Critical patent/CN102560513A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种钢丝表面处理工艺，其特征在于：该工艺依次包括如下步骤：（一）对半成品的钢丝进行酸洗，酸洗时间为5-10分钟；（二）采用纯水对酸洗后的钢丝进行清洗；（三）对清洗后的钢丝进行中和处理；（四）对中和处理后的钢丝进行二次清洗；（五）磷化处理，并在磷化池中添加催化剂；（六）进行二次中和处理；（七）干燥。本发明效率高、无污染，钢丝表面均匀度较好。

Description

一种钢丝表面处理工艺
技术领域
本发明涉及一种表面处理工艺，尤其涉及一种钢丝表面处理工艺。
背景技术
钢丝是钢材的板、管、型、丝四大品种之一，是用热轧盘条经冷拉制成的再加工产品 ，在钢丝的生产过程中为提高钢丝的品质，通常会对钢丝进行表面处理，以大幅提升钢丝的机械性能，从而满足各种机械零件和工具的不同使用需求。
但是，传统的钢丝表面处理工艺还存在效率低、钢丝表面均匀度差，污染大的缺陷与问题。
发明内容
本发明所要解决的技术问题是提供一种效率高、无污染，钢丝表面均匀度较好的钢丝表面处理工艺。
为解决上述技术问题，本发明提供一种钢丝表面处理工艺，该工艺依次包括如下步骤：
（一）对半成品的钢丝进行酸洗，酸洗时间为5-10分钟；
（二）采用纯水对酸洗后的钢丝进行清洗；
（三）对清洗后的钢丝进行中和处理；
（四）对中和处理后的钢丝进行二次清洗；
（五）磷化处理，并在磷化池中添加催化剂；
（六）进行二次中和处理；
（七）干燥。
所述步骤一中的酸洗时间为6分钟。
所述步骤二和所述步骤四中采用喷淋的方式对酸洗后的钢丝进行清洗。
所述步骤七中采用热吹风的方式对钢丝进行干。
与现有技术相比，本发明的有益效果为：
由于本发明的一种钢丝表面处理工艺将钢丝酸洗和磷化在同一生产线上不间断的连续完成，所以有效的提高了生产效率，同时采用酸洗池和磷化池的方式对钢丝进行酸洗和磷化，酸洗液和磷化液在酸洗池和磷化池内均不易挥发，所以对环境无污染，此外在酸洗后对钢丝进行中和处理，从而可以有效提高磷化质量，因此本发明效率高、无污染，钢丝表面均匀度较好。
具体实施方式
以下结合具体实施方式对本发明做进一步详细说明
一种钢丝表面处理工艺，该工艺依次包括如下步骤：
（一）对半成品的钢丝进行酸洗，酸洗时间为5-10分钟；
（二）采用纯水并通过喷淋的方式对酸洗后的钢丝进行清洗；
（三）对清洗后的钢丝进行中和处理；
（四）对中和处理后的钢丝进行二次清洗，同样采用纯水并通过喷淋的方式进行清洗；
（五）磷化处理，并在磷化池中添加催化剂，优选该催化剂可为任何公知的磷化工艺中所使用的催化剂；
（六）进行二次中和处理；
（七）干燥，优选在用热吹风的方式对钢丝进行干燥。
以上工艺中将钢丝酸洗和磷化在同一生产线上不间断的连续完成，所以有效的提高了生产效率，同时采用酸洗池和磷化池的方式对钢丝进行酸洗和磷化，避免了采用雾化的方式易污染环境的缺陷，所以本发明的工艺对环境无污染，此外在酸洗后对钢丝进行中和处理，可以有效提高磷化质量，从而提高钢丝表面均匀度较好。
实施例1：
  一种钢丝表面处理工艺，该工艺依次包括如下步骤：
（一）对半成品的钢丝进行酸洗，酸洗时间为6分钟；
（二）采用纯水并通过喷淋的方式对酸洗后的钢丝进行清洗；
（三）对清洗后的钢丝进行中和处理；
（四）对中和处理后的钢丝采用纯水并通过喷淋的方式进行二次清洗；
（五）磷化处理，并在磷化池中添加公知的磷化工艺中所使用的催化剂；
（六）进行二次中和处理；
（七）采用热吹风的方式对钢丝进行干燥。 
实施例2：
一种钢丝表面处理工艺，该工艺依次包括如下步骤：
（一）对半成品的钢丝进行酸洗，酸洗时间为5分钟；
（二）采用纯水并通过喷淋的方式对酸洗后的钢丝进行清洗；
（三）对清洗后的钢丝进行中和处理；
（四）对中和处理后的钢丝采用纯水并通过喷淋的方式进行二次清洗；
（五）磷化处理，并在磷化池中添加公知的磷化工艺中所使用的催化剂；
（六）进行二次中和处理；
（七）采用热吹风的方式对钢丝进行干燥。
实施例3：
一种钢丝表面处理工艺，该工艺依次包括如下步骤：
（一）对半成品的钢丝进行酸洗，酸洗时间为10分钟；
（二）采用纯水并通过喷淋的方式对酸洗后的钢丝进行清洗；
（三）对清洗后的钢丝进行中和处理；
（四）对中和处理后的钢丝采用纯水并通过喷淋的方式进行二次清洗；
（五）磷化处理，并在磷化池中添加公知的磷化工艺中所使用的催化剂；
（六）进行二次中和处理；
（七）采用热吹风的方式对钢丝进行干燥。
以上实施例仅为本发明其中的一种实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。

Claims (4)

1.一种钢丝表面处理工艺，其特征在于：该工艺依次包括如下步骤：
（一）对半成品的钢丝进行酸洗，酸洗时间为5-10分钟；
（二）采用纯水对酸洗后的钢丝进行清洗；
（三）对清洗后的钢丝进行中和处理；
（四）对中和处理后的钢丝进行二次清洗；
（五）磷化处理，并在磷化池中添加催化剂；
（六）进行二次中和处理；
（七）干燥。
2.根据权利要求1所述的一种钢丝表面处理工艺，其特征在于：所述步骤一中的酸洗时间为6分钟。
3.根据权利要求1所述的一种钢丝表面处理工艺，其特征在于：所述步骤二和所述步骤四中采用喷淋的方式对酸洗后的钢丝进行清洗。
4.根据权利要求1所述的一种钢丝表面处理工艺，其特征在于：所述步骤七中采用热吹风的方式对钢丝进行干燥。
CN201210030823XA 2012-02-13 2012-02-13 一种钢丝表面处理工艺 Pending CN102560513A (zh)