CN102241397A - 冷等静压石墨制造方法 - Google Patents
冷等静压石墨制造方法 Download PDFInfo
- Publication number
- CN102241397A CN102241397A CN2011101247205A CN201110124720A CN102241397A CN 102241397 A CN102241397 A CN 102241397A CN 2011101247205 A CN2011101247205 A CN 2011101247205A CN 201110124720 A CN201110124720 A CN 201110124720A CN 102241397 A CN102241397 A CN 102241397A
- Authority
- CN
- China
- Prior art keywords
- days
- powder
- press
- temperature
- heats
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种冷等静压石墨制造方法，一次焙烧：300℃以下升温用三天，每班升温50℃，温度达到300℃后保温；300℃～600℃升温用五天，每班升温20℃。600℃以上升温六天，每班升温50℃，温度升到1100℃后停止升温，保温6天后一次焙烧结束，一次焙烧过程用时20天；一次浸渍，浸渍采用液态沥青，浸渍时间为4个小时；大大缩短生产周期，提高产品的强度、密度及其它各项理化性能。
Description
技术领域
本发明涉及一种冷等静压石墨制造方法，尤其是一种缩短了生产周期，简化了工艺，提高了产品性能的石墨制造方法，属于石墨制造技术领域。
背景技术
传统等静压石墨生产工艺都是采用经过高温2000℃到3000℃煅烧后的石油焦，其真比重2.06g/cm3，经过多次浸渍、多次焙烧、石墨化后制得的石墨产品，生产周期一般是6～8个月，强度在30～35MPa，比重1.7g/cm3～1.75g/cm3。
发明内容
本发明所要解决的技术问题是针对现有技术的不足提供一种缩短了生产周期，简化了工艺，提高了产品性能的石墨制造方法，采用如下技术方案：
一种冷等静压石墨制造方法，配料后进行压粉成型，之后进行一次焙烧：300℃以下升温用三天，每班升温50℃，温度达到300℃后保温；300℃～600℃升温用五天，每班升温20℃，温度达到600℃后保温；600℃以上升温六天，每班升温50℃，温度升到1100℃后停止升温，保温6天后一次焙烧结束，一次焙烧过程用时20天；一次浸渍：浸渍采用液态沥青，浸渍时间为4个小时；石墨化：石墨化炉3天均匀升温达到2000℃，压力控制在-0.05MPa(气氛是一氧化碳)。
所述的冷等静压石墨制造方法，所述配料：采用经过1500℃～1600℃煅烧处理的生石油焦，经过初碎后，进入磨粉机，进行磨料，磨粉后的颗粒经过1200目的筛网，通过率在90％以上为合格粉料；按重量比7∶4的比例分别称量120℃高温沥青粉和合格料粉送入混合机混料，混料完毕等待压粉成型。
所述的冷等静压石墨制造方法，所述压粉成型：压粉采用冷等静压机压制成型，压制过程中压力保持在80兆帕，压制时间为40分钟，温度在控制在20℃。
本发明采用较低温度处理过后的生焦，经初次粉碎，用提升机提到备料仓内，采用磨粉机进行磨料，颗粒经过筛选进入储料仓，然后与120℃高温沥青混合，混合合格后进行压制，压制好的产品进行一次焙烧，一次焙烧结束后采用卧式浸渍缸进行一次浸渍，浸渍完成后经石墨化制得最终产品。大大缩短生产周期，提高产品的强度、密度及其它各项理化性能。
具体实施方式
以下结合具体实施例，对本发明进行详细说明。
将经过1500℃～1600℃处理的生石油焦(真比重可达1.6g/cm3)，首先在颚式破碎机中进行初碎，用斗式提升机提升到备料仓内，由备料仓进入磨粉机，进行磨料，磨粉后的颗粒经过1200目的筛网，通过率在90％以上为合格粉料，按重量比7∶4的比例分别称量120℃高温沥青粉和合格料粉送入混合机混料，混料完毕等待压粉。
压粉成型：压粉采用冷等静压机压制成型，压制过程中压力保持在80兆帕，压制时间为40分钟，温度在控制在20℃，成型后比重应达到1.4g/cm3。
一次焙烧：300℃以下升温用三天，每班(每班八小时，一天三班，下同)升温50℃，温度达到300℃后保温。300℃～600℃升温用五天，每班升温20℃，600℃以上升温六天，每班升温50℃，温度升到1100℃后停止升温，保温6天后一次焙烧结束。整个一次焙烧过程时间为20天。经过一次焙烧比重达到1.7g/cm3。
一次浸渍：浸渍采用的是常规液态沥青，浸渍时间为4个小时，经过一次浸渍后比重达到1.8g/cm3。
石墨化：石墨化炉3天均匀升温达到2000℃，压力控制在-0.05MPa(气氛是一氧化碳)，石墨化后比重可达到1.9g/cm3。
以上整个过程与传统等静压石墨生产工艺相比缩短了4-5个月周期。质量标准达到了传统三浸四焙的要求，各项理化指标见表1所示。
表1等静压技术性能及各项理化指标
应当理解的是，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，而所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (3)
1.一种冷等静压石墨制造方法，其特征在于，配料后进行压粉成型，之后进行一次焙烧：300℃以下升温用三天，每班升温50℃，温度达到300℃后保温；300℃～600℃升温用五天，每班升温20℃；600℃以上升温六天，每班升温50℃，温度升到1100℃后停止升温，保温6天后一次焙烧结束，一次焙烧过程用时20天；一次浸渍：浸渍采用液态沥青，浸渍时间为4个小时；石墨化：石墨化炉3天均匀升温达到2000℃，压力控制在-0.05MPa。
2.根据权利要求1所述的冷等静压石墨制造方法，其特征在于，所述配料：采用经过1500℃～1600℃煅烧处理的生石油焦，经过初碎后，进入磨粉机，进行磨料，磨粉后的颗粒经过1200目的筛网，通过率在90％以上为合格粉料；按重量比7∶4的比例分别称量120℃高温沥青粉和合格料粉送入混合机混料，混料完毕等待压粉成型。
3.根据权利要求1所述的冷等静压石墨制造方法，其特征在于，所述压粉成型：压粉采用冷等静压机压制成型，压制过程中压力保持在80兆帕，压制时间为40分钟，温度在控制在20℃。