CN102234349B - Wdx-3树脂的制备方法 - Google Patents
Wdx-3树脂的制备方法 Download PDFInfo
- Publication number
- CN102234349B CN102234349B CN2011100996362A CN201110099636A CN102234349B CN 102234349 B CN102234349 B CN 102234349B CN 2011100996362 A CN2011100996362 A CN 2011100996362A CN 201110099636 A CN201110099636 A CN 201110099636A CN 102234349 B CN102234349 B CN 102234349B
- Authority
- CN
- China
- Prior art keywords
- hours
- temperature
- wdx
- resin
- gasoline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种WDX-3树脂的制备方法,主要是以苯乙烯、二乙烯苯、汽油为主要原料,经过合理配比及特殊的工艺步骤制备出WDX-3树脂。
Description
技术领域
本发明涉及离子交换树脂的制备工艺,具体地说,是一种WDX-3树脂的制备方法。
背景技术
交换树脂主要用于纯水、高纯水制备、废水处理、生化制品提取、稀有金属提取、湿法冶金中钨、钼、钒等的提取,具有机械强度好、耐热性高等特点。
发明内容
本发明目的在于提供一种WDX-3树脂的制备方法。
本发明目的是通过如下技术手段实现的:
1、投料量:苯乙烯279kg,二乙烯苯321kg,200#汽油480kg。
2、操作步骤:
(1)按规定配好水相,升温至45℃,充分搅拌20分钟;
(2)停止搅拌,将混合好的单体加入开机搅拌,视粒度情况调好转速;
(3)以5℃~6℃/10min的升温速率升温至75℃保温定型,并保持温度2小时;
(4)在10分钟内将温度升高至80℃,保温3小时,然后在半小时内将温度升高至95℃,保温6小时;
(5)用热水洗净至水清澈为止;
(6)用蒸汽吹尽汽油,烘干;
(7)烘干后白球用甲醇在40℃搅拌浸泡3小时,回收甲醇后大量水洗;
(8)抽干,包装。
具体实施方式
下面结合实施例对本发明进一步描述,但并非用以限定本发明。
实施例1:
按照如下方法制备WDX-3树脂:
1、投料量:苯乙烯279kg,二乙烯苯321kg,200#汽油480kg。
2、操作步骤:
(1)按规定配好水相,升温至45℃,充分搅拌20分钟;
(2)停止搅拌,将混合好的单体加入开机搅拌,视粒度情况调好转速;
(3)以5℃~6℃/10min的升温速率升温至75℃保温定型,并保持温度2小时;
(4)在10分钟内将温度升高至80℃,保温3小时,然后在半小时内将温度升高至95℃,保温6小时;
(5)用热水洗净至水清澈为止;
(6)用蒸汽吹尽汽油,烘干;
(7)烘干后白球用甲醇在40℃搅拌浸泡3小时,回收甲醇后大量水洗;
(8)抽干,包装。
Claims (1)
1.一种WDX-3树脂的制备方法,其特征在于,包括如下步骤:
(1)投料量:苯乙烯279kg,二乙烯苯321kg,200#汽油480kg;
(2)操作步骤:
①按规定配好水相,升温至45℃,充分搅拌20分钟;
②停止搅拌,将混合好的单体加入开机搅拌,视粒度情况调好转速;
③以5℃~6℃/10min的升温速率升温至75℃保温定型,并保持温度2小时;
④在10分钟内将温度升高至80℃,保温3小时,然后在半小时内将温度升高至95℃,保温6小时;
⑤用热水洗净至水清澈为止;
⑥用蒸汽吹尽汽油,烘干;
⑦烘干后白球用甲醇在40℃搅拌浸泡3小时,回收甲醇后大量水洗;
⑧抽干,包装。