CN102212648A - 一种lf精炼炉钢包渣线砌筑方法 - Google Patents
一种lf精炼炉钢包渣线砌筑方法 Download PDFInfo
- Publication number
- CN102212648A CN102212648A CN2011101147813A CN201110114781A CN102212648A CN 102212648 A CN102212648 A CN 102212648A CN 2011101147813 A CN2011101147813 A CN 2011101147813A CN 201110114781 A CN201110114781 A CN 201110114781A CN 102212648 A CN102212648 A CN 102212648A
- Authority
- CN
- China
- Prior art keywords
- layer
- building
- stones
- laying bricks
- ladle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种LF精炼炉钢包渣线砌筑方法，属于冶金技术领域，它包括下述步骤：(1)包壁打结好后，将包壁的上表面清理干净，磨平；(2)铺一层刚玉泥料；(3)砌筑渣线，即将耐火砖面紧靠永久衬竖立砌筑，在砌筑第一层耐火砖的过程中，根据预先计算好的两种规格的耐火砖的位置砌筑两种规格的耐火砖，耐火砖之间互相靠紧砌筑；(4)砌筑好一层后，开始砌筑第二层，砌筑第二层时要与第一层的砖缝错开，砌筑方法重复步骤(3)。本发明砌筑简单，节省砌筑时间，砌筑时背缝无需填充料，砌筑后整个渣线为一个平面，外表面光滑平整，没有错台，抗渣浸蚀能力强。
Description
技术领域
本发明属于冶金技术领域，具体涉及一种LF精炼炉钢包渣线砌筑方法。
背景技术
LF钢包精炼炉一般使用浇注料作为包底和包壁，渣线使用镁碳砖或者镁铝碳砖，渣线砌筑时一般采用两种方法砌筑过：一是万能弧的砖型，每块砖水平互相紧靠砌筑，采用此方法砌筑的LF钢包精炼炉渣线平缝多，熔渣易进入缝隙，渣线寿命低。二是楔形砖型使用平砌的方法，用楔形砖水平围砌而成，相邻耐火砖层之间用泥料找平，每层耐火砖层使用两到三种不同型号的耐火砖。砌筑时与LF钢包精炼炉工作衬砖与包壁永久衬的接触面有一定的空隙，需用填充料填好，捣实。这样砌筑出来的渣线层从外面看，每层之间有不等的错台，背缝处需用填充料填充。这种方法砌筑的LF钢包精炼炉，外形有交错的台阶，遇到钢水冲刷很容易被浸蚀掉，横缝较多，钢水和钢渣易进入缝隙，造成钢包在使用过程中损坏加快。另外后背缝因有缝隙用填充料填充，在使用过程中，受到过冷、过热或者外力作用，有发生掉砖的现象，使用寿命短。
发明内容
本发明提供一种LF精炼炉钢包渣线砌筑方法，其目的是可以砌筑出使用寿命长的LF精炼炉钢包渣线。
本发明采用两种规格的耐火砖，即砖1尺寸（mm）a×b×c1／c2／c3／c4为180×140×108／92／107／91；砖2尺寸（mm）a×b×c1／c2／c3／c4为180×140×103／97／102／96。砖1、砖2均为上下两面是等腰梯形，前后两面是长方形，左右两面是等腰梯形。
一种LF精炼炉钢包渣线砌筑方法，包括下述步骤：
1、包壁打结好后，将包壁的上表面清理干净，磨平；
2、铺一层刚玉泥料；
3、砌筑渣线，即将耐火砖面紧靠永久衬竖立砌筑，在砌筑第一层耐火砖的过程中，根据预先计算好的两种规格的耐火砖的位置砌筑两种规格的耐火砖，耐火砖之间互相靠紧砌筑；
4、砌筑好一层后，开始砌筑第二层，砌筑第二层时要与第一层的砖缝错开，砌筑方法重复步骤3。
砌筑好后每环耐火砖层无需用耐火泥找平，渣线的后背缝也不用任何填充料，其操作简单。由于第二层的底部与第一层的上部接触，且砖有与钢包高度方向一致的倾斜度，所以采用本发明砌筑出来的渣线表面平整，光滑，没有阶梯，能够紧靠钢包壁永久衬。砌筑完成后整个渣线在一个平面，在使用过程中抗渣侵蚀。
本发明的耐火砖的角度与钢包渣线壁的角度一致，也就是说每块耐火砖立式砌起来的倾斜度与钢包高度方向的倾斜度一致，砌筑时背缝能直接靠紧永久衬，不用任何填充料，更安全，牢固。
本发明砌筑的80吨LF钢包精炼炉钢包渣线寿命由15次提高至30次，使用寿命提高了一倍。
附图说明：
图1是本发明的砌筑砖的结构图。
具体实施方式：
实施例：本实施例采用的砖的尺寸有两种：即砖1尺寸（mm）a×b×c1／c2／c3／c4为180×140×108／92／107／91；砖2尺寸（mm）a×b×c1／c2／c3／c4为180×140×103／97／102／96。
本实施例为80吨LF精炼炉钢包，其砌筑步骤为：1、包底和包壁用刚玉浇注料打结，渣线用上述规格的镁碳砖砌筑；
2、包壁打结好并烘烤后，将包壁的上表面清理干净，磨平；
3、铺一层刚玉泥料；
4、根据LF钢包精炼炉钢包的规格，设计其所需要两种规格的砖即砖1和砖2的数量及位置，即每砌多少块砖1需要多少块砖2；
5、将砖1紧靠永久衬竖立砌筑，然后根据预先计算好的位置砌入砖2，要求每块砖互相靠紧砌筑，砌筑完毕一环；
6、砌筑第二层，砌筑第二层时要与第一层的砖缝错开，第二层采用步骤5的方法砌筑，依次类推，砌筑第三层、第四层、第五层、第六层、第七层。
本实施例每一层所用砖1为30--40 块，所用砖2为40-50 块。
Claims (4)
1.一种LF精炼炉钢包渣线砌筑方法，其特征是包括下述步骤：
（1）、包壁打结好后，将包壁的上表面清理干净，磨平；
（2）、铺一层刚玉泥料；
（3）、砌筑渣线，即将耐火砖面紧靠永久衬竖立砌筑，在砌筑第一层耐火砖的过程中，根据预先计算好的两种规格的耐火砖的位置砌筑两种规格的耐火砖，耐火砖之间互相靠紧砌筑；
（4）、砌筑好一层后，开始砌筑第二层，砌筑第二层时要与第一层的砖缝错开，砌筑方法重复步骤（3）。
2. 根据权利要求1所述的一种LF精炼炉钢包渣线砌筑方法，其特征是所述的耐火砖为上下两面是等腰梯形，前后两面是长方形，左右两面是等腰梯形。
3.根据权利要求2所述的一种LF精炼炉钢包渣线砌筑方法，其特征是所述的耐火砖为两种规格，其中一种规格为a×b×c1／c2／c3／c4=180 mm×140 mm×108 mm／92 mm／107 mm／91 mm；另一种规格为a×b×c1／c2／c3／c4=180 mm×140 mm×103 mm／97 mm／102 mm／96 mm。
4.根据权利要求1所述的一种LF精炼炉钢包渣线砌筑方法，其特征是所述的每层耐火砖砌筑的渣线均由两种不同规格的耐火砖组成。