CN102167975A - 一种红外防伪发光材料及其制备方法和应用 - Google Patents

一种红外防伪发光材料及其制备方法和应用 Download PDF

Info

Publication number
CN102167975A
CN102167975A CN2011100437452A CN201110043745A CN102167975A CN 102167975 A CN102167975 A CN 102167975A CN 2011100437452 A CN2011100437452 A CN 2011100437452A CN 201110043745 A CN201110043745 A CN 201110043745A CN 102167975 A CN102167975 A CN 102167975A
Authority
CN
China
Prior art keywords
infrared
counterfeiting
false
luminescent material
znaf
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100437452A
Other languages
English (en)
Inventor
姚瑞刚
陈进
周斌
钱伟民
姚瑞琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU CITY DELI ANTI-COUNTERFEITING MATERIAL Co Ltd
Original Assignee
BENGBU CITY DELI ANTI-COUNTERFEITING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU CITY DELI ANTI-COUNTERFEITING MATERIAL Co Ltd filed Critical BENGBU CITY DELI ANTI-COUNTERFEITING MATERIAL Co Ltd
Priority to CN2011100437452A priority Critical patent/CN102167975A/zh
Publication of CN102167975A publication Critical patent/CN102167975A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种红外防伪发光材料，是通过常规的稀土氟化物制备方法获得，其化学表达式为：NaY1-x-yYbxEryF4·zNaF；其中0.12≤x≤0.20，0.001≤y≤0.01，0.1≤z≤2摩尔。该材料在780-1060nm的红外光照射下，显示出耀眼的绿色或者红色可见光，并且这种材料的物理稳定性极好，是制作防伪产品的特种原料，尤其是制造红外防伪油墨、防伪印油和防伪涂料的理想防伪颜料。

Description

一种红外防伪发光材料及其制备方法和应用
技术领域
本发明属于防伪技术用特种材料领域，具体是一种红外防伪发光材料及其制备方法和应用
背景技术
目前，随着科学技术的不断发展，人们对应用于产品上的防伪技术要求越来越高，由于原来使用的紫外防伪及其制造方法已经是公知技术，所以防伪效果大大的降低，这就需要新的防伪材料来进行替代。
发明内容
本发明所要解决的技术问题就是提供一种红外防伪发光材料，其化学表达式为：
NaY1-x-yYbxEryF4·zNaF。
所述红外防伪发光材料在780-1060nm的红外光照射下，显示出耀眼的绿色和红色可见光，并且这种材料的物理稳定性极好，是制作防伪产品的特种原料，尤其是制造防伪油墨、防伪印油和防伪涂料的理想防伪颜料。
本发明中红外防伪发光材料的化学表达式为：
NaY1-x-yYbxEryF4·zNaF，其中0.12≤x≤0.20，0.001≤y≤0.01，0.1≤z≤2摩尔。
其在制备时，按NaY1-x-yYbxEryF4·zNaF的化学表达式，用稀土氟化物按照常规方法制备而成，将所述稀土氟化物放入电子高温炉中，条件为真空(0.5个大气压)或者常压空气下，赔烘温度为1260-1360℃，赔烘时间大于10小时，然后粉碎研磨，过280-380目的筛，即得到红外粉末材料，然后在780-1060nm的红外光激发下，发射538-548nm的可见绿光或者640-660nm的可见红光。
本发明的有益效果是按照上述方法得到的红外防伪发光材料，制造方法简单，成本较低，其物理稳定性极好，是制作防伪产品的特种原料，尤其是可以应用于制造红外防伪油墨、防伪印油和防伪涂料，使用含量为总重量5-35％。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1：按化学表达式NaY1-x-yYbxEryF4·zNaF，用稀土氟化物常规制备方法制取，在电子高温炉中，条件为真空(0.5个大气压)下，赔烘1260℃烧结12小时，然后粉碎研磨，过280-380目的筛，即可得到的红外粉末材料，在780-1060nm的红外光激发下，发射538-548nm的可见绿光。
实施例2：按化学表达式NaY1-x-yYbxEryF4·zNaF，用稀土氟化物常规制备方法制取，在电子高温炉中，条件为常压空气下，赔烘1360℃烧结13小时，然后粉碎研磨，过280-380目的筛，即可得到的红外粉末材料，在780-1060nm的红外光激发下，发射640-660nm的可见红光。
实施例3：用实施例1制得的红外发光粉末重量30％，采用市场可购买的胶印调墨油重量70％，用三辊研磨机研磨即可得到红外防伪油墨。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (4)

1.一种红外防伪发光材料，其特征在于：化学表达式为：
NaY1-x-yYbxEryF4·zNaF。
2.根据权利要求1所述红外防伪发光材料，其特征在于：
化学表达式NaY1-x-yYbxEryF4·zNaF，其中0.12≤x≤0.20，0.001≤y≤0.01，0.1≤z≤2摩尔。
3.根据权利要求1所述NaY1-x-yYbxEryF4·zNaF红外防伪发光材料的制备方法，其特征在于；用稀土氟化物按照常规方法制备而成，将所述稀土氟化物放入电子高温炉中，条件为真空或者常压空气下，赔烘温度为1260-1360℃，赔烘时间大于10小时，然后粉碎研磨，过280-380目的筛，即得到红外粉末材料，在780-1060nm的红外光激发下，发射538-548nm的可见绿光或者640-660nm的可见红光。
4.根据权利要求3所述红外防伪发光材料的制备方法，其特征在于：所述红外防伪发光材料主要应用于制造红外防伪油墨、防伪印油和防伪涂料，使用含量为总重量5-35％。
CN2011100437452A 2011-02-23 2011-02-23 一种红外防伪发光材料及其制备方法和应用 Pending CN102167975A (zh)