CN102162188A - 一种阻燃棉织物整理方法 - Google Patents

一种阻燃棉织物整理方法 Download PDF

Info

Publication number
CN102162188A
CN102162188A CN 201110003390 CN201110003390A CN102162188A CN 102162188 A CN102162188 A CN 102162188A CN 201110003390 CN201110003390 CN 201110003390 CN 201110003390 A CN201110003390 A CN 201110003390A CN 102162188 A CN102162188 A CN 102162188A
Authority
CN
China
Prior art keywords
cotton fabric
flame
liquid
proof cotton
sorting according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110003390
Other languages
English (en)
Inventor
赵玉芬
叶勇
鞠志宇
邹如意
王乐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhengzhou University
Original Assignee
Zhengzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhengzhou University filed Critical Zhengzhou University
Priority to CN 201110003390 priority Critical patent/CN102162188A/zh
Publication of CN102162188A publication Critical patent/CN102162188A/zh
Pending legal-status Critical Current

Abstract

本发明公开了阻燃棉织物整理方法，包括以下步骤：(1)使用退浆液进行退浆处理；(2)使用阻燃整理液进行浸浴；(3)压轧处理；(4)烘干；(5)将烘干的棉织物放入蒸馏水中，用酸调节pH；(6)分别进行皂洗和水洗；(7)压轧并烘干。由于该工艺未使用多羟甲基三聚氰氨交联剂，大大降低了甲醛的释放量。同时该工艺不需要焙烘流程，不仅符合国家的节能减排政策，而且对织物性能如白度、手感、力学等性能影响也显著改善。本阻燃整理工艺流程短、操作条件比较温和、安全可靠，阻燃整理效果优良。

Description

一种阻燃棉织物整理方法
技术领域
本发明是阻燃棉织物整理新方法，属于阻燃棉织物整理工艺改进领域。
背景技术
用于棉、麻、粘胶等纤维素纤维的耐久阻燃整理剂，目前主要是含磷、氮、卤素类的化合物，常用的prohan、pyrovatex、Fyrol-76等工艺。由于在纤维素纤维上获得耐久性的方式均依赖于N-羟基反应体系，特别是为提高阻燃织物的耐洗性，需加入较多量的交联剂多羟甲基三聚氰氨树脂，造成织物上的游离甲醛质量分数较高，因此，游离甲醛问题不可避免。近来，新的环保要求和法规不断被世界各国执行，另外，传统阻燃整理工艺需要高温焙烘，对织物的白度、手感和力学等性能有很大影响。传统的加工方式受到挑战，开发新型无甲醛阻燃剂及其阻燃整理工艺成为当务之急。
发明内容
本发明使用含磷、氮类化合物MDPPA为阻燃剂。使用二氯丙烷为交联剂，目的降低甲醛的释放量，改善阻燃整理后织物的白度、手感和力学等性能。本发明的目的通过如下途径实现：
阻燃棉织物整理方法，包含以下步骤：(1)使用退浆液进行退浆处理；(2)使用阻燃整理液进行浸浴；(3)压轧处理；(4)烘干；(5)将烘干的棉织物放入蒸馏水中，用酸调节pH；(6)分别进行皂洗和水洗；(7)压轧并烘干。
所述的阻燃棉织物整理方法，步骤(1)：退浆液配方为1000mL水中含有2g氯胺T、3g石油磺酸钠、3g烧碱和0.1g硫酸铜；退浆液用量为：按照10g织物需300mL-400mL退浆液的比例，将织物放入退浆液中煮沸10分钟左右取出，再用清水漂洗至洗净。
所述的阻燃棉织物整理方法，步骤(2)中阻燃整理液配方为：水∶MDPPA∶碱∶渗透剂＝80∶20∶18∶0.2(质量比)，其中所述碱采用无机强碱NaOH；所述渗透剂为JFC。
所述的阻燃棉织物整理方法，步骤(2)中浸浴方法为：将棉织物放入所述阻燃整理液中，然后滴加一定量的二氯丙醇，缓慢加热到80-90℃反应0.5-1小时；其中二氯丙烷为1，2-二氯丙烷或1，3-二氯丙烷，用量为每100份溶液中加入13-15份二氯丙烷。
所述的阻燃棉织物整理方法，步骤(3)中压轧为一次压轧，轧余率70-75％。
所述的阻燃棉织物整理方法，步骤(4)中烘干，烘干温度为80-90℃，烘5-8分钟。
所述的阻燃棉织物整理方法，步骤(5)中调节pH使用的酸为无机酸盐酸或磷酸，pH调至6-8。
所述的阻燃棉织物整理方法，步骤(6)中：皂洗步骤中，采用的皂洗液为：每1000g水需皂粉3g；皂洗条件为在35-45℃，洗涤3分钟。
所述的阻燃棉织物整理方法，步骤(6)中水洗条件为：在35-45℃，在蒸馏水中洗涤3分钟。
所述的阻燃棉织物整理方法，步骤(7)中所述压轧的轧余率50％；所述烘干，在90-100℃，直到烘干。
整理液中的无机碱、阻燃剂、交联剂和渗透剂均可以回收重新利用。
采用本发明的方法整理的织物，经过耐久阻燃性能测试，符合国家二级阻燃织物标准，耐洗次数30次以上，白度为86％，撕破强力保留率为75％和较好的手感。
本发明的阻燃棉织物整理工艺流程符合国家节能减排政策，阻燃整理工艺流程短、操作条件比较温和、安全可靠，产品阻燃效果和产品质量都有显著提高。因此，本发明的技术方案与现有技术相比有突出的实用、节约和环保等特点。
附图说明
图1为本发明技术路线图；
具体实施方式
实施例1
退浆液配制：退浆液配方为1000mL水中含有2g氯胺T、3g石油磺酸钠、3g烧碱和0.1g硫酸铜.
实施例2
整理液配制；水∶N-羟甲基-3-二甲氧磷酰基丙酰胺(简称MDPPA)∶碱∶渗透剂＝80∶20∶18∶0.2(质量比)，其中所述碱采用无机强碱NaOH；所述渗透剂为脂肪醇聚氧乙烯醚(简称JFC。
实施例3.
(1)、按照10g浆纱需300mL-400mL退浆液，将织物放入锅中煮沸10分钟左右取出，再用清水漂洗至洗净。
(2)、在100份整理液中放入40份棉织物，然后滴加13-15份的1，3-二氯丙醇，缓慢加热到80-90℃反应0.5-1小时。
(3)、然后用镊子夹出棉织物，一次压轧，轧余率70-75％。接着在80-90℃，烘5-8分钟。
(4)、将烘干的棉织物放入蒸馏水中然后用5％的磷酸调节pH为6-8，然后用镊子夹出放入100份的皂洗液和蒸馏水中，保持温度在35-45℃，分别洗涤3分钟。
(5)、压轧，轧余率50％，在90-100℃，直到烘干。
经过耐久阻燃性能测试符合国家二级阻燃织物标准，耐洗次数35次以上，白度为86％，撕破强力保留率为70％和较好的手感。
实施例4.
与实施例3区别在于(4)中用5％的盐酸调节pH。
经过耐久阻燃性能测试符合国家二级阻燃织物标准，耐洗次数32次以上，白度为82％，撕破强力保留率为68％和较好的手感。
实施例5.
与实施例3区别在于(2)中用1，2-二氯丙醇做交联剂。
经过耐久阻燃性能测试符合国家二级阻燃织物标准，耐洗次数34次以上，白度为85％，撕破强力保留率为72％和较好的手感。
实施例6.
与实施例5区别在于(4)中用5％的盐酸调节pH。
经过耐久阻燃性能测试符合国家二级阻燃织物标准，耐洗次数31次以上，白度为81％，撕破强力保留率为69％和较好的手感。
应当理解的是，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，而所有这些改进和变换都应属于本发明所附权利要求的保护范围。

Claims (10)

1.阻燃棉织物整理方法，其特征在于，包括以下步骤：(1)使用退浆液进行退浆处理；(2)使用阻燃整理液进行浸浴；(3)压轧处理；(4)烘干；(5)将烘干的棉织物放入蒸馏水中，用酸调节pH；(6)分别进行皂洗和水洗；(7)压轧并烘干。
2.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(1)：退浆液配方为1000mL水中含有2g氯胺T、3g石油磺酸钠、3g烧碱和0.1g硫酸铜；退浆液用量为：按照10g织物需300mL-400mL退浆液的比例，将织物放入退浆液中煮沸10分钟左右取出，再用清水漂洗至洗净。
3.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(2)中阻燃整理液配方为：水∶MDPPA∶碱∶渗透剂＝80∶20∶18∶0.2(质量比)，其中所述碱采用无机强碱NaOH；所述渗透剂为JFC。
4.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(2)中浸浴方法为：将棉织物放入所述阻燃整理液中，然后滴加一定量的二氯丙醇，缓慢加热到80-90℃反应0.5-1小时；其中二氯丙烷为1，2-二氯丙烷或1，3-二氯丙烷，用量为每100份溶液中加入13-15份二氯丙烷。
5.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(3)中压轧为一次压轧，轧余率70-75％。
6.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(4)中烘干，烘干温度为80-90℃，烘5-8分钟。
7.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(5)中调节pH使用的酸为无机酸盐酸或磷酸，pH调至6-8。
8.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(6)中：皂洗步骤中，采用的皂洗液为：每1000g水需皂粉3g；皂洗条件为在35-45℃，洗涤3分钟。
9.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(6)中水洗条件为：在35-45℃，在蒸馏水中洗涤3分钟。
10.根据权利要求1所述的阻燃棉织物整理方法，其特征在于，步骤(7)中所述压轧的轧余率50％；所述烘干，在90-100℃，直到烘干。
CN 201110003390 2011-01-10 2011-01-10 一种阻燃棉织物整理方法 Pending CN102162188A (zh)