CN102127300A - 一种氟硅橡胶改性硅橡胶耐油配制原料 - Google Patents

一种氟硅橡胶改性硅橡胶耐油配制原料 Download PDF

Info

Publication number
CN102127300A
CN102127300A CN2011100063844A CN201110006384A CN102127300A CN 102127300 A CN102127300 A CN 102127300A CN 2011100063844 A CN2011100063844 A CN 2011100063844A CN 201110006384 A CN201110006384 A CN 201110006384A CN 102127300 A CN102127300 A CN 102127300A
Authority
CN
China
Prior art keywords
silicone rubber
parts
oil
raw material
silicon rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100063844A
Other languages
English (en)
Inventor
张磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG MEICHEN SCIENCE AND TECHNOLOGY CO LTD
Original Assignee
SHANDONG MEICHEN SCIENCE AND TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG MEICHEN SCIENCE AND TECHNOLOGY CO LTD filed Critical SHANDONG MEICHEN SCIENCE AND TECHNOLOGY CO LTD
Priority to CN2011100063844A priority Critical patent/CN102127300A/zh
Publication of CN102127300A publication Critical patent/CN102127300A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种氟硅橡胶改性硅橡胶耐油配制原料，其特征按质量份如下，甲基乙烯基硅橡胶，50～90；甲基乙烯基三氟丙基硅橡胶，10～50；气相法白炭黑，30～40；高活性氧化镁，1～3；AN-3，0.5～2.5；二甲基二甲氧基硅烷，2～5；硅藻土，50～90；钛白粉，40～80；2，5-二甲基-2，5-二叔丁基过氧化己烷，0.5～1.2。本发明的实施有效提高了硅橡胶的耐油性能，耐ASTM 3#油(150℃*70h)体积变化率不大于15％，该配方可部分取代氟硅橡胶用于耐油场合。

Description

一种氟硅橡胶改性硅橡胶耐油配制原料
技术领域
本发明属于橡胶技术领域，特别涉及的是一种甲基乙烯基三氟丙基硅橡胶(氟硅橡胶)改性耐油硅橡胶配制原料。
背景技术
硅橡胶由于其特殊的分子结构，决定了其具有优异的耐高低温性、耐臭氧性、耐化学侵蚀性及电气性能，因此，硅橡胶在国民经济的各个方面，尤其是在汽车行业得到了广泛的应用。但由于硅橡胶本身对非极性油抗耐性不佳，这就大大限制了硅橡胶的应用范围，并且随着人们环保意识的提高，对汽车排放、燃油渗透等都提出了越来越高的要求，传统的硅橡胶已难以满足这些要求。一些厂家使用氟硅橡胶代替硅橡胶用于一些耐油的场合，但由于氟硅橡胶价格昂贵，难以推广使用。在某些场合，如汽车涡轮增压器胶管，一些厂家采用硅胶管内衬氟硅橡胶的复合结构，但由于氟硅橡胶与硅橡胶粘合困难，这种复合结构胶管需要使用复杂的工艺方能实现。
发明内容
本发明的目的在于提供一种耐油硅橡胶配制原料，其具体的技术方案如下：
用量以质量份计，甲基乙烯基硅橡胶，50～90；甲基乙烯基三氟丙基硅橡胶，10～50；气相法白炭黑，30～40；高活性氧化镁，1～3；AN-3，0.5～2.5；二甲基二甲氧基硅烷，2～5；硅藻土，50～90；钛白粉，40～80；2，5-二甲基-2，5-二叔丁基过氧化己烷，0.5～1.2。
本发明在甲基乙烯基硅橡胶配方中引入了甲基乙烯基三氟丙基硅橡胶(氟硅橡胶)，由于甲基乙烯基硅橡胶与氟硅橡胶的主链相同，二者极易通过共混形成均相胶料，氟硅橡胶侧链上的三氟丙基，可有效阻止非极性溶剂对共混胶料的侵蚀，从而实现了氟硅橡胶对硅橡胶的改性，提高了硅橡胶的耐油性能。气相法白炭黑、硅藻土等无机补强剂的加入，可有效改善硅橡胶在非极性溶剂中的溶胀程度，在一定程度上也有利于硅橡胶耐油性能的提高.AN-3是美国道康宁公司生产的一种硅橡胶助剂，它能有效提高硅橡胶的耐高温油性能。
本发明的实施有效提高了硅橡胶的耐油性能，耐ASTM 3#油(150℃*70h)体积变化率不大于15％，该配方可部分取代氟硅橡胶用于耐油场合；同时，由于胶料中同时含有硅橡胶与氟硅橡胶成分，该配方与硅胶及该配方与氟硅胶的粘合强度均不小于1.2KN/m，因此，对于耐油要求较高，必须使用氟硅橡胶的场合，该配方可以作为氟硅橡胶与硅橡胶的中间层，将两者粘合到一起，形成氟硅橡胶与硅橡胶复合结构。
具体实施方式
实施例1
用量以质量份计：
  序号   组分   用量/份
  1   甲基乙烯基硅橡胶   50
  2   甲基乙烯基三氟丙基硅橡胶   50
  3   气相法白炭黑   40
  4   高活性氧化镁   3
  5   AN-3   2.5
  6   二甲基二甲氧基硅烷   4
  7   硅藻土   75
  8   钛白粉   75
  9   2，5-二甲基-2，5-二叔丁基过氧化己   0.9
耐油性能：
耐ASTM 3#油(150℃*70h)体积变化率    9.3％
耐燃料C(23℃*70h)体积变化率         3.8％
粘合强度：
与硅橡胶粘合强度                    1.94KN/m
与氟硅胶粘合强度                    1.75KN/m
实施例2
用量以质量份计：
  序号   组分   用量/份
  1   甲基乙烯基硅橡胶   60
  2   甲基乙烯基三氟丙基硅橡胶   40
  3   气相法白炭黑   30
  4   高活性氧化镁   3
  5   AN-3   1.5
  6   二甲基二甲氧基硅烷   3
  7   硅藻土   70
  8   钛白粉   75
  9   2，5-二甲基-2，5-二叔丁基过氧化己   0.7
耐油性能：
耐ASTM 3#油(150℃*70h)体积变化率    12.3％
耐燃料C(23℃*70h)体积变化率         4.6％
粘合强度：
与硅橡胶粘合强度                    2.77KN/m
与氟硅胶粘合强度                    1.60KN/m
实施例3
用量以质量份计：
  序号   组分   用量/份
  1   甲基乙烯基硅橡胶   70
  2   甲基乙烯基三氟丙基硅橡胶   30
  3   气相法白炭黑   35
  4   高活性氧化镁   2.5
  5   AN-3   1.3
  6   二甲基二甲氧基硅烷   2.5
  7   硅藻土   60
  8   钛白粉   80
  9   2，5-二甲基-2，5-二叔丁基过氧化己   1.0
耐油性能：
耐ASTM 3#油(150℃*70h)体积变化率    13.2％
耐燃料C(23℃*70h)体积变化率         5.8％
粘合强度：
与硅橡胶粘合强度                    2.89KN/m
与氟硅胶粘合强度                    1.53KN/m
实施例4
用量以质量份计：
  序号   组分   用量/份
  1   甲基乙烯基硅橡胶   90
  2   甲基乙烯基三氟丙基硅橡胶   10
  3   气相法白炭黑   40
  4   高活性氧化镁   3
  5   AN-3   2.5
  6   二甲基二甲氧基硅烷   2.5
  7   硅藻土   75
  8   钛白粉   75
  9   2，5-二甲基-2，5-二叔丁基过氧化己   1.2
耐油性能：
耐ASTM 3#油(150℃*70h)体积变化率    14.3％
耐燃料C(23℃*70h)体积变化率         6.01％
粘合强度：
与硅橡胶粘合强度                    硅胶破坏，无法从界面剥离
与氟硅胶粘合强度                    1.32KN/m。

Claims (1)

1.一种氟硅橡胶改性硅橡胶耐油配制原料，其特征按质量份如下：甲基乙烯基硅橡胶，50～90；甲基乙烯基三氟丙基硅橡胶，10～50；气相法白炭黑，30～40；高活性氧化镁，1～3；AN-3，0.5～2.5；二甲基二甲氧基硅烷，2～5；硅藻土，50～90；钛白粉，40～80；2，5-二甲基-2，5-二叔丁基过氧化己烷，0.5～1.2。
CN2011100063844A 2011-01-11 2011-01-11 一种氟硅橡胶改性硅橡胶耐油配制原料 Pending CN102127300A (zh)