CN102086330B - 电热涂料 - Google Patents

电热涂料 Download PDF

Info

Publication number
CN102086330B
CN102086330B CN 201110023430 CN201110023430A CN102086330B CN 102086330 B CN102086330 B CN 102086330B CN 201110023430 CN201110023430 CN 201110023430 CN 201110023430 A CN201110023430 A CN 201110023430A CN 102086330 B CN102086330 B CN 102086330B
Authority
CN
China
Prior art keywords
parts
coating
electro
butylacetate
pimelinketone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201110023430
Other languages
English (en)
Other versions
CN102086330A (zh
Inventor
杨辉
谢卫
张拴勤
刘胜超
王柏森
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DABAN PAINT Co Ltd JIANGYIN
SHANGHAI JUTONG INDUSTRY Co Ltd
63983 Troops of PLA
Original Assignee
DABAN PAINT Co Ltd JIANGYIN
SHANGHAI JUTONG INDUSTRY Co Ltd
63983 Troops of PLA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DABAN PAINT Co Ltd JIANGYIN, SHANGHAI JUTONG INDUSTRY Co Ltd, 63983 Troops of PLA filed Critical DABAN PAINT Co Ltd JIANGYIN
Priority to CN 201110023430 priority Critical patent/CN102086330B/zh
Publication of CN102086330A publication Critical patent/CN102086330A/zh
Application granted granted Critical
Publication of CN102086330B publication Critical patent/CN102086330B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种电热涂料，涉及可用于建筑物的室内外加热取暖的涂料，其涂覆在室内墙上、办公桌上、室外的岗哨处，使用安全电压即可实现加热取暖，通过电阻率的控制，满足不同的升温要求，可以达到比环境温度高5℃～20℃的性能，为此，本发明还提供了电热涂料的加工方法。本发明通过下述技术方案是予以实现：其包括下述重量份材料：成膜物质40份~60份、颜填料15份~30份、助剂1份~2份、溶剂20份~30份，上述物质按比例放入球磨机内，经充分混合、研磨而成，制成细度范围30μm~60μm的涂料，即为电热涂料。

Description

电热涂料
技术领域
本发明涉及可用于建筑物的室内外加热取暖，可制成电热餐桌、电热水器和工业上的中低温烘烤电炉的涂料，具体为电热涂料。
背景技术
目前市场上公开了几种电热涂料专利（公开号CN1068582、CN1112592），它们主要是采用碳粉和石墨作为填料，存在的问题是这些电热涂料的电阻都在几十欧姆以上，若进一步增大导电填料含量来降低电阻，则涂层的附着力变差，实际使用时发热效率相对较低，需要较高的电压（高于36伏安全电压），不利于实际应用。
发明内容
针对上述问题，本发明提供了一种电热涂料，其涂覆在室内墙上、办公桌上、室外的岗哨处，使用安全电压即可实现加热取暖，通过电阻率的控制，满足不同的升温要求，可以达到比环境温度高5℃～20℃的性能，为此，本发明还提供了电热涂料的加工方法。
其技术方案是这样的：其包括下述重量份材料：成膜物质40份~60份、颜填料15份~30份、助剂1份~2份、溶剂20份~30份，上述物质按比例放入球磨机内，经充分混合、研磨而成，制成细度范围30μm~60μm的涂料。
所述成膜物质为丙烯酸树脂、环氧树脂或者聚氨酯树脂；所述颜填料包括5份～15份Ni粉、10份～20份银包铜粉含重量百分含量为10%～30%银；所述助剂包括附着力增进剂Silok629，含量占成膜物质0.5%～1%，和分散剂Efka4010,含量占颜料0.5%～1%；所述根据不同的成膜物质选择不同的溶剂，包括聚苯乙烯、甲苯、乙酸丁酯、环己酮等；所述丙烯酸树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯20：二甲苯60：环己酮20；所述环氧树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯40：丁酮40：环己酮20；所述聚氨酯树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯25：二甲苯60：环己酮15。
本发明选用银包铜作为导电填料，它提高了铜粉的导电性，降低了银粉的成本，又解决了铜粉容易被氧化的问题，因此可以使涂层达到较低的电阻率（电阻率范围:0.1×10-4Ω·m～1×10-4Ω·m），又适用于工程化生产。所制备的电热涂料通过不同的成膜物质，保证涂料可以涂覆在不同的基底上，同时通过助剂体系的优选很好的解决了涂层附着力的问题。由于涂层电阻率比较低且可以调整，通过不同长、宽、厚度的调整可以达到不同的电阻。例如在20cm×30cm，厚度0.15mm的涂层电阻可以达到1～5Ω，因此在安全电压（36伏）下具有良好的发热效果。
具体实施方式
实施例1
本发明包括下述重量份材料：成膜物质40份、颜填料22.5份、助剂1份、溶剂25份，上述物质按比例放入球磨机内，经充分混合、研磨而成，制成细度范围45μm的涂料。
成膜物质为丙烯酸树脂、环氧树脂或者聚氨酯树脂；颜填料包括5份Ni粉、20份银包铜粉，其中含重量百分含量为20%银；助剂包括附着力增进剂Silok629，含量占成膜物质0.75%，和分散剂Efka4010,含量占颜料0.75%；丙烯酸树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯20：二甲苯60：环己酮20；环氧树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯40：丁酮40：环己酮20；聚氨酯树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯25：二甲苯60：环己酮15。
实施例2
本发明包括下述重量份材料：成膜物质60份、颜填料30份、助剂2份、溶剂30份，上述物质按比例放入球磨机内，经充分混合、研磨而成，制成细度范围30μm的涂料。
成膜物质为丙烯酸树脂、环氧树脂或者聚氨酯树脂；颜填料包括15份Ni粉、10份银包铜粉，其中含重量百分含量为30%银；助剂包括附着力增进剂Silok629，含量占成膜物质1%，和分散剂Efka4010,含量占颜料0. 5%；丙烯酸树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯20：二甲苯60：环己酮20；环氧树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯40：丁酮40：环己酮20；聚氨酯树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯25：二甲苯60：环己酮15。
实施例3
本发明包括下述重量份材料：成膜物质50份、颜填料15份、助剂1.5份、溶剂20份，上述物质按比例放入球磨机内，经充分混合、研磨而成，制成细度范围60μm的涂料。
成膜物质为丙烯酸树脂、环氧树脂或者聚氨酯树脂；颜填料包括10份Ni粉、15份银包铜粉，其中含重量百分含量为10%银；助剂包括附着力增进剂Silok629，含量占成膜物质0.5%，和分散剂Efka4010,含量占颜料1%；丙烯酸树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯20：二甲苯60：环己酮20；环氧树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯40：丁酮40：环己酮20；聚氨酯树脂对应的稀释剂包括以下体积比的材料：乙酸丁酯25：二甲苯60：环己酮15。 

Claims (1)

1.电热涂料，其特征在于：其包括下述重量份材料：成膜物质40份~60份、颜填料15份~30份、助剂1份~2份、溶剂20份~30份，上述物质按比例放入球磨机内，经充分混合、研磨而成，制成细度范围30μm~60μm的涂料；所述成膜物质为丙烯酸树脂、环氧树脂或者聚氨酯树脂；所述颜填料包括5份～15份Ni粉、10份～20份银包铜粉含重量百分含量为10%～30%银；所述助剂包括附着力增进剂Silok629，含量占成膜物质0.5%～1%，和分散剂Efka4010，含量占颜料0.5%～1%；所述丙烯酸树脂对应的溶剂包括以下体积比的材料：乙酸丁酯20：二甲苯60：环己酮20；所述环氧树脂对应的溶剂包括以下体积比的材料：乙酸丁酯40：丁酮40：环己酮20；所述聚氨酯树脂对应的溶剂包括以下体积比的材料：乙酸丁酯25：二甲苯60：环己酮15。
CN 201110023430 2011-01-21 2011-01-21 电热涂料 Expired - Fee Related CN102086330B (zh)