CN1465630A - 节能型无机电热涂料 - Google Patents

节能型无机电热涂料 Download PDF

Info

Publication number
CN1465630A
CN1465630A CNA021333890A CN02133389A CN1465630A CN 1465630 A CN1465630 A CN 1465630A CN A021333890 A CNA021333890 A CN A021333890A CN 02133389 A CN02133389 A CN 02133389A CN 1465630 A CN1465630 A CN 1465630A
Authority
CN
China
Prior art keywords
electric
oxide
coating material
saving type
type inorganic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA021333890A
Other languages
English (en)
Other versions
CN1214081C (zh
Inventor
朱春富
罗显荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 02133389 priority Critical patent/CN1214081C/zh
Publication of CN1465630A publication Critical patent/CN1465630A/zh
Application granted granted Critical
Publication of CN1214081C publication Critical patent/CN1214081C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

节能型无机电热涂料。本发明属于电热材料，特别是无机的电热涂料。本发明由电热涂料和与其配套使用的电绝缘涂料组成，(1)电热涂料由20％～40％的石墨粉、8％～10％的助剂，余量为基料组成；(2)电绝缘涂料30％～40％的云母粉、8％～10％的助剂，余量为基料组成。本涂料的成膜性、附着性及耐水性较好，并且制造成本低，还可适用于220伏，以及36伏～12伏的电压。

Description

节能型无机电热涂料
技术领域
本发明属于电热材料，特别是无机的电热涂料。
技术背景
传统的电加热器是电热丝与耐火材料基板、绝缘材料组合而成，这种电加热器通电后会产生明火，在有的特殊环境使用很不安全；电热丝的局部发热温度高，但总的发热面积小，在整体上欲达到设定的温度需要的时间长，故热效率低，耗电多；电热丝加热器的结构较复杂，使用寿命较短，所以其成本高，安全性较差。近年市场上出现了以甲苯为溶剂，由有机物和贵金属粉末为原料而制造的有机电热涂料，或者以硅酸钠为基料配制的电热涂料，该类电热涂料虽然比电热丝的加热板有了进步，但其成膜性、柔韧性和附着性都不理想，适应的工作电压范围也较窄。
发明内容
本实用新型所要解决的技术问题是提供一种节能型无机电热涂料，用其制备的电热板件结构简单，成本低，具有良好的成膜性、柔韧性和附着性。
解决本实用新型的技术问题所采用的方案是：本涂料由电热涂料和与其配套使用的电绝缘涂料组成。电热涂料由20％～40％的石墨粉、8％～10％的助剂，余量为基料组成；电绝缘涂料30％～40％的云母粉、8％～10％的助剂，余量为基料组成。电热涂料采用的助剂为氧化铜和铬酸钾或氧化锌，基料采用磷酸、氢氧化铝、氧化镁或R661丙烯酸(北京东方化工厂引进美国技术的产品)；电绝缘涂料的助剂为氧化铜和铬酸钾，基料采用磷酸、氢氧化铝、氧化镁、氧化钙及氧化硅微量。
本发明上述方案是提出的电热涂料，其配方较合理，成本也较低。首先将本电绝缘涂料的水溶性浆料均匀地喷涂在耐高温的金属、搪瓷基板上，经烘烤固化，可与基板间获得良好的结合，即使受到较高的温度，也不容易发生脱落，并且还能以较薄的涂层同时达到很好的电绝缘作用和传递热量的作用。再将电热涂料喷涂于电绝缘涂料上，烘烤固化，电热涂料就被牢固地附着于金属、搪瓷基板上。本涂料皆为水溶性的，且很容易经烘烤与金属、搪瓷板固化，因此容易保证喷涂层均匀，附着性强，成膜好的技术要求，从而也就适宜制作成不同功率的电热元件。
具体实施方式
实施例1：
配制电绝缘涂料：按下述重量百分比配制，云母粉30％、磷酸38％、铬酸钾4％、氧化铜4％、氢氧化铝12％、氧化镁12％、另外添加氧化钙微量、氧化硅微量，再加入水，调配均匀，用胶体磨研磨到粒度小于10微米，制成电绝缘涂料。将此涂料均匀喷涂金属、搪瓷基板上，烘烤固化，即可达到电绝缘效果，并为后续与电热涂料结合作好准备。
配制电热涂料：按下述重量百分比配制，高纯石墨粉32％、铬酸钾4％、磷酸30％、氢氧化铝20％、氧化铜4％、氧化镁10％，加水适量，搅拌均匀，用胶体磨研磨到粒度小于10微米，制成电热涂料。将此涂料均匀喷涂在预先经过上述绝缘层处理的金属、搪瓷基板上，烘烤固化，即制成电热板。装入封闭的壳体，填充保温隔热材料，就可做成工作电压为220伏及36～12伏的带电热涂料层的加热器。
实施例2：
配制电绝缘涂料：按下述重量百分比配制，云母粉30％、磷酸38％、铬酸钾4％、氧化铜4％、氢氧化铝12％、氧化镁12％、另外添加氧化钙微量、氧化硅微量，再加入水，调配均匀，用胶体磨研磨到粒度小于10微米，制成电绝缘涂料。将此涂料均匀喷涂金属、搪瓷基板上，烘烤固化，即可达到电绝缘效果，并为后续与电热涂料结合作好准备。
配制电热涂料：按下述重量百分比配制，高纯石墨粉30％、R661丙烯酸56％(北京东方化工厂引进美国技术的产品)、氧化铜粉10％、氧化锌4％，加水适量，搅拌均匀，用胶体磨研磨到粒度小于10微米，制成电热涂料。将此涂料均匀喷涂在预先经过上述绝缘层处理的金属、搪瓷基板上，烘烤固化，即制成电热板。装入封闭的壳体，填充保温隔热材料，就可做成工作电压为36～12伏的带电热涂料层的加热器。

Claims (6)

1、一种节能型无机电热涂料，其特征是由电热涂料和与其配套使用的电绝缘涂料组成，(1)电热涂料由20％～40％的石墨粉、8％～10％的助剂，余量为基料组成；(2)电绝缘涂料30％～40％的云母粉、8％～10％的助剂，余量为基料组成。
2、按权利要求1所述的节能型无机电热涂料，其特征是(1)电热涂料采用的助剂为氧化铜和铬酸钾或氧化锌，基料采用磷酸、氢氧化铝、氧化镁或R661丙烯酸；(2)电绝缘涂料的助剂为氧化铜和铬酸钾，基料采用磷酸、氢氧化铝、氧化镁、氧化钙及氧化硅微量。
3、按权利要求2所述的节能型无机电热涂料，其特征是电热涂料的配方为，石墨粉32％、铬酸钾4％、磷酸30％、氢氧化铝20％、氧化铜4％、氧化镁10％。
4、按权利要求2所述的节能型无机电热涂料，其特征是电热涂料的配方为，石墨粉30％、R661丙烯酸56％、氧化锌4％、氧化铜10％。
5、按权利要求2所述的节能型无机电热涂料，其特征是电绝缘涂料的配方为，云母粉30％、磷酸38％、铬酸钾4％、氧化铜4％、氢氧化铝12％、氧化镁12％、另外添加氧化钙微量、氧化硅微量。
6、按权利要求3、4所述的节能型无机电热涂料，其特征是电热涂料中的石墨粉采用粒度小于10微米的粉末。
CN 02133389 2002-06-27 2002-06-27 节能型无机电热涂料 Expired - Fee Related CN1214081C (zh)