CN102083865A - 通过聚合单体溶液的液滴生产吸水性聚合物颗粒的方法 - Google Patents
通过聚合单体溶液的液滴生产吸水性聚合物颗粒的方法 Download PDFInfo
- Publication number
- CN102083865A CN102083865A CN2009801263586A CN200980126358A CN102083865A CN 102083865 A CN102083865 A CN 102083865A CN 2009801263586 A CN2009801263586 A CN 2009801263586A CN 200980126358 A CN200980126358 A CN 200980126358A CN 102083865 A CN102083865 A CN 102083865A
- Authority
- CN
- China
- Prior art keywords
- monomer solution
- water
- hole
- weight
- polymeric particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种生产吸水性聚合物颗粒的方法,所述方法通过在反应室中,在围绕的气相中聚合单体溶液的液滴而进行,所述单体溶液经至少一个孔计量加入所述反应室中,每孔直径为210-290μm,计量速率为每孔0.9-5kg/h。
Description
本发明涉及一种生产吸水性聚合物颗粒的方法,所述方法通过在反应室中,在围绕的气相中聚合单体溶液的液滴而进行,其中所述单体溶液经至少一个孔计量加入所述反应室中。
专著″Modern Superabsorbent Polymer Technology″,F.L.Buchholzand A.T.Graham,Wiley-VCH,1998,第71-103页描述了吸水性聚合物颗粒的生产。
作为吸收水溶液的产品,吸水性聚合物用于生产尿布、棉塞、卫生棉和其他卫生制品,也可用作商品蔬菜种植业中的保水剂。吸水性聚合物也称为“高吸收性聚合物”或“超吸收剂”。
喷雾聚合允许将聚合和干燥的处理步骤结合起来。此外,可通过合适的过程控制使粒度处于一定界限内。
在例如EP 0 348 180 A1、EP 0 816 383 A1、WO 96/40427 A1、US4,020,256、US 2002/0193546、DE 35 19 013 A1、WO 2008/040715 A2和WO 2008/052971 A1中,描述了通过聚合单体溶液的液滴来生产吸水性聚合物颗粒。
WO 2008/040715 A2描述了一种喷雾聚合方法,其中单体溶液中的引发剂在液滴产生之前具有限定的停留时间。
WO 2008/052971 A1描述了一种具有特定的温度规则的喷雾聚合方法。
本发明的一个目的是提供一种生产吸水性聚合物颗粒的方法,所述方法通过在一种围绕所述单体溶液液滴的气相中聚合所述液滴而进行。
更特别地,本发明的一个目的是提供一种生产具有窄单峰粒度分布和高密度的吸水性聚合物颗粒的方法。
所述目的通过一种如下的生产吸水性聚合物颗粒的方法实现,所述方法通过在反应室中,在围绕的气相中聚合单体溶液的液滴而进行,所述单体溶液包含:
a)至少一种可被至少部分中和的、带有酸基团的烯键式不饱和单体,
b)至少一种交联剂,
c)至少一种引发剂,和
d)水,
所述单体溶液经至少一个孔计量加入所述反应室中,其中每孔直径为210-290μm,每孔计量速率为为0.9-5kg/h。
每孔计量速率(以kg/h表示)优选至少为
-1.9269·10-7x3+2.3433·10-4x2-5.4364·10-2x+3.7719
其中x为每孔直径(以μm表示)。
每孔计量速率(以kg/h表示)优选最多为
5.5158·10-8x4-5.5844·10-5x3+2.0635·10-2x2-3.2606x+1.8698·102
其中x同样为每孔直径(以μm表示)。
选择孔的直径和计量速率以使所得到的液滴的平均直径优选为300-700μm、更优选350-650μm、最优选400-600μm。所述平均液滴直径用例如MalvernS(Malvern Instruments Ltd.;Malvern;UK)通过激光衍射测定。在孔的直径恒定的情况下,平均液滴直径随着每孔计量速率的升高而减小。
所述单体溶液在20℃下的动态粘度优选为0.002-0.02Pa·s,更优选0.004-0.015Pa·s,最优选0.005-0.01Pa·s。平均液滴直径随着动态粘度的升高而增大。
所述单体溶液在20℃下的密度优选为1-1.3g/cm3,更优选1.05-1.25g/cm3,更优选1.1-1.2g/cm3。
所述单体溶液在20℃下的表面张力为0.02-0.06N/m、更优选0.03-0.05N/m、更优选0.035-0.045N/m。平均液滴直径随着表面张力的升高而增大。
所述单体溶液的温度在其通过所述孔时优选为10-60℃,更优选15-60℃,最优选20-40℃。
本发明基于如下发现:通过增加孔直径和超比例(greater-than-proportional)增加每孔计量速率,可使平均液滴大小保持恒定,同时使所得到的吸水性聚合物颗粒的密度增加。高密度吸水性聚合物颗粒占用更少的体积并可更快地计量。
过高的计量速率导致双峰粒度分布,从而导致不利地小颗粒直径的吸水性聚合物颗粒的比例升高。
所述吸水性聚合物颗粒通常不溶于水。
所述单体a)优选为水溶性的,即在23℃下在水中的溶解度通常为至少1g/100g水,优选至少5g/100g水,更优选至少25g/100g水,最优选至少35g/100g水。
合适的单体a)为,例如,烯键式不饱和羧酸,如丙烯酸、甲基丙烯酸和衣康酸。特别优选的单体为丙烯酸和甲基丙烯酸。非常特别优选丙烯酸。
其他合适的单体a)为,例如,烯键式不饱和磺酸,如苯乙烯磺酸和2-丙烯酰氨基-2-甲基丙磺酸(AMPS)。
杂质可对所述聚合具有很大的影响。因此所用原材料应具有最大的纯度。因此专门纯化所述单体a)通常是有利的。合适的纯化方法描述于例如WO 2002/055469 A1、WO 2003/078378 A1和WO 2004/035514 A1中。合适的单体a)为,例如,根据WO 2004/035514 A1纯化的丙烯酸,其含有:99.8460重量%的丙烯酸、0.0950重量%的乙酸、0.0332重量%的水、0.0203重量%的丙酸、0.0001重量%的糠醛、0.0001重量%的马来酸酐、0.0003重量%的二丙烯酸和0.0050%的氢醌单甲醚。
丙烯酸和/或其盐在单体a)总量中的比例优选为至少50摩尔%,更优选至少90摩尔%,最优选至少95摩尔%。
单体a)的酸基团通常被部分中和,优选中和程度为25-85摩尔%,优选50-80摩尔%,更优选60-75摩尔%,为此可使用常规中和剂,优选碱金属氢氧化物、碱金属氧化物、碱金属碳酸盐或碱金属碳酸氢盐,及其混合物。也可使用铵盐代替碱金属盐。特别优选的碱金属是钠和钾,但非常特别优选氢氧化钠、碳酸钠或碳酸氢钠,及其混合物。所述中和通常通过混入水溶液、熔体或优选固体形式的中和剂来实现。例如,水含量显著低于50重量%的氢氧化钠可以以熔点高于23℃的蜡状物质的形式存在。在此情况下,可以以片材或高温熔体的形式计量加入。
所述单体a)通常包含聚合抑制剂,优选氢醌单醚,作为贮存稳定剂。
所述单体溶液优选含有至多250重量ppm、优选至多130重量ppm、更优选至多70重量ppm、优选至少10重量ppm、更优选至少30重量ppm,特别是约50重量ppm的氢醌单醚,各自均基于未中和单体a)计。例如,所述单体溶液可使用带有酸基团的烯键式不饱和单体与合适含量的氢醌单醚来制备。然而,所述氢醌单醚也可通过例如在活性碳上吸收而从所述单体溶液中除去。
优选的氢醌单醚为氢醌单甲基醚(MEHQ)和/或α-生育酚(维他命E)。
合适的交联剂b)为具有至少两个适于交联的基团的化合物。这些基团为例如可通过自由基聚合进入聚合物链的烯键式不饱和基团,以及可与所述单体a)的酸基团形成共价键的官能团。此外,可与所述单体a)的至少两个酸基团形成配位键的多价金属盐也适合作为交联剂b)。
优选地,交联剂b)为含有至少两个可聚合基团的化合物,其可通过自由基聚合进入聚合物网络。合适的交联剂b)为,例如乙二醇二甲基丙烯酸酯、二甘醇二丙烯酸酯、聚乙二醇二丙烯酸酯、甲基丙烯酸烯丙酯、三羟甲基丙烷三丙烯酸酯、三烯丙基胺、四烯丙基氯化铵、四烯丙氧基乙烷,如EP 0 530 438 A1中所述;二丙烯酸酯和三丙烯酸酯,如EP 0 547847 A1、EP 0 559 476 A1、EP 0 632 068 A1、WO 93/21237 A1、WO2003/104299 A1、WO 2003/104300 A1、WO 2003/104301 A1和DE 103 31450 A1中所述;除丙烯酸酯基团外还含有烯键式不饱和基团的混合丙烯酸酯,如DE 103 31 456 A1和DE 103 55 401 A1中所述;或者交联剂混合物,如例如DE 195 43 368 A1、DE 196 46 484 A1、WO 90/15830 A1和WO 2002/032962 A2中所述。
优选的交联剂b)为季戊四醇三烯丙基醚、四烯丙氧基乙烷、亚甲基双甲基丙烯酰胺、15-重乙氧基化三羟甲基丙烷三丙烯酸酯、聚乙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯和三烯丙胺。
非常特别优选的交联剂b)为经丙烯酸或甲基丙烯酸酯化成二丙烯酸酯或三丙烯酸酯的聚乙氧基化和/或聚丙氧基化的丙三醇,例如WO2003/104301 A1所述。特别有利的是3至10-重乙氧基化丙三醇的二丙烯酸酯和/或三丙烯酸酯。非常特别优选1至5-重乙氧基化和/或丙氧基化丙三醇的二丙烯酸酯或三丙烯酸酯。最优选3至5-重乙氧基化和/或丙氧基化丙三醇的三丙烯酸酯,尤其是3-重乙氧基化丙三醇的三丙烯酸酯。
交联剂b)的量优选为0.01-1.5重量%、更优选0.05-1重量%、最优选0.1-0.6重量%,各自均基于单体a)计。随着交联剂含量的升高,离心保留容量(CRC)下降,并且在21.0g/cm2(AUL0.3psi)压力下的吸收经历最大值。
所用的引发剂c)可为在所述聚合条件下裂解为自由基的所有化合物,例如过氧化物、氢过氧化物、过氧化氢、过硫酸盐、偶氮化合物和称为氧化还原引发剂的化合物。优选使用水溶性引发剂。在某些情况下,有利的是使用多种引发剂的混合物,例如过氧化氢和过硫酸钠或过硫酸钾的混合物。过氧化氢和过硫酸钠的混合物可以以任意比例使用。
特别优选的引发剂c)为偶氮引发剂,例如2,2′-偶氮双[2-(2-咪唑啉-2-基)丙烷]二盐酸盐和2,2′-偶氮双[2-(5-甲基-2-咪唑啉-2-基)丙烷]二盐酸盐;以及光敏引发剂,例如2-羟基-2-甲基苯丙酮和1-[4-(2-羟乙氧基)苯基]-2-羟基-2-甲基-1-丙-1-酮;氧化还原引发剂例如过硫酸钠/羟甲基亚磺酸、过二硫酸铵/羟甲基亚磺酸、过氧化氢/羟甲基亚磺酸、过硫酸钠/抗坏血酸、过二硫酸铵/抗坏血酸和过氧化氢/抗坏血酸;光敏引发剂,例如1-[4-(2-羟乙氧基)苯基]-2-羟基-2-甲基-1-丙-1-酮;以及其混合物。
所述引发剂以常规量使用,例如基于单体a)计为0.001-5重量%,优选0.01-2重量%。
所述单体溶液的水含量优选小于65重量%,优选小于62重量%,更优选小于60重量%,最优选小于58重量%。
将所述单体溶液通过至少一个孔计量加入反应室中以形成液滴。所述孔可位于例如液滴化器板中。
液滴化器板是具有至少一个孔的板,液体从顶部进入所述孔。可使所述液滴化器板或所述液体振动,这可在所述液滴化器板的下方于每孔处产生一连串理想地单分散的液滴。在一个优选实施方案中,不使所述滴化器板振动。
所述孔的数量和直径根据所需容量和液滴大小来选择。所述液滴直径通常为所述孔直径的1.9倍。此处重要的是,待液滴化的液体通过所述孔的速度不太快,并且通过孔后的压力下降不太大。否则,所述液体不是被液滴化,而是液体射流因高动能而散裂(喷雾)。基于每孔通过量和孔直径的雷诺数优选小于2000,更优选小于1600,更优选小于1400,并且最优选小于1200。
所述液滴化器板通常具有至少一个、优选至少10个、更优选至少50个并且通常最多10000个、优选最多5000个、更优选最多1000个孔,所述孔通常均匀地分布在液滴化器板上,优选以所谓的三角形节距分布,即每三个孔构成一个等边三角形的各个角。
所述孔的间隔优选为1-50mm、更优选2.5-20mm,最优选5-10mm。
所述聚合反应器中通过一股气体。可使所述载气与所述单体溶液自由下落的液滴以顺流或逆流、优选顺流——即从顶部向下——的方式通过所述反应室。在一次通过后,优选回收所述载气的至少一部分、优选至少50%、更优选至少75%,作为循环气体进入所述反应室中。通常,在每次通过后排放所述载气的一部分,优选最多10%、更优选最多3%,最优选最多1%。
所述载气的氧气含量优选为0.5-15体积%,更优选1-10体积%,更优选2-7体积%。
除氧气以外,所述载体还优选包含氮气。所述载气的氮含量优选为至少80体积%,更优选至少90体积%,最优选至少95体积%。
优选调节所述气体速度以使所述聚合反应器中的流体达到例如不存在与主要流体方向相反的对流,所述气体速度为例如0.01-5m/s,优选0.02-4m/s,更优选0.05-3m/s,最优选0.1-2m/s。
流经反应器的气体合适地预热至所述反应器上游的反应温度。
气体进口温度,即气体进入所述反应室时的温度优选为160-250℃,更优选180-230℃,最优选190-220℃。
有利地,控制所述气体的进口温度以使气体出口温度,即气体离开所述反应室时的温度,为100-180℃,更优选110-160℃,最优选120-140℃。
所述反应可在加压或减压下进行,优选相对环境压力下降最多100mbar的压力。
所述反应尾气,即离开所述反应室的气体,可例如在热交换器中冷却。这使得水和未转化的单体a)冷凝。然后可将至少一部分所述反应尾气重加热并作为循环气体再循环至所述反应器中。一部分所述反应尾气可排出并用新鲜气体替换,在这种情况下,可将所述反应尾气中存在的水和未转化的单体a)移出并回收。
特别优选热集成系统,即使用冷却尾气过程中的一部分废热来加热循环气体。
可对所述反应器进行跟踪加热(trace-heated)。在这种情况下,调节所述跟踪加热以使壁温高于反应器内部温度至少5℃,这样可靠地防止了所述反应器壁上的冷凝。
所述聚合物颗粒可进行后交联以进一步改善性能。合适的后交联剂是含有可与所述聚合物颗粒的至少两个羧酸酯基形成共价键的基团的化合物。合适的化合物为,例如,多官能胺、多官能酰胺-胺、多官能环氧化合物,如EP 0 083 022 A2、EP 0 543 303 A1和EP 0 937736 A2中所述;二官能醇或多官能醇,如DE 33 14 019 A1、DE 35 23617 A1和EP 0 450 922 A2中所述;或者β-羟烷基酰胺,如DE 102 04938 A1和US 6,239,230中所述。
此外,作为合适的后交联剂,DE 40 20 780 C1描述了环状碳酸酯;DE 198 07 502 A1描述了2-噁唑烷酮及其衍生物,例如2-羟乙基-2-噁唑烷酮;DE 198 07 992 C1描述了二2-噁唑烷酮和聚2-噁唑烷酮;DE 198 54 573 A1描述了2-氧代四氢-1,3-噁嗪及其衍生物;DE 19854 574 A1描述了N-酰基-2-噁唑烷酮;DE 102 04 937 A1描述了环脲;DE 103 34 584 A1描述了二环酰氨乙缩醛;EP 1 199 327 A2描述了氧杂环丁烷和环脲;WO 2003/31482 A1描述了吗啉-2,3-二酮及其衍生物。
优选的后交联剂为碳酸亚乙酯、乙二醇二缩水甘油醚、聚酰胺与表氯醇的反应产物、以及丙二醇与1,4-丁二醇的混合物。
非常特别优选的后交联剂为2-羟乙基噁唑烷-2-酮、噁唑烷-2-酮和1,3-丙二醇。
此外,也可使用包含其他可聚合的烯键式不饱和基团的后交联剂,如DE 37 13 601 A1中所述。
后交联剂的量优选为0.001-2重量%,更优选0.02-1重量%,最优选0.05-0.2重量%,各自均基于聚合物颗粒计。
在本发明的一个优选实施方案中,除后交联剂外,多价阳离子也可在所述后交联之前、期间或之后施用于所述颗粒表面。
可用于本发明方法的多价阳离子是,例如,二价阳离子如锌、镁、钙、铁和锶的阳离子,三价阳离子如铝、铁、铬、稀土和锰的阳离子,四价阳离子如钛和锆的阳离子。可用的抗衡离子为氯离子、溴离子、硫酸根、硫酸氢根、碳酸根、碳酸氢根、硝酸根、磷酸根、磷酸氢根、磷酸二氢根和羧酸根(如乙酸根和乳酸根)。优选硫酸铝和乳酸铝。除金属盐外,也可使用多胺作为多价阳离子。
所用多价阳离子的量为,例如0.001-1.5重量%,优选0.005-1重量%,更优选0.02-0.8重量%,各自基于聚合物颗粒计。
所述后交联通常通过将所述后交联剂的溶液喷雾到干燥的聚合物颗粒上进行。喷雾后,将用后交联剂涂覆的聚合物颗粒进行热干燥,所述后交联反应可在干燥之前或干燥过程中发生。
后交联剂溶液的喷雾施用优选在带有移动混合工具的混合器中进行,例如螺杆混合器、盘式混合器和桨叶式混合器。然而,也可在流化床中喷雾所述后交联剂。特别优选卧式混合器例如桨叶式混合器,非常特别优选立式混合器。卧式混合器与立式混合器之间的区别在于搅拌轴的位置,即卧式混合器具有水平安装的搅拌轴,而立式混合器具有垂直安装的搅拌轴。合适的混合器为例如卧式犁铧式混合器(Gebr.Maschinenbau GmbH;Paderborn;Germany)、Vrieco-Nauta连续混合器(Hosokawa Micron BV;Doetinchem;theNetherlands)、Processall Mixmill混合器(Processall Incorporated;Cincinnati;US)和Schugi混合器(Hosokawa Micron BV;Doetinchem;the Netherlands)。
所述后交联剂通常以水溶液的形式使用。非水性溶剂的含量或溶剂总量可用于调整后交联剂在所述聚合物颗粒中的渗透深度。
当只用水作为溶剂时,加入表面活性剂是有利的。这可提高润湿性能并降低结块的可能性。然而,优选使用溶剂混合物,例如异丙醇/水、1,3-丙二醇/水和丙二醇/水,其中混合质量比优选为20∶80至40∶60。
热干燥优选在接触式干燥器中、更优选在桨叶式干燥器中、最优选在盘式干燥器中进行。合适的干燥器为例如Hosokawa卧式桨叶式干燥器(Hosokawa Micron GmbH;Leingarten;Germany)、Hosokawa盘式干燥器(Hosokawa Micron GmbH;Leingarten;Germany)和Nara桨叶式干燥器(NARA Machinery Europe;Frechen;Germany)。此外,还可使用流化床干燥器。
干燥可在混合器本身中通过加热夹套或吹入热空气实现。下游干燥器同样适合,如架式干燥器、旋转管式炉或可加热螺杆。特别有利的是在流化床干燥器中混合和干燥。
优选的干燥温度为100-250℃,优选120-220℃,更优选130-210℃,最优选150-200℃。在该温度下,在反应混合器或干燥器中的优选停留时间优选为至少10分钟,更优选至少20分钟,最优选至少30分钟,并且通常最多60分钟。
为进一步提高性能,可对后交联的聚合物颗粒进行涂覆或继而进行润湿。适于提高膨胀率和渗透性(SFC)的涂料为,例如,无机惰性物质例如不溶于水的金属盐、有机聚合物、阳离子聚合物和二价或多价金属阳离子聚合物。用于粘合粉末的合适涂料为,例如,多元醇。抵抗所述聚合物颗粒的不利结块趋势的合适涂料为,例如,热解法二氧化硅如200,和表面活性剂如20。用于提高色彩稳定性(黄化稳定性)的合适涂料为,例如,还原剂如次磷酸钠、亚硫酸钠、亚硫酸氢钠、FF6和FF7(Brüggemann Chemicals;Heilbronn;Germany)。
本发明还提供可通过本发明方法获得的吸水性聚合物颗粒。
可通过本发明方法获得的吸水性聚合物颗粒的水分含量通常为至少10重量%,优选至少12重量%,更优选至少14重量%,最优选至少15重量%,并且通常小于20重量%。
可通过本发明方法获得的吸水性聚合物颗粒的密度通常为至少0.55g/cm3,优选至少0.57g/cm3,更优选至少0.59g/cm3,最优选至少0.6g/cm3,并且通常小于0.75g/cm3。
可通过本发明方法获得的吸水性聚合物颗粒的平均直径优选为300-450μm,更优选320-420μm,非常特别优选340-400μm。
可通过本发明方法获得的吸水性聚合物颗粒的形状为部分凹陷的球形(图1)并近似圆形,即所述聚合物颗粒的平均球度(mSPHT)为至少0.84,优选至少0.86,更优选至少0.88,最优选至少0.9。球度(SPHT)定义为
其中A为聚合物颗粒的截面面积,U为聚合物颗粒的截面周长。平均球度(mSPHT)是体积平均球度。
较低平均球度(mSPHT)的聚合物颗粒通过反向悬浮聚合获得,此时所述聚合物颗粒在聚合过程中或在聚合后附聚。
将通过常规溶液聚合(凝胶聚合)产生的吸水性聚合物颗粒干燥后研磨并分级,以获得不规则聚合物颗粒。这些聚合物颗粒的平均球度(mSPHT)为约0.72至约0.78。
可通过本发明方法获得的吸水性聚合物颗粒的离心保留容量(CRC)通常为至少15g/g,优选至少20g/g、优选至少25g/g,更优选至少30g/g、最优选至少35g/g。所述吸水性聚合物颗粒的离心保留容量(CRC)通常小于100g/g。离心保留容量(CRC)通过EDANA(欧洲非织布协会,European Disposable and Nonwovens Association)推荐的测试方法No.WSP 241.2-05″Centrifuge retention capacity″进行测定。
所述吸水性聚合物颗粒通过下述测试方法测试。
方法:
除非另有指明,所述测量应在23±2℃的环境温度和50±10%的相对空气湿度下进行。将所述吸水性聚合物颗粒在分析之前进行充分混合。
平均液滴大小
单体溶液的平均液滴大小(D50)是恰好50体积%的液滴小于该值的液滴大小,用MalvernS(Malvern Instruments Ltd.;Malvern;GB)测定。使用了450mm透镜以及“RTSizer”控制和评估软件。将measurement ready设为0.1-2000μm。液滴化器板/激光束距离为1.05m,液滴/透镜距离为15cm。
液滴大小的分布宽度
液滴大小的分布宽度(SPAN)为
其中D10为恰好10体积%的液滴小于该值的液滴大小,D50为恰好50体积%的液滴小于该值的液滴大小,D90为恰好90体积%的液滴小于该值的液滴大小。此处分布宽度为0对应于一连串单分散液滴。所述分布宽度用MalvernS(Malvern Instruments Ltd.;Malvern;GB)测定。使用了450mm透镜以及″RTSizer″控制和评估软件。将measurement ready设为0.1-2000μm。液滴化器板/激光束距离为1.05m,液滴/透镜距离为15cm。
平均粒度(粒度分布)
吸水性聚合物颗粒的粒度分布通过EDANA(欧洲非织布协会)推荐的测试方法No.WSP 220.2-05“Particle Size Distribution”进行测定。
水分含量
吸水性聚合物颗粒的水分含量通过EDANA(欧洲非织布协会)推荐的测试方法No.WSP 230.2-05″Moisture content″进行测定。
离心保留容量
吸水性聚合物颗粒的离心保留容量(CRC)通过EDANA(欧洲非织布协会)推荐的测试方法No.WSP 241.2-05″CentrifugeRetention Capacity″进行测定。
49.2g/cm
2
压力下的吸收
49.2g/cm2(AUL0.7psi)压力下的吸收类似于EDANA(欧洲非织布协会)推荐的测试方法No.WSP 242.2-05″Absorption underPressure″进行测定,不同在于使用49.2g/cm2代替21.0g/cm2的压力。
密度
密度通过EDANA(欧洲非织布协会)推荐的测试方法No.WSP260.2-05″Density″进行测定。
所述EDANA测试方法获自例如欧洲非织布协会,AvenueEugène Plasky 157,B-1030 Brussels,Belgium。
实施例
实施例1
将包含31.6重量%的丙烯酸钠、9.9重量%的丙烯酸、0.17重量%的2,2′-偶氮双[2-(2-咪唑啉-2-基)丙烷]二盐酸盐、0.085重量%的过二硫酸钠、0.058重量%的3-重乙氧基化丙三醇三丙烯酸酯(约85重量%)和水的单体溶液液滴化。用作液滴化器的孔板具有6×200μm的孔、13×230μm的孔、9×250μm的孔、3×270μm的孔或2×290μm的孔。
分析所获得的液滴。结果汇总于表1。
表1:喷雾谱的分析
结果显示液滴大小随着孔的直径的增大而增大,并随着计量速率的升高而减小。此外,存在一个范围,在此范围内液滴大小分布的宽度(span)不依赖计量速率。在一个限定的计量速率以上,计量速率的进一步增加导致出现双峰粒度分布,并且直径小于100μm的液滴比例显著增加。
实施例2(非本发明)
在一个加热液滴化塔(高12m、宽2m、顺流的气体速度0.1m/s)中,将包含31.6重量%的丙烯酸钠、9.9重量%的丙烯酸、0.17重量%的2,2′-偶氮双[2-(2-咪唑啉-2-基)丙烷]二盐酸盐、0.085重量%的过二硫酸钠、0.058重量%的3-重乙氧基化丙三醇三丙烯酸酯(约85重量%)和水的单体溶液液滴化。所述单体溶液在20℃下的动态粘度为0.0065Pa·s,密度为1.165g/cm3,表面张力为0.039N/m。液滴化器板具有20×200μm的孔。所述混合物的计量速率为20.5-28.0kg/h。调节气体预热的热输出量以使所述液滴化塔的气体出口温度恒定在130℃。
分析所获得的吸水性聚合物颗粒。结果汇总于表3。
实施例3
步骤如实施例2。液滴化器板具有9×230μm的孔。所述混合物的计量速率为18.0-22.0kg/h。
分析所获得的吸水性聚合物颗粒。结果汇总于表3。
实施例4
步骤如实施例2。液滴化器板具有6×250μm的孔。所述混合物的计量速率为18.0-20.5kg/h。
分析所获得的吸水性聚合物颗粒。结果汇总于表3。
实施例5
步骤如实施例2。液滴化器板具有3×270μm的孔。所述混合物的计量速率为13.0-14.0kg/h。
分析所获得的吸水性聚合物颗粒。结果汇总于表3。
表2:设置
*)非本发明
表3:结果
*)非本发明
结果显示密度随着孔直径的增大而升高。所述吸水性聚合物颗粒的其他性能保持不变。
Claims (10)
1.一种生产吸水性聚合物颗粒的方法,所述方法通过在反应室中,在围绕的气相中聚合单体溶液的液滴而进行,所述单体溶液包含:
a)至少一种可被至少部分中和的、带有酸基团的烯键式不饱和单体,
b)至少一种交联剂,
c)至少一种引发剂,和
d)水,
所述单体溶液经至少一个孔计量加入所述反应室中,其中每孔直径为210-290μm,每孔计量速率为0.9-5kg/h。
2.权利要求1的方法,其中所述每孔计量速率(以kg/h表示)至少为
-1.9269·10-7x3+2.3433·10-4x2-5.4364·10-2x+3.7719
其中x为每孔直径(以μm表示)。
3.权利要求1或2的方法,其中所述每孔计量速率(以kg/h表示)最多为
5.5158·10-8x4-5.5844·10-5x3+2.0635·10-2x2-3.2606x+1.8698·102
其中x为每孔直径(以μm表示)。
4.权利要求1-3之一的方法,其中所述液滴的平均直径为300-700μm。
5.权利要求1-4之一的方法,其中所述单体溶液在20℃下的动态粘度为0.002-0.02Pa·s。
6.权利要求1-5之一的方法,其中所述单体溶液在20℃下的密度为1-1.3g/cm3。
7.权利要求1-6之一的方法,其中所述单体溶液在20℃下的表面张力为0.02-0.06N/m。
8.权利要求7的方法,其中所述单体溶液在其通过所述孔时的温度为10-60℃。
9.权利要求1-8之一的方法,其中所述吸水性聚合物颗粒的离心保留容量为至少15g/g。
10.通过权利要求1-9之一的方法获得的吸水性聚合物颗粒,其密度为至少0.55g/cm3,平均颗粒直径为300-450μm,水分含量为至少10重量%。