CN102050719A - 一种非水合成硬脂酸钙的加工方法 - Google Patents
一种非水合成硬脂酸钙的加工方法 Download PDFInfo
- Publication number
- CN102050719A CN102050719A CN2009102128831A CN200910212883A CN102050719A CN 102050719 A CN102050719 A CN 102050719A CN 2009102128831 A CN2009102128831 A CN 2009102128831A CN 200910212883 A CN200910212883 A CN 200910212883A CN 102050719 A CN102050719 A CN 102050719A
- Authority
- CN
- China
- Prior art keywords
- calcium stearate
- nonaqueous
- synthetic calcium
- industrial
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种非水合成硬脂酸钙的加工方法,是采用工业级硬脂酸188-200kg、工业品氢氧化钙24-26kg、52-62℃工业品石蜡烃50-150kg;在反应釜中加热温度控制在100-130℃;搅拌反应2-3小时即得。本发明产物收得率为99.0%。提高了产品的产量、质量。设备投入少、工序少,减少了成本,提高了效益。降低了工人的劳动强度。杜绝了环境污染。
Description
技术领域:本发明涉及到一种非水合成硬脂酸钙的加工方法。
背景技术:传统的合成硬脂酸钙的加工方法,在生产过程中需要消耗大量的碱和酸,成本相对较高;并产生大量的含盐废水,约为产物的4-5倍重量;须经过分离、烘干、机械粉碎等多种工序,能源消耗大;生产设备多、投资大,有细粉尘污染,工人劳动强度大。
其化学反应方程式为:
2、2C17H35COONa+CaCl2→(C17H35COO)2Ca+2NaCl
发明内容:本发明的目的就是要提供一种非水合成硬脂酸钙的加工方法,它能很好地克服传统的加工方法所存在的问题,本发明的目的是这样实现的,一种非水合成硬脂酸钙的加工方法,其特征在于:采用工业级硬脂酸188-200Kg、工业品氢氧化钙24-26Kg、52-62℃工业品石蜡烃50-150Kg;在反应釜中加热温度控制在100-130℃;搅拌反应2-3小时即得。
其化学反应方程式为:
本发明产物收得率为99.0%。提高了产品的产量、质量。设备投入少、工序少,减少了成本,提高了效益。降低了工人的劳动强度。杜绝了环境污染。
具体实施方式:
一种非水合成硬脂酸钙的加工方法,其特征在于:采用工业级硬脂酸188-200Kg、工业品氢氧化钙24-26Kg、工业品石蜡烃50-150Kg;在反应釜中加热温度控制在100-130℃;搅拌反应2-3小时即得。
其化学反应方程式为:
具体实施时,利用硬脂酸的弱酸性和氢氧化钙的碱性进行酸碱反应,生产硬脂酸钙。采用工业级硬脂酸型号1838195Kg、工业品氢氧化钙25Kg、工业品石蜡烃100Kg;在反应釜中加热温度控制在115℃;搅拌反应2.5小时即得。产品收率为99.0%。
Claims (1)