CN102031048A - Flat varnish for waterborne wood - Google Patents
Flat varnish for waterborne wood Download PDFInfo
- Publication number
- CN102031048A CN102031048A CN 201010589707 CN201010589707A CN102031048A CN 102031048 A CN102031048 A CN 102031048A CN 201010589707 CN201010589707 CN 201010589707 CN 201010589707 A CN201010589707 A CN 201010589707A CN 102031048 A CN102031048 A CN 102031048A
- Authority
- CN
- China
- Prior art keywords
- water
- percent
- agent
- varnish
- matte varnish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a flat varnish for waterborne wood, comprising the following components in parts by weight: 30-70 percent of waterborne acrylic emulsion, 0-30 percent of waterborne aliphatic polyurethane and mixture emulsion, 3-10 percent of film forming aid, 0.01-2 percent of antifoaming agent, 0.01-2 percent of dispersing agent, 0.1-5 percent of extinction powder, 0-2 percent of wetting agent, 0.01-2 percent of rheological additive, 0.01-2 percent of wax additive, 0.01-2 percent of hand-feeling addictive, 0.01-2 percent of thickening agent, 0.01-2 percent of ammonia water, 0.01-2 percent of coupling agent and 5-30 percent of water. The flat varnish for waterborne wood has the advantage of ensuring that a varnish film has better fullness, hardness, high chemical resistance, super-strong hand feeling and strong adhesive force on an oil primer. In addition, the flat varnish for waterborne wood can solve the compatibility between the aquosity and the oilness, ensure the varnish film cannot fall off after being dried and can meet the requirement for consumers on high environmental protection, low odor and less pollution.
Description
Technical field
The present invention relates to a kind of coating of chemical field, particularly relate to the protective cover that is applied to industrial wood furniture surface.
Background technology
The woodwork coating of China's use at present mostly is solvent-borne type greatly, and these woodwork coatings all contain a large amount of organic volatile compounds (VOC), and serious harm producers and workmen's is healthy.Along with the enhancing of people's environmental consciousness, conventional solvent type coating faces a severe challenge, advantage such as that water-borne coatings has is nontoxic, nonflammable, nonpollution environment.Water-borne coatings combines the high performance of solvent based coating with the low VOC content of water-borne coatings, environmental effect is good, construction is convenient relatively.But China's water-borne coatings now is in the technology starting stage, and film performance does not often reach human consumer's requirement, has defectives such as easily subsiding, fill inadequately, fullness ratio is not enough, hardness is not strong.
Summary of the invention
At above-mentioned technological deficiency, the technical problem to be solved in the present invention is to improve the sticking power of water-based woodenware matte varnish on oil primer, needs to solve the difficult compatible technological difficulties of water oil simultaneously.Even use the outstanding ACRYLIC EMULSION of sticking power as main film forming substance, but the ply adhesion only according to emulsion is far from being enough, other auxiliary agents that also need to arrange in pairs or groups improve sticking power between water oil, also need solve consistency between water-based and oiliness by hydrophilic and lipophilic film coalescence aid simultaneously.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is: a kind of water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 30-70%, water-based aliphatic polyurethane and mixture emulsion 0-30%, film coalescence aid 3-10%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.
Further: in above-mentioned water-based woodenware matte varnish, described aqueous acrylic emulsion and aqueous polyurethane emulsion are a kind of filmogens of key.Described film coalescence aid is one or more of the pure ether solvent used always of those skilled in the art.Described defoamer is mineral oil defoaming agent, silicone based defoamer, the type siloxane defoamer that those skilled in the art use always.Described dispersion agent is nonionogenic tenside, polyacrylic acid amine salt.Described flatting silica is the silicon-dioxide flatting silica.Described wetting agent is a siloxane type surfactants.Described auxiliary rheological agents is polyurethane-modified rheological agent.Described wax assistant is one or both in polyethylene wax, the amide waxe.Described feel auxiliary agent is organosilicon surface auxiliary agent, scratch resistance auxiliary agent, the slip(ping)agent that those skilled in the art use always.Described thickening material is one or more in polyacrylic thickening material, polyurethanes thickening material, the associative thickener.Described ammoniacal liquor is high purity ammoniacal liquor.Described coupling agent is a silane coupling agent.Described water is a kind of in pure water, distilled water, the deionized water.
The system lacquer method of using always according to those skilled in the art, aqueous acrylic emulsion and aqueous polyurethane emulsion are put into system lacquer container by formula rate, add entry and film coalescence aid, dispersion agent, defoamer, wax assistant, auxiliary rheological agents and flatting silica while stirring, high speed dispersion adds feel auxiliary agent, thickening material, wetting agent and ammoniacal liquor to fineness after qualified more while stirring, promptly gets this water-based woodenware matte varnish after mixing.
Compared with prior art, the prescription of above-mentioned water-based woodenware matte varnish is aqueous acrylic emulsion 30-70%, aqueous polyurethane and mixture emulsion 0-30%, film coalescence aid 3-10%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, water 5-30%.Select ACRYLIC EMULSION and polyaminoester emulsion to mix and use, make paint film have better fullness ratio, hardness, high chemical resistance.Product has used wax assistant and feel auxiliary agent, makes product have superpower feel.This prescription at first selects to have the ACRYLIC EMULSION of excellent adhesive attraction as main film forming substance, the polyaminoester emulsion of arranging in pairs or groups again strengthens the consistency of aqueous finish paint and oil primer, can not only give the sticking power of paint film excellence, and can solve compatibility problem between water-based and oiliness, guarantee can not come off behind the drying varniss, next is the selection of film coalescence aid, must select hydrophilic film coalescence aid and the combination of oil loving film coalescence aid, thoroughly solve the compatible problem between water-based and oiliness, give a complete smooth paint film simultaneously, make that by coupling agent self-crosslinking intensity increases greatly between emulsion particle at last, solve water-based paint film and the intermembranous problem of not adhering to of oil-base paint, the smell of high-performance oil primer is coated under the environmental protection finish paint of low smell, what this construction technology was produced films, and can reach the high-performance of oil paint, can satisfy the high environmental protection of human consumer again, low smell, oligosaprobic environmental requirement.
Embodiment
Following examples are that water-based woodenware matte varnish is preferably filled a prescription; these prescriptions are the indefiniteness embodiment; it is to be used to specify the present invention, and those skilled in the art can be protection scope of the present invention according to thinking of the present invention and the prescription that the proportioning of selecting materials filters out fully.
Embodiment 1
A kind of water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 40%, water-based aliphatic polyurethane and mixture emulsion 28%, film coalescence aid 3-10%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.The system lacquer method of using always according to those skilled in the art makes this varnish.This water-based woodenware matte varnish has makes paint film have better fullness ratio, hardness, high chemical resistance, superpower feel, the strong adhesion on oil primer.And it can solve the compatibility problem between water-based and oiliness, and this varnish is guaranteed can not come off behind the drying varniss, can satisfy the high environmental protection of human consumer again, low smell, oligosaprobic requirement.
Embodiment 2
A kind of water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 45%, water-based aliphatic polyurethane and mixture emulsion 26%, film coalescence aid 9%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.The system lacquer method of using always according to those skilled in the art makes this varnish.This water-based woodenware matte varnish has makes paint film have better fullness ratio, hardness, high chemical resistance, superpower feel, the strong adhesion on oil primer.And it can solve the compatibility problem between water-based and oiliness, and this varnish is guaranteed can not come off behind the drying varniss, can satisfy the high environmental protection of human consumer again, low smell, oligosaprobic requirement.
Embodiment 3
A kind of water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 50%, water-based aliphatic polyurethane and mixture emulsion 24%, film coalescence aid 8%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.The system lacquer method of using always according to those skilled in the art makes this varnish.This water-based woodenware matte varnish has makes paint film have better fullness ratio, hardness, high chemical resistance, superpower feel, the strong adhesion on oil primer.And it can solve the compatibility problem between water-based and oiliness, and this varnish is guaranteed can not come off behind the drying varniss, can satisfy the high environmental protection of human consumer again, low smell, oligosaprobic requirement.
Embodiment 4
A kind of water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 55%, water-based aliphatic polyurethane and mixture emulsion 22%, film coalescence aid 7%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.The system lacquer method of using always according to those skilled in the art makes this varnish.This water-based woodenware matte varnish has makes paint film have better fullness ratio, hardness, high chemical resistance, superpower feel, the strong adhesion on oil primer.And it can solve the compatibility problem between water-based and oiliness, and this varnish is guaranteed can not come off behind the drying varniss, can satisfy the high environmental protection of human consumer again, low smell, oligosaprobic requirement.
Embodiment 5
A kind of water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 60%, water-based aliphatic polyurethane and mixture emulsion 20%, film coalescence aid 6%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.The system lacquer method of using always according to those skilled in the art makes this varnish.This water-based woodenware matte varnish has makes paint film have better fullness ratio, hardness, high chemical resistance, superpower feel, the strong adhesion on oil primer.And it can solve the compatibility problem between water-based and oiliness, and this varnish is guaranteed can not come off behind the drying varniss, can satisfy the high environmental protection of human consumer again, low smell, oligosaprobic requirement.
Embodiment 6
One one kinds of water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 65%, water-based aliphatic polyurethane and mixture emulsion 18%, film coalescence aid 5%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.The system lacquer method of using always according to those skilled in the art makes this varnish.This water-based woodenware matte varnish has makes paint film have better fullness ratio, hardness, high chemical resistance, superpower feel, the strong adhesion on oil primer.And it can solve the compatibility problem between water-based and oiliness, and this varnish is guaranteed can not come off behind the drying varniss, can satisfy the high environmental protection of human consumer again, low smell, oligosaprobic requirement.
In the above-described embodiments:Described dispersion agent is the polyacrylic acid amine salt.Described flatting silica is the silicon-dioxide flatting silica.Described wetting agent is a siloxane type surfactants.Described auxiliary rheological agents is polyurethane-modified rheological agent.Described wax assistant is one or both in polyethylene wax, the amide waxe.Described thickening material is one or more in polyacrylic thickening material, polyurethanes thickening material, the associative thickener.Described ammoniacal liquor is high purity ammoniacal liquor; Described coupling agent is a silane coupling agent; Described water is a kind of in pure water, distilled water, the deionized water.
Claims (8)
1. water-based woodenware matte varnish, by weight: aqueous acrylic emulsion 30-70%, water-based aliphatic polyurethane and mixture emulsion 0-30%, film coalescence aid 3-10%, defoamer 0.01-2%, dispersion agent 0.01-2%, flatting silica 0.1-5%, wetting agent 0-2%, auxiliary rheological agents 0.01-2%, wax assistant 0.01-2%, feel auxiliary agent 0.01-2%, thickening material 0.01-2%, ammoniacal liquor 0.01-2%, coupling agent 0.01-2%, water 5-30%.
2. water-based woodenware matte varnish according to claim 1 is characterized in that: described dispersion agent is the polyacrylic acid amine salt.
3. water-based woodenware matte varnish according to claim 2 is characterized in that: described flatting silica is the silicon-dioxide flatting silica.
4. water-based woodenware matte varnish according to claim 3 is characterized in that: described wetting agent is a siloxane type surfactants.
5. water-based woodenware matte varnish according to claim 4 is characterized in that: described auxiliary rheological agents is polyurethane-modified rheological agent.
6. water-based woodenware matte varnish according to claim 5 is characterized in that: described wax assistant is one or both in polyethylene wax, the amide waxe.
7. water-based woodenware matte varnish according to claim 6 is characterized in that: described thickening material is one or more in polyacrylic thickening material, polyurethanes thickening material, the associative thickener.
8. water-based woodenware matte varnish according to claim 7 is characterized in that: described ammoniacal liquor is high purity ammoniacal liquor; Described coupling agent is a silane coupling agent; Described water is a kind of in pure water, distilled water, the deionized water.