CN104725941A - Water-based quick-drying paint - Google Patents
Water-based quick-drying paint Download PDFInfo
- Publication number
- CN104725941A CN104725941A CN201310712123.3A CN201310712123A CN104725941A CN 104725941 A CN104725941 A CN 104725941A CN 201310712123 A CN201310712123 A CN 201310712123A CN 104725941 A CN104725941 A CN 104725941A
- Authority
- CN
- China
- Prior art keywords
- water
- drying paint
- based quick
- agent
- quick drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of water-based paint, and specifically relates to a water-based quick-drying paint. The water-based quick-drying paint is composed of following ingredients, by weight, 25 to 55% of a polymer emulsion, 20 to 40% of a filler, 2 to 5% of a film forming auxiliary agent, 1 to 8% of a functional auxiliary agent, and the balance water. According to the water-based quick-drying paint, self-crosslinked acrylic emulsion is combined with styrene-acrylic emulsion with high solid content, so that obtained paint films possesses quick drying performance.
Description
Technical field
The present invention relates to water-borne coatings field, be specifically related to a kind of water-based quick drying paint.
Background technology
Aqueous acrylic urethane's coating of low-temperature curing now occupies an important position in automobile solid color enamel with the weather resistance of its excellence, weathering resistance, high gloss and resistance to marring, but this system generally need 70 DEG C at baking 30 ~ 40min can carry out polished finish, if the power consumption of this process is converted to consumption of coal, be equivalent to 300,000,000 tons of standard coals.If the baking that can realize lower temperature shorter time can carry out polished finish, will greatly save the consumption of the energy, also can enhance productivity simultaneously, shorten the production time.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of water-borne coatings of quick-drying.
Technical problem to be solved by this invention is achieved by the following technical programs:
A kind of water-based quick drying paint, is made up of the component of following weight percent:
Polymer emulsion 25 ~ 55%; Weighting agent 20 ~ 40%; Film coalescence aid 2 ~ 5%; Functional agent 1 ~ 8%; 100% is supplemented to water.
Further, described polymer emulsion is the mixture of ACRYLIC EMULSION, benzene emulsion.
ACRYLIC EMULSION is 3870 self-crosslinking acrylic emulsions of DSM company, and it has low smell, and quick-drying is easily polished, the transparency is good, and endurance is excellent, the feature of high rigidity, and benzene emulsion selects the A-1110 of Wei Laihui, it has large arch dam, quick-drying, the feature of high barrier property.
Further, described weighting agent is at least one in silica powder, silicon powder, light calcium carbonate, water-ground limestone, titanium dioxide.
Further, described functional agent is at least one in wetting agent, thickening material, dispersion agent and defoamer.Wetting agent is the wetting agent that the art is commonly used, as BYK346; Thickening material is the thickening material that the art is commonly used, as polyamide wax; Dispersion agent is the dispersion agent that the art is commonly used, as BYK194; Defoamer is the defoamer that the art is commonly used, as BYK024.
Further, at least one in described film coalescence aid diethylene glycol dimethyl ether, dipropylene glycol methyl ether, propylene glycol phenylate.
Further, the weight percent of each component is preferably:
ACRYLIC EMULSION 10 ~ 15%; Benzene emulsion 25 ~ 35%; Weighting agent 20 ~ 40%; Film coalescence aid 2 ~ 5%; Wetting agent 0.5 ~ 2%; Thickening material 0.5 ~ 2%; Dispersion agent 0.5 ~ 2%; Defoamer 0.5 ~ 2%; 100% is supplemented to water.
The present invention has following beneficial effect:
The present invention selects the collocation of the ACRYLIC EMULSION of self-crosslinking to have the benzene emulsion of large arch dam, makes become paint film have the characteristic of quick-drying.
Embodiment
Below in conjunction with embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention, is not limitation of the invention.
embodiment 1
ACRYLIC EMULSION 12%; Benzene emulsion 34%; Talcum powder 14%; Water-ground limestone 17%; Propylene glycol phenylate 5%; BYK346 0.5%; Polyamide wax 0.5%; BYK194 1%; BYK024 1%; 100% is supplemented to water.
embodiment 2
ACRYLIC EMULSION 15%; Benzene emulsion 28%; Silicon powder 18%; Talcum powder 15%; Dipropylene glycol methyl ether 3%; BYK346 1%; Polyamide wax 1%; BYK194 1%; BYK024 1%; 100% is supplemented to water.
embodiment 3
ACRYLIC EMULSION 14%; Benzene emulsion 32%; Light calcium carbonate 14%; Talcum powder 20%; Propylene glycol phenylate 3%; BYK346 1%; Polyamide wax 1%; BYK194 0.5%; BYK024 0.5%; 100% is supplemented to water.
The above embodiment only have expressed embodiments of the present invention; it describes comparatively concrete and detailed; but therefore can not be interpreted as the restriction to the scope of the claims of the present invention; in every case the technical scheme adopting the form of equivalent replacement or equivalent transformation to obtain, all should drop within protection scope of the present invention.
Claims (6)
1. a water-based quick drying paint, is characterized in that being made up of the component of following weight percent:
Polymer emulsion 25 ~ 55%;
Weighting agent 20 ~ 40%;
Film coalescence aid 2 ~ 5%;
Functional agent 1 ~ 8%;
100% is supplemented to water.
2. a kind of water-based quick drying paint according to claim 1, is characterized in that: described polymer emulsion is the mixture of ACRYLIC EMULSION, benzene emulsion.
3. a kind of water-based quick drying paint according to claim 1, is characterized in that: described weighting agent is at least one in silica powder, silicon powder, light calcium carbonate, water-ground limestone, titanium dioxide.
4. a kind of water-based quick drying paint according to claim 1, is characterized in that: described functional agent is at least one in wetting agent, thickening material, dispersion agent and defoamer.
5. a kind of water-based quick drying paint according to claim 1, is characterized in that: at least one in described film coalescence aid diethylene glycol dimethyl ether, dipropylene glycol methyl ether, propylene glycol phenylate.
6. a kind of water-based quick drying paint according to claim 1, is characterized in that: the weight percent of each component is preferably:
ACRYLIC EMULSION 10 ~ 15%;
Benzene emulsion 25 ~ 35%;
Weighting agent 20 ~ 40%;
Film coalescence aid 2 ~ 5%;
Wetting agent 0.5 ~ 2%;
Thickening material 0.5 ~ 2%;
Dispersion agent 0.5 ~ 2%;
Defoamer 0.5 ~ 2%;
100% is supplemented to water.