CN102021543A - 一种复合络合剂及含有该复合络合剂的化学镀镍溶液 - Google Patents
一种复合络合剂及含有该复合络合剂的化学镀镍溶液 Download PDFInfo
- Publication number
- CN102021543A CN102021543A CN 201010585393 CN201010585393A CN102021543A CN 102021543 A CN102021543 A CN 102021543A CN 201010585393 CN201010585393 CN 201010585393 CN 201010585393 A CN201010585393 A CN 201010585393A CN 102021543 A CN102021543 A CN 102021543A
- Authority
- CN
- China
- Prior art keywords
- plating solution
- acid
- chemical nickel
- compound complex
- complexing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种复合络合剂及含有该复合络合剂的化学镀镍溶液。本发明复合络合剂成分己二酸5~100g;酒石酸3~15g;苹果酸或柠檬酸中的一种或两种4~15g;丁二酸或丙酸5~6g。本发明解决了现有技术镀液循环周期短的缺点,同时本发明的化学镀镍溶液不含铅、镉等18种全球高度关注的污染物,具有较低的工作温度,高硬度,同时优良的耐蚀性能,符合清洁生产的要求。
Description
技术领域
本发明涉及一种化学镀镍领域,具体涉及一种复合络合剂及含有该复合络合剂的化学镀镍溶液。
背景技术
化学镀是利用合适的还原剂,将溶液中的金属离子还原出来,并沉积在经催化活化的镀件表面的一种化学处理过程。
近年来,化学镀作为一种表面处理技术在工业上日益受到重视,其应用范围覆盖了工业生产的各个领域。化学镀镍的不断发展归结于该技术具有良好的工艺性,化学镀镍层具有独特的物理、化学和机械性能,而且工艺设备简单,易于控制和掌握,镀层均匀平整,适用于复杂形状零件,对环境友好,这些都是电镀技术所不具备的。
公开号为CN1600899A的中国专利申请,公开了一种化学镀镍复合添加剂,该复合添加剂由柠檬酸等络合剂、乙酸钠等缓冲剂、丁二酸等加速剂和硫脲等稳定剂组成;它虽然避免了大量分析调整多种成分的麻烦,使用较方便;但是镀液的使用寿命只有6-8个循环周期,不能达到“节能降耗、减污增效”的发展要求。
发明内容
本发明的目的在于克服现有技术的缺陷,提供一种复合络合剂及含有该复合络合剂的化学镀镍溶液,本发明解决了现有技术镀液循环周期短的缺点,同时本发明的化学镀镍溶液不含铅、镉等18种全球高度关注的污染物,具有较低的工作温度,高硬度,同时优良的耐蚀性能,符合清洁生产的要求。
本发明的目的通过以下技术方案来实现:
一种复合络合剂,一升水溶液中各组分的含量为:
己二酸 5~100g
酒石酸 3~15g
苹果酸或柠檬酸中的一种或两种 4~15g
丁二酸或丙酸 5~6g。
含有所述的复合络合剂的化学镀镍溶液,其特征在于,组成为:
硫酸镍 25~35g/L
乳酸 7~10ml/L
乙酸钠 5~10g/L
次亚磷酸钠 20~40g/L
复合络合剂 8~30g/L
稳定剂 0.1~1.5g/L
表面活性剂 0.2~1g/L。
所述稳定剂为氧化钼、硫脲、硫代硫酸钠或碘化钾中的一种或两种以上。
所述表面活性剂为十二烷基硫酸钠、月桂酸硫酸钠或十二烷基苯磺酸钠中的一种或两种。
所述化学镀镍溶液的使用温度为80~88℃。
本发明相对于现有技术所具有的优点和有益效果:
(1)本发明的复合络合剂采用己二酸与羧酸按特定比例复配,得到的的镀液使用周期长,硬度高,未经热处理硬度达500HV,经过热处理,硬度达900HV;耐蚀性好,中性盐雾试验达1000小时(20μm以上)。
(2)本发明通过选择稳定剂的组成和添加比例,镀液稳定性好、循环周期达到10周期以上,沉积速度大于10μm/h,(88℃)。
(3)本发明的化学镀镍溶液不含铅、镉等18种全球高度关注的污染物,具有较低的工作温度,高硬度,同时优良的耐蚀性能,完全符合清洁生产的要求。
具体实施方式
实施例1
本发明环保化学镀镍溶液,配方组成为:
硫酸镍 35g/L
乳酸 7ml/L
乙酸钠 5g/L
次亚磷酸钠 30g/L
复合络合剂 8g/L
稳定剂 0.1g/L
月桂酸硫酸钠 0.2g/L
本发明环保化学镀镍溶液按照上述配方称取原料,稀释至1L得到化学镀镍溶液。
复合络合剂的组成为:
一升水溶液中各组成成分的含量为:己二酸5g,酒石酸10g,苹果酸4g,柠檬酸10g,丁二酸5g。
称取硫酸镍35g,乳酸7ml,乙酸钠5g,次亚磷酸钠30g,复合络合剂8g,稳定剂(硫代硫酸钠)0.1g,月桂酸硫酸钠0.2g,溶于水,搅拌均匀配成1升的化学镀镍溶液。
实施例2
本发明环保化学镀镍溶液,配方组成为:
硫酸镍 25g/L
乳酸 10ml/L
乙酸钠 10g/L
次亚磷酸钠 20g/L
复合络合剂 30g/L
稳定剂 1.5g/L
十二烷基硫酸钠 1g/L
本发明环保化学镀镍溶液按照上述配方称取原料,稀释至1L得到化学镀镍溶液。
复合络合剂的组成为:
一升水溶液中各组成成分的含量为:己二酸100g,酒石酸3g,苹果酸8g,丁二酸6g。
称取硫酸镍25g,乳酸10ml,乙酸钠10g,次亚磷酸20g,复合络合剂30g,稳定剂(硫脲1g和碘酸钾0.5g),十二烷基硫酸钠1g,溶于水,搅拌均匀配成1升的化学镀镍溶液。
实施例3
本发明环保化学镀镍溶液,配方组成为:
硫酸镍 30g/L
乳酸 8ml/L
乙酸钠 5g/L
次亚磷酸钠 40g/L
复合络合剂 20g/L
稳定剂 1g/L
十二烷基硫酸钠 0.2g/L
本发明环保化学镀镍溶液按照上述配方称取原料,稀释至1L得到化学镀镍溶液。
复合络合剂的组成为:
一升水溶液中各组成成分的含量为:丁二酸5g、己二酸50g、酒石酸中15g、苹果酸5g。
称取硫酸镍30g,乳酸8ml,乙酸钠5g,次亚磷酸钠40g,复合络合剂20g,稳定剂(氧化钼0.2g,硫代硫酸钠0.1g,碘酸钾0.7g),十二烷基硫酸钠0.2g,溶于水,搅拌均匀,配成1升的化学镀镍溶液。
应用实施例
将实施例1,2和3的镀液各放入三个1升的玻璃镀槽中,用恒温水浴箱控制镀镍温度为88℃,使用氨水调节镀液pH值为5.5。将经处理过的四片钢板(50mm×30mm×1.2mm),浸入到镀液中,1小时后将镀件取出,清洗后,肉眼可见在镀件表面有一层均匀、致密、光亮的镀层。结果如表1所示。
表1
项目 | 实施例1 | 实施例2 | 实施例3 |
硬度热化后 | 900HV | 900HV | 900HV |
盐雾试验的耐盐雾性(hr) | 1000 | 1000 | 1000 |
循环周期(个) | 10 | 10 | 10 |
沉积速度(μm/h) | 12 | 11 | 13 |
本发明镀液使用10个周期后,沉积速度仍能达到10μm/h。
本发明的复合络合剂采用己二酸与羧酸按特定比例复配,得到的的镀液使用周期长,硬度高,未经热处理硬度达500HV,经过热处理,硬度达900HV;耐蚀性好,中性盐雾试验达1000小时(20μm以上)。本发明通过选择稳定剂的组成和添加比例,镀液稳定性好(88℃)。本发明的化学镀镍溶液不含铅、镉等18种全球高度关注的污染物,具有较低的工作温度,高硬度,同时优良的耐蚀性能,完全符合清洁生产的要求。
Claims (5)
1.一种复合络合剂,其特征在于,一升水溶液中各组分的含量为:
己二酸 5~100g
酒石酸 3~15g
苹果酸或柠檬酸中的一种或两种 4~15g
丁二酸或丙酸 5~6g。
2.含有权利要求1所述的复合络合剂的化学镀镍溶液,其特征在于,组成为:
硫酸镍 25~35g/L
乳酸 7~10ml/L
乙酸钠 5~10g/L
次亚磷酸钠 20~40g/L
复合络合剂 8~30g/L
稳定剂 0.1~1.5g/L
表面活性剂 0.2~1g/L。
3.根据权利要求1所述的化学镀镍溶液,其特征在于,所述稳定剂为氧化钼、硫脲、硫代硫酸钠或碘化钾中的一种或两种以上。
4.根据权利要求1所述的化学镀镍溶液,其特征在于,所述表面活性剂为十二烷基硫酸钠、月桂酸硫酸钠或十二烷基苯磺酸钠中的一种或两种。
5.根据权利要求1所述的化学镀镍溶液,其特征在于,所述化学镀镍溶液的使用温度为80~88℃。