CN101979361A - 钛金高科技保健陶瓷材料 - Google Patents

钛金高科技保健陶瓷材料 Download PDF

Info

Publication number
CN101979361A
CN101979361A CN 201010294553 CN201010294553A CN101979361A CN 101979361 A CN101979361 A CN 101979361A CN 201010294553 CN201010294553 CN 201010294553 CN 201010294553 A CN201010294553 A CN 201010294553A CN 101979361 A CN101979361 A CN 101979361A
Authority
CN
China
Prior art keywords
oxide
titanium
percent
ceramic material
care
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010294553
Other languages
English (en)
Inventor
梁福标
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGZHOU JIAYU TIMEKEEPER CO Ltd
Original Assignee
GUANGZHOU JIAYU TIMEKEEPER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGZHOU JIAYU TIMEKEEPER CO Ltd filed Critical GUANGZHOU JIAYU TIMEKEEPER CO Ltd
Priority to CN 201010294553 priority Critical patent/CN101979361A/zh
Publication of CN101979361A publication Critical patent/CN101979361A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种钛金高科技保健陶瓷材料。以重量百分含量计，由0.1～2％的氧化钛，84.572～87.605％的氧化锆，4.622～4.758％的氧化铱，1.962～2.088％的氧化铝，2.156～2.463％的氧化硅，1.716～2.364％的氧化铪，0.132～0.206％的氧化镁及1.435～1.811％的其他氧化物组成。本发明所产生的负离子和远红外线远高于普通氧化锆陶瓷产品，具有促进人体新陈代谢和血液循环的效用。

Description

钛金高科技保健陶瓷材料
技术领域
本发明属于材料技术领域，更具体是涉及一种钛金高科技保健陶瓷材料。
背景技术
现有的氧化锆陶瓷材料是高纯度的氧化锆和氧化铱的混合物烧制而成，不含有钛金成份，也不具备保健作用。
现有保健首饰、手表产品是将锗粒、钛合金等一些保健产品镶嵌于首饰、手表等产品的底部，而实际能够发挥效用的只是镶嵌物，作用的范围较小，对于一些皮肤有敏感或过敏反应的人士会产生副作用，同时镶嵌物可能会产生脱落的现象；从美观的角度讲，镶嵌物同首饰等并不能合成一体，影响产品的外观效果。
发明内容
本发明的目的在于克服现有技术存在的不足，提供一种钛金高科技保健陶瓷材料。
为达到上述目的，本发明采取了如下的技术方案：
钛金高科技保健陶瓷材料，以重量百分百计，由如下成分组成：
氧化钛：0.1～2％
氧化锆：84.572～87.605％
氧化铱：4.622～4.758％
氧化铝：1.962～2.088％
氧化硅：2.156～2.463％
氧化铪：1.716～2.364％
氧化镁：0.132～0.206％
其他氧化物：1.435～1.811％。
本发明的陶瓷材料的制备方法如下：
将钛元素及一些微量元素添加到氧化锆粉体中，经过注塑成型和1300～1700℃的高温烧结后形成。
与现有技术相比，本发明具有如下有益效果：
1、本发明是在粉体配制时已将钛金属及一些微量元素按照一定的配比混入到氧化锆粉体当中，而在烧结过程中经过一些特殊处理，使钛元素保留并融入到氧化锆陶瓷中。从外观上看能够保持氧化锆陶瓷高光泽、高硬度、高耐磨性能，同时均匀分布的钛及其他对人体有益的微量元素能够释放远红外线和负离子，促进人体内的血液循环，对人体产生保健效果。
2、本发明所产生的负离子和远红外线远高于普通氧化锆陶瓷产品，具有促进人体新陈代谢和血液循环的效用。
具体实施方式
以下结合具体实施例来对本发明作进一步的描述，但本发明所要求保护的范围并不局限于实施例所涉及之范围。
实施例1：
钛金高科技保健陶瓷材料的组分及比例如下：
  成分   重量比例(％)
  1   氧化钠Na2O   0.021
  2   氧化镁MgO   0.132
  3   氧化铝Al2O3   2.088
  4   氧化硅SiO2   2.156
  5   氧化磷P2O5   0.387
  6   氯Cl   0.062
  7   氧化钾K2O   0.011
  8   氧化钙CaO   0.142
  9   氧化钛TiO2   0.100
  10   氧化锰MnO   0.011
  11   氧化铁Fe2O3   0.022
  12   氧化镍NiO   0.028
  13   氧化铱Y2O3   4.758
  14   氧化锆ZrO2   87.605
  15   氧化镧La2O3   0.206
  16   氧化铈CeO2   0.317
  17   氧化钕Nd2O3   0.166
  18   氧化铪HfO2   1.716
  19   氧化铊Tl2O2   0.017
  20   氧化钍ThO2   0.055
实施例2
钛金高科技保健陶瓷材料的组分及比例如下：
  组分   重量百分比(％)
  1   氧化钠Na2O   0.024
  2   氧化镁MgO   0.156
  3   氧化铝Al2O3   2.067
  4   氧化硅SiO2   2.364
  5   氧化磷P2O5   0.401
  6   氯Cl   0.066
  7   氧化钾K2O   0.014
  8   氧化钙CaO   0.184
  9   氧化钛TiO2   0.271
  10   氧化锰MnO   0.013
  11   氧化铁Fe2O3   0.020
  12   氧化镍NiO   0.030
  13   氧化铱Y2O3   4.723
  14   氧化锆ZrO2   87.138
  15   氧化镧La2O3   0.217
  16   氧化铈CeO2   0.322
  17   氧化钕Nd2O3   0.175
  18   氧化铪HfO2   1.738
  19   氧化铊Tl2O2   0.019
  20   氧化钍ThO2   0.058
实施例3
钛金高科技保健陶瓷材料的组分及比例如下：
 组分   重量比例(％)
  1  氧化钠Na2O   0.036
  2  氧化镁MgO   0.206
  3  氧化铝Al2O3   1.962
  4  氧化硅SiO2   2.463
  5  氧化磷P2O5   0.487
  6  氯Cl   0.071
  7  氧化钾K2O   0.017
  8  氧化钙CaO   0.196
  9  氧化钛TiO2   2.000
  10  氧化锰MnO   0.015
  11  氧化铁Fe2O3   0.018
  12  氧化镍NiO   0.033
  13  氧化铱Y2O3   4.622
  14  氧化锆ZrO2   84.572
  15  氧化镧La2O3   0.288
  16  氧化铈CeO2   0.376
  17  氧化钕Nd2O3   0.189
  18  氧化铪HfO2   2.364
  19  氧化铊Tl2O2   0.022
  20  氧化钍ThO2   0.063
上述实施例1～3的陶瓷材料的制备方法为：将钛元素及一些微量元素添加到氧化锆粉体中，经过注塑成型和1300～1700℃的高温烧结后形成。

Claims (4)

1.钛金高科技保健陶瓷材料，其特征在于：以重量百分含量计，由如下成分组成：
氧化钛：0.1～2
氧化锆：84.572～87.605
氧化铱：4.622～4.758
氧化铝：1.962～2.088
氧化硅：2.156～2.463
氧化铪：1.716～2.364
氧化镁：0.132～0.206
其他氧化物：1.435～1.811。
2.根据权利要求1所述的钛金高科技保健陶瓷材料，其特征在于：以重量百分含量计，由如下成分组成：
氧化钠：0.021，氧化镁：0.132，氧化铝：2.088，氧化硅：2.156，
氧化磷：0.387，氯：0.062，氧化钾：0.011，氧化钙：0.142，
氧化钛：0.100，氧化锰：0.011，氧化铁：0.022，氧化镍：0.028，
氧化铱：4.758，氧化锆：87.605，氧化镧：0.206，氧化铈：0.317，
氧化钕：0.166，氧化铪：1.716，氧化铊：0.017，氧化钍：0.055。
3.根据权利要求1所述的钛金高科技保健陶瓷材料，其特征在于：以重量百分含量计，由如下成分组成：
氧化钠：0.024，氧化镁：0.156，氧化铝：2.067，氧化硅：2.364，
氧化磷：0.401，氯：0.066，氧化钾：0.014，氧化钙：0.184，
氧化钛：0.271，氧化锰：0.013，氧化铁：0.020，氧化镍：0.030，
氧化铱：4.723，氧化锆：87.138，氧化镧：0.217，氧化铈：0.322，
氧化钕：0.175，氧化铪：1.738，氧化铊：0.019，氧化钍：0.058。
4.根据权利要求1所述的钛金高科技保健陶瓷材料，其特征在于：以重量百分含量计，由如下成分组成：
氧化钠：0.036，氧化镁：0.206，氧化铝：1.962，氧化硅：2.463，
氧化磷：0.487，氯：0.071，氧化钾：0.017，氧化钙：0.196，
氧化钛：2.000，氧化锰：0.015，氧化铁：0.018，氧化镍：0.033，
氧化铱：4.622，氧化锆：84.572，氧化镧：0.288，氧化铈：0.376，
氧化钕：0.189，氧化铪：2.364，氧化铊：0.022，氧化钍：0.063。
CN 201010294553 2010-09-28 2010-09-28 钛金高科技保健陶瓷材料 Pending CN101979361A (zh)