CN101979327B - 一种钙钛矿型氧化物LaMnO3空心球的制备方法 - Google Patents
一种钙钛矿型氧化物LaMnO3空心球的制备方法 Download PDFInfo
- Publication number
- CN101979327B CN101979327B CN2010102894551A CN201010289455A CN101979327B CN 101979327 B CN101979327 B CN 101979327B CN 2010102894551 A CN2010102894551 A CN 2010102894551A CN 201010289455 A CN201010289455 A CN 201010289455A CN 101979327 B CN101979327 B CN 101979327B
- Authority
- CN
- China
- Prior art keywords
- atmosphere
- pmma
- product
- temperature
- hollow ball
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种钙钛矿型氧化物LaMnO3空心球的制备方法,将六水硝酸镧∶质量分数为50%的Mn(NO3)2水溶液按摩尔比为1∶1溶于聚乙二醇400,每0.01mol硝酸镧所用聚乙二醇400为2-6mL,然后加入甲醇,将上述混合液倾入装有PMMA的容器中使之完全湿润,然后抽滤、室温干燥,装入磁舟置于管式炉中,先在N2气氛下以1℃/min的速率从室温升至300℃并在该温度下保持3h,待降至50℃后切换成空气气氛,再以1℃/min的速率升至750℃并在该温度下保持4h。本发明具有原料廉价易得,制备过程简单,产物粒子形貌和孔尺寸可控等特征。
Description
技术领域
本发明涉及一种钙钛矿型氧化物空心球的制备方法,具体地说涉及一种以聚甲基丙烯酸甲酯(PMMA)为硬模板制备钙钛矿型氧化物LaMnO3空心球的方法。
背景技术
钙钛矿型氧化物空心球因具有轻质、高强度、高比表面积等优异性能而使其在电、磁、吸附和催化等物理和化学领域具有很大的应用前景。
目前,空心球结构化合物的制备方法很多,主要分为2大类:模板法和非模板法。模板法又分为沉积和表面反应法、逐层组装法和微封装法;非模板法分为液滴法、喷雾干燥法和乳液相分离法。已有文献报道过钙钛矿型氧化物空心球的制备方法。例如:Li等(X.Li et al.,Chem.Mater.,2010,22,4879-4889)以硝酸镧和硝酸铁为金属源,以去离子水为溶剂,采用水热和柠檬酸络合联用技术,将所得复合金属柠檬酸盐于800℃焙烧后制得了钙钛矿型氧化物LaFeO3空心球。Tian等(X.L.Tian et al.,Cryst.Growth Des.,2010,10,3990-3995)以氢氧化钡,二氧化钛为金属源,采用熔融盐法,制得了钙钛矿型氧化物BaTiO3空心球。Kim等(Y.N.Kim et al.,J.Appl.Phys.,2004,95,7088-7090)采用SiO2微球为硬模板,蔗糖为碳源,合成三维有序大孔碳,然后以醋酸镧、醋酸钙和醋酸锰为金属源,以乙二醇甲醚和乙醇为溶剂,得到的前驱体溶液浸渍大孔碳,产物在氧气气氛中于800℃焙烧后制得了钙钛矿型氧化物La0.7Ca0.3MnO3空心球。迄今为止,国内外文献和专利尚无报道过采用PMMA微球为硬模板直接制备钙钛矿型氧化物锰酸镧空心球的方法。
锰酸镧空心球因具有轻质,高强度的特点和拥有较高比表面积,从而有利于反应物或吸附质分子的扩散与吸附,使之在多相催化及吸附领域具有重要的应用价值。因此,研发制备钙钛矿型氧化物锰酸镧空心球的方法具有重要意义。硬模板法能较好地控制产物的形貌和尺寸,适于制备钙钛矿型氧化物LaMnO3空心球。
本发明描述的方法是采用以PMMA微球为硬模板,以聚乙二醇400为添加剂,以甲醇为溶剂,将含有以上添加剂、溶剂和可溶性金属盐的混合溶液浸渍PMMA后,采用两步焙烧法(即先在氮气气氛中焙烧,再在空气气氛中焙烧)制备钙钛矿型氧化物LaMnO3空心球。其中聚乙二醇和PMMA微球对于获得空心球状结构的目标产物起到了重要作用。迄今为止,尚无文献和专利报道过使用PMMA微球为硬模板和聚乙二醇为添加剂制备钙钛矿型氧化物LaMnO3空心球。
发明内容
本发明的目的在于提供一种钙钛矿型氧化物LaMnO3空心球的制备方法。
本发明的一种钙钛矿型氧化物LaMnO3空心球的制备方法,即以密堆积排列的PMMA微球为硬模板和以聚乙二醇为添加剂的方法制备钙钛矿型氧化物LaMnO3空心球,步骤如下:
按照六水硝酸镧:质量分数为50%的Mn(NO3)2水溶液中Mn(NO3)2摩尔比为1∶1的比例溶于聚乙二醇400(分子量为400)中,每0.01mol六水硝酸镧所用聚乙二醇400为2-6mL,常温下磁力搅拌4h,形成均一溶液,再加入甲醇,使总金属浓度为1mol/L,将上述混合液倾入装有PMMA的容器中,浸渍约5h,使之完全湿润,随后抽滤、室温干燥12h,装入磁舟置于管式炉中,先在N2气氛下(20mL/min)以1℃/min的速率从室温升至300℃并在该温度下保持3h,待降至50℃后切换成空气气氛(20mL/min),再以1℃/min的速率升至750℃并在该温度下保持4h,得到单相钙钛矿型氧化物LaMnO3空心球。
本发明具有原料廉价易得,制备过程简单,产物粒子形貌和孔尺寸可控等特征。
利用D8 ADVANCE型X射线衍射仪(XRD)、ZEISS SUPRA 55型高分辨扫描电子显微镜(HRSEM)等仪器表征所得目标产物的晶体结构和粒子形貌。结果表明,依照本发明方法所制得的LaMnO3样品呈现纳米空心球状结构。
附图说明
图1为所制得钙钛矿型氧化物LaMnO3样品的XRD谱图,其中曲线1(a)、1(b)和1(c)分别为实施例1、实施例2和实施例3样品的XRD谱图。
图2为所制得的钙钛矿型氧化物LaMnO3样品的HRSEM照片,其中图2(a)、2(b)和2(c)分别为实施例1、实施例2和实施例3样品的HRSEM照片。
具体实施方式
为了进一步了解本发明,下面以实施例作详细说明,并给出附图描述本发明得到的钙钛矿型氧化物LaMnO3空心球。
实施例1:称取6.5g La(NO3)3·6H2O和4.15mL质量分数为50%的Mn(NO3)2水溶液,置于烧杯中,加入3mL聚乙二醇400,磁力搅拌4h后,形成均一溶液,再加入18mL甲醇。此溶液为前驱体溶液。将上述混合液倾入装有1.0g聚甲基丙烯酸甲酯(PMMA)微球硬模板的烧杯中。为保持PMMA的原有有序排列,在此混合液倾入过程中不搅拌。混合液浸渍PMMA大约5h后抽滤得到的固体在室温下干燥12h,随后将固体装入磁舟置于管式炉中,先在N2气氛下(20mL/min)以1℃/min的速率从室温升至300℃并在该温度下保持3h,待降至50℃后切换成空气气氛(20mL/min),再以1℃/min的速率升至750℃并在该温度下保持4h,即得到钙钛矿型氧化物LaMnO3空心球,球径约为50nm。
实施例2:称取6.5g La(NO3)3·6H2O和4.15mL质量分数为50%的Mn(NO3)2水溶液,置于烧杯中,加入5mL聚乙二醇400,磁力搅拌4h后,形成均一溶液,再加入16mL甲醇。此溶液为前驱体溶液。将上述混合液倾入装有1.0g PMMA的烧杯中。为保持PMMA的原有有序排列,在此混合液倾入过程中不搅拌。混合液浸渍PMMA大约5h后抽滤得到的固体在室温下干燥12h,随后将固体装入磁舟置于管式炉中,先在N2气氛下(20mL/min)以1℃/min的速率从室温升至300℃并在该温度下保持3h,待降至50℃后切换成空气气氛(20mL/min),再以1℃/min的速率升至750℃并在该温度下保持4h,即得到钙钛矿型氧化物LaMnO3空心球,球径约为50nm。
实施例3:称取6.5g La(NO3)3·6H2O和4.15mL质量分数为50%的Mn(NO3)2水溶液,置于烧杯中,加入7mL聚乙二醇400,磁力搅拌4h后,形成均一溶液,再加入14mL甲醇。此溶液为前驱体溶液。将上述混合液倾入装有1.0g PMMA硬模板的烧杯中。为保持PMMA的原有有序排列,在此混合液倾入过程中不搅拌。混合液浸渍PMMA大约5h后抽滤得到的固体在室温下干燥24h,随后将固体装入磁舟置于管式炉中,先在N2气氛下(20mL/min)以1℃/min的速率从室温升至300℃并在该温度下保持3h,待降至50℃后切换成空气气氛(20mL/min),再以1℃/min的速率升至750℃并在该温度下保持4h,即得到钙钛矿型氧化物LaMnO3空心球,球径约为25nm。
Claims (2)
1.一种钙钛矿型氧化物LaMnO3空心球的制备方法,其特征在于,即以密堆积排列的PMMA微球为硬模板和以聚乙二醇为添加剂,步骤如下:
按照六水硝酸镧:质量分数为50%的Mn(NO3)2水溶液中Mn(NO3)2摩尔比为1∶1的比例溶于聚乙二醇400中,每0.01mol六水硝酸镧所用聚乙二醇400为2-6mL,常温下磁力搅拌4h,形成均一溶液,再加入甲醇,使总金属浓度为1mol/L,将上述混合液倾入装有PMMA的容器中,浸渍5h,使之完全湿润,随后抽滤、室温干燥12h,装入磁舟置于管式炉中,先在N2气氛下以1℃/min的速率从室温升至300℃并在该温度下保持3h,待降至50℃后切换成空气气氛,再以1℃/min的速率升至750℃并在该温度下保持4h,得到单相钙钛矿型氧化物LaMnO3空心球。
2.按照权利要求1所述的制备方法,其特征在于,所述N2气氛为20mL/min,空气气氛为20mL/min。