CN101914671A - 钢锭加热节能方法 - Google Patents

钢锭加热节能方法 Download PDF

Info

Publication number
CN101914671A
CN101914671A CN2010102587661A CN201010258766A CN101914671A CN 101914671 A CN101914671 A CN 101914671A CN 2010102587661 A CN2010102587661 A CN 2010102587661A CN 201010258766 A CN201010258766 A CN 201010258766A CN 101914671 A CN101914671 A CN 101914671A
Authority
CN
China
Prior art keywords
temperature
heating
preheating
steel ingot
forging
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010102587661A
Other languages
English (en)
Other versions
CN101914671B (zh
Inventor
张奇志
胡永平
任胜利
田君
石宝凤
李连贵
青格勒图
高军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia North Heavy Industries Group Co Ltd
Original Assignee
Inner Mongolia North Heavy Industries Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia North Heavy Industries Group Co Ltd filed Critical Inner Mongolia North Heavy Industries Group Co Ltd
Priority to CN2010102587661A priority Critical patent/CN101914671B/zh
Publication of CN101914671A publication Critical patent/CN101914671A/zh
Application granted granted Critical
Publication of CN101914671B publication Critical patent/CN101914671B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种钢锭加热节能方法，属于机械制造领域。本发明将10～17.5吨冷钢锭装入温度为620℃～650℃加热炉中，保温时间为8～12小时；然后以50～70℃/h的升温速度升温到830℃～860℃，保温10～18小时，再升温至锻造温度1200℃-1240℃，保温后出炉锻造。本发明通过提高装炉温度和预热温度，加快升温速度，使钢锭在预热阶段就完成预热过程和奥氏体转变的全部过程，钢锭预热加热时间可缩短25％左右，节能降耗显著，处于国内领先水平。

Description

钢锭加热节能方法
技术领域
本发明涉及一种钢锭加热节能方法，属于机械制造领域。
背景技术
工厂10～17.5t的PCrNi3MoV钢锭加热到锻造温度需要预热加热的总时间45小时以上，加热时间长能耗大，不适应工厂高效快捷生产。天然气的燃料热值效率大、先进精炼设备的使用和冶炼技术工艺水平的提升，钢质纯净度不断提高，为提高加热升温速度和研究制定钢锭新的节能加热工艺创造了条件。
发明内容
本发明的目的在于提供一种能够缩短钢锭锻造温度预热加热时间，生产效率高，能耗小的钢锭加热节能方法。
技术解决方案：本发明将10-17.5吨冷钢锭装入温度为620℃-650℃加热炉中，保温时间为8-12小时；然后以50～70℃/h的升温速度预热温度为830℃-860℃，保温10-18小时，升温至锻造温度1200℃-1240，保温后出炉锻造。
本发明在热装炉的条件下，采用提高装炉温度，加大温差，加快热量传递速度，缩短钢锭到装炉温度的时间。到装炉温度后保持一定的时间，使内外保持温度一致，组织均匀化，为下一步的分级预热和奥氏体化做好准备。提高预热温度到奥氏体化的温度，使钢锭在预热阶段就完成预热过程和奥氏体转变的全部过程，缩短预热加热时间，同时也缩小加热到锻造温度的温差，保证了直接加热到锻造温度。由于奥氏体良好的塑韧性可适当提高加热速度，以较大的加热速度直接加热到锻造温度，缩短加热到锻造温度的时间和保温时间。
本发明是以天然气为热源的台车式加热炉加热10～17.5t的PCrNi3MoV钢锭的一种加热方法。改变原有的钢锭预热加热工艺，解决锻造加热时间长，能耗大、效率低的问题。
本发明特点：1.提高装炉温度和预热温度，加快升温速度，使钢锭在预热阶段就完成预热过程和奥氏体转变的全部过程。
2.有效缩短冷炮钢钢锭预热加热时间25％左右，提高生产率，节能降耗显著。
具体实施例：
本发明在天然气加热的台车式加热炉中加热10t的PCrNi3MoV坯料：将冷钢锭装入温度为650℃加热炉中，保温时间为8h；然后以60℃/h的升温速度升温至850±10℃，保温时间10小时，使钢锭在预热阶段就完成预热过程和奥氏体转变的全部过程，缩短预热加热时间，再以100℃/h的升温速度加热到锻造温度1220±20℃，保温3h。最后出炉锻造。

Claims (1)

1.钢锭加热节能方法，其特征在于，将10～17.5吨冷钢锭装入温度为620℃～650℃加热炉中，保温时间为8～12小时；然后以50～70℃/h的升温速度升温到830℃～860℃，保温10～18小时，再升温至锻造温度1200℃-1240℃，保温后出炉锻造。
CN2010102587661A 2010-08-11 2010-08-11 钢锭加热节能方法 Active CN101914671B (zh)