CN101705346B - 提高zg270-500偏心体硬度的热处理方法 - Google Patents
提高zg270-500偏心体硬度的热处理方法 Download PDFInfo
- Publication number
- CN101705346B CN101705346B CN200910230346XA CN200910230346A CN101705346B CN 101705346 B CN101705346 B CN 101705346B CN 200910230346X A CN200910230346X A CN 200910230346XA CN 200910230346 A CN200910230346 A CN 200910230346A CN 101705346 B CN101705346 B CN 101705346B
- Authority
- CN
- China
- Prior art keywords
- eccentric body
- cooled
- heating
- hours
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种提高ZG270-500偏心体硬度的热处理方法，包括以下步骤：将偏心体放置在加热炉中加热高于650℃，并保温3以上小时；然后放到加热炉中加热高于850℃，保温5小时以上出炉，放置在空气中冷却至室温；将上述冷却至室温的偏心体放置在加热炉中加热至650℃，并保温至3小时以上；将上述偏心体继续加热至850℃以上，并保温5小时以上，然后在空气中冷却至偏心体尖角处发黑其他部位温度在840～860℃，接着对偏心体最大厚度的部位进行水冷最后将偏心体整体放入15～80℃油中冷却50-60分钟；回火。本发明的对偏心体最大厚度的部位采用水冷，再整体进行油冷的方式，使偏心体各个部位的硬度均匀，均达到≥180HB的技术要求。
Description
(一)技术领域
本发明涉及一种热处理方法，特别涉及一种提高ZG270-500偏心体硬度的热处理方法。
(二)背景技术
按照现行国家标准，铸钢ZG270-500以机械性能表示，材料化学成分作参考，因此在保证机械性能的前提下其化学成分波动范围很大，由于偏心体部位截面大，有效厚度热处理相差大。ZG270-500材料的偏心体，正常热处理工艺只能进行正火处理，硬度在140HB左右，无法达到硬度≥180HB的使用要求。若改变热处理方式提高冷却速度，极易产生裂纹，造成零件报废。
(三)发明内容
本发明要解决的技术问题是提供了一种提高ZG270-500偏心体硬度的热处理方法，能够使偏心体硬度≥180HB，满足压力机的使用要求。
为了解决上述技术问题，本发明是通过以下措施来实现的：
一种提高ZG270-500偏心体硬度的热处理方法，其特征在于，包括以下步骤：
1)偏心体的正火：
(1)将偏心体放置在加热炉中加热高于650℃，并保温3以上小时；
(2)将保温后的偏心体放到加热炉中加热高于850℃，保温5小时以上出炉，放置在空气中冷却至室温；
2)偏心体先水冷再整体冷油：
(1)等温：将上述冷却至室温的偏心体放置在加热炉中加热至650℃，并保温至3小时以上；
(2)加热：将上述偏心体继续加热至850℃以上，并保温5小时以上，然后在空气中冷却至偏心体尖角处发黑其他部位温度在840～860℃，接着对偏心体最大厚度的部位进行在10～40℃水中冷却3-10分钟，最后将偏心体整体放入15～80℃油中冷却50-60分钟；
(3)回火：在350-400℃回火炉中保温6小时以上，放置在空气中自然冷却。
进一步地，步骤1)中(1)的偏心体加热后的温度为650℃、保温3小时，步骤1)中(2)偏心体加热后的加热温度为850℃、保温3小时，步骤2)中(1)偏心体加热后的温度为650℃，保温3小时，步骤2)中(2)偏心体加热后的温度为850℃，保温5小时，步骤2)中(3)回火温度为350℃。
更进一步地，步骤1)中(1)的偏心体加热后的温度为670℃、保温5小时，步骤1)中(2)偏心体加热后的加热温度为880℃、保温5小时，步骤2)中(1)偏心体加热后的温度为670℃，保温5小时，步骤2)中(2)偏心体加热后的温度为880℃，保温7小时，步骤2)中(3)回火温度为400℃。
本发明的有益效果：
1、对偏心体最大厚度的部位采用水冷，再整体进行油冷的方式，使偏心体各个部位的硬度均匀，均达到≥180HB的技术要求。
2、先对偏心体进行正火处理消除了铸造应力且使组织均匀，保证ZG270-500偏心体水冷不开裂。
3、整个步骤采用现有设备实施方便，操作简单。
(四)具体实施方式
一种提高ZG270-500偏心体硬度的热处理方法，其特征在于，包括以下步骤：
1)偏心体的正火：
(1)将偏心体放置在加热炉中加热高于650～670℃，并保温3以上小时；
(2)将保温后的偏心体放到加热炉中加热高于850～870℃，保温5小时以上出炉，放置在空气中冷却至室温；
2)偏心体先水冷再整体冷油：
(1)等温：将上述冷却至室温的偏心体放置在加热炉中加热至650～670℃，并保温至3小时以上；
(2)加热：将上述偏心体继续加热至850℃～880℃，并保温5小时以上，然后在空气中冷却至偏心体尖角处发黑其他部位温度在840～860℃，接着对偏心体最大厚度的部位进行在10～40℃水中冷却3-10分钟，最后将偏心体整体放入15～80℃油中冷却50-60分钟；
(3)回火：在350-400℃回火炉中保温6小时以上，放置在空气中自然冷却。
对于ZG270-500材料的偏心体，本发明采用的冷却方式不同于传统的冷却，采用先局部水冷、再整体油冷的冷却方式，可使偏心体的整体硬度在加工后达到≥180HB，满足零件的使用要求。本方式已生产偏心体5件，零件的最大厚度热处理时最大为460mm，最小为100mm。加工后偏心体硬度达到了≥180HB的使用要求，5台压力机已产出。
Claims (1)
1.一种提高ZG270-500偏心体硬度的热处理方法，其特征在于，包括以下步骤：
1)偏心体的正火：
(1)将偏心体放置在加热炉中加热高于650℃，并保温3小时以上；
(2)将保温后的偏心体放到加热炉中加热高于850℃，保温5小时以上出炉，放置在空气中冷却至室温；
2)偏心体先水冷再整体冷油：
(1)等温：将上述冷却至室温的偏心体放置在加热炉中加热至650℃，并保温至3小时以上；
(2)加热：将上述偏心体继续加热至850℃以上，并保温5小时以上，然后在空气中冷却至偏心体尖角处发黑其他部位温度在840～860℃，接着对偏心体最大厚度的部位进行在10～40℃水中冷却3-10分钟，最后将偏心体整体放入15～80℃油中冷却50-60分钟；
(3)回火：在350-400℃回火炉中保温6小时以上，放置在空气中自然冷却。