CN101875540A - Red attapulgite plasticine and production method thereof - Google Patents

Abstract

The invention discloses a red attapulgite plasticine and a production method thereof, wherein the technical scheme has the key point that the production method comprises the following steps of: after propanediol, trimeric sodium phosphate, konjaku flour, capsanthin, amaranth, coccinellin, beet red, lac red, chrysanthemum, mulberry red, red cabbage, perillanin and monascorubin are dissolved into deionized water to obtain a red gel solution, slowly adding high-viscosity attapulgite clay silt and anatase titanium dioxide into the red gel solution for uniformly stirring and mixing to obtain a semi-finished product, adding dimethyl polysiloxane into the semi-finished product for uniformly stirring to obtain a mixture as the finished product of the red attapulgite plasticine. The red attapulgite plasticine has high viscosity, good softness and plasticity and bright color, the performance of each selected haematochrome has characteristics per se and can be complemented in the invention, the red attapulgite plasticine has the characteristics of strong moisture retention, small shrinkage rate and no deformation, and the red attapulgite plasticine is applicable to industrial art shape designing, art education and toys for children.

Description

Red attapulgite plasticine and production method thereof

Technical field

The present invention relates to plasticine, be specifically related to a kind of red attapulgite plasticine and production method thereof.

Background technology

The red plasticine of selling on the market is made up of flour, talcum powder, Paris white, breeze, grease, spices, pigment, sanitas, poster paint, industrial pigment and water.

Flour mixes with water under normal temperature condition, and adhesive property is lower, talcum powder, Paris white and breeze with can not form the mineral colloid after water mixes, be to depend on flour and grease and be bonded together fully.The plastic poor-performing of this plasticine, the finished product after the making are easy to generate drying, cracking, distortion, mouldy and rotten, also can make the operator that a kind of greasy feeling is arranged on hand in making processes, and it is bad to reuse effect.

Not only color is not bright-coloured to use poster paint and the synthetic red plasticine of industrial pigment, but also can produce pollution.

Summary of the invention

The objective of the invention is to overcome weak point in the prior art, a kind of red attapulgite plasticine and production method thereof are provided.

Red attapulgite plasticine is red by the sticking attapulgite clay powder of height, propylene glycol, tripoly phosphate sodium STPP, dimethyl polysiloxane, anatase thpe white powder, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac, Sorghum pigment, mulberries are red, cabbage red, purple perilla are red, Monascus color and deionized water are formed.

The production method of red attapulgite plasticine:, Sorghum pigment red when propylene glycol, tripoly phosphate sodium STPP, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac, mulberries are red, cabbage red, purple perilla is red and Monascus color is red gel solution after being dissolved in the deionized water, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the red gel solution stir, mix the back and be work in-process, dimethyl polysiloxane added in the work in-process stir, the mixture after stirring is the finished product of red attapulgite plasticine.

Attapulgite clay has higher plasticity-under aqueous situation, good stability, and the hardness of attapulgite clay is Mohs 2～3 degree; Attapulgite clay is viscosity when moist, viscosity can reach more than the 3000mPas, the dry post-shrinkage ratio of attapulgite clay is little, and does not produce be full of cracks, and high sticking attapulgite clay powder is the powdery attapulgite stone clay that the complete processing of employing raising viscosity of attapulgite clay is produced.

Propylene glycol is the stable water-absorbent liquid of a kind of water white transparency toughness, and almost tasteless odorless is water-soluble, thereby is widely used as moisture adsorbent, emulsifying agent, antifreezing agent, lubricant and solvent in food, medicine and cosmetic industry.

Tripoly phosphate sodium STPP be white in color particle or powdery, soluble in water, be a kind of water retention agent, tenderizer and thickening material, and can stablize the vividness of pigment in the red attapulgite plasticine.

Dimethyl polysiloxane is a kind of water white thick liquid, and odorless is tasteless, water insoluble, is used for defoamer, fruit glaze agent and anticaking agent.

Anatase thpe white powder has excellent water dispersible and remarkable optical property, form and aspect stability, and size-grade distribution is good, has the characteristics of high gloss, high reducing power, high covering power, helps producing the red attapulgite plasticine of various different colours.

Rhizoma amorphophalli powder is the tasteless powder that flows of a kind of white, can be dispersed in hot water and the cold water, and main application is jelling agent, thickening material, membrane-forming agent, emulsifying agent and stablizer.

Capsanthin is a kind of natural pigment that extracts from red pepper, and main component is a Capsorubin, and is bright in colour, heat-resisting, fast light, not influenced by environment pH value and metal ion.

Amaranth, famille rose, beet red, shellac are red, Sorghum pigment, mulberries are red, cabbage red, purple perilla is red and Monascus color is an edible haematochrome.

The present invention is achieved by following technical proposals:

1, the batching of red attapulgite plasticine is made up of following component by weight percentage: high sticking attapulgite clay powder 45～65%, propylene glycol 0.1～10%, tripoly phosphate sodium STPP 0.1～5%, dimethyl polysiloxane 0.1～5%, anatase thpe white powder 0.1～5%, Rhizoma amorphophalli powder 0.1～5%, capsanthin 0.0005～1%, amaranth 0.0001～1%, carmine 0.0001～1%, beet red 0.0001～1%, shellac red 0.0001～1%, Sorghum pigment 0.0001～1%, mulberries red 0.0001～1%, cabbage red 0.0001～1%, purple perilla red 0.0001～1%, Monascus color 0.0001～1% and deionized water 20～35%.

2, the production method of red attapulgite plasticine: (1) adds deionized water in the stirrer earlier, and again that propylene glycol, tripoly phosphate sodium STPP, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac is red, Sorghum pigment, mulberries are red, cabbage red, purple perilla is red and Monascus color adds in the deionized water and stirs; (2) red, the cabbage red of, Sorghum pigment red, mulberries when propylene glycol, tripoly phosphate sodium STPP, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac, purple perilla is red and Monascus color is red gel solution after being dissolved in the deionized water, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the red gel solution stir, mix the back and be the work in-process of red attapulgite plasticine; (3) dimethyl polysiloxane is added in the work in-process of red attapulgite plasticine and stir, the mixture after stirring is the finished product of red attapulgite plasticine.

The sticking attapulgite clay powder of described height is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, it is characterized in that, and from the attapulgite clay of mining area exploitation, need be through 30～120 days natural weathering; Modification processing method is: calculate by weight percentage, take from the attapulgite clay 94～98% after the right weathering, evenly add 2～6% yellow soda ash, import jointly in the fermentation vat, add clear water and soak ageing, soak time is 72～120 hours; Get the attapulgite clay after the immersion, stir in the input stirrer, and the attapulgite clay after will stirring, be extruded into thin slice through extrusion machine, its gauge control is at 0.5～2 millimeter, with the attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after the airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94～98% after the airing, High hydrophilous resin 0.5～5% and Mierocrystalline cellulose 0.5～3%, above-mentioned batching is stirred, and carry out abrasive dust in the back input grinding machine that stirs, particle fineness≤0.074 millimeter.

Above-mentioned production technique is to adopt " improving the complete processing of viscosity of attapulgite clay " in application on June 20th, 2005 by the inventor, and the Chinese patent Granted publication number is: CN 1317067C, Granted publication day: on May 23rd, 2007.

Red attapulgite plasticine viscosity height, soft plasticity-is good, bright in luster, selected haematochrome performance respectively has characteristics, can obtain complementation in the present invention, red attapulgite plasticine has that water-retentivity is strong, shrinking percentage is little, indeformable, not hardening, do not produce be full of cracks, not mouldy, never degenerate not skin irritation, nontoxic, non-corrosiveness and do not have the characteristics of greasy feeling.

The red attapulgite plasticine production technique is simple, and is with low cost, and can be repeatedly used, and the stronger market competitiveness is arranged.

Red attapulgite plasticine is applicable to industrial art shape-designing, art education and toy for children.

Embodiment

The invention will be further described below in conjunction with embodiment:

1, the batching of red attapulgite plasticine is made up of following component by weight percentage: high sticking attapulgite clay powder 56%, propylene glycol 8%, tripoly phosphate sodium STPP 2%, dimethyl polysiloxane 2.5%, anatase thpe white powder 2%, Rhizoma amorphophalli powder 1%, capsanthin 0.3567%, amaranth 0.12%, carmine 0.01%, beet red 0.01%, shellac red 0.001%, Sorghum pigment 0.001%, mulberries red 0.001%, cabbage red 0.0001%, purple perilla red 0.0001%, Monascus color 0.0001% and deionized water 28%.

2, the production method of red attapulgite plasticine: (1) adds deionized water in the stirrer earlier, and again that propylene glycol, tripoly phosphate sodium STPP, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac is red, Sorghum pigment, mulberries are red, cabbage red, purple perilla is red and Monascus color adds in the deionized water and stirs; (2) red, the cabbage red of, Sorghum pigment red, mulberries when propylene glycol, tripoly phosphate sodium STPP, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac, purple perilla is red and Monascus color is red gel solution after being dissolved in the deionized water, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the red gel solution stir, mix the back and be the work in-process of red attapulgite plasticine; (3) dimethyl polysiloxane is added in the work in-process of red attapulgite plasticine and stir, the mixture after stirring is the finished product of red attapulgite plasticine.

Claims (1)

1. red attapulgite plasticine and production method thereof, it is characterized in that the batching of red attapulgite plasticine is made up of following component by weight percentage: high sticking attapulgite clay powder 45～65%, propylene glycol 0.1～10%, tripoly phosphate sodium STPP 0.1～5%, dimethyl polysiloxane 0.1～5%, anatase thpe white powder 0.1～5%, Rhizoma amorphophalli powder 0.1～5%, capsanthin 0.0005～1%, amaranth 0.0001～1%, carmine 0.0001～1%, beet red 0.0001～1%, shellac red 0.0001～1%, Sorghum pigment 0.0001～1%, mulberries red 0.0001～1%, cabbage red 0.0001～1%, purple perilla red 0.0001～1%, Monascus color 0.0001～1% and deionized water 20～35%;

The production method of described red attapulgite plasticine: (1) adds deionized water in the stirrer earlier, and again that propylene glycol, tripoly phosphate sodium STPP, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac is red, Sorghum pigment, mulberries are red, cabbage red, purple perilla is red and Monascus color adds in the deionized water and stirs; (2) red, the cabbage red of, Sorghum pigment red, mulberries when propylene glycol, tripoly phosphate sodium STPP, Rhizoma amorphophalli powder, capsanthin, amaranth, famille rose, beet red, shellac, purple perilla is red and Monascus color is red gel solution after being dissolved in the deionized water, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the red gel solution stir, mix the back and be the work in-process of red attapulgite plasticine; (3) dimethyl polysiloxane is added in the work in-process of red attapulgite plasticine and stir, the mixture after stirring is the finished product of red attapulgite plasticine;

The sticking attapulgite clay powder of described height is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, it is characterized in that, and from the attapulgite clay of mining area exploitation, need be through 30～120 days natural weathering; Modification processing method is: calculate by weight percentage, take from the attapulgite clay 94～98% after the right weathering, evenly add 2～6% yellow soda ash, import jointly in the fermentation vat, add clear water and soak ageing, soak time is 72～120 hours; Get the attapulgite clay after the immersion, stir in the input stirrer, and the attapulgite clay after will stirring, be extruded into thin slice through extrusion machine, its gauge control is at 0.5～2 millimeter, with the attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after the airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94～98% after the airing, High hydrophilous resin 0.5～5% and Mierocrystalline cellulose 0.5～3%, above-mentioned batching is stirred, and carry out abrasive dust in the back input grinding machine that stirs, particle fineness≤0.074 millimeter.