CN110093027A - A kind of powder puff with can temperature become polychrome sponge and its manufacture craft - Google Patents
A kind of powder puff with can temperature become polychrome sponge and its manufacture craft Download PDFInfo
- Publication number
- CN110093027A CN110093027A CN201910420434.XA CN201910420434A CN110093027A CN 110093027 A CN110093027 A CN 110093027A CN 201910420434 A CN201910420434 A CN 201910420434A CN 110093027 A CN110093027 A CN 110093027A
- Authority
- CN
- China
- Prior art keywords
- temperature
- component
- sponge
- polychrome
- become
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The embodiment of the invention discloses a kind of powder puffs with that warm can become polychrome sponge and its manufacture craft, belongs to technical field of polymer materials.The powder puff respectively includes first component and second component with that warm can become the raw material that polychrome sponge includes two groups or more, each group of raw material, wherein the weight ratio of first component and second component is 1.5~2.5:0.8~1.2；Filler that first component is 40~50% by weight percentage, 1.7~4% surfactant, 1~2% emulsifier, 0.5~1% temperature-sensitive toner, 0.3~1% aqueous color paste, surplus are that water forms, and second group is divided into hydrophilic polyurethane performed polymer；The powder puff, which is used, warm can become the temperature-sensitive toner that polychrome sponge includes two or more.The sponge toner of the embodiment of the present invention does not dissipate, and the color of added temperature-sensitive toner is presented, while also with good physical property, oder levels are low, good environmental protection, while having good shape recovery and touch sensitivity, is adapted for use in cosmetics.
Description
Technical field
The present embodiments relate to technical field of polymer materials, and in particular to a kind of powder puff with can temperature become polychrome sponge and
Its manufacture craft.
Background technique
Sponge is one kind of polyurethane foam plastics, belongs to flexible polyurethane foam.Because there is the cellular knot of cellular
Structure has the characteristics that excellent flexibility, elasticity, water imbibition, water resistance, is widely used in sofa, mattress, clothes, flexible package
Etc. industries.
In the synthesis process of sponge, mainly by the processes such as chain length reaction, foaming and crosslinking, point of these reactions and raw material
Minor structure, degree of functionality, molecular weight etc. are related.
Currently, most of in sponge production use the box foaming of a step, under high velocity agitation by various raw materials, add rapidly
Enter shaping box, the reaction such as chain growth, foaming, crosslinking, solidification is completed in forming box, to complete sponge production.
Traditional sponge does not have the function of changing color according to environment temperature, but the appearance of temperature-sensitive toner material, passes through
Temperature-sensitive toner is added in the manufacture craft of sponge, is expected to that the sponge for changing color according to environment temperature is made.
Powder puff is one kind of cosmetic applicators, for picking foundation cream and modification dressing, by being polished to sponge, mesh
It is preceding not yet to occur changing the powder puff of color according to environment temperature on the market.
Summary of the invention
For this purpose, the embodiment of the present invention provide a kind of powder puff with can temperature become polychrome sponge and its manufacture craft, it is existing to solve
Not yet occurs the problem of changing the powder puff of color according to environment temperature in technology.
To achieve the goals above, the embodiment of the present invention provides the following technical solutions:
According to a first aspect of the embodiments of the present invention, it is extra large with that warm can become polychrome that the embodiment of the invention provides a kind of powder puffs
Silk floss, the powder puff respectively include first component with that warm can become the raw material that polychrome sponge includes two groups or more, each group of raw material
With second component, wherein the weight ratio of first component and second component is 1.5~2.5:0.8~1.2；
First component by weight percentage be 40~50% filler, 1.7~4% surfactant, 1~2% cream
Agent, 0.5~1% temperature-sensitive toner, 0.3~1% aqueous color paste, surplus are water composition, and second group is divided into hydrophilic polyurethane
Performed polymer；The powder puff, which is used, warm can become the temperature-sensitive toner that polychrome sponge includes two or more.
Further, the temperature-sensitive toner is selected from purple temperature-sensitive toner, green temperature-sensitive toner, orange temperature-sensitive toner, yellow
Any one of temperature-sensitive toner, orange temperature-sensitive toner, blue temperature-sensitive toner, red temperature-sensitive toner.
Further, the aqueous color paste is selected from red aqueous color paste, yellow aqueous color paste, blue water-based mill base, green
Aqueous color paste, black water mill base, white water-borne mill base are any one or more of.
Further, the filler is 400-800 mesh wollastonite in powder.
Further, the surfactant is selected from one of PE6800, PE6200, polyether silicone oil or a variety of.
Further, the emulsifier is 1000NI.
According to a second aspect of the embodiments of the present invention, using the embodiment of the invention provides a kind of above-mentioned powder puff warm can become more
The manufacture craft of color sponge, the technique the following steps are included:
1) the first component in every group of raw material is uniformly mixed respectively under normal pressure, under agitation, second component is added, is made
Two groups or more foam mixture；
2) two groups or more foam mixture respectively through high-voltage tube simultaneously be pumped into be delivered to polyurethane foaming machine into
It is continuous that foaming bubble is made in row foaming and molding；
3) foam sponge made from step 2) is delivered to dryer and carries out drying and processing, powder puff is made and uses and warm can become polychrome
Sponge.
Further, in step 1), the temperature of first component is 16~20 DEG C, and the temperature of second component is 30~35 DEG C.
Further, in step 1), mixing speed 3500-5000r/min.
Further, in step 3), the temperature of the dryer is 100~150 DEG C
Temperature-sensitive toner is prepared by electron transfer type organic compound system.Electron transfer type organic compound is a kind of
Organic chromophoric system with special chemical structure.At a certain temperature because the molecular structure of the organic matter occurs for electronics transfer
Variation, to realize color transition.This electrochromic substance is not only bright-colored, but also may be implemented from " colored-colorless " state
Color change, this is not available for heavy metal double salt Complex Type and liquid crystal type reversible temperature-sensitive electrochromic substance.
The powder puff of the embodiment of the present invention temperature-sensitive toner that warm can become polychrome sponge and use two or more, and
In room temperature or following two or more temperature-sensitive toner and more than one mill bases can be presented in more than one aqueous color paste
Color, sponge retains the color of more than one mill bases after heat effect.
The embodiment of the present invention has the advantages that
The powder puff of the embodiment of the present invention with can temperature become polychrome sponge by the way that the first component for setting proportion in every group of raw material (is filled out
Material, surfactant, emulsifier, temperature-sensitive toner, water) it is sent out with second component (hydrophilic polyurethane performed polymer) progress pre-reaction
Mixture is steeped, two groups or more foam mixture is pumped into through high-voltage tube respectively then and is delivered to polyurethane foaming machine progress
Foaming and molding is made after drying, and resulting sponge toner does not dissipate, and the color of added temperature-sensitive toner is presented, while also having
Operating process is simple, the low feature of production cost.
For powder puff made from the embodiment of the present invention with that warm can become polychrome sponge with good physical property, oder levels are low,
Good environmental protection, while there is good shape recovery and touch sensitivity, it is adapted for use in cosmetics.
Specific embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book is understood other advantages and efficacy of the present invention easily, it is clear that described embodiment is the present invention one
Section Example, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not doing
Every other embodiment obtained under the premise of creative work out, shall fall within the protection scope of the present invention.
PE6800 is purchased from BASF Chemical Company；1000NI is purchased from BASF Chemical Company；
PE6200 is purchased from BASF Chemical Company；Wollastonite in powder is purchased from Guangzhou side's benefit chemical industry；Polyether silicone oil activating agent is purchased from river
Men Yiben chemistry；Temperature-sensitive toner is purchased from U.S. LCR；Aqueous color paste is purchased from the poly- hat chemical industry in Dongguan.
Embodiment 1
The powder puff of the present embodiment with can temperature become polychrome sponge by including 1 component of first, 2 component of 2 component of first, 1 component of second and second,
Wherein:
1 component of first is 42% 400 mesh wollastonites in powder, 0.7% PE6800,1.2% by weight percentage
It is PE6200,0.5% polyether silicone oil, 1.2% 1000NI, 1% purple temperature-sensitive toner, 0.5% red aqueous color paste, remaining
Amount is that water forms, and 1 group of second is divided into hydrophilic polyurethane performed polymer, and the weight ratio of 1 component of 1 component of first and second is 2.2:1；
2 component of first is 48% 400 mesh wollastonites in powder, 0.5% PE6800,1.8% by weight percentage
It is PE6200,0.2% polyether silicone oil, 1% 1000NI, 0.8% green temperature-sensitive toner, 0.3% white water-borne mill base, remaining
Amount is that water forms, and 2 groups of second are divided into hydrophilic polyurethane performed polymer, and the weight ratio of 2 component of 2 component of first and second is 1.8:1；
The weight ratio of 1 component of first and 2 component of first is 3:1.
The powder puff of the present embodiment with can temperature become polychrome sponge manufacture craft the following steps are included:
1) each raw material of 1 component of first is uniformly mixed under normal pressure and is maintained at 18 DEG C, in the stirring that speed is 3500r/min
Under the conditions of, 1 component of second that temperature is 32 DEG C is added, the first foam mixture is made；Each raw material of 2 component of first is uniformly mixed and protects
It holds at 20 DEG C, in the case where speed is the stirring condition of 3500r/min, 2 component of second that temperature is 35 DEG C is added, it is mixed that the second foaming is made
Close material
2) the first foam mixture made from step 1) and the second foam mixture are pumped into through high-voltage tube simultaneously respectively defeated
It send to polyurethane foaming machine and carries out foaming and molding, it is continuous that foaming bubble is made；
3) foam sponge made from step 2) is delivered to dryer, carries out drying and processing at 110 DEG C, powder puff is made and uses
It can temperature change polychrome sponge.
Embodiment 2
The powder puff of the present embodiment with can temperature become polychrome sponge by including 1 component of first, 2 component of 2 component of first, 1 component of second and second,
Wherein:
1 component of first is 50% 800 mesh wollastonites in powder, 0.6% PE6800,1.5% by weight percentage
PE6200,0.8% polyether silicone oil, 1.5% 1000NI, 0.8% orange temperature-sensitive toner, the 0.6% aqueous water slurry of yellow,
Surplus is water composition, and 1 group of second is divided into hydrophilic polyurethane performed polymer, and the weight ratio of 1 component of 1 component of first and second is 2:1；
2 component of first by weight percentage be 45% 800 mesh wollastonites in powder, 0.8% PE6800,2% PE6200,
0.6% polyether silicone oil, 1.8% 1000NI, 0.5% red temperature-sensitive toner, 0.5% blue water-based water slurry, surplus are
Water composition, 2 groups of second are divided into hydrophilic polyurethane performed polymer, and the weight ratio of 2 component of 2 component of first and second is 2.5:0.8；
The weight ratio of 1 component of first and 2 component of first is 1:1.
The powder puff of the present embodiment with can temperature become the manufacture craft of polychrome sponge with embodiment 1.
Embodiment 3
The powder puff of the present embodiment with can temperature become polychrome sponge by including 1 component of first, 2 component of 2 component of first, 1 component of second and second,
Wherein:
1 component of first by weight percentage be 40% 600 mesh wollastonites in powder, 1% PE6800,1.2% PE6200,
0.3% polyether silicone oil, 1.6% 1000NI, 0.6% purple temperature-sensitive toner, 0.4% white water-borne mill base, surplus are
Water composition, 1 group of second is divided into hydrophilic polyurethane performed polymer, and the weight ratio of 1 component of 1 component of first and second is 1.8:1；
2 component of first is 42% 600 mesh wollastonites in powder, 0.5% PE6800,1.1% by weight percentage
PE6200,0.9% polyether silicone oil, 1.8% 1000NI, 0.9% blue temperature-sensitive toner, 0.8% white water-borne mill base,
Surplus is water composition, and 2 groups of second are divided into hydrophilic polyurethane performed polymer, and the weight ratio of 2 component of 2 component of first and second is 2:1；
The weight ratio of 1 component of first and 2 component of first is 0.1~10:1.
The powder puff of the present embodiment with can temperature become the manufacture craft of polychrome sponge with embodiment 1.
Embodiment 4
The powder puff of the present embodiment with can temperature become polychrome sponge by including 1 component of first, 2 component of 2 component of first, 1 component of second and second,
Wherein:
1 component of first is 50% 400 mesh wollastonites in powder, 0.5% PE6800,1.6% by weight percentage
PE6200,0.6% polyether silicone oil, 1.4% 1000NI, 0.7% orange temperature-sensitive toner, 0.2% white water-borne mill base,
0.3% red aqueous color paste, surplus are water composition, and 1 group of second is divided into hydrophilic polyurethane performed polymer, 1 component of 1 component of first and second
Weight ratio be 2:1；
2 component of first is 40% 400 mesh wollastonites in powder, 0.8% PE6800,1.8% by weight percentage
PE6200,0.8% polyether silicone oil, 1.2% 1000NI, 0.7% purple temperature-sensitive toner, 0.3% red aqueous color paste,
0.5% yellow aqueous color paste, surplus are water composition, and 2 groups of second are divided into hydrophilic polyurethane performed polymer, 2 component of 2 component of first and second
Weight ratio be 2.5:1；
The weight ratio of 1 component of first and 2 component of first is 1:3.
The powder puff of the present embodiment with can temperature become the manufacture craft of polychrome sponge with embodiment 1.
Embodiment 5
The powder puff of the present embodiment with can temperature become polychrome sponge by include 1 component of first, 2 component of first, 3 component of first, 1 component of second,
2 component of second, 3 component of second, in which:
1 component of first is 46% 600 mesh wollastonites in powder, 0.6% PE6800,1.3% by weight percentage
PE6200,0.4% polyether silicone oil, 1.5% 1000NI, 0.6% blue temperature-sensitive toner, 0.6% white water-borne mill base,
Surplus is water composition, and 1 group of second is divided into hydrophilic polyurethane performed polymer, and the weight ratio of 1 component of 1 component of first and second is 2.5:0.8；
2 component of first is 48% 600 mesh wollastonites in powder, 0.9% PE6800,1.4% by weight percentage
It is PE6200,1% polyether silicone oil, 1.1% 1000NI, 0.9% yellow temperature-sensitive toner, 0.4% white water-borne mill base, remaining
Amount is that water forms, and 2 groups of second are divided into hydrophilic polyurethane performed polymer, and the weight ratio of 2 component of 2 component of first and second is 1.5:1.2；
3 component of first is 45% 600 mesh wollastonites in powder, 0.6% PE6800,1.8% by weight percentage
PE6200,0.8% polyether silicone oil, 1.4% 1000NI, 0.7% purple temperature-sensitive toner, 0.8% red aqueous color paste,
Surplus is water composition, and 2 groups of second are divided into hydrophilic polyurethane performed polymer, and the weight ratio of 2 component of 2 component of first and second is 2:1；
The weight ratio of 3 component of 1 component of first, 2 component of first and first is 1:1:1.
The powder puff of the present embodiment with can temperature become the manufacture craft of polychrome sponge with embodiment 1.
Test case
To powder puff made from embodiment 1-5 with can temperature become polychrome sponge physical property test, the results are shown in Table 1.
Table 1
| Group | Density kg/m3 | Voidage/mm | Tensile strength/kgf | Hardness/H | Oder levels |
| Embodiment 1 | 156.2 | 0.108 | 4.6 | 52.6 | ≤2 |
| Embodiment 2 | 148.7 | 0.095 | 4.1 | 47.2 | ≤2 |
| Embodiment 3 | 145.5 | 0.086 | 4.5 | 54.3 | ≤2 |
| Embodiment 4 | 154.3 | 0.115 | 4.3 | 50.5 | ≤2 |
| Embodiment 5 | 158.1 | 0.092 | 4.8 | 46.8 | ≤2 |
As it can be seen from table 1 the powder puff of the embodiment of the present invention, which is used, warm can become polychrome sponge with good physical property, together
When oder levels it is low, good environmental protection is adapted for use in cosmetics.
To powder puff made from embodiment 1-5 with can temperature become the shape recovery of polychrome sponge and touch sensitivity evaluate.
Shape recovery: rubbing sample in water, it is made sufficiently to absorb water.Then sample is taken out from water, is held in palm
Time after moisture is squeezed out completely, when shape when palm is decontroled in measurement to sample is restored.
It is touch sensitivity: without coarse rough feeling, to indicate touch sensitivity good.
Evaluation result is shown in Table 2.
Table 2
| Group | Shape recovery/second | It is touch sensitivity |
| Embodiment 1 | 3.0 | It is touch sensitivity good |
| Embodiment 2 | 3.5 | It is touch sensitivity good |
| Embodiment 3 | 3.4 | It is touch sensitivity good |
| Embodiment 4 | 2.9 | It is touch sensitivity good |
| Embodiment 5 | 2.6 | It is touch sensitivity good |
From table 2 it can be seen that the powder puff of the embodiment of the present invention, which is used, warm can become polychrome sponge with good shape recovery
With it is touch sensitivity.
Although above having used general explanation and specific embodiment, the present invention is described in detail, at this
On the basis of invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Therefore,
These modifications or improvements without departing from theon the basis of the spirit of the present invention are fallen within the scope of the claimed invention.
Claims (10)
1. a kind of powder puff with can temperature become polychrome sponge, which is characterized in that the powder puff with can temperature become polychrome sponge include two groups or
Raw material more than two, each group of raw material respectively include first component and second component, wherein the weight ratio of first component and second component is
1.5~2.5:0.8~1.2；
First component by weight percentage be 40~50% filler, 1.7~4% surfactant, 1~2% emulsifier,
0.5~1% temperature-sensitive toner, 0.3~1% aqueous color paste, surplus are water composition, and second group is divided into hydrophilic polyurethane pre-polymerization
Body；The powder puff, which is used, warm can become the temperature-sensitive toner that polychrome sponge includes two or more.
2. powder puff according to claim 1, which is used, warm to become polychrome sponge, which is characterized in that the temperature-sensitive toner is selected from purple
It is temperature-sensitive toner, green temperature-sensitive toner, orange temperature-sensitive toner, yellow temperature-sensitive toner, orange temperature-sensitive toner, blue temperature-sensitive toner, red
Any one of color sensation warm colour powder.
3. powder puff according to claim 1, which is used, warm to become polychrome sponge, which is characterized in that the aqueous color paste is selected from red
Aqueous color paste, yellow aqueous color paste, blue water-based mill base, green aqueous color paste, black water mill base, in white water-borne mill base
It is any one or more.
4. powder puff according to claim 1, which is used, warm to become polychrome sponge, which is characterized in that the filler is 400-800 mesh
Wollastonite in powder.
5. powder puff according to claim 1, which is used, warm to become polychrome sponge, which is characterized in that the surfactant is selected from
One of PE6800, PE6200, polyether silicone oil are a variety of.
6. powder puff according to claim 1, which is used, warm to become polychrome sponge, which is characterized in that the emulsifier is 1000NI.
7. a kind of powder puff described in claim 1 with can temperature become the manufacture craft of polychrome sponge, which is characterized in that the technique packet
Include following steps:
1) the first component in every group of raw material is uniformly mixed respectively under normal pressure, under agitation, second component is added, is made two groups
Or foam mixture more than two；
2) two groups or more foam mixture is pumped into simultaneously through high-voltage tube respectively and is delivered to polyurethane foaming machine and is sent out
It is continuous that foaming bubble is made in foam forming；
3) foam sponge made from step 2) is delivered to dryer and carries out drying and processing, powder puff, which is made, and uses warm can become polychrome sea
It is continuous.
8. powder puff according to claim 7 with can temperature become the manufacture craft of polychrome sponge, which is characterized in that in step 1),
The temperature of first component is 16~20 DEG C, and the temperature of second component is 30~35 DEG C.
9. powder puff according to claim 7 with can temperature become the manufacture craft of polychrome sponge, which is characterized in that in step 1),
Mixing speed is 3500-5000r/min.
10. powder puff according to claim 7 with can temperature become the manufacture craft of polychrome sponge, which is characterized in that in step 3),
The temperature of the dryer is 100~150 DEG C.