CN101875545B - Oily attapulgite plasticine and production method thereof - Google Patents
Oily attapulgite plasticine and production method thereof Download PDFInfo
- Publication number
- CN101875545B CN101875545B CN2010101327188A CN201010132718A CN101875545B CN 101875545 B CN101875545 B CN 101875545B CN 2010101327188 A CN2010101327188 A CN 2010101327188A CN 201010132718 A CN201010132718 A CN 201010132718A CN 101875545 B CN101875545 B CN 101875545B
- Authority
- CN
- China
- Prior art keywords
- attapulgite
- oily
- attapulgite clay
- plasticine
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses oily attapulgite plasticine and a production method thereof. The key point of the technical scheme is that: the method comprises the following steps of: dissolving glycerin, Arabic gum, sodium tripolyphosphate, capsicum red pigment, curcumin, gardenia blue, methylparaben and propylparaben in deionized water to form colored gel solution; slowly adding attapulgite clay powder with high viscosity and anatase titanium dioxide into the colored gel solution and uniformly stirring and mixing to form a semi-finished product; and adding palm oil into the semi-finished product and stirring, wherein the uniformly stirred mixture is a finished product of the oily attapulgite plasticine. The oily attapulgite plasticine has the characteristics of high viscosity, softness, high plasticity, high water holding capacity, small shrinkage, no deformation, no hardening, no cracks, no mildew, no degeneration, no irritation to the skin, no toxicity, no corrosion and no greasy feeling, and is suitable for industrial art style design, art education and toys for children.
Description
Technical field
The present invention relates to plasticine, be specifically related to a kind of oily attapulgite plasticine and production method thereof.
Background technology
The oiliness plasticine of selling on the market is made up of flour, grease, talcum powder, Paris white, breeze, spices, pigment, sanitas, poster paint, industrial pigment and water.
Flour mixes with water under normal temperature condition, and adhesive property is lower, talcum powder, Paris white and breeze with can not form the mineral colloid after water mixes, be to depend on flour and grease and be bonded together fully.The plastic poor-performing of this plasticine, the finished product after the making are easy to generate drying, cracking, distortion, mouldy and rotten, also can make the operator that a kind of greasy feeling is arranged on hand in making processes, and it is bad to reuse effect.
Summary of the invention
The objective of the invention is to overcome weak point in the prior art, a kind of oily attapulgite plasticine and production method thereof are provided.
Oily attapulgite plasticine is made up of the sticking attapulgite clay powder of height, plam oil, anatase thpe white powder, glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M, propylben and deionized water.
The production method of oily attapulgite plasticine: after glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M and propylben are dissolved in the deionized water, be colored gelating soln, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the colored gelating soln stir, mix the back and be work in-process, plam oil added in the work in-process stir, the mixture after stirring is the finished product of oily attapulgite plasticine.
Attapulgite clay has higher plasticity-under aqueous situation, good stability, and the hardness of attapulgite clay is Mohs 2～3 degree; Attapulgite clay is viscosity when moist, and its viscosity can reach more than the 3000mPas, and the dry post-shrinkage ratio of attapulgite clay is little, and does not produce be full of cracks.High sticking attapulgite clay powder is the powdery attapulgite stone clay that adopts the complete processing production that improves viscosity of attapulgite clay.
Plam oil is the higher grease of a species saturation, is natural high-efficiency antioxidant agent, good lubricity and cheap.
Anatase thpe white powder has high gloss, high reducing power, high covering power and the good characteristics of size-grade distribution, helps producing the Yellow attapulgite plasticine of various different colours.
Glycerol has another name called glycerine, is a kind of colourless, odorless, the sweet thick liquid of flavor, can be miscible with water, water retention is arranged, and can make oily attapulgite plasticine keep soft, high resilience.
Gum arabic has solvability, good emulsifying thickening characteristic and stable film forming characteristics in the water highly, can also improve the last light effect of oily attapulgite plasticine.
Tripoly phosphate sodium STPP be white in color particle or powdery, soluble in water, be a kind of moisture content retention agent, tenderizer and thickening material, and can stablize the vividness of pigment in the oily attapulgite plasticine.
Capsanthin is a kind of natural pigment that extracts from red pepper, and main component is a Capsorubin, and is bright in colour, heat-resisting, fast light, not influenced by environment pH value and metal ion.
Turmeric yellow is the xanthein that contains in the stem tuber of per nnial herb turmeric, is orange-yellow powder, and tinting strength is better, has antioxygenation; Turmeric yellow is fine to most bacteriostatic effects, and is particularly inhibited to Bacillus subtilus, streptococcus aureus and intestinal bacteria.
Gardenia blue pigment is a kind of natural food colour, and the mazarine powder is soluble in water, with other natural pigment compatibility, can mix the oily attapulgite plasticine of different color and lusters.
Tegosept M has the broad-spectrum antibacterial effect, to Gram-positive, and negative bacteria, yeast and mould have very strong restraining effect, and the low and safety economy of working concentration uses validity period long.Tegosept M is compatible with various chemical substances easily, and the composite use of Tegosept M and propylben is to reach better preservative effect.
The present invention is achieved by following technical proposals:
1, the batching of oily attapulgite plasticine is made up of following component by weight percentage: high sticking attapulgite clay powder 45～65%, plam oil 5～20%, anatase thpe white powder 0.1～5%, glycerol 0.1～5%, gum arabic 0.1～5%, tripoly phosphate sodium STPP 0.1～5%, capsanthin 0.0001～1%, turmeric yellow 0.0001～1%, gardenia blue pigment 0.0001～1%, Tegosept M 0.01～0.5%, propylben 0.01～0.5% and deionized water 15～30%.
2, the production method of oily attapulgite plasticine: (1) adds deionized water in the stirrer earlier, glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M and propylben is added in the deionized water stir again; (2) after being dissolved in the deionized water, glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M and propylben be colored gelating soln, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the colored gelating soln stir, mix the back and be the work in-process of oily attapulgite plasticine; (3) plam oil is added in the work in-process of oily attapulgite plasticine and stir, the mixture after stirring is the finished product of oily attapulgite plasticine.
The sticking attapulgite clay powder of described height is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, it is characterized in that, and from the attapulgite clay of mining area exploitation, need be through 30～120 days natural weathering; Modification processing method is: calculate by weight percentage, take from the attapulgite clay 94～98% after the right weathering, evenly add 2～6% yellow soda ash, import jointly in the fermentation vat, add clear water and soak ageing, soak time is 72～120 hours; Get the attapulgite clay after the immersion, stir in the input stirrer, and the attapulgite clay after will stirring, be extruded into thin slice through extrusion machine, its gauge control is at 0.5～2 millimeter, with the attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after the airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94～98% after the airing, High hydrophilous resin 0.5～5% and Mierocrystalline cellulose 0.5～3%, above-mentioned batching is stirred, and carry out abrasive dust in the back input grinding machine that stirs, particle fineness≤0.074 millimeter.
Above-mentioned production technique is to adopt " improving the complete processing of viscosity of attapulgite clay " in application on June 20th, 2005 by the inventor, and the Chinese patent Granted publication number is: CN 1317067C, Granted publication day: on May 23rd, 2007.
Oily attapulgite plasticine viscosity height, soft plasticity-is good, have that water-retentivity is strong, shrinking percentage is little, indeformable, not hardening, do not produce be full of cracks, not mouldy, never degenerate not skin irritation, nontoxic, non-corrosiveness and do not have the characteristics of greasy feeling.
The oily attapulgite plasticine production technique is simple, and is with low cost, and can be repeatedly used, and the stronger market competitiveness is arranged.
Oily attapulgite plasticine is applicable to industrial art shape-designing, art education and toy for children.
Embodiment
The invention will be further described below in conjunction with embodiment:
1, the batching of oily attapulgite plasticine is made up of following component by weight percentage: high sticking attapulgite clay powder 55%, plam oil 12%, anatase thpe white powder 6%, glycerol 4%, gum arabic 3%, tripoly phosphate sodium STPP 1.3998%, capsanthin 0.5%, turmeric yellow 0.0001%, gardenia blue pigment 0.0001%, Tegosept M 0.05%, propylben 0.05% and deionized water 18%.
2, the production method of oily attapulgite plasticine: (1) adds deionized water in the stirrer earlier, glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M and propylben is added in the deionized water stir again; (2) after being dissolved in the deionized water, glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M and propylben be colored gelating soln, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the colored gelating soln stir, mix the back and be the work in-process of oily attapulgite plasticine; (3) plam oil is added in the work in-process of oily attapulgite plasticine and stir, the mixture after stirring is the finished product of oily attapulgite plasticine.
Claims (1)
1. oily attapulgite plasticine, it is characterized in that the batching of oily attapulgite plasticine is made up of following component by weight percentage: high sticking attapulgite clay powder 45～65%, plam oil 5～20%, anatase thpe white powder 0.1～5%, glycerol 0.1～5%, gum arabic 0.1～5%, tripoly phosphate sodium STPP 0.1～5%, capsanthin 0.0001～1%, turmeric yellow 0.0001～1%, gardenia blue pigment 0.0001～1%, Tegosept M 0.01～0.5%, propylben 0.01～0.5% and deionized water 15～30%;
The production method of described oily attapulgite plasticine: (1) adds deionized water in the stirrer earlier, glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M and propylben is added in the deionized water stir again; (2) after being dissolved in the deionized water, glycerol, gum arabic, tripoly phosphate sodium STPP, capsanthin, turmeric yellow, gardenia blue pigment, Tegosept M and propylben be colored gelating soln, the sticking attapulgite clay powder of height and anatase thpe white powder slowly added in the colored gelating soln stir, mix the back and be the work in-process of oily attapulgite plasticine; (3) plam oil is added in the work in-process of oily attapulgite plasticine and stir, the mixture after stirring is the finished product of oily attapulgite plasticine;
The sticking attapulgite clay powder of described height is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, from the attapulgite clay of mining area exploitation, and need be through 30～120 days natural weathering; Modification processing method is: calculate by weight percentage, take from the attapulgite clay 94～98% after the right weathering, evenly add 2～6% yellow soda ash, import jointly in the fermentation vat, add clear water and soak ageing, soak time is 72～120 hours; Get the attapulgite clay after the immersion, stir in the input stirrer, and the attapulgite clay after will stirring, be extruded into thin slice through extrusion machine, its gauge control is at 0.5～2 millimeter, with the attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after the airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94～98% after the airing, High hydrophilous resin 0.5～5% and Mierocrystalline cellulose 0.5～3%, above-mentioned batching is stirred, and carry out abrasive dust in the back input grinding machine that stirs, particle fineness≤0.074 millimeter.