CN101875552B - Powdery attapulgite hand inkpad and production method thereof - Google Patents
Powdery attapulgite hand inkpad and production method thereof Download PDFInfo
- Publication number
- CN101875552B CN101875552B CN2010101326823A CN201010132682A CN101875552B CN 101875552 B CN101875552 B CN 101875552B CN 2010101326823 A CN2010101326823 A CN 2010101326823A CN 201010132682 A CN201010132682 A CN 201010132682A CN 101875552 B CN101875552 B CN 101875552B
- Authority
- CN
- China
- Prior art keywords
- attapulgite
- hand inkpad
- inkpad
- hand
- powdery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a powdery attapulgite hand inkpad and a production method thereof. The powdery attapulgite hand inkpad is mainly characterized by comprising high-viscosity attapulgite clay powder, quick lime powder, anatase-type titanium dioxide, instant sodium silicate powder and modified carboxymethyl hydroxypropyl cellulose. The production method of the powdery attapulgite hand inkpad comprises the following steps of: adding the ingredients of the powdery attapulgite hand inkpad into a stirrer and stirring, inputting into a flour mill after even stirring and then milling, and packaging into a finished product of the powdery attapulgite hand inkpad. The wetted powdery attapulgite hand inkpad is kneaded into a whole wet inkpad block which is then flatted and burnished by a flat board to form a hand inkpad, and the palm closely presses the hand inkpad to finish the whole process of handprint production. A hand inkpad produced by the powdery attapulgite hand inkpad has exquisite texture and good softness plasticity; the pressed handprint has the characteristics of clear texture, small shrinkage after solidification, good strength, no deformation or crack and convenient permanent preservation; and the powdery attapulgite hand inkpad is suitable for production on site.
Description
Technical field
The present invention relates to ink paste, be specifically related to a kind of powdery attapulgite hand inkpad and production method thereof.
Background technology
With hand inkpad is that baby does a collection childhood memory that is worth, the special date for we stay next fine, real witness, be the precious souvenir that hand inkpad writes down our brothers' marking, present friend's best present.
The person's that gets the seal hand by being pressed on the ink paste, can be stayed the clear permanent fine marking, should have after hand inkpad solidifies true, three-dimensional, firm indeformable, be convenient to permanent preservation.
The hand inkpad of Xiao Shouing is made up of terra alba, spices and pigment in the market, and terra alba is too fast with water mixing after coagulation speed, causes the impression of the hand sharpness that is pressed on the hand inkpad relatively poor, and the low water resistance of intensity is bad.
Summary of the invention
The objective of the invention is to overcome weak point in the prior art, a kind of powdery attapulgite hand inkpad and production method thereof are provided.
Powdery attapulgite hand inkpad is made up of the sticking attapulgite clay powder of height, calcium lime powder, anatase thpe white powder, quick dissolving sodium silicate powder and modified carboxy methyl hydroxypropylcellulose.The batching adding stirrer of powdery attapulgite hand inkpad is stirred, and the back input pulverizing mill that stirs carries out abrasive dust, is packaged as the finished product of powdery attapulgite hand inkpad.
Attapulgite clay has higher plasticity-under aqueous situation, good stability, and the hardness of attapulgite clay is Mohs 2～3 degree; Attapulgite clay is viscosity when moist, viscosity can reach more than the 3000mPas, the dry post-shrinkage ratio of attapulgite clay is little, and does not produce be full of cracks, and high sticking attapulgite clay powder is the powdery attapulgite stone clay that the complete processing of employing raising viscosity of attapulgite clay is produced.
Calcium lime powder is levigate by lump lime and fine powder that obtain, and its main component is CaO, and calcium lime powder is used for the glueability that the present invention can improve powdery attapulgite hand inkpad, increases ultimate compression strength.
Anatase thpe white powder has excellent water dispersible and remarkable optical property, form and aspect stability, and size-grade distribution is good, has the characteristics of high gloss, high reducing power, high covering power.
Quick dissolving sodium silicate powder can be dissolved in water fast, is used for ultimate compression strength, folding strength and stable rate of drying that the present invention can improve powdery attapulgite hand inkpad.
The modified carboxy methyl hydroxypropylcellulose can be dissolved in cold water or hot water rapidly, has good thixotropy performance, and thickening material is effective, can increase the flexibility of powdery attapulgite hand inkpad.
The present invention is achieved by following technical proposals:
1, the batching of powdery attapulgite hand inkpad is made up of following component by weight percentage: high sticking attapulgite clay powder 65～85%, calcium lime powder 5～30%, anatase thpe white powder 0.1～5%, quick dissolving sodium silicate powder 0.1～5% and modified carboxy methyl hydroxypropylcellulose 0.1～5%.
2, the production method of powdery attapulgite hand inkpad: the batching adding stirrer of powdery attapulgite hand inkpad is stirred, mixture input pulverizing mill after stirring carries out abrasive dust, particle fineness is packaged as the finished product of powdery attapulgite hand inkpad less than 0.074 millimeter.
The sticking attapulgite clay powder of described height is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, it is characterized in that, and from the attapulgite clay of mining area exploitation, need be through 30～120 days natural weathering; Modification processing method is: calculate by weight percentage, take from the attapulgite clay 94～98% after the right weathering, evenly add 2～6% yellow soda ash, import jointly in the fermentation vat, add clear water and soak ageing, soak time is 72～120 hours; Get the attapulgite clay after the immersion, stir in the input stirrer, and the attapulgite clay after will stirring, be extruded into thin slice through extrusion machine, its gauge control is at 0.5～2 millimeter, with the attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after the airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94～98% after the airing, High hydrophilous resin 0.5～5% and Mierocrystalline cellulose 0.5～3%, above-mentioned batching is stirred, and carry out abrasive dust in the back input grinding machine that stirs, particle fineness≤0.074 millimeter.
Above-mentioned production technique is to adopt " improving the complete processing of viscosity of attapulgite clay " in application on June 20th, 2005 by the inventor, and the Chinese patent Granted publication number is: CN 1317067C, Granted publication day: on May 23rd, 2007.
Powdery attapulgite hand inkpad field fabrication and using method: earlier powdery attapulgite hand inkpad is added in the container, when water slowly adds powdery attapulgite hand inkpad, carry out continual mixing thoroughly, fully powdery attapulgite hand inkpad is stopped to add water after moistening when water, after 10 minutes, quick dissolving sodium silicate powder in the powdery attapulgite hand inkpad and modified carboxy methyl hydroxypropylcellulose are added to high sticking attapulgite clay powder, in calcium lime powder and the anatase thpe white powder, powdery attapulgite hand inkpad after moistening is crumpled as a whole moist clod, moist clod paved be placed in the framework, with smooth plank is moist clod pressing and press polish hand inkpad, the centre of the palm is pressed on the hand inkpad, palm slowly leaves hand inkpad after 5 seconds, finishes the whole process of making impression of the hand.
Described framework is a kind of ornament that is used to place and preserve hand inkpad.
The hand inkpad that uses powdery attapulgite hand inkpad to make has that quality exquisiteness, soft plasticity-are good, the impression of the hand clean mark of compacting, solidify that post-shrinkage ratio is little, intensity good indeformable, do not produce be full of cracks and be convenient to the characteristics of permanent preservation.
Powdery attapulgite hand inkpad is applicable to the field fabrication hand inkpad.
Embodiment
The invention will be further described below in conjunction with embodiment:
1, the batching of powdery attapulgite hand inkpad is made up of following component by weight percentage: high sticking attapulgite clay powder 80%, calcium lime powder 16%, anatase thpe white powder 2%, quick dissolving sodium silicate powder 1.2% and modified carboxy methyl hydroxypropylcellulose 0.8%.
2, the production method of powdery attapulgite hand inkpad: the batching adding stirrer of powdery attapulgite hand inkpad is stirred, mixture input pulverizing mill after stirring carries out abrasive dust, particle fineness is packaged as the finished product of powdery attapulgite hand inkpad less than 0.074 millimeter.
Claims (1)
1. powdery attapulgite hand inkpad, it is characterized in that the batching of powdery attapulgite hand inkpad is made up of following component by weight percentage: high sticking attapulgite clay powder 65～85%, calcium lime powder 5～30%, anatase thpe white powder 0.1～5%, quick dissolving sodium silicate powder 0.1～5% and modified carboxy methyl hydroxypropylcellulose 0.1～5%;
The production method of described powdery attapulgite hand inkpad: the batching adding stirrer of powdery attapulgite hand inkpad is stirred, mixture input pulverizing mill after stirring carries out abrasive dust, particle fineness is packaged as the finished product of powdery attapulgite hand inkpad less than 0.074 millimeter;
The sticking attapulgite clay powder of described height is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, from the attapulgite clay of mining area exploitation, and need be through 30～120 days natural weathering; Modification processing method is: calculate by weight percentage, take from the attapulgite clay 94～98% after the right weathering, evenly add 2～6% yellow soda ash, import jointly in the fermentation vat, add clear water and soak ageing, soak time is 72～120 hours; Get the attapulgite clay after the immersion, stir in the input stirrer, and the attapulgite clay after will stirring, be extruded into thin slice through extrusion machine, its gauge control is at 0.5～2 millimeter, with the attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after the airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94～98% after the airing, High hydrophilous resin 0.5～5% and Mierocrystalline cellulose 0.5～3%, above-mentioned batching is stirred, and carry out abrasive dust in the back input grinding machine that stirs, particle fineness≤0.074 millimeter.