CN101875126A - 一种颗粒钼铁的处理方法 - Google Patents
一种颗粒钼铁的处理方法 Download PDFInfo
- Publication number
- CN101875126A CN101875126A CN2009102426027A CN200910242602A CN101875126A CN 101875126 A CN101875126 A CN 101875126A CN 2009102426027 A CN2009102426027 A CN 2009102426027A CN 200910242602 A CN200910242602 A CN 200910242602A CN 101875126 A CN101875126 A CN 101875126A
- Authority
- CN
- China
- Prior art keywords
- ferromolybdenum
- granules
- molybdenum
- screenings
- sintering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种颗粒钼铁的处理方法，涉及一种颗粒钼铁，特别是粒度范围在5mm以下的颗粒钼铁的回收方法。其特征在于其处理过程是将钼铁经粉碎机成颗粒钼铁后，进行过筛，将筛下物经过压制成型，再在保护性气氛下进行烧结。本发明的方法，将粒度范围在5mm以下的颗粒钼铁筛出、筛下物经过油压机压制成一定形状，在氢气保护下用马弗炉进行预烧结，使其具有一定的强度，有效增加粒度钼铁粒度、提高强度、有效减少了钼铁生产过程中钼铁的添加量，减少了热量损失，处理工艺简单、处理量大，钼铁回利用率高。
Description
技术领域
一种颗粒钼铁的处理方法，涉及一种颗粒钼铁，特别是粒度范围在5mm以下的颗粒钼铁的回收方法。
背景技术
钼铁作为钼的添加剂广泛用于合金钢或特种钢的生产，世界60％以上的钼金属用于合金钢的生产。钼铁的生产方法大多采用炉外法，以三氧化钼为主要原料，添加硅铁、铝粉、铁磷、萤石等辅料，通过金属热还原生产出钼铁锭，然后粉碎到客户需要的粒度范围，作为成品出售。在粉碎过程中，会产生约10％左右粒径小于5mm的钼铁小颗粒，这些小粒度钼铁，客户往往不愿意接受。工厂一般采用回炉熔炼的方式处理，但由于钼铁溶化的温度较高，需要消耗大量的热量，因此每次处理的量有限，且处理的量少于新产生的小粒度钼铁量，久而久之，会造成一定的库存积压。
发明内容
本发明的目的就是针对上述已有技术存在的不足，提供一种能有效增加粒度钼铁粒度、提高强度、有效减少钼铁生产过程中钼铁的添加量，减少热量损失，处理工艺简单、处理量大，的颗粒钼铁的处理方法。
本发明的目的是通过以下技术方案实现的。
一种颗粒钼铁的处理方法，其特征在于其处理过程是将钼铁经粉碎机成颗粒钼铁后，进行过筛，将筛下物经过压制成型，再在保护性气氛下进行烧结。
本发明的一种颗粒钼铁的处理方法，其特征在于所述的进行过筛过程是采用的是160或200目筛。
本发明的一种颗粒钼铁的处理方法，其特征在于所述的将筛下物经过压制成型过程压制压力为3～5公斤/cm2，压制成直径和高度在50～100mm的圆柱体。
本发明的一种颗粒钼铁的处理方法，其特征在于所述的在保护性气氛下进行烧结过程是在氢气气氛下，1200～1500℃，烧结2小时烧结。
本发明的方法，将粒度范围在5mm以下的颗粒钼铁粉碎、过筛、筛下物经过油压机压制成一定形状，在氢气保护下用马弗炉进行预烧结，使其具有一定的强度，有效增加粒度钼铁粒度、提高强度、有效减少了钼铁生产过程中小颗粒钼铁的添加量，减少了热量损失，处理工艺简单、处理量大，回收利用率高。
具体实施方式
一种颗粒钼铁的处理方法，其过程是将钼铁颗粒经粉碎机粉碎成钼铁粉末后，再进行筛分，将筛下物经过油压机压制成型，在氢气保护下用马弗炉进行预烧结，使其具有一定的强度。
本发明的一种颗粒钼铁的处理方法，钼铁经粉碎机粉碎成钼铁粉末后，过160～200目筛，钼铁粉在压力为3～5公斤/cm2压力下压制成直径和高度在50～100mm的圆柱，将这些圆柱在在氢气保护气氛下在马弗炉内烧结2小时，烧结温度1200～1500℃，待物料冷却后，及得到钼铁块成品。
实施例1
将钼铁经万能粉碎机粉碎，过200钼筛、取30克在手动粉末压片机上以3公斤/cm2的压力压制成直径和高度在30mm的圆柱，将圆柱在氢气保护气氛下在马弗炉内烧结2小时，烧结温度1200℃，待物料冷却后，及得到钼铁块成品。
实施例2
将小粒度钼铁经万能粉碎机粉碎，过200钼筛、取100克在手动粉末压片机上以5公斤/cm2的压力压制成直径和高度在100mm的圆柱，将圆柱在氢气保护气氛下在马弗炉内烧结2小时，烧结温度1500℃，待物料冷却后，及得到钼铁块成品。
实施例3
将小粒度钼铁经万能粉碎机粉碎，过200钼筛、加入无水乙醇做润滑剂，取100克在手动粉末压片机上以4公斤/cm2压力压制成直径和高度在100mm的圆柱，将圆柱在氢气保护气氛下在马弗炉内烧结2小时，烧结温度1500℃，待物料冷却后，及得到钼铁块成品。经检验钼铁指标完全合格。
实施例4
将钼铁经万能粉碎机粉碎，过160钼筛、取30克在手动粉末压片机上以3公斤/cm2的压力压制成直径和高度在30mm的圆柱，将圆柱在氢气保护气氛下在马弗炉内烧结2小时，烧结温度1200℃，待物料冷却后，及得到钼铁块成品。
Claims (4)
1.一种颗粒钼铁的处理方法，其特征在于其处理过程是将钼铁经粉碎机成钼铁粉末后，进行过筛，将筛下物经过压制成型，再在保护性气氛下进行烧结。
2.根据权利要求1所述的一种颗粒钼铁的处理方法，其特征在于所述的进行过筛过程是采用的是160或200目筛。
3.根据权利要求1所述的一种颗粒钼铁的处理方法，其特征在于所述的将筛下物经过压制成型过程压制压力为3～5公斤/cm2，压制成直径和高度在50～100mm的圆柱体。
4.根据权利要求1所述的一种颗粒钼铁的处理方法，其特征在于所述的在保护性气氛下进行烧结过程是在氢气气氛下，1200～1500℃，烧结2小时烧结。