CN101851803B - 一种保健功能粘胶纤维及其制备方法 - Google Patents
一种保健功能粘胶纤维及其制备方法 Download PDFInfo
- Publication number
- CN101851803B CN101851803B CN2010101919674A CN201010191967A CN101851803B CN 101851803 B CN101851803 B CN 101851803B CN 2010101919674 A CN2010101919674 A CN 2010101919674A CN 201010191967 A CN201010191967 A CN 201010191967A CN 101851803 B CN101851803 B CN 101851803B
- Authority
- CN
- China
- Prior art keywords
- sodium alginate
- health
- viscose
- viscose fiber
- care function
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种保健功能粘胶纤维及其制备方法。本发明涉及一种粘胶纤维。本发明的目的是提供一种有保健功能且纺丝性能好的粘胶纤维及其制备方法。本发明的技术方案是,包括粘胶纤维,粘胶纤维中含有海藻酸钠粉和炉甘石粉。一种制备权利要求1所述保健功能粘胶纤维的工艺,包括制胶、纺丝工序,(1)将海藻酸钠粉溶于氢氧化钠溶液中制成海藻酸钠胶体溶液,(2)将炉甘石粉在搅拌下缓慢加入上述海藻酸钠胶体溶液中,(3)在纤维素黄酸酯溶解过程中将上述(2)制成的含有炉甘石粉的海藻酸钠胶体溶液加入粘胶中,经混合、研磨制成具有保健功能的纺丝液。本发明用于制备保健功能粘胶纤维。
Description
技术领域:
本发明涉及一种粘胶纤维,特别是一种保健功能粘胶纤维及其制备方法。
背景技术:
针对市场的需求,具有保健功能的纤维不断出现,如海藻粘胶纤维。炉甘石粉具有强吸水性,还具有收敛、清凉止痒、抑菌等效果。但其分散液的稳定性较差,致使纺丝困难。
发明内容:
本发明的目的是提供一种有保健功能且纺丝性能好的粘胶纤维及其制备方法。本发明的技术方案是,包括粘胶纤维,其特征在于:粘胶纤维中含有海藻酸钠粉和炉甘石粉。海藻酸钠粉和炉甘石粉之和与粘胶纤维的重量比为1-8%,海藻酸钠粉与炉甘石粉的重量比为1-5∶1-30。一种制备权利要求1所述保健功能粘胶纤维的工艺,包括制胶、纺丝工序,其特征在于:(1)将海藻酸钠粉溶于氢氧化钠溶液中制成海藻酸钠胶体溶液,(2)将炉甘石粉在搅拌下缓慢加入上述海藻酸钠胶体溶液中,(3)在纤维素黄酸酯溶解过程中将上述(2)制成的含有炉甘石粉的海藻酸钠胶体溶液加入粘胶中,经混合、研磨制成具有保健功能的纺丝液。本发明与现有技术比较具有保健、美容及辅助医疗的显著优点。
具体实施方式:
本发明利用海藻酸钠的高粘性将炉甘石粉均匀地分散在其溶液中,避免了炉甘石粉在纺丝过程中发生沉淀,从而提高了其纺丝性能,本发明采用了常规的粘胶纺丝工艺,即可纺出具有保健功能的粘胶纤维。
本发明有以下实施例:
实施例1:发明人结合生产实际试纺出了166.7dtex、133.3dtex等规格的粘胶长丝和1.67dtex的短纤维。
1.产品规格:1 66.7dtex粘胶长丝
原料:棉浆 炉甘石粉 海藻酸钠粉
复合粉体加入量:1%
(a)将海藻酸钠粉按重量1∶50的比例在50~75℃的温度范围内经搅拌(时间3小时)溶解于浓度为1mol/L的NaOH溶液中,制成具有一定粘度的海藻酸钠胶体溶液。
(b)将炉甘石粉在边搅拌的情况下缓慢加入到上述所配的海藻胶体溶液中,所配浓度为5%(视海藻酸钠胶体溶液为母液)。制成复合功能添加剂。
(c)在纤维素黄酸酯溶解过程中将(b)所配复合添加剂均匀加入粘胶中,经4小时混合、研磨成具有抗菌、护肤、保健功能的纺丝液(间歇法生产)。其指标为:
甲纤:7.5~9.5%
含碱:5±0.5%
粘度:28~50秒
熟成度:9.2±2ml
(d)将含有功能添加剂的共混纺丝液经常规三道过滤,然后再增加一层府绸滤布过滤,在常规酸浴条件下,以79米/分的速度纺丝,再经洗涤、上油、烘干得到具有多种功能的粘胶纤维。
实施例2、
2.产品规格:产品规格133.3dtex粘胶长丝
原料:棉浆 炉甘石粉 海藻酸钠粉
复合粉体加入量:5%
(a)将海藻酸钠粉按重量1∶80的比例在50~75℃的温度范围内经搅拌(时间3小时)溶解于0.5mol/L的NaOH溶液中,制成具有一定粘度的海藻酸钠胶体溶液。
(b)将炉甘石粉在边搅拌的情况下缓慢加入到上述所配的海藻胶体溶液中,所配浓度为10%(视海藻酸钠胶体溶液为母液)。制成复合功能添加剂。
(c)在纤维素黄酸酯溶解过程中将(b)所配复合添加剂均匀加入粘胶中,经4小时混合、研磨成具有抗菌、护肤、保健功能的纺丝液(间歇法生产)。
(d)用400目滤布过滤后经纺前注射设备在纺丝前通过动静态混合(连续法生产)使其均匀的加入到纺丝液中,在常规的酸浴条件下,以80米/分的速度纺丝,再经洗涤、上油、烘干得到具有多种功能的粘胶纤维。
(1)纺丝工艺参数
紧张牵伸 d紧=2.692%
盘间牵伸 d盘=20%
丝口牵伸 d口=-0.5%
总牵伸 D总=22.62%
(2)纺丝浴组成
硫酸:132±1g/L
硫酸锌:11±0.5g/L
硫酸钠:275±3g/L
酸浴落差:2≤2g/L
(3)洗涤工艺条件
酸洗浓度:3±0.2g/L
酸洗温度:室温
脱硫浓度:5±0.5g/L
脱硫温度:60±2℃
实施例3:1.67dtex粘胶短纤维
原料:棉浆 炉甘石粉 海藻酸钠粉
复合粉体加入量:8%
将海藻酸钠粉按重量1∶200的比例在50~75℃的温度范围内经搅拌(时间3小时)溶解于1.5mol/L的NaOH溶液中,制成具有一定粘度的海藻酸钠胶体溶液。
(a)将炉甘石粉在边搅拌的情况下缓慢加入到上述所配的海藻胶体溶液中,所配浓度为20%(视海藻酸钠胶体溶液为母液)。制成复合功能添加剂。
(b)将炉甘石粉在边搅拌的情况下缓慢加入到上述所配的海藻胶体溶液中,所配浓度为10%(视海藻酸钠胶体溶液为母液)。制成复合功能添加剂。
(c)在纤维素黄酸酯溶解过程中将(b)所配复合添加剂均匀加入粘胶中(间歇法),经4小时混合、研磨成具有抗菌、护肤、保健功能的纺丝液。其指标为:
甲纤:8.5~9.5%
含碱:4.0~6.0%
粘度:30~50秒
熟成度:8~15ml(10%NH4CL值)
(d)将含有功能添加剂的共混纺丝液经常规三道过滤,然后再增加一层府绸滤布过滤,在常规酸浴条件下,以79米/分的速度纺丝,再经洗涤、烘干得到具有多种功能的粘胶纤维。
(1)纺丝工艺参数
喷丝头抽伸 51~55%
导盘抽伸 13~15%
塑化抽伸 21~25%
总抽伸 85~95%
(2)纺丝浴组成(克/升):
硫酸: 105±1g/L
硫酸锌: 13±0.5g/L
硫酸钠: 330±10g/L
酸浴落差: ≤10g/L
(3)洗涤工艺条件
脱硫浓度: 2~8g/L
脱硫温度: 70~80℃
酸洗浓度: 0.5~3g/L
酸洗温度: 20~50℃
复合功能粘胶纤维的各项物理指标均符合GB/T13758-92和GB/T14463-93国家标准,粉体在纤维内外分布均匀,染色性能良好。
本发明与传统产品相比有如下优点:
该纤维具有良好的化学、物理性能及纤维素纤维穿着舒适的特点,其组织结构通过扫描电子显微镜检测,显示出纤维断面与众不同的多孔结构,纤维的轴心线方向可见不规则结构。这种小结晶低趋向和较高的孔隙率使该纤维具有了非常重要的性能——有利于该纤维有效成分的摄取和转移,能够使这些有效物质在纤维和皮肤表面发生相互作用。
该纤维具有卓越的抗菌、消炎、止痒、清凉、收敛保护、润颜、护肤修护等附加功效,用其制作的美容护肤品能促进血液循环,有利于表皮细胞的新陈代谢,其中矿物盐等对促进胶原细胞再生、防止其皱,使皮肤保持适度的膨润和弹性起着非常重要的作用。用该种纤维纯纺或混纺的纱线加工的织物和无纺布可以广泛的用于加工工装(包括手套)、运动装、保健内衣、袜类、婴儿内衣裤、家用纺织品(包括装饰布、床上用品和填充物),非制造及家庭和医疗卫生用品,切实起到卫生保健医疗的目的。该纤维具有纤维素纤维的一切优良性能,复合功能粉体的加入不影响对纤维的加工和织造,且染色性能优良,其特有的组织结构使其具有穿着舒适、透气、吸汗、爽身等诸多优点,能加工成理想的纺织保健面料,重要的是其所含的有效成份具有永久性,不会因洗涤而消失(不同于面料后整理工艺),手感良好。
Claims (1)
1.一种保健功能粘胶纤维的制备方法,包括制胶、纺丝工序,其特征在于:(1)将海藻酸钠粉溶于氢氧化钠溶液中制成海藻酸钠胶体溶液,(2)将炉甘石粉在搅拌下缓慢加入上述海藻酸钠胶体溶液中,海藻酸钠粉与炉甘石粉的重量比为1-5∶1-30,(3)在纤维素黄酸酯溶解过程中将上述(2)制成的含有炉甘石粉的海藻酸钠胶体溶液加入粘胶中,海藻酸钠粉与炉甘石粉之和与粘胶纤维的重量比为1∶8%,经混合、研磨制成具有保健功能的粘胶纤维纺丝液。