CN101812876B - 一种全水泥基不燃泡沫保温夹芯板 - Google Patents

一种全水泥基不燃泡沫保温夹芯板 Download PDF

Info

Publication number
CN101812876B
CN101812876B CN 200910212328 CN200910212328A CN101812876B CN 101812876 B CN101812876 B CN 101812876B CN 200910212328 CN200910212328 CN 200910212328 CN 200910212328 A CN200910212328 A CN 200910212328A CN 101812876 B CN101812876 B CN 101812876B
Authority
CN
China
Prior art keywords
density
cement
foaming layer
foam concrete
cement foaming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 200910212328
Other languages
English (en)
Other versions
CN101812876A (zh
Inventor
朱恒杰
于崇明
兰代英
李福山
洪宝友
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING HUALI UNITED HIGH-TECH Co Ltd
Original Assignee
BEIJING HUALI UNITED HIGH-TECH Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING HUALI UNITED HIGH-TECH Co Ltd filed Critical BEIJING HUALI UNITED HIGH-TECH Co Ltd
Priority to CN 200910212328 priority Critical patent/CN101812876B/zh
Publication of CN101812876A publication Critical patent/CN101812876A/zh
Application granted granted Critical
Publication of CN101812876B publication Critical patent/CN101812876B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种全水泥基不燃泡沫保温夹芯板，它包括两层密度为750～1000kg/m3的高密度水泥发泡层，在所述两高密度水泥发泡层之间固定连接有一密度为250～400kg/m3的低密度水泥发泡层，在所述两层高密度水泥发泡层内设置有一增强网片，制作方法制作而成，将水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土涂抹在模具的底面平板上，再在其上设有增强网片，然后继续涂抹高密度泡沫混凝土，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层，再同样方法制作低密度水泥发泡层；再制作高密度水泥发泡层，本发明可以广泛应用于建筑物的保温工程中。

Description

一种全水泥基不燃泡沫保温夹芯板
技术领域
本发明涉及一种用于建筑外墙的材料，特别是关于一种全水泥基不燃泡沫保温夹芯板。
背景技术
随着全球能源紧缺矛盾的日益突出，世界各国纷纷出台节能减排政策。“十一五”期间，我国城镇建筑节能率将达到50％，其中，部分大城市、北方寒冷地区节能率将达到65％，这样就对制造保温材料的技术和工艺提出新的要求。目前，国内外常采用的保温材料为：聚苯乙烯泡沫塑料和聚氨酯硬质泡沫材料，然而上述两种保温材料存在易燃、受压力较大时容易变形而且使用寿命比较短，一般为15～25年等缺陷。
发明内容
针对上述问题，本发明的目的是提供一种不易燃、使用寿命较长且保温性能更好的一种全水泥基不燃泡沫保温夹芯板。
为实现上述目的，本发明采取以下技术方案：一种全水泥基不燃泡沫保温夹芯板，其特征在于：它包括两层密度为750～1000kg/m3的高密度水泥发泡层，在所述两高密度水泥发泡层之间固定连接有一密度为250～400kg/m3的低密度水泥发泡层，在所述两层高密度水泥发泡层内设置有一增强网片；所述的保温夹芯板是由如下的制作方法制作而成，所述的制作方法包括如下步骤：1)制作一模具，模具由一底面平板及一连接在底面平板四周的挡板组成；2)将密度为750～1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土涂抹在模具的底面平板上，再在其上设有增强网片，然后继续涂抹高密度泡沫混凝土，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层；3)将密度为250～400kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的低密度泡沫混凝土涂抹在高密度水泥发泡层上，找平后待低密度泡沫混凝土干透，形成低密度水泥发泡层；4)将密度为750～1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土涂抹在低密度水泥发泡层上，再设置一增强网片，然后继续涂抹高密度泡沫混凝土，找平后待高密度泡沫混凝土干透，形成全水泥基不燃发泡保温夹芯板。
所述高密度水泥发泡层的密度为750～800kg/m3；所述低密度水泥发泡层的密度为250～300kg/m3。
所述增强网片为钢丝网或者玻璃纤维网中的一种。
本发明由于采取以上技术方案，其具有以下优点：1、本发明由于采用了水泥和泡沫混合的结构，使得导热热阻数值更大，因此保温性能更好。2、本发明由于采用了水泥作为板材的内层结构，因此化学稳定性更好，使用寿命更长。本发明可以广泛应用于建筑物的保温工程中。
附图说明
图1是本发明立体示意图
图2是图1的俯视图
图3是本发明的模具示意图
具体实施方式
下面结合附图和实施例对本发明的进行详细的描述。
如图1、图2所示，本发明包括两层密度为600～1000kg/m3的高密度水泥发泡层1，在所述两高密度水泥发泡层之间固定连接有一密度为200～400kg/m3的低密度水泥发泡层2，在所述两层高密度水泥发泡层内分别设置有一增强网片3。
如图3所示，实施例一的制作方法步骤如下：
1)制作一水泥发泡层模具4，模具4由一底面平板41及一连接在底面平板41四周的挡板42组成；
2)将密度为600～1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土涂抹在模具4的底面平板41上，再在其上设有增强网片3，然后继续涂抹高密度泡沫混凝土，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层1；
3)将密度为200～400kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的水泥砂浆涂抹在高密度水泥发泡层1上，找平后待低密度泡沫混凝土干透，形成低密度水泥发泡层2；
4)将密度为600～1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土涂抹低密度水泥发泡层2上，再在其上设有增强网片3，然后继续涂抹高密度泡沫混凝土，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层1；形成全水泥基不燃发泡保温夹芯板。
如图3所示，实施例二的制作方法步骤如下：
1)制作一模具4，模具4由一底面平板41及一连接在底面平板41四周的挡板42组成；
2)将密度为600kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土砂浆涂抹在模具4的底面平板41上，再在其上设有增强网片3，然后继续涂抹高密度泡沫混凝土砂浆，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层1；
3)将密度为200kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的低密度泡沫混凝土砂浆涂抹在高密度水泥发泡层1上，找平后待低密度泡沫混凝土干透，形成低密度水泥发泡层2；
4)将密度为600kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土砂浆涂抹在低密度水泥发泡层2上，再在其上设有增强网片3，然后继续涂抹高密度泡沫混凝土砂浆，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层1；形成全水泥基不燃发泡保温夹芯板。
如图3所示，实施例三的制作方法步骤如下：
1)制作一模具4，模具4由一底面平板41及一连接在底面平板41四周的挡板42组成；
2)将密度为1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土砂浆涂抹在模具4的底面平板41上，再在其上设有增强网片3，然后继续涂抹高密度泡沫混凝土砂浆，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层1；
3)将密度为400kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的水泥砂浆涂抹在高密度水泥发泡层1上，找平后待低密度泡沫混凝土干透，形成低密度水泥发泡层2；
4)将密度为1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土砂浆涂抹在低密度水泥发泡层2上，再在其上设有增强网片3，然后继续涂抹高密度泡沫混凝土砂浆，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层1；形成全水泥基不燃发泡保温夹芯板。
上述实施例中，增强网片3为钢丝网或者玻璃纤维网中的一种。

Claims (3)

1.一种全水泥基不燃泡沫保温夹芯板，其特征在于：它包括两层密度为750～1000kg/m3的高密度水泥发泡层，在所述两高密度水泥发泡层之间固定连接有一密度为250～400kg/m3的低密度水泥发泡层，在所述两层高密度水泥发泡层内设置有一增强网片；所述的保温夹芯板是由如下的制作方法制作而成，所述的制作方法包括如下步骤：
1)制作一模具，模具由一底面平板及一连接在底面平板四周的挡板组成；
2)将密度为750～1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土涂抹在模具的底面平板上，再在其上设有增强网片，然后继续涂抹高密度泡沫混凝土，找平后待高密度泡沫混凝土干透，形成高密度水泥发泡层；
3)将密度为250～400kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的低密度泡沫混凝土涂抹在高密度水泥发泡层上，找平后待低密度泡沫混凝土干透，形成低密度水泥发泡层；
4)将密度为750～1000kg/m3的水泥、有机高分子材料合成的发泡剂制作出的泡沫和水混合搅拌，将得到的高密度泡沫混凝土涂抹在低密度水泥发泡层上，再设置一增强网片，然后继续涂抹高密度泡沫混凝土，找平后待高密度泡沫混凝土干透，形成全水泥基不燃发泡保温夹芯板。
2.如权利要求1所述的一种全水泥基不燃泡沫保温夹芯板，其特征在于：所述高密度水泥发泡层的密度为750～800kg/m3；所述低密度水泥发泡层的密度为250～300kg/m3。
3.如权利要求1或2所述的一种全水泥基不燃泡沫保温夹芯板，其特征在于：所述增强网片为钢丝网或者玻璃纤维网中的一种。
CN 200910212328 2009-11-06 2009-11-06 一种全水泥基不燃泡沫保温夹芯板 Active CN101812876B (zh)