CN1017712B - 复合隔热保温涂料及其生产工艺 - Google Patents
复合隔热保温涂料及其生产工艺Info
- Publication number
- CN1017712B CN1017712B CN 90105780 CN90105780A CN1017712B CN 1017712 B CN1017712 B CN 1017712B CN 90105780 CN90105780 CN 90105780 CN 90105780 A CN90105780 A CN 90105780A CN 1017712 B CN1017712 B CN 1017712B
- Authority
- CN
- China
- Prior art keywords
- add
- construction
- compound heat
- heat
- perlite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
本发明属于复合隔热保温涂料及其生产工艺。该保温涂料由镁铝硅酸盐、增强纤维、改性添加剂、填充剂、复合高温粘接剂、消泡剂和水按比例,经原料的表面除杂、精选、粉碎、混合浸泡、搅拌、消泡静置工艺复合而成。需常温施工时,则在上述涂料按比例加入氧化钙和石膏。该涂料保温效果好、能冷热施工、易成型、粘接性好、无毒不腐蚀设备,表面光洁、美观。广泛用于各种设备、炉窑及建筑物的隔热保温。
Description
本发明属于复合型隔热保温涂料。
国内近几年已生产一种复合硅酸盐隔热保温涂料,属于热固型保温涂料(热施工涂料)。只能在60℃以上的热设备上经多次涂刷干燥成型,施工速度极慢,工期长,热施工
害施工人员身体健康,同时不能在设备停产检修时室温施 高使用温度在800℃以下,因此限制了它的使用范围。
本发明的目的:就是提供一种既适用于热施工又适用于室温冷施工的复合隔热保温涂料及其生产工艺。
本发明产品是以镁铝硅酸盐矿为主要成分,与填充剂如珍珠岩或蛭石,增强纤维如陶瓷纤维,改性添加剂如
或茶籽皂素,复合高温粘接剂如改性水玻璃和磷酸盐,消泡剂如硅油或辛醇及水复合而成热固型保温涂料。如需在室温施工,则在上述热固型隔热保温涂料中,加入氧化钙与石膏而制得冷固型隔热保温涂料。
本发明产品的组分与配方(重量%)
陶瓷纤维 5-9%
快-T或茶籽皂素 2-8%
珍珠岩或蛭石 4-10%
改性水玻璃和磷酸盐 7-12%
硅油或辛醇
余量为水
如需要室温冷施工,则在上述产品中加入氧化钙与石膏复合固凝剂4-12%
上述复合隔热保温涂料的生产工艺
附图1为复合隔热保温涂料生产工艺流程图,图中1为原料镁铝硅酸盐矿的除杂、粉碎;2为镁铝硅酸盐 陶瓷纤维、快-T或茶籽皂素混合浸泡处理;3为混合搅拌;4为消泡静置;5为室温施工用隔热保温涂料;6为氧化钙与石膏;7为改性水玻璃和磷酸盐;8为珍珠岩或蛭石;9为快 T或茶籽皂素;10为水;11为硅油或辛醇;12为热固型隔热保温涂料。
生产工艺:首先除去镁铝硅酸盐矿的表面杂渣,经磁力机精选,粉碎成粒度为0.1-2mm的粉末,并在其中按上述比例加入珍珠岩或蛭石,快 T或茶籽皂素,陶瓷纤维及少量水,混合浸泡处理,放入搅拌池中,按比例加入改性水玻璃和磷酸盐、水,以300-600小时转 分的搅拌速度进行混合搅拌,搅拌时间为0.5-1.5小时,再按比例加入硅油或辛醇搅拌消泡,静置5-7小时,当室温施工时,则在其涂料中按比例加入氧化钙和石膏
本发明实施例:
1、组分与配方(重量%
镁铝硅酸盐
快-T或茶籽皂素
陶瓷纤维 8%
珍珠岩或蛭石 9%
改性水玻璃和磷酸盐 11%
硅油或辛醇 4%
氧化钙与石膏 11%
水 40%
2、产品性能:
该产品的干容重小于200kg/m3,导热系数为0.0352-0.057kcal/m.b.℃,孔隙率72%,收缩率17.5%,抗压强度2.5-3kg/cm2,最高使用温度800-1200℃,最低使用温度-30℃。
该保温涂料经试用检测,保温效果好,施工速度快,达到本发明的目的。
本发明属复合隔热保温涂料及其生产工艺,采用了新配方,改进了生产工艺,加入复合高温粘接剂,以提高使用温度,加入消泡剂,以缩短生产周期,加入复合固凝剂,以快速固化成型。这种复合型隔热保温涂料,具有良好的保温效果,生产周期能缩短3-5倍,无毒,无环境污染。不仅能在设备带热条件下使用,还能在设备检修和安装时室温下使用,易成型,施工速度快,工期短,干燥后粘接性能好,表面光滑、美观,不易脱落开裂,不粉化、不腐蚀设备。该保温涂料不仅用于一般设备的保温,特别适用于异型管件、阀、闸、球体、旋转体设备的保温,广泛用于化工,轻工、石油、冶金、电力、建筑、国防等部门各种设备的隔热保温。
Claims (3)
1、一种复合型隔热保温涂料,其特征在于组成和重量百分比为:
镁铝硅酸盐 5-12%;
陶瓷纤维 5-9%;
快-T或茶籽皂素 2-8%;
珍珠岩或蛭石 4-10%;
改性水玻璃和磷酸盐 7-12%;
硅油或辛醇 1-5%;
氧化钙与石膏 4-12%;
水 余量。
2、根据权利要求1所述的复合型隔热保温涂料,其特征在于具体的组成和重量百分比为
镁铝硅酸盐 10%;
陶瓷纤维 8%;
快一T-或茶籽皂素 7%;
珍珠岩或蛭石 9%;
改性水玻璃和磷酸盐 11%
硅油或辛醇 4%;
氧化钙与石膏 11%;
水 40%。
3、实施权利要求1或2所述复合型隔热保温涂料的生产工艺,包括镁铝硅酸盐矿的表面除杂,经磁力机精选,粉碎成粒状、按比例在其中加入陶瓷纤维,珍珠岩或蛭石,快一T或茶籽皂素和少量水,混合浸泡处理,放入搅拌池中再按比例加入改性水玻璃和磷酸盐、水,混合搅拌、消泡静置其特征在于:
(1)粉碎后的镁铝硅酸盐粉末粒度为0.1-2mm
(2)混合搅拌的速度为300-600转/分,其搅拌时间为0.5-1.5小时;
(3)加入硅油或辛醇,消泡静置时间为5-7小时。
(4)室温冷施工时,加入氧化钙与石膏。