CN101709177B - Waterborne digital ink-jet printing sublimation ink and preparation method thereof - Google Patents
Waterborne digital ink-jet printing sublimation ink and preparation method thereof Download PDFInfo
- Publication number
- CN101709177B CN101709177B CN 200910199869 CN200910199869A CN101709177B CN 101709177 B CN101709177 B CN 101709177B CN 200910199869 CN200910199869 CN 200910199869 CN 200910199869 A CN200910199869 A CN 200910199869A CN 101709177 B CN101709177 B CN 101709177B
- Authority
- CN
- China
- Prior art keywords
- disperse
- ink
- red
- percent
- yellow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides waterborne digital ink-jet printing sublimation ink and a preparation method thereof. The ink comprises the following components in percentage by mass: 1 to 10 percent of disperse dye, 2 to 15 percent of dispersing agent, 10 to 60 percent of deionized water, 10 to 50 percent of water soluble organic solvent, 0.1 to 5 percent of surface active agent, 0.05 to 0.5 percent of germicide, and 0.05 to 0.5 percent of defoaming agent. The preparation method comprises the following steps of: mixing 1 to 20 percent of dispersing agent, 10 to 40 percent of water soluble organic solvent, 0.1 to 2 percent of germicide, 0.1 to 2 percent of defoaming agent, and 30 to 50 percent of deionized water, adding 1 to 20 percent of disperse dye while stirring, and grinding the mixed solution to obtain color paste; uniformly mixing 15 to 50 percent of color paste, 10 to 30 percent of water soluble organic solvent, 0.1 to 5 percent of surface active agent and 20 to 50 percent of deionized water and filtering the mixed solution to obtain the waterborne digital ink-jet printing sublimation ink. When the waterborne digital ink-jet printing sublimation ink is used in a large-sized ink-jet printer using waterborne ink, the good printing smoothness and the water retention of a printing head are achieved, and the preparation process is simple.
Description
Technical field
The invention belongs to digital ink-jet marking ink and preparation field thereof, particularly relate to a kind of waterborne digital ink-jet printing sublimation ink and preparation method thereof.
Background technology
Ink-jet printed technology can be satisfied with human consumer's personalization, diversified demand with its short run, short processes flow process and quick characteristics of paying, and is widely used in every field such as outdoor advertising air brushing, textile inkjet printing.
Ink-jet ink is the key in the inkjet technology, and printing ink can be divided into pigment style and dye-type two big classes according to toner kind difference, can be divided into water-based and solvent-borne type two big classes again by the solvent species difference.Water-base ink is with its low smell, low volatility, thereby has eco-friendly characteristic, looked at by numerous human consumer parents, and pigmented ink is widely used in the outdoor advertising with its good sun-resistant fastness characteristic.Along with the enhancing of entire society's environmental consciousness, be that the advertisement of main raw material is put on agenda with cloth gradually with the trevira.Trevira is one of most important in the world textile fibres kind; And pigment tack on trevira is not good; Therefore must just might be attached to polyester fibre surface by means of special tackiness agent, but the use of tackiness agent tends to make the fabric hardening and influences its soft hand feeling.Dispersed dye can get into the intermolecular fabric coloring that makes of trevira through distillation, do not influence the feel of fabric.Simultaneously the status of dispersed dye in polyester textile is ink-jet printed is very outstanding, and preparation is that the water-base ink of main tinting material has important application value with dispersed dye.
Dispersed dye are water insoluble or be slightly soluble in water, therefore through adopting dispersion agent that dispersed dye are carried out surface-treated, dispersed dye are dispersed in the WATER AS FLOW MEDIUM, and improve the performance of keeping humidity of ink through adding suitable water-miscible organic solvent.Screening to tensio-active agent is then very important, and suitable tensio-active agent can make ink have the surface tension that adapts to shower nozzle and polyester textile simultaneously.
USP 20070107626 is a dispersion agent with the multipolymer of phenmethyl methacrylic ester and methylacrylic acid, makes the black disperse dye ink; Select and have utmost point low solubility the (dispersed dye of 10-5～10-3g) among the patent ZL200410077014.X for use; Adopt the lignin macromolecule dispersing agent that dispersed dye are carried out surface-treated, making the disperse dyes granule median size is the water fever distillation digital ink-jet marking ink of 100～300nm.
Summary of the invention
Technical problem to be solved by this invention provides a kind of waterborne digital ink-jet printing sublimation ink and preparation method thereof, and this ink has good spue fluency and shower nozzle performance of keeping humidity on the large-scale air brushing machine that uses water-base ink, and preparation technology is simple.
A kind of waterborne digital ink-jet printing sublimation ink of the present invention; By mass percentage, comprising: 1～10% dispersed dye, 2～15% dispersion agents, 10～60% water, 10～50% water-miscible organic solvents, 0.1～5% tensio-active agent, 0.05～0.5% sterilant and 0.05～0.5% skimmer.
Described dispersed dye are:
C.I. EX-SF DISPERSE BLUE EX-SF 300 3; C.I. EX-SF DISPERSE BLUE EX-SF 300 14; C.I. EX-SF DISPERSE BLUE EX-SF 300 20; C.I. EX-SF DISPERSE BLUE EX-SF 300 35; C.I. Disperse Blue-56; C.I. Disperse Blue-60; C.I. EX-SF DISPERSE BLUE EX-SF 300 72; C.I. EX-SF DISPERSE BLUE EX-SF 300 73; C.I. Disperse Blue-79; C.I. EX-SF DISPERSE BLUE EX-SF 300 87; C.I. EX-SF DISPERSE BLUE EX-SF 300 165; C.I. EX-SF DISPERSE BLUE EX-SF 300 183; C.I. EX-SF DISPERSE BLUE EX-SF 300 301; C.I. Disperse Red 4; C.I. Disperse Red 9; C.I. dispersion red 11; C.I. Red-1 200 9; C.I. Disperse Red 50; C.I. Disperse Red 53; C.I. Disperse Red 54; C.I. Red-60 200; C.I. Disperse Red 72; C.I. Disperse Red 73; C.I. Disperse Red 74; C.I. Disperse Red 82; C.I. disperse red 86; C.I. Red-1 200 53; C.I. Red 167; C.I. Red-1 200 77; C.I. Disperse Red 277; C.I. Disperse Red 278; C.I. DISPERSE YELLOW 3; C.I. DISPERSE YELLOW 5; C.I. DISPERSE YELLOW 7; C.I. DISPERSE YELLOW 23; C.I. Disperse Yellow 42; C.I. DISPERSE YELLOW 50; C.I. DISPERSE YELLOW 54; C.I. dispersion yellow 64; C.I. DISPERSE YELLOW 79; C.I. DISPERSE YELLOW 82; C.I. DISPERSE YELLOW 104 or C.I. DISPERSE YELLOW 124.
Described dispersion agent is one or more of polycarboxylic acid macromolecule dispersing agent, comprising: the homopolymer or the multipolymer of ROHM, PS maleic anhydride.
Described water-miscible organic solvent is selected from ethanol, n-propyl alcohol, Virahol, propyl carbinol, terepthaloyl moietie, glycol ether, 1; Ammediol, 1; 4-butyleneglycol, 1, in 6-pinakon, glycol ether, Diethylene Glycol, Tri Ethyleneglycol, tetraethylene-glycol, Macrogol 200, PEG 400, Polyethylene Glycol-600, polyoxyethylene glycol 800, the USP Kosher 2～6 kinds.
Described tensio-active agent is selected from one or more among OP-7, OP-10, OP-15, paregal O-10, paregal O-20, paregal O-25, peregal A-10, Tween40, Tween60, Tween65, Tween80, SG-10, SE-10, the OE-15.
Described sterilant is anilid class, imidazoles, thiazoles, isothiazolones verivate, quaternary ammonium salt, two croak class or phenols sterilant.
Described skimmer is the ZGK 5 of phenylethyl alcohol oleic acid ester, toluylic acid bay alcohol ester, silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, T 46155 polyoxy propyl alcohol amidogen ether, polyoxypropylene glyceryl ether, polyoxypropylene or special modification.
Particularly; Described blue ink comprises: 3g C.I. Disperse Blue-60, DH-X100 dispersion agent, 0.6g Zelan 338,18g terepthaloyl moietie, 6g glycol ether, 3g USP Kosher, 0.3g tensio-active agent OP-15,0.03g sterilant ZC-501,0.03g phenylethyl alcohol oleic acid ester and 26.04g deionized water.
Particularly, described red ink comprises: 3g C.I. Red-1 200 77,3g styrene-maleic anhydride copolymer, 18g terepthaloyl moietie, 6g glycol ether, 3g USP Kosher, 0.3g tensio-active agent OP-7,0.03g sterilant SZSH-S, 0.03g polyoxyethylene polyoxypropylene tetramethylolmethane ether and 26.64g deionized water.
Particularly; Described yellow ink comprises: 3g C.I. DISPERSE YELLOW 54,3g H-40 dispersion agent, 0.6g Zelan 338,18g terepthaloyl moietie, 6g glycol ether, 3g USP Kosher, 0.3g tensio-active agent paregal O-20,0.03g sterilant ZC-501,0.03g polyoxypropylene glyceryl ether and 26.04g deionized water.
Particularly; Described black ink comprises: 2g C.I. Disperse Blue-60,0.7g C.I. Red-1 200 77,0.2g C.I. DISPERSE YELLOW 54,2g DH-X100 dispersion agent, 0.2g H-40 dispersion agent, 1.14g Zelan 338,18.2g terepthaloyl moietie, 6g glycol ether, 2.5g USP Kosher, 0.3g tensio-active agent SE-10,0.022g sterilant ZC-501,0.007g sterilant SZSH-S, 0.02g phenylethyl alcohol oleic acid ester, 0.007g polyoxyethylene polyoxypropylene tetramethylolmethane ether, 0.002g polyoxypropylene glyceryl ether and 26.702g deionized water.
Described ink flash-point is at 60～120 ℃, and temperature viscosity in the time of 25 ℃ is 2.0～8.5cp, and surface tension is 20～40mN/m.
The preparation method of a kind of waterborne digital ink-jet printing sublimation ink of the present invention comprises:
(1) preparation of mill base: by mass percentage, with 1～20% said dispersion agent, 10～40% said water-miscible organic solvents; 0.1～2% said sterilant, 0.1～2% said skimmer; 30～50% deionized waters mix at normal temperatures, and stirrer stirs 0.1～0.5h down for 400～1000 rev/mins, in mixed solution, add dispersed dye 1～20% in the time of stirring; 1500～5000 rev/mins of following shredders grind 10～40h then, obtain dispersible pigment color paste;
(2) preparation of ink: by mass percentage, with 15～50% said dispersible pigment color pastes, 10～30% said water-miscible organic solvents; 0.1～5% said tensio-active agent; 20～50% deionized waters mix at normal temperatures, stir 0.5～3h, and 0.2～2 μ m strainer filters and promptly gets then.
At least comprise dispersed dye, macromolecule dispersing agent, nonionogenic tenside, deionized water and 2～6 kinds of water-miscible organic solvents that a kind of median size is 100～300nm in the ink of the present invention.The present invention adopts one or more macromolecule dispersing agents that dispersed dye are carried out finishing, and dispersed dye can stably be scattered in the ink.Other compositions have good consistency in requirement macromolecule dispersing agent and the ink, can suitably reduce the surface tension of ink simultaneously; The present invention also adds multiple water-miscible organic solvent to improve the surface tension of ink; And the performance of keeping humidity of increase ink; Prevent that ink is dry and stop up shower nozzle in shower nozzle, can also play the effect of regulating ink viscosity simultaneously, improved the print performance of ink effectively.Printing test is the result show: waterborne digital ink-jet printing ink prepared in accordance with the present invention has good spue fluency and shower nozzle performance of keeping humidity.
Beneficial effect
(1) the disperse dyes granule particle diameter with the macromolecule dispersing agent modification is controlled at 100～300nm in the ink, deposits to be difficult for being gathered into the macrobead insolubles in the process, has good stability in storage to guarantee ink system.
(2) owing to the adding of multiple organic solvent, adjusted surface tension, viscosity, performance of keeping humidity and the lathering property of ink, and can make the ink of different surfaces tension force and viscosity according to different shower nozzle models.Printing test is the result show: on the large-scale air brushing machine that uses water-base ink, waterborne digital ink-jet printing sublimation ink prepared in accordance with the present invention has good spue fluency and shower nozzle performance of keeping humidity.
Embodiment
Below in conjunction with specific embodiment, further set forth the present invention.Should be understood that these embodiment only to be used to the present invention is described and be not used in the restriction scope of the present invention.Should be understood that in addition those skilled in the art can do various changes or modification to the present invention after the content of having read the present invention's instruction, these equivalent form of values fall within the application's appended claims institute restricted portion equally.
Embodiment 1: the preparation of blue ink
(1) preparation of mill base; Take by weighing macromolecule dispersing agent DH-X100 (the red brightness chemical industry in Shanghai ltd), the 2g Zelan 338 of 10g respectively; Add 30g terepthaloyl moietie, 0.1g sterilant ZC-501 (Shanghai Ze Chuan chemical industry ltd), 0.1g skimmer phenylethyl alcohol oleic acid ester and 47.8g deionized water; The employing impeller mixes, and in whipping process, in mixed solution, adds 10g C.I. Disperse Blue-60.Adopt shredder under 3500 rev/mins rotating speed, to grind 40h then, promptly get be uniformly dispersed, stable mill base.(2) preparation of ink; Take by weighing the 30g mill base; Add 9g terepthaloyl moietie, 6g glycol ether, 3g USP Kosher, 0.3g tensio-active agent OP-15 (Shanghai Kai Bite chemical industry ltd), 11.7g deionized water; After stirring under the normal temperature, the employing aperture is that the strainer filtration of 0.45 μ m promptly gets blue water-based heat sublimation ink.Surface tension was 28.3mN/m when this ink was 25 ℃ in temperature, and viscosity is 3.9cP, and the median size of disperse dyes granule is 250nm, and Zeta potential is-36mV.
Embodiment 2: the preparation of red ink
(1) preparation of mill base; Take by weighing the 10g Zelan 338; Add 30g terepthaloyl moietie, 0.1g sterilant SZSH-S (Beijing divine boat bright magnificent skill trade ltd), 0.1g skimmer polyoxyethylene polyoxypropylene tetramethylolmethane ether and 49.8g deionized water, adopt impeller to mix, when stirring, in mixed solution, add 10g C.I. Red-1 200 77; Adopt the rotating speed of 3500 rev/mins of shredders to grind down 36h then, promptly get be uniformly dispersed, stable mill base.(2) preparation of ink; Take by weighing the 30g mill base; Add 9g terepthaloyl moietie, 6g glycol ether, 3g USP Kosher, 0.3g tensio-active agent OP-7 (Shanghai Kai Bite chemical industry ltd), 11.7g deionized water; After stirring under the normal temperature, the employing aperture is that the strainer filtration of 0.45 μ m promptly gets red water-based heat sublimation ink.Surface tension was 28.7mN/m when this ink was 25 ℃ in temperature, and viscosity is 3.8cP, and the median size of disperse dyes granule is 220nm, and Zeta potential is-34mV.
Embodiment 3: the preparation of yellow ink
(1) preparation of mill base; (gold letter in Shunde District, Foshan City is coated with chemical industry ltd, 2g Zelan 338 to take by weighing the macromolecule dispersing agent H-40 of 10g respectively; Add 30g terepthaloyl moietie, 0.1g sterilant ZC-501 (Shanghai Ze Chuan chemical industry ltd), 0.1g skimmer polyoxypropylene glyceryl ether, 47.8g deionized water; The employing impeller mixes; In mixed solution, add 10g C.I. DISPERSE YELLOW 54 in the whipping process, adopt the rotating speed of 3500 rev/mins of shredders to grind 30h down then, promptly get be uniformly dispersed, stable mill base.(2) preparation of ink; Take by weighing the 30g mill base; Add 9g terepthaloyl moietie, 6g glycol ether, 3g USP Kosher, 0.3g tensio-active agent paregal O-20 (Xingtai, the Hebei province king of section auxiliary agent ltd) and 11.7g deionized water; After stirring under the normal temperature, the employing aperture is that the strainer filtration of 0.45 μ m promptly gets yellow water-based heat sublimation ink.Surface tension was 29mN/m when this ink was 25 ℃ in temperature, and viscosity is 3.7cP, and the median size of disperse dyes granule is 200nm, and Zeta potential is-40mV.
Embodiment 4: the preparation of black ink
Take by weighing the above-mentioned blue mill base of 20g, the red mill base of 7g, the yellow mill base of 2g at first respectively; Be made into black color paste in proportion; Add 9.5g terepthaloyl moietie, 6g glycol ether, 2.5g USP Kosher, 0.3g tensio-active agent SE-10 (sky, Shanghai format worker ltd), 12.7g deionized water then; After stirring under the normal temperature, the employing aperture is that the strainer filtration of 0.45 μ m promptly gets the black water heat sublimation ink.Surface tension was 29.1mN/m when this ink was 25 ℃ in temperature, and viscosity is 3.8cP, and the median size of disperse dyes granule is 240nm, and Zeta potential is-37.6mV.
Claims (3)
1. waterborne digital ink-jet printing sublimation ink; By mass percentage, comprising: this ink comprises: 1～10% dispersed dye, 2～15% dispersion agents, 10～60% deionized waters, 10～50% water-miscible organic solvents, 0.1～5% tensio-active agent, 0.05～0.5% sterilant and 0.05～0.5% skimmer;
Described dispersion agent is the PS copolymer-maleic anhydride;
Described water-miscible organic solvent is selected from ethanol, n-propyl alcohol, Virahol, propyl carbinol, terepthaloyl moietie, glycol ether, 1; Ammediol, 1; 4-butyleneglycol, 1, in 6-pinakon, glycol ether, Diethylene Glycol, Tri Ethyleneglycol, tetraethylene-glycol, Macrogol 200, PEG 400, Polyethylene Glycol-600, polyoxyethylene glycol 800, the USP Kosher 2～6 kinds;
Described ink flash-point is at 60～120 ℃, and temperature viscosity in the time of 25 ℃ is 2.0～8.5cp, and surface tension is 20～40mN/m.
2. a kind of waterborne digital ink-jet printing sublimation ink according to claim 1 is characterized in that, described dispersed dye are:
C.I. EX-SF DISPERSE BLUE EX-SF 300 3, C.I. EX-SF DISPERSE BLUE EX-SF 300 14, C.I. EX-SF DISPERSE BLUE EX-SF 300 20, C.I. EX-SF DISPERSE BLUE EX-SF 300 35, C.I. Disperse Blue-56,
C.I. Disperse Blue-60, C.I. EX-SF DISPERSE BLUE EX-SF 300 72, C.I. EX-SF DISPERSE BLUE EX-SF 300 73, C.I. Disperse Blue-79, C.I. EX-SF DISPERSE BLUE EX-SF 300 87,
C.I. EX-SF DISPERSE BLUE EX-SF 300 165, C.I. EX-SF DISPERSE BLUE EX-SF 300 183, C.I. EX-SF DISPERSE BLUE EX-SF 300 301, C.I. Disperse Red 4, C.I. Disperse Red 9,
C.I. dispersion red 11, C.I. Red-1 200 9, C.I. Disperse Red 50, C.I. Disperse Red 53, C.I. Disperse Red 54,
C.I. Red-60 200, C.I. Disperse Red 72, C.I. Disperse Red 73, C.I. Disperse Red 74, C.I. Disperse Red 82,
C.I. disperse red 86, C.I. Red-1 200 53, C.I. Red 167, C.I. Red-1 200 77, C.I. Disperse Red 277,
C.I. Disperse Red 278, C.I. DISPERSE YELLOW 3, C.I. DISPERSE YELLOW 5, C.I. DISPERSE YELLOW 7, C.I. DISPERSE YELLOW 23,
C.I. Disperse Yellow 42, C.I. DISPERSE YELLOW 50, C.I. DISPERSE YELLOW 54, C.I. dispersion yellow 64, C.I. DISPERSE YELLOW 79,
C.I. DISPERSE YELLOW 82, C.I. DISPERSE YELLOW 104 or C.I. DISPERSE YELLOW 124.
3. a kind of waterborne digital ink-jet printing sublimation ink according to claim 1; It is characterized in that described tensio-active agent is selected from one or more among OP-7, OP-10, OP-15, paregal O-10, paregal O-20, paregal O-25, peregal A-10, Tween40, Tween60, Tween65, Tween80, SG-10, the SE-10; Described sterilant is anilid class, imidazoles, thiazoles, quaternary ammonium salt, two croak class or phenols sterilant; Described skimmer is phenylethyl alcohol oleic acid ester, toluylic acid bay alcohol ester, silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, T 46155 polyoxy propyl alcohol amidogen ether, polyoxypropylene glyceryl ether or polyoxypropylene.