CN101696368A - 一种水溶性高温链条润滑剂组合物 - Google Patents

一种水溶性高温链条润滑剂组合物 Download PDF

Info

Publication number
CN101696368A
CN101696368A CN200910236608A CN200910236608A CN101696368A CN 101696368 A CN101696368 A CN 101696368A CN 200910236608 A CN200910236608 A CN 200910236608A CN 200910236608 A CN200910236608 A CN 200910236608A CN 101696368 A CN101696368 A CN 101696368A
Authority
CN
China
Prior art keywords
oil
temperature
water
temperature chain
base oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910236608A
Other languages
English (en)
Inventor
李刚
杜守琴
王金波
曾玉芬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MASUDA RISSOIL (BEIJING) CHEMICALS CO Ltd
Original Assignee
MASUDA RISSOIL (BEIJING) CHEMICALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MASUDA RISSOIL (BEIJING) CHEMICALS CO Ltd filed Critical MASUDA RISSOIL (BEIJING) CHEMICALS CO Ltd
Priority to CN200910236608A priority Critical patent/CN101696368A/zh
Publication of CN101696368A publication Critical patent/CN101696368A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种以水溶性聚醚为基础油的高温链条油,其中包括(1)70~98%水溶性聚醚类基础油;(2)0.5~5%的高温抗氧剂;(3)0~10%的特定分子量的聚异丁烯;(4)0~3%的抗磨剂;(5)0~1%的防锈剂。本发明涉及的高温链条油40℃粘度为135~165cst,并具有较低的挥发性和较好的氧化安定性,最高使用温度可达230℃。

Description

一种水溶性高温链条润滑剂组合物
技术领域
本发明涉及一种润滑油,具体地说,涉及一种应用于汽车涂装行业高温输送链条润滑的组合物。
技术背景
链传动不但适于在大扭矩和低转速下使用,而且在腐蚀性和潮湿环境中,以及在高速传动中使用都能显示出优越性。链条的平稳运行和链节的灵活自如、减小磨损依赖于链条润滑系统的良好润滑效果,链条润滑系统要将耐高温的润滑油定时、定量地注入链条的销轴和套筒之间的间隙来保证良好的润滑效果和链条的正常运行。随着我国纺织、印染、石化、建材及交通等行业的迅速发展,这些设备的传动系统工作温度越来越高,对链条油的要求也日趋苛刻。
汽车涂装行业使用的高温设备,链条通常在180~220℃的条件下运行。汽车行业已广泛使用水溶性漆进行涂装,一旦油溶性的链条油在高温下滴落到水溶性漆中,就会使喷涂后的表面产生鱼眼、凹坑和针眼等问题,此时精制矿物油已无法满足使用要求,必须使用合成润滑油为基础油。目前高温链条油所选基础油有PAO(聚α-烯烃)、酯类油和聚醚三大类。
PAO(聚α-烯烃)的分子结构与精制矿物油类似,属于碳氢化合物;具有比矿物油更好的耐高温性能、很高的粘度指数和更低的倾点,非常适合宽温度范围下使用。但与其它合成有相比高温性能较差。美国专利US5151205报道,以PAO为基础油,加入少量的酯类油作增溶剂,以2-4%的聚丁烯为增粘剂,再配以适当的功能添加剂所得的链条油具有低蒸发损失及持久的润滑性能,而在相同的使用条件下,矿物油型链条油产生大量可烟,而该配方油在使用中几乎无烟产生。
与PAO相比,酯类油具有更好的承载能力。依据原料类型和分子结构酯类油又可分为双酯、多元醇酯醇酯、复酯、芳香酸酯等几种类型。双酯油的粘温性能和低温性能(用倾点指标衡量)与PAO类似,耐高温性能优于PAO,理论上双酯油可以看作化学纯物质,高温条件下蒸发损失很小。因此双酯与PAO的混合物作为全合成发动机油基础油已得到广泛使用,但由于双酯油通常只有低粘度产品,一般要与其它酯类油复配作为高温链条油基础油。
聚醚具有良好的高低温性能、很高的粘度指数,且在高温、高压下不结焦、具有良好的润滑性,并可根据需要,易于得到各种高粘度的聚醚,聚醚很适合作各种润滑油基础油。水溶性聚醚可以在汽车涂装线水性漆中溶解不发生化学反应,并与水溶性漆具有优异的相容性。
以往专利所涉及的高温链条油都属于非水溶性高温链条油,此发明为水溶性高温链条油。
发明内容
根据链条的结构特点,链条油产生的少量氧化产物、油泥和积炭都会对链条负荷产生较大影响;由于高温链条油长期在高温条件下运行,每次补充量极少,链条油在金属表面形成薄膜,导致油品更易挥发、滴落和氧化。如何降低链条油的蒸发损失、提高氧化安定性和确保适宜的粘附性是开发水溶性高温链条油的关键。
本发明涉及一种以水溶性聚醚为基础油的高温链条油,其中包括(1)70~98%水溶性聚醚类基础油;(2)0.5~5%的高温抗氧剂;(3)0~10%的特定分子量的聚异丁烯;(4)0~3%的抗磨剂;(5)0~1%的防锈剂。本发明涉及的高温链条油40℃粘度为135~165cst,并具有较低的挥发性和较好的氧化安定性,最高使用温度可达230℃。
本发明所选用的基础油包括水溶性聚醚类基础油和聚异丁烯两部分,其中聚醚类基础油为70~98%的水溶性聚醚类基础油,聚异丁烯为0~10%的特定分子量的聚异丁烯。
水溶性聚醚类基础油可以使用进口或国产聚醚。所选聚醚类基础油40℃粘度为135~165cst,最好是40℃粘度为140~160cst。粘度过低会增大蒸发损失,粘度过高会影响链条油的渗透性和喷射性能。
聚异丁烯既是本发明的基础油,也是本发明的粘附剂。由于聚异丁烯在高温条件下不产生积炭,但有分解倾向,因此合理选择聚异丁烯的分子量和用量对防止滴落有很大意义。本发明所用聚异丁烯为低分子聚异丁烯,平均分子量为900~3000,最好是900~2400;本发明聚异丁烯用量为0~10%,最好是1~3%,用量过大会缩短在润滑周期,用量过小会降低粘附性,增大滴落倾向。
本发明所用添加剂包括包括0.5~5%的抗氧剂,0~3%的抗磨剂和0~1%的防锈剂。抗氧剂为烷基二苯胺、苯基α-萘胺、烷基苯基α-萘胺、硫氮杂蒽、硫胺及受阻酚类抗氧剂中的至少一种,优化用量为1~3%,样可以有效避免高温条件下抗氧剂沉积。
本发明所用的抗磨剂是磷酸三苯酯、磷酸三甲酚酯、亚磷酸酯、磷酸酯铵盐及硫代磷酸酯中的至少一种,优化用量1~2%;防锈剂是甲基苯三唑铜腐蚀抑制剂,优化用量为0~0.5%。上述两种添加剂用量须仔细平衡,否则会导致氧化安定性急剧下降。
具体实施方式
以下实施例用于说明本发明,但不用来限制本发明的范围。
本发明产品的生产过程以100kg试验产品为例,生产过程如下:
调和釜中加入约50kg水溶性聚醚类基础油,加热搅拌至110~130℃,加入抗氧剂保温搅拌30分钟,至抗氧剂全部溶解;加入聚异丁烯,保温搅拌30分钟,至溶液均一透明;加入剩余的水溶性聚醚类基础油,在80~90℃加入其他添加剂,搅拌1.5小时,至防锈剂全部溶解。用100目不锈钢滤网过滤既得成品。
成品采用下列方法检测理化指标:
GB/T265石油产品运动粘度测定法和动力粘度计算法,
GB/T2541石油产品粘度指数计算表,
GB/T261石油产品闪点测定法(闭口杯法),
GB/T3535石油倾点测定法。
成品的高温性能采用高温烘烤进行评定,既将规定量的成品油在230℃条件下烘烤8小时,目测观察有无沉积物;230℃条件下烘烤24小时后测定重量损失和粘度变化。
实施例原料及检测结果见表一
表一:实施例组成及检测结果
Figure G2009102366083D0000041
虽然,上文中已经用一般性说明及具体实施方案对本发明作了详尽的描述,但在本发明基础上,可以对之作一些修改或改进,这对本领域技术人员而言是显而易见的。因此,在不偏离本发明精神的基础上所做的这些修改或改进,均属于本发明要求保护的范围。

Claims (6)

1.一种以水溶性聚醚为基础油的高温链条油,其中包括(1)70~98%水溶性聚醚类基础油,(2)0.5~5%的高温抗氧剂,(3)0~10%的特定分子量的聚异丁烯,(4)0~3%的抗磨剂,(5)0~1%的防锈剂。
2.根据权利要求书(1)所述高温链条油,其特征在于所述的水溶性聚醚类基础油,在40℃粘度为135~165cst。
3.根据权利要求书(1)所述高温链条油,其特征在于所述的高温抗氧剂为烷基二苯胺、苯基α-萘胺、烷基苯基α-萘胺、硫氮杂蒽、硫胺及受阻酚类抗氧剂中的至少一种。
4.根据权利要求书(1)所述高温链条油,其特征在于所述的聚异丁烯为低分子聚异丁烯,平均分子量为900~3000。
5.根据权利要求书(1)所述高温链条油,其特征在于所述的抗磨剂是磷酸三苯酯、磷酸三甲酚酯、亚磷酸酯、磷酸酯铵盐及硫代磷酸酯中的至少一种。
6.根据权利要求书(6)所述,其特征为防锈剂是甲基苯三唑铜腐蚀抑制剂。
CN200910236608A 2009-10-26 2009-10-26 一种水溶性高温链条润滑剂组合物 Pending CN101696368A (zh)