CN101628728A - 白刚玉超精细研磨微粉的生产方法 - Google Patents

白刚玉超精细研磨微粉的生产方法 Download PDF

Info

Publication number
CN101628728A
CN101628728A CN200910042529A CN200910042529A CN101628728A CN 101628728 A CN101628728 A CN 101628728A CN 200910042529 A CN200910042529 A CN 200910042529A CN 200910042529 A CN200910042529 A CN 200910042529A CN 101628728 A CN101628728 A CN 101628728A
Authority
CN
China
Prior art keywords
grading
settling
dispersion agent
grades
siphon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910042529A
Other languages
English (en)
Other versions
CN101628728B (zh
Inventor
丁瑞成
丁建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zibo Jinjiyuan Abrasives Co ltd
Original Assignee
HANSHOU JINCHENG ABRASIVE MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANSHOU JINCHENG ABRASIVE MATERIAL CO Ltd filed Critical HANSHOU JINCHENG ABRASIVE MATERIAL CO Ltd
Priority to CN2009100425299A priority Critical patent/CN101628728B/zh
Publication of CN101628728A publication Critical patent/CN101628728A/zh
Application granted granted Critical
Publication of CN101628728B publication Critical patent/CN101628728B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

白刚玉超精细研磨微粉的生产方法，是以氢氧化铝为原料，经过煅烧、粉碎、酸洗、分级和烘干后制得的，对于粒径在40微米以下的微粉，采用水力沉降法分级，分级由细到粗进行，先分细级别的，后分粗级别的，直至全部分级完毕。本发明的分级方法在严格控制料浆浓度、沉降时间、虹吸高度的同时，加入了高效的分散剂，分散剂的分子在水中穿插在团聚颗粒之间，包附在所有大小不同的微粒的周围，受分散剂分子电荷的排斥，使微粒再不能团聚在一起，既使得分级的精度提高，又使得最终产品可以保持松散状态。

Description

白刚玉超精细研磨微粉的生产方法
【技术领域】
本发明涉及氧化铝微粉的制备，即白刚玉超精细研磨微粉的生产方法。
【背景技术】
白刚玉微粉，主要化学成份为三氧化二铝，是一种理想的研磨材料，呈白色，莫氏硬度为9，显微硬度(HV)2200～2300千克/平方毫米，随着高科技的发展，具有越来越广泛的用途，如计算机芯片的生产，电子通讯产品硅片元件的生产，火箭发动机耐温元件的制造，高温气轮机叶片的制造等都需要大量的高质量的白刚玉微粉，对白刚玉微粉的品质提出了更高的要求，要求微粉的粒度分布窄，颗粒形状扁平，无大粒，生产中，由于微粉之间的粒径很小，表面能增加，容易带电荷，各种不同粒径的颗粒团聚在一起，这种团聚的颗粒是不能进行分级的，在水力分级中，团聚的颗粒提前下沉，从而破坏了分级的精度，这一直是微粉生产中的一个难题。
【发明内容】
为了克服传统微粉生产中，水力分级时不同粒径的微粒团聚在一起，至使同一个批号的微粉中粒径分布宽的缺点，本发明提出了添加分散剂的水力沉降法分级的新工艺。
这种白刚玉超精细研磨微粉的生产方法，是以氢氧化铝为原料，经过煅烧、粉碎、酸洗、分级和烘干后制得的，其特征在于，对于粒径在40微米以下的微粉，采用水力沉降法分级，沉降池高1.5～2.5m，直径1～1.5m，为圆桶形，池内壁用玻璃钢涂覆，池内安有搅拌装置；
生产时，将经过酸洗后的浓度为300～600克/升的料浆投入沉淀池中，液面至池口下10～20cm，加入料浆中固体物料重量的万分之一至千分之一的分散剂，搅拌0.5～1小时，然后静置沉降，使浆面稳定，到达设定的沉降时间后，用虹吸管把上层料浆放出，放出高度20～30cm，然后在沉淀池中加清水至虹吸前初始的液面高度，并补加第一次投放的分散剂重量的5％～10％，再与前次一样的搅拌、沉降、虹吸，如此操作8～10次，即可获得一个级别的微粒；此后仍向沉降池内加清水和分散剂，搅拌、沉降、虹吸，但要缩短沉降的时间，按照新设定的沉降时间操作8～10次，又可获得另一个级别的微粒；
分级由细到粗进行，先分细级别的，后分粗级别的，直至全部分级完毕。
分散剂可由水玻璃和桃树胶组成，其重量比例为2∶1，水玻璃为市场上工业用的液态水玻璃。
分散剂也可由水玻璃、桃树胶和聚丙烯甲磺酸钠组成，它们之间的重量比为3∶2∶1。
分散剂也可由水玻璃、桃树胶、聚丙烯甲磺酸钠和三乙醇铵组成，它们之间的重量比为4∶3∶2∶1。
本发明的分级方法在严格控制料浆浓度、沉降时间、虹吸高度的同时，加入了高效的分散剂，分散剂的分子在水中穿插在团聚颗粒之间，包附在所有大小不同的微粒的周围，受分散剂分子电荷的排斥，使微粒再不能团聚在一起，既使得分级的精度提高，又使得最终产品可以保持松散状态。
【具体实施方式】
下面结合实施例对本发明的具体实施方式详细说明如下：
一、准备原料，为经过煅烧、粉碎后的粒径在40微米以下的白刚玉微粉；
二、建造高2米、直径1.5米的圆桶形的沉降池，池内壁涂覆的玻璃钢厚1cm，池中安有搅拌机；
三、将经过酸洗车间酸洗后的浓度为500克/升的料浆投入沉淀池中，水面至池口下15cm，加入料浆中固体物料重量万分之五的分散剂，搅拌1小时，然后静置沉降，使浆面稳定，4个小时后，用虹吸管把上层25cm的料浆放出，然后在沉淀池中加清水至池口下15cm，并补加第一次投放的分散剂重量的8％，再与前次一样的搅拌、沉降、虹吸，如此操作8次，即得到粒径为5.9～4.7微米的微粒；
四、此后仍向沉降池内加清水和分散剂，搅拌、沉降、虹吸，但要缩短沉降时间，按照新设定的时间操作8次，又可获得另一个级别的微粒，现举例如下：
  沉淀时间(小时)   所得的微粒粒径(微米)
  4   5.9～4.7
  3   8.9～7.1
  2   11.5～8.9
  1   18～14.5
  0.5   87.5～73.5
分级由细到粗依次进行，先分细级别的后分粗级别的，直至全部分级完毕；
五、分散剂的组成和效果列表如下：
  分散剂的成份   重量比   使用效果
 水玻璃(工业用的液态的)和桃树胶   2∶1   一般
 水玻璃(工业用的液态的)、桃树胶、聚丙烯甲磺酸钠 3∶2∶1 较好
 水玻璃(工业用的液态的)、桃树胶、聚丙烯甲磺酸钠、三乙醇铵 4∶3∶2∶1 最好
说明：所用水玻璃的密度为1.4克/立方厘米

Claims (4)

1、白刚玉超精细研磨微粉的生产方法，是以氢氧化铝为原料，经过煅烧、粉碎、酸洗、分级和烘干后制得的，其特征在于，对于粒径在40微米以下的微粉，采用水力沉降法分级，沉降池高1.5～2.5m，直径1～1.5m，为圆桶形，池内壁用玻璃钢涂覆，池内安有搅拌装置；
生产时，将经过酸洗后的浓度为300～600克/升的料浆投入沉淀池中，液面至池口下10～20cm，加入料浆中固体物料重量的万分之一至千分之一的分散剂，搅拌0.5～1小时，然后静置沉降，使浆面稳定，到达设定的沉降时间后，用虹吸管把上层料浆放出，放出高度20～30cm，然后在沉淀池中加清水至虹吸前初始的液面高度，并补加第一次投放的分散剂重量的5％～10％，再与前次一样的搅拌、沉降、虹吸，如此操作8～10次，即可获得一个级别的微粒；此后仍向沉降池内加清水和分散剂，搅拌、沉降、虹吸，但要缩短沉降的时间，按照新设定的沉降时间操作8～10次，又可获得另一个级别的微粒；
分级由细到粗进行，先分细级别的，后分粗级别的，直至全部分级完毕。
2、根据权利要求1所述的白刚玉超精细研磨微粉的生产方法，其特征在于：分散剂由水玻璃和桃树胶组成，其重量比例为2∶1，水玻璃为市场上工业用的液态水玻璃。
3、根据权利要求1所述的白刚玉超精细研磨微粉的生产方法，其特征在于：分散剂由水玻璃、桃树胶和聚丙烯甲磺酸钠组成，它们之间的重量比为3∶2∶1。
4、根据权利要求1所述的白刚玉超精细研磨微粉的生产方法，其特征在于：分散剂由水玻璃、桃树胶、聚丙烯甲磺酸钠和三乙醇铵组成，它们之间的重量比为4∶3∶2∶1。
CN2009100425299A 2009-01-17 2009-01-17 白刚玉超精细研磨微粉的生产方法 Expired - Fee Related CN101628728B (zh)