CN101618900B - 一种用于地毯废水处理的无机絮凝剂 - Google Patents

一种用于地毯废水处理的无机絮凝剂 Download PDF

Info

Publication number
CN101618900B
CN101618900B CN2009101015554A CN200910101555A CN101618900B CN 101618900 B CN101618900 B CN 101618900B CN 2009101015554 A CN2009101015554 A CN 2009101015554A CN 200910101555 A CN200910101555 A CN 200910101555A CN 101618900 B CN101618900 B CN 101618900B
Authority
CN
China
Prior art keywords
flocculating agent
inorganic flocculating
waste water
zeolite
carpet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2009101015554A
Other languages
English (en)
Other versions
CN101618900A (zh
Inventor
郑展望
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhe Jiang Shuangliang Sunda Environment Protection Co ltd
Original Assignee
ZHEJIANG SUNDA WATER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG SUNDA WATER CO Ltd filed Critical ZHEJIANG SUNDA WATER CO Ltd
Priority to CN2009101015554A priority Critical patent/CN101618900B/zh
Publication of CN101618900A publication Critical patent/CN101618900A/zh
Application granted granted Critical
Publication of CN101618900B publication Critical patent/CN101618900B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了用于地毯废水处理的无机絮凝剂，由质量配比如下的原料制成：沸石30％～50％，蒙脱石30％～40％，氢氧化钙10％～15％，硫酸铝5％～10％，活性炭2％～10％。本发明有益效果主要体现在：本发明无机絮凝剂处理地毯废水的效果好，原料易得，成本低廉，与生化处理法比较，占地面积小，操作方便。

Description

一种用于地毯废水处理的无机絮凝剂
(一)技术领域
本发明涉及一种用于生产地毯过程中的地毯废水处理的无机絮凝剂。
(二)背景技术
地毯废水是指在地毯生产过程中产生的废水，成份复杂，COD约500～1700mg/L，BOD约100～700mg/L，地毯废水含有较多的悬浮物和胶体污染物，色度高，富营养化及恶臭味大，处理难度较高。目前，虽然地毯废水有一些处理方法，如北京某地毯厂采用厌氧酸化-好氧法处理。但这些方法都存在缺点，要么是流程复杂；要么是成本高；或占地面积大等。
针对地毯厂大都是一些小厂，工厂分散。本发明提供一种高效和廉价的地毯废水处理的絮凝剂，用于地毯废水的处理，占地少，方法简便，有很好的实用价值。
(三)发明内容
本发明目的是提供一种高效和廉价的地毯废水处理的絮凝剂，用于地毯生产过程中产生的废水——地毯废水的处理。
本发明采用的技术方案是：
一种用于地毯废水处理的无机絮凝剂，由质量配比如下的原料制成：
沸石        30％～50％
蒙脱石      30％～40％
氢氧化钙    10％～15％
硫酸铝      5％～10％
活性炭      2％～10％。
沸石的一般化学式为：AmBpO2p·nH2O，结构式为A(x/q)[(AlO2)x(SiO2)y]n(H2O)其中：A为Ca、Na、K、Ba、Sr等阳离子，B为Al和Si，p为阳离子化合价，m为阳离子数，n为水分子数，x为Al原子数，y为Si原子数，(y/x)通常在1～5之间，(x+y)是单位晶胞中四面体的个数。沸石的主要成分是SiO2-Al2O3，在不超过850℃的高温下，沸石的晶格不会被破坏，在水份逸散的部位能形成3-10A的微孔群，数以千万计的微孔群能选择性的过滤或吸附废水中的有机或无机物质。沸石矿物是含碱性含水硅酸盐和一种柱状或纤维状聚合体，含于玄武岩或辉长岩中。
蒙脱石化学组成为(Na，Ca)0.33(Al，Mg)2【Si4O10】(OH)2·nH2O，晶体属单斜晶系的含水层状结构硅酸盐矿物，也属于SiO2-Al2O3类，其组分含SiO2约60％，含Al2O3 14％和Na2O 3.5％，蒙脱石广泛分布在长石和粘土矿中，在膨润土中含量丰富，可从中提炼获得。蒙脱石不溶于水，与沸石共用时，能通过微孔吸附和离子交换，与沸石在废水处理中起互补作用。
氢氧化钙调节酸碱度，并与粉末活性炭一起除臭和脱色作用。
硫酸铝是一种无机混凝剂，对悬浮物有很好的混凝沉淀作用，与其他物质一起互补，强化其混凝沉淀效果。
本发明中，各原料含水量要求在9％以下。
优选的，所述无机絮凝剂由质量配比如下的原料制成：
沸石        40％
蒙脱石      35％
氢氧化钙    12％
硫酸铝      8％
活性炭      5％。
沸石有30多种，较常见的有斜发沸石、菱沸石、钙沸石、片沸石、钠沸石、丝光沸石、辉沸石等，都以含钙、钠为主。这些沸石都可使用。本发明优选斜发沸石为无机絮凝剂原料。
所述无机絮凝剂由如下方法制备得到：取配方量的沸石、蒙脱石、氢氧化钙、硫酸铝和活性炭，分别粉碎至80目～200目，混合均匀，测定其含水量在9％以下，分装得所述无机絮凝剂。
本发明还涉及所述絮凝剂在地毯废水处理中的应用。具体的，所述应用为：将所述絮凝剂加入至废水中，添加量为10～30g/L，调节pH6.5～7.5(优选为7.0左右)，在15℃～35℃下搅拌20～60min，然后对废水进行沉淀处理，通常静置0.5～1h，得到处理后的地毯废水，其COD、悬浮固体含量和色度去除率分别达到78～85％、90～99％和88～98％。
本发明有益效果主要体现在：本发明无机絮凝剂处理地毯废水的效果好，原料易得，成本低廉，与生化处理法比较，占地面积小，操作方便。
(四)具体实施方式
下面结合具体实施例对本发明进行进一步描述，但本发明的保护范围并不仅限于此：
实施例1：无机絮凝剂的制备
分别将沸石、蒙脱石、工业氢氧化钙和硫酸铝粉碎，经120目筛网过筛，在总量100kg的原料中，其配比如下：
斜发沸石(浙江神石矿业有限公司出品)  40wt％
蒙脱石(浙江安吉县金泰膨润土有限公司，JT-518高纯度蒙脱石)    35wt％
工业氢氧化钙  12wt％
硫酸铝        8wt％
粉末活性炭    5wt％。
测定其含水量在8.2％，分装，得所述无机絮凝剂。
实施例2：无机絮凝剂的制备
分别将沸石、蒙脱石、工业氢氧化钙和硫酸铝粉碎，经100目筛网过筛，其配比如下：
斜发沸石(浙江神石矿业有限公司出品)    45wt％
蒙脱石(浙江安吉县金泰膨润土有限公司，JT-518高纯度蒙脱石)    30wt％
工业氢氧化钙  10wt％
硫酸铝        5wt％
粉末活性炭    10wt％。
测定其含水量在8.0％，分装，得所述无机絮凝剂。
实施例3：无机絮凝剂的制备
分别将沸石、蒙脱石、工业氢氧化钙和硫酸铝粉碎，经100目筛网过筛，其配比如下：
丝光沸石(浙江神石矿业有限公司出品)    30wt％
蒙脱石(浙江安吉县金泰膨润土有限公司，JT-518高纯度蒙脱石)    40wt％
工业氢氧化钙  15wt％
硫酸铝        10wt％
粉末活性炭    5wt％。
测定其含水量在8.5％，分装，得所述无机絮凝剂。
实施例4：地毯废水的处理
某地毯废水1000ml，COD值为1120mg/L，悬浮固体含量为670mg/L，颜色为褐色，色度为0.64，并有臭味，加入13.5g实施例1制得的无机絮凝剂，在常温下搅拌5分钟，静置30分钟，测定其COD、悬浮固体含量和色度，其去除率分别为82％、98.5％和96％，处理后的水呈现无色，透明，无臭味。
实施例5：地毯废水的处理
取实施例4相同的地毯废水1000ml，加入18g实施例2制得的无机絮凝剂，在15℃下搅拌5分钟，静置50分钟，测定其COD、悬浮固体含量和色度，其去除率分别为80％、97％和94％，处理后的水呈现无色，透明，无臭味。
实施例6：地毯废水的处理
取实施例4相同的地毯废水1000ml，加入18g实施例3制得的无机絮凝剂，在35℃下搅拌9分钟，静置60分钟，测定其COD、悬浮固体含量和色度，其去除率分别为81％、98％和95％，处理后的水呈现无色，透明，无臭味。

Claims (6)

1.一种用于地毯废水处理的无机絮凝剂，由质量配比如下的原料制成：
沸石      30％～50％
蒙脱石    30％～40％
氢氧化钙  10％～15％
硫酸铝    5％～10％
活性炭    2％～10％。
2.如权利要求1所述的无机絮凝剂，其特征在于所述无机絮凝剂由质量配比如下的原料制成：
沸石      40％
蒙脱石    35％
氢氧化钙  12％
硫酸铝    8％
活性炭    5％。
3.如权利要求1或2所述的无机絮凝剂，其特征在于所述沸石为钠沸石、斜发沸石、菱沸石、钙沸石、片沸石、丝光沸石、辉沸石中的一种。
4.如权利要求3所述的无机絮凝剂，其特征在于所述沸石为斜发沸石。
5.如权利要求1或2所述的无机絮凝剂，其特征在于所述无机絮凝剂由如下方法制备得到：取配方量的沸石、蒙脱石、氢氧化钙、硫酸铝和活性炭，分别粉碎至80目～200目，混合均匀，制得所述无机絮凝剂。
6.如权利要求1所述的无机絮凝剂在地毯废水处理中的应用，其特征在于所述的应用为：将所述絮凝剂加入地毯废水中，添加量为10～30g/L，调节pH6.5～7.5，搅拌20～60min、沉淀处理0.5～1h，得到处理后的地毯废水。
CN2009101015554A 2009-08-10 2009-08-10 一种用于地毯废水处理的无机絮凝剂 Active CN101618900B (zh)