CN101585563B - 一种复合净水剂及其制备方法 - Google Patents

一种复合净水剂及其制备方法 Download PDF

Info

Publication number
CN101585563B
CN101585563B CN2009100994105A CN200910099410A CN101585563B CN 101585563 B CN101585563 B CN 101585563B CN 2009100994105 A CN2009100994105 A CN 2009100994105A CN 200910099410 A CN200910099410 A CN 200910099410A CN 101585563 B CN101585563 B CN 101585563B
Authority
CN
China
Prior art keywords
water
weight
matrix
purifying agent
content
Prior art date
Application number
CN2009100994105A
Other languages
English (en)
Other versions
CN101585563A (zh
Inventor
吕安平
Original Assignee
吕安平
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 吕安平 filed Critical 吕安平
Priority to CN2009100994105A priority Critical patent/CN101585563B/zh
Publication of CN101585563A publication Critical patent/CN101585563A/zh
Application granted granted Critical
Publication of CN101585563B publication Critical patent/CN101585563B/zh

Abstract

本发明涉及一种复合新型净水剂及其制备方法,它将活性炭和沸石两种材料结合后成型造粒,形成一种复合新型净水剂,达到了水处理工艺应用中对净水剂材料特殊使用和处理效果的要求。其脱色、脱臭、去除水中氨氮、COD等水质处理效果显著,可应用于各种水处理工程,以及饮水机滤芯和水产养殖业。

Description

一种复合净水剂及其制备方法

技术领域

[0001] 本发明涉及水处理剂,特别是一种复合新型净水剂及其制备方法。 背景技术

[0002] 现今,工业化、城市化不断推进,环境污染同步增加,又因污水处理管理不善,监督 不力,致使很多水源受到不同程度的污染,主要表现为水中氨氮、有机物增加,“富营养”化 过程加快、藻类滋生,导致水体缺氧,发黑发臭,水中氨氮(NH4-N)在亚硝化杆菌作用下进一 步消化成N02_、NO”均会对人体健康产生不同程度的危害,受污染水源的自来水经常出现 异味、感官不适、味觉不良,直接影响了居民饮用。

[0003] 传统饮用水处理工艺中,通常采用单项固体吸附剂活性炭或沸石来净化水质。沸 石是一种架状结构的铝硅酸盐矿物,具有独特的吸附性能和离子交换性能,在水处理中可 去除水中氨氮(NH4-N)等污染物。

[0004] 活性炭是一种多孔径的固质炭化物,其吸附能力很强,过滤速度快,具有脱色、脱 臭和阳离子交换功能。但活性炭的阳离子交换功能具有局限性,对水质中的污染物氨氮 (NH4-N)几乎无去除能力。

[0005] 因此,采用单项固体吸附剂活性炭或沸石净化水质,其净化功能不全面。另外,活 性炭成本较高,使用前清洗去除粉尘很麻烦。

发明内容

[0006] 本发明为解决采用单项固体吸附剂活性炭或沸石净化水质功能不够全面的问题。 提供一种复合新型净水剂及其制备方法,使其净化水质功能全面,并且耐水性强、成本低, 使用方便。

[0007] 为此,本发明的技术方案为:一种复合新型净水剂,由挤压成型的活性炭和复合材 料混合物组成,其成分为:

[0008] A. 活性炭 用量为1份(以体积计),粒度为6-100目;[0009] B. 复合材料 用量为1份(以体积计),该复合材料由以下成分混合组成[0010] a. 沸石 含量为50-75% (重量),粒度为10-300目;[0011] b. 白硅酸盐水泥 含量为15-35% (重量),常规粉体;[0012] C. 石膏 含量为5-15% (重量),常规粉体。

[0013] 本发明所述一种复合新型净水剂,其优选的复合材料由以下成分混合组成:

[0014] a.沸石 含量为50% (重量),粒度为200-300目;

[0015] b.白硅酸盐水泥 含量为35% (重量);常规粉体;

[0016] c.石膏 含量为15% (重量),常规粉体。

[0017] 本发明所述一种复合新型净水剂的制备方法,其步骤为:

[0018] A.按所述复合材料成分范围选取沸石、白硅酸盐水泥和石膏,然后置于搅拌机内 搅拌混合;[0019] B.按1 : 1(体积计)比例选取所述复合材料和活性炭,并加水在搅拌机内搅拌混 合,加水量为20%复合材料重量;

[0020] C.将加水混合后的混合物置于颗粒挤压机内成型造粒;

[0021] D.将所述成型颗粒自然晾干,48小时后,再烘干为成品,烘干温度为100-30(TC, 时间2小时。

[0022] 本发明利用活性炭和沸石两种不同物质结构的水处理材料,通过水固型胶粘剂 白硅酸盐水泥和石膏的混合胶接,重新成型造粒,形成一种复合新型净水剂。其成本低, 使用方便,净化水质功能比单项固体吸附剂活性炭或沸石全面,脱色、脱臭、去除水中氨氮 (NH4-N)等水质处理效果显著,去除率氨氮(NH4-N)可达90%以上,C0Dto30%以上,氰化物 33%以上,成型颗粒抗压强度大于3Pa,耐水性强,可长期在水中发挥功效,不溶解,不粉化。

具体实施方式

[0023] 实施例1 :

[0024] 一种复合新型净水剂,由挤压成型的活性炭和复合材料混合物组成,其成分为:

[0025] A. 活性炭 用量为1份(以体积计),粒度为6目;[0026] B. 复合材料 用量为1份(以体积计),该复合材料由以下成分混合组成[0027] a. 沸石 含量为50-75 % (重量),粒度为10目;[0028] b. 白硅酸盐水泥 含量为15-35% (重量),常规粉体;[0029] C. 石膏 含量为5-15% (重量),常规粉体。

[0030] 测试结果:颗粒抗压强度为3.8Pa,色(度)小于15,无臭味,去除率氨氮 (NH4-N) 90. 60 %,C0Dfc30. 5 %,氰化物 33. 33 % .

[0031] 实施例2:

[0032] 一种复合新型净水剂,由挤压成型的活性炭和复合材料混合物组成,其成分为:

[0033] A. 活性炭 用量为1份(以体积计),粒度为100目; [0034] B. 复合材料 用量为1份(以体积计),该复合材料由以下成分混合组成 [0035] a. 沸石 含量为50% (1 ■量),粒度为200-300目;[0036] b. 白硅酸盐水泥 含量为35% (1 ■量);常规粉体;[0037] C. 石膏 含量为15% (1 ■量),常规粉体。

[0038] 测试结果:颗粒抗压强度为7.8Pa,色(度)小于15,无臭味,去除率氨氮 (NH4-N)93. 5%, C0Dfc33. 6%,氰化物 36. 8% .

[0039] 实施例1、实施例2所述的一种复合新型净水剂的制备方法,其步骤均为:

[0040] A.按所述复合材料成分范围选取沸石、白硅酸盐水泥和石膏,然后置于搅拌机内 搅拌混合,沸石均选用浙江省缙云县出产的天然斜发沸石,粒度为10-300目;

[0041] B.按1 : 1(体积计)比例选取所述复合材料和活性炭,并加纯净水在搅拌机内搅 拌混合,加水量为20%复合材料重量;

[0042] C.将加水混合后的混合物置于颗粒挤压机内成型造粒,颗粒形状为直径3_5mm、 长度8-10mm圆柱型;

[0043] D.将所述成型颗粒自然晾干,48小时后,再烘干为成品,烘干温度为100-30(TC, 时间2小时。[0044] 本发明净水剂去除水中氨氮(NH4-N)的主要原理是离子交换。在与水接触中,其 表面伴随产生的生物菌落,与本发明净水剂有相辅相成的作用。试验发现,本发明净水剂表 面生物菌落生长缓慢,生化作用很弱,不足以大量降低本发明净水剂氨氮(NH4-N)含量。

[0045] 本发明净水剂吸附功能发挥加成作用,当水温20°C时,本发明净水剂表面生成大 量微生物,滤层以下15cm处约有0. 5 X 10个生物菌落/g载体。此时,本发明净水剂去除率 氨氮(NH4-N)效果明显提高,可达去除率氨氮(NH4-N)93. 5%,C0Dto33. 6%,氰化物36. 8% .

[0046] 本发明净水剂将活性炭和沸石两种材料结合后成型造粒,形成一种复合新型净水 剂,达到了水处理工艺应用中对净水剂材料的特殊使用和处理效果的要求。其脱色、脱臭、 去除水中氨氮、COD等水质处理效果显著。可应用于各种水处理工程,以及饮水机滤芯和水 产养殖业。

Claims (3)

1. 一种复合型净水剂,由挤压成型的活性炭和复合材料混合物组成,其成分为:
2.权利要求1所述的一种复合型净水剂,其复合材料由以下成分混合组成:
3.权利要求1或2所述一种复合型净水剂的制备方法,其步骤为:A.按所述复合材料成分范围选取沸石、白硅酸盐水泥和石膏,然后置于搅拌机内搅拌 混合;B.按1 : 1体积比例,选取所述复合材料和活性炭,并加水在搅拌机内搅拌混合,加水 量为20%复合基材料重量;C.将加水混合后的混合物置于颗粒挤压机内成型造粒;D.将所述成型颗粒自然晾干,48小时后,再烘干为成品,烘干温度为100-300°C,时间2A.活性炭B.复合材料a.沸石b.白硅酸盐水泥c.石膏用量为1份,以体积计,粒度为6-100目;用量为1份,以体积计,该复合材料由以下成分混合组成含量为50-75%,以重量计,粒度为10-300目;含量为15-35%,以重量计,常规粉体;含量为5-15%,以重量计,常规粉体。a.沸石b.白硅酸盐水泥c.石膏含量为50%,以重量计,粒度为200-300目; 含量为35%,以重量计;常规粉体; 含量为15%,以重量计,常规粉体。
CN2009100994105A 2009-06-06 2009-06-06 一种复合净水剂及其制备方法 CN101585563B (zh)