CN101579805A - 一种卸扣热模压生产工艺及其模具 - Google Patents
一种卸扣热模压生产工艺及其模具 Download PDFInfo
- Publication number
- CN101579805A CN101579805A CNA2009101480185A CN200910148018A CN101579805A CN 101579805 A CN101579805 A CN 101579805A CN A2009101480185 A CNA2009101480185 A CN A2009101480185A CN 200910148018 A CN200910148018 A CN 200910148018A CN 101579805 A CN101579805 A CN 101579805A
- Authority
- CN
- China
- Prior art keywords
- die
- shackle
- cavity
- counterdie
- round steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种卸扣热模压生产工艺及其模具。本发明选择圆钢坯料,借助模具采用压制工艺生产卸扣,与传统锤锻生产工艺相比,大幅降低了工人的劳动强度和噪音污染,明显提高了产品质量和生产效率,节约生产成本并有利于实现生产过程的自动化。为了使热模压成形工艺中的圆钢坯料两端聚料、成球能顺利实现,还使用到一种模具,模具由上模和下模构成,上模由下端面开口的腔体,下模由结构相同可打开、闭合的左、右开合模组成,闭合时构成贯通下模上下的腔体。
Description
技术领域
本发明涉及一种卸扣热模压生产工艺,本发明还涉及这种用于卸扣热模压生产工艺的液压模具。
背景技术
传统的卸扣生产方法为:采用自由锻和胎模锻,通过摔子镦粗、拔长、压痕、球摔扣形、中部拔长、赶铁摔扁、冲孔、弯曲、矫正修整等工艺过程来完成,其存在以下问题:A、生产效率低,劳动强度大;B、锤锻时噪音污染很大;C、生产出来的产品外观粗糙、尺寸精度差;D、材料的利用率较低;E、成本相对较高。另外,由于本产品的生产一直以锤锻工艺生产,因此,没有相关的压制模具。
发明内容
本发明要解决的技术问题是提供一种生产效率高、劳动强度低、便于生产过程自动化的卸扣热模压生产工艺,有效地节约生产成本和材料;为此,本发明还提供了实现该卸扣热模压生产工艺的模具。
为解决上述技术问题,本发明的技术方案为:一种卸扣热模压生产工艺,其步骤为:先选择圆钢坯料,然后将圆钢坯料两端加热压制成球体,再对两端的球体进行压扁、冲孔及翻面扩孔,然后将冲孔后的圆钢坯料弯曲成U型卸扣,并进行进行表面整理,最后对卸扣两端的冲孔进行镗孔处理;其特征在于:所述圆钢坯料两端的球体加热压制方法为:先将圆钢坯料的端部加热,使其端部温度保持在750-1220℃,然后将圆钢坯料的端部伸入液压机的圆锥形模具内,对端部进行压制聚料,使其端部呈圆锥体;再将聚料后的端部加热,其端部温度保持在750-1220℃,最后伸入液压机的球状模腔,将其端部圆锥体聚料成球体。
进一步地,所述聚料次数为N次,N≥1。
本发明还提供了一种卸扣热模压生产工艺的模具,由上模和下模构成,所述上模与液压机的压头连接,下模与液压机的进料口连接;其特征在于:所述上模由上模块下端面中心开有腔体构成;所述下模由结构相同的左、右开合模组成,所述下模闭合时构成贯通上下的腔体。
进一步地,所述上模的腔体为半球型或类圆锥体型。
进一步地,所述下模的腔体由下模上端面开口的半球形腔体及半球形腔体底端中心开贯穿下模的圆柱孔构成,所述半球形与圆柱孔轴线一致。
进一步地,所述下模的腔体由下模上端面开口的类圆锥体形腔体及类圆锥体形腔体底端中心开贯穿下模的圆柱孔构成,所述类圆锥体形与圆柱孔轴线一致。
本发明的优点在于:根据卸扣规格,直接选择相应的圆钢坯料,借助模具将两端热压制成形,无噪音污染,明显降低了工人的劳动强度,易于实现生产过程的自动化从而提高生产速度和效率;而且采用模压成形工艺生产的产品,其内部及表面质量、尺寸精度、产品成品率和材料利用率大幅提高,有效的节约了产品成本,优于传统锤锻生产工艺。
附图说明
图1为本发明的卸扣热模压生产工艺的第一种模具结构示意图。
图2为本发明的卸扣热模压生产工艺的第一种模具工作示意图。
图3为本发明的卸扣热模压生产工艺的第一种模具下模剖视图。
图4为本发明的卸扣热模压生产工艺的第二种模具结构示意图。
图5为本发明的卸扣热模压生产工艺的第三种模具结构示意图。
具体实施方式
实施例1
为生产A类的直型锚卸扣(A类直型锚卸扣:3.5≤λ≤5.5;λ为工件聚料成球部分料长与工件直径之比,下同)。
第一步是备料,根据卸扣规格,选择相应的圆钢坯料。
第二步为聚料,将圆钢坯料的一端加热,使其温度保持750-1220℃,装入压制模具内。本实施例的模具如图1、2所示,该模具由上模1和下模2构成,其中,上模1与压制设备的压杆30连接,左右开合的下模2与两侧的夹紧机构29连接;其具体结构为:上模1由圆柱型金属块28下端面中心开有类圆锥体型腔体6构成;下模2由结构相同的左、右开合模4、5组合而成(可参见图3),下模2闭合时整体看,是由圆柱型金属块7上端面中心开由类圆锥体型腔体8及在类圆锥体型腔体8底端中心开贯穿金属块的圆柱孔9构成,该圆柱孔9与压制设备底梁的进料口31相通。具体动作时,打开下模2,将圆钢坯料从进料口31进装入模具,闭合下模2,左、右开合模4、5在两侧夹紧机构29的作用下,将圆钢坯料夹紧,与压杆30连接的上模1对圆钢坯料的顶端进行压制,在类圆锥体形腔体6、8的作用下压制成类圆锥体形;坯料另一端的聚料操作相同。
第三步是成球,将圆钢坯料聚料后的类圆锥体加热,使其温度保持在750-1220℃,装入有模具的压制设备中压制,如图4所示,该步骤中使用到的模具结构为:上模10由圆柱型金属块11下端面中心开有半球形腔体12构成;下模13由结构相同的左、右开合模14、15组合而成,下模13闭合时整体看,是由圆柱型金属块16上端面中心开有由半球型腔体17及在半球型腔体17底端中心开贯穿下模的圆柱孔18构成,该圆柱孔18与压制设备底梁的进料口31相通。该上模10和下模13闭合时构成的内腔为球体,通过与步骤二中相同的压制方法,将端部压制成球;坯料另一端的成球操作相同。
第四步为球体压扁,将坯料两端的球体加热,压扁。
第五步成孔,将坯料两端的扁球体加热,冲扩孔。
第六步弯形,将圆钢坯料加热,将坯料弯曲成为U型卸扣,
实施例2
为生产B类直型锚卸扣(3.0≤λ≤4.5),工艺方法与实施例1基本相同:第一步是备料;第二步为聚料;第三步是成球;第四步为球体压扁;第五步成孔;第六步弯形。其中由于λ相对较小,在聚料时采用如图5所示的模具,其具体结构和聚料动作为:上模19由圆柱型金属块20下端面中心开有类圆锥体型腔体21构成;下模22由结构相同的左、右开合模23、24组合而成,下模22闭合成整体时,由圆柱型金属块25上端面中心开有由半球型腔体26及在半球型腔体26底端中心开贯穿金属块的圆柱孔27构成,该圆柱孔27与压制设备底梁的进料口31相通。
实施例3
为生产C类直型锚卸扣(λ≤3.5),具体实施方法与实施例1相同,当由于其λ很小,只需要对圆钢坯料两端直接成球即可,在生产这种直型锚卸扣时,需以下几个步骤:第一步是备料;第二步是成球;第三步为球体压扁;第四步成孔;第五步弯形。由于直接成球,所选用的压制模具为图4所示的模具,其结构与成球动作在实施例1中已经陈述,在此不再累述。
Claims (6)
1.一种卸扣热模压生产工艺,其步骤为:先选择圆钢坯料,然后将圆钢坯料两端加热压制成球体,再对两端的球体进行压扁、冲孔及翻面扩孔,然后将冲孔后的圆钢坯料弯曲成U型卸扣,并进行表面整理,最后对卸扣两端的冲孔进行镗孔处理;其特征在于:所述圆钢坯料两端的球体加热压制方法为:先将圆钢坯料的端部加热,使其端部温度保持在750-1220℃,然后将圆钢坯料的端部伸入液压机的圆锥形模具内,对端部进行压制聚料,使其端部呈圆锥体;再将聚料后的端部加热,其端部温度保持在750-1220℃,最后伸入液压机的球状模腔,将其端部圆锥体聚料成球体。
2.根据权利要求1所述的一种卸扣热模压生产工艺,其特征在于:所述聚料次数为N次,N≥1。
3.根据权利要求1所述的一种卸扣热模压生产工艺的模具,由上模和下模构成,所述上模与液压机的压头连接,下模与液压机的进料口连接;其特征在于:所述上模由上模块下端面中心开有腔体构成;所述下模由结构相同的左、右开合模组成,所述下模闭合时构成贯通上下的腔体。
4.根据权利要求3所述的一种卸扣热模压生产工艺的模具,其特征在于:所述上模的腔体为半球型或类圆锥体型。
5.根据权利要求3所述的一种卸扣热模压生产工艺的模具,其特征在于:所述下模的腔体由下模上端面开口的半球形腔体及半球形腔体底端中心开贯穿下模的圆柱孔构成,所述半球形与圆柱孔轴线一致。
6.根据权利要求3所述的一种卸扣热模压生产工艺的模具,其特征在于:所述下模的腔体由下模上端面开口的类圆锥体形腔体及类圆锥体形腔体底端中心开贯穿下模的圆柱孔构成,所述类圆锥体形与圆柱孔轴线一致。