CN101565273A - 搪瓷釉料及其制备方法以及用其制备搪瓷青花瓷的方法 - Google Patents
搪瓷釉料及其制备方法以及用其制备搪瓷青花瓷的方法 Download PDFInfo
- Publication number
- CN101565273A CN101565273A CNA2009100393423A CN200910039342A CN101565273A CN 101565273 A CN101565273 A CN 101565273A CN A2009100393423 A CNA2009100393423 A CN A2009100393423A CN 200910039342 A CN200910039342 A CN 200910039342A CN 101565273 A CN101565273 A CN 101565273A
- Authority
- CN
- China
- Prior art keywords
- enamel
- frit
- percent
- porcelain
- vitreous enamel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种搪瓷釉料及其制备方法以及使用其制备搪瓷青花瓷的方法，其各组分的重量百分比为：搪瓷基料5－20，336A钴兰色素45－60，黑色素0.05－0.5，丝印调墨油25－40；其中搪瓷基料也包含多种组分，各组分重量百份比为：石英20－30，硼砂25－35，长石15－25，纯碱2－6，冰晶5－7，氟化钙3－6，硝酸钠2－5。上述搪瓷釉料烧制出的产品不但搪瓷与底胚结合牢固，而且表面散发青花图案，犹如青花瓷。产品古典、高雅，美观。
Description
技术领域
本发明涉及一种搪瓷釉料，制作该搪瓷釉料的方法，以及使用该搪瓷釉料制备搪瓷青花瓷的方法。
技术背景
搪瓷是金属及其表面涂覆的瓷釉经过烧制两者表面发生物理化学反应而牢固结合的一种复合材料，其既具有金属固有的机械强度和加工性能，又具有涂层所具有的耐腐蚀、耐磨、耐热、无毒及可装饰性。其被广泛应用人们的日常生活终，如餐具、厨具、墙壁、地板等。青花是我国古代陶瓷技术中的瑰宝，其图案白底兰花，古典、高雅，深受人们喜爱。如果烧制出来的搪瓷的表面能够具有青花团，那将使搪瓷的外观得到极大地美化，能使搪瓷产品更受人们的喜爱，从而得到更好应用与推广。
发明内容
本发明旨在给出一种能够在表面烧制出青花图案的搪瓷釉料，以美化搪瓷产品的外观，更好地满足人们的需要。
一种搪瓷釉料，其特征是，其由下述重量百分比的原料制成：
搪瓷基料5-20，钴兰色素45-60，黑色素0.05-0.5，丝印调墨油25-40；
所述搪瓷基料又由下列重量百份比的原料制成：
石英20-30，硼砂25-35，长石15-25，纯碱2-6，冰晶5-7，氟化钙3-6，硝酸钠2-5。
一种搪瓷釉料的制备方法，其特征是，包括下述顺序的步骤：
(a)、按上述搪瓷基料中各原料重量百分配比称量各原料，放入坩埚中，在1200℃下熔化，熔化好后，将其投入水中冷淬，而后捞出烘干，凝固得块状熔块；
(b)、研磨熔块至能够通过300目的筛子的大小，再烘干；
(c)、按上述重量百分比称量钴兰色素、黑色素、丝印调墨油和经步骤(a)和(b)制得的搪瓷基料，将其混合后，放入三辊研磨机中研磨两遍，即可制得搪瓷青花瓷釉料。
一种搪瓷青花瓷的制备方法，其特征是，包括如下顺序的步骤：
将上述方法制得的搪瓷釉料直接丝印或通过转写纸复制到搪瓷底胚上；
而后置于120-250℃烘干或自然干燥后；
再在780-830℃的炉中烧制而成。
本发明的搪瓷釉料，其釉料中不但含有搪瓷基料还含有336A钴兰色素，其既保证了搪瓷釉料与底胚间的相互融合，又使搪瓷釉料在烧制后表面能够散发青花的图案。其使搪瓷釉料烧制出来的搪瓷青花瓷产品，其表面犹如青花瓷，古典、高雅。极大地美化了搪瓷产品，能让搪瓷产品更受人们的喜爱，得到更好应用与推广。同时，本发明采用一定的搪瓷基料作为载体，使得工艺幅度增大，有利于大幅面的青花瓷搪瓷的装饰。此外，本发明的搪瓷釉料的制作工艺简单，成本低廉，安全可靠，可适于批量生产。
所述的丝印调墨油可为丝印用的调墨油，其以陶瓷丝印用的调墨油为佳。
所述钴兰色素以336A钴兰为佳。
所述黑色素可为铁黑。
具体实施方式
实施例1
一种搪瓷釉料，其由下述重量百分比的原料制成：
搪瓷基料5-20，钴兰色素45-60，黑色素0.05-0.5，丝印调墨油25-40；
所述搪瓷基料又由下列重量百份比的原料制成：
石英20-30，硼砂25-35，长石15-25，纯碱2-6，冰晶5-7，氟化钙3-6，硝酸钠2-5。
所述钴兰色素为336A钴兰。
按上述重量百分比混合搪瓷基料中的各原料，并将其放入坩埚中，在1200℃的高温下进行熔化，熔化好后，将其投入水中冷淬，再捞出烘干得凝固的熔块，将熔块投入球磨罐中，研磨至过300目筛的大小，倒入容器中烘干备用。
按上述重量百分比混合搪瓷釉料的各组成原料，将混合后的料浆，放入三辊研磨机研磨两遍，即可制得本发明的搪瓷釉料。
将上述制得的浆状搪瓷釉料，通过直接丝印或转写纸转印到底坯上，置于120-250℃下烘干或自然干燥后，再将工件置于780-830℃烧成炉中烧成即可制得具有青花图案的搪瓷产品-搪瓷青花瓷。
实施例2.
一种搪瓷釉料，其由下述重量百分比的原料制成：
搪瓷基料5，336A钴兰色素55，黑色素0.05，丝印调墨油39.95；
所述搪瓷基料又由下列重量百份比的原料制成：
石英30，硼砂35，长石20，纯碱2，冰晶5，氟化钙3，硝酸钠5。
实施例3.
一种搪瓷釉料，其由下述重量百分比的原料制成：
搪瓷基料20，336A钴兰色素54.5，黑色素0.5，丝印调墨油25；
所述搪瓷基料又由下列重量百份比的原料制成：
石英30，硼砂25，长石24，纯碱6，冰晶7，氟化钙6，硝酸钠2。
实施例4
一种搪瓷釉料，其由下述重量百分比的原料制成：
搪瓷基料9.5，336A钴兰色素60，黑色素0.5，丝印调墨油30；
所述搪瓷基料又由下列重量百份比的原料制成：
石英30，硼砂35，长石15，纯碱6，冰晶6，氟化钙6，硝酸钠2。
实施例5
一种搪瓷釉料，其搪瓷釉料的各组成成分的重量百分比见下表。
| 搪瓷基料 | 336A钴兰色素 | 黑色素 | 丝印调墨油 |
| 15 | 55 | 0.1 | 30 |
其搪瓷基料中的各组分的重量百分比见下表。
| 原料 | 石英 | 长石 | 氟化钙 | 硝酸钠 | 硼砂 | 纯碱 | 冰晶 |
| 组成 | 20 | 25 | 6.0 | 4.0 | 33 | 5.0 | 7.0 |
用其烧制出来的搪瓷产品的效果较佳。
Claims (6)
1、一种搪瓷釉料，其特征是，其由下述重量百分比的原料制成：
搪瓷基料5-20，钴兰色素45-60，黑色素0.05-0.5，丝印调墨油25-40；
所述搪瓷基料又由下列重量百份比的原料制成：
石英20-30，硼砂：25-35，长石15-25，纯碱2-6，冰晶5-7，氟化钙3-6，硝酸钠2-5。
2、根据权利要求1所述搪瓷釉料，其特征是，所述搪瓷釉料中搪瓷基料占14.9重量百分比，钴兰色素55重量百分比，黑色素0.1重量百分比，丝印调墨油30重量百分比。
3、根据权利要求1所述搪瓷釉料，其特征是，所述搪瓷基料由下列重量百分比的原料制成：石英20，硼砂33，长石25，纯碱5，冰晶7，氟化钙6，硝酸钠4。
4、根据权利要求1至3中任何一项所述搪瓷釉料，其特征是，所述钴兰色素为336A钴兰。
5、一种搪瓷釉料的制备方法，其特征是，包括下述顺序的步骤：
(a)、按权利要求1或3中所述的搪瓷基料中各原料重量百分配比称量各原料，放入坩埚中，在1200℃下熔化，熔化好后，将其投入水中冷淬，而后捞出烘干，凝固得块状熔块；
(b)、研磨熔块至能够通过300目的筛子的大小，再烘干；
(c)、按权利要求1或2所述重量百分比称量钴兰色素、黑色素、丝印调墨油和经步骤(a)和(b)制得的搪瓷基料，将其混合后，放入三辊研磨机中研磨两遍，即可制得搪瓷釉料。
6、一种搪瓷青花瓷的制备方法，其特征是，包括如下顺序的步骤：
将权利要求4制得的搪瓷釉料直接丝印或通过转写纸复制到搪瓷底胚上；
而后置于120-250℃烘干或自然干燥后；
再在780-830℃的炉中烧制而成。