CN101524833A - 锆刚玉超涂层砂布 - Google Patents
锆刚玉超涂层砂布 Download PDFInfo
- Publication number
- CN101524833A CN101524833A CN200810008033A CN200810008033A CN101524833A CN 101524833 A CN101524833 A CN 101524833A CN 200810008033 A CN200810008033 A CN 200810008033A CN 200810008033 A CN200810008033 A CN 200810008033A CN 101524833 A CN101524833 A CN 101524833A
- Authority
- CN
- China
- Prior art keywords
- corundum
- zirconia
- abrasive cloth
- coating
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
锆刚玉超涂层砂布，它涉及一种磨削用的砂布，具体涉及一种刚玉超涂层砂布。它采用以下技术方案：首先选择载体纯化纤布坯再进行特殊处理，对坯布表面进行起毛，把坯布表面的毛均匀的剪去，再水洗烘干，在210－250℃进行高温定型，然后进行两次轧浆，再正面涂层，背面涂层配方；最后制造生产，选用锆刚玉磨料和高温煅烧棕刚玉磨料，采用锆刚玉和棕刚玉以7∶3的比例进行锆刚玉静电植砂和重力植砂；采用第一次、第二次复胶。本发明主要用于不锈钢等金属领域的抛光研磨，这是一般砂布所做不到的。
Description
技术领域：
本发明涉及一种磨削用的砂布，具体涉及一种刚玉超涂层砂布。
背景技术：
目前国内高品级磨削材料用量面广量大，每年用量在2亿平方米左右，国内涂料磨具产品档次较低。特别在耐磨性，耐水性方面性能较差。缺少适用高速成磨削产品，特别是在耐水性能方面，国内所使用的耐水产品还停留在60年代水平基础上，具体表现为：(1)耐水性能，在水中浸泡后砂布整体发软，磨削效率低。(2)采用的醇酸树酯粘结强强度低，在使用中磨料容易脱落，耐磨性差。(3)所用的胶粘剂脆性大，砂布容易老化，放置二个月左右出现龟裂现象，严重影响使用性能。
发明内容：
本发明的目的是提供一种锆刚玉超涂层砂布，它能够增加耐热性、增加耐磨性，抗静电性，抗阻塞，使被打磨的工件余料不把砂布缝隙阻住，增加耐磨性。
为了解决背景技术所存在的问题，本发明是采用以下技术方案：首先选择载体纯化纤布坯再进行特殊处理，对坯布表面进行起毛，把坯布表面的毛均匀的剪去，使坯布表面干净，再水洗烘干，在210-250℃进行高温定型，使坯布形状在一个稳定的前提下进行再处理，为了基布的平整而且在制造植砂时底胶不容易渗透，而且还阿能和底胶进行很好的接合，然后进行两次轧浆，然后正面涂层，背面涂层配方；最后制造生产，选用锆刚玉磨料和高温煅烧棕刚玉磨料，因锆刚玉中主要含有氧化锆成分，氧化锆很硬容易断裂，所以采用锆刚玉和棕刚玉以7∶3的比例进行锆刚玉静电植砂和重力植砂。棕刚玉这样的好处是有利于磨削效果好。锆刚玉最大的好处是磨削以后如果断掉可以再出现新的韧尖。为了增加耐磨性和耐热性，最后采用第一次、第二次复胶。本发明中不仅可以增加耐热性还可以增加耐磨性，抗静电性，抗阻塞，使被打磨的工件余料不把砂布缝隙阻住，增加耐磨性。本发明主要用于不锈钢等金属领域的抛光研磨，这是一般砂布所做不到的。
具体实施方式：
本具体实施方式采用以下技术方案：首先选择载体纯化纤布坯再进行特殊处理，对坯布表面进行起毛，把坯布表面的毛均匀的剪去，使坯布表面干净，再水洗烘干，在210-250℃进行高温定型，使坯布形状在一个稳定的前提下进行再处理，为了基布的平整而且在制造植砂时底胶不容易渗透，而且还阿能和底胶进行很好的接合，然后进行两次轧浆，然后正面涂层，背面涂层配方；最后制造生产，选用锆刚玉磨料和高温煅烧棕刚玉磨料，因锆刚玉中主要含有氧化锆成分，氧化锆很硬容易断裂，所以我们采用锆刚玉和棕刚玉以7∶3的比例进行锆刚玉静电植砂和重力植砂。棕刚玉这样的好处是有利于磨削效果好。锆刚玉最大的好处是磨削以后如果断掉可以再出现新的韧尖。为了增加耐磨性和耐热性，最后采用第一次、第二次复胶。锆刚玉最大的好处是磨削以后如果断掉可以再出现新的韧尖。
所述的第一次轧浆配方为：轧浆酚醛树脂KP-8510：20份；水：80份；消泡剂NX2：0.4份；渗透剂LX113：0.4份。
所述第二次轧浆配方为：25％PVA217：238份；KP-8510：45份；水：170；消泡剂NX2：0.4；渗透剂LX113：0.4份。
所述的正面涂层的配方为：酚醛树脂KP-60：87份；
PVA-205(25％)：12份；S-20：0.2份；CaCo3：50份；NX2：0.4份；KM-550结合剂：0.6份。
所述的背面涂层的配方为：酚醛树脂KP-8501：69份；CaCo3：38份；丁苯332：60份；S-20：0.4份；NX2：0.2份。
所述的值砂配方为：KP-75：100份；CaCo3：80份；S-20：0.8份；EC冰(1∶1)适量。
所述的第一次复胶配方为：KP-75：80份；耐热性冰晶石：70份；EC冰(1∶2)适量。
所述的第二次复胶配方：KBF4：141份；钛白粉：2份；环氧树脂：8份；环氧固化剂：6份；硅藻土：0.75份；EC冰(1∶1)适量。
Claims (5)
1、锆刚玉超涂层砂布，其特征在于它采用以下技术方案：首先选择载体纯化纤布坯再进行特殊处理，对坯布表面进行起毛，把坯布表面的毛均匀的剪去，再水洗烘干，在210-250℃进行高温定型，然后进行两次轧浆，再正面涂层，背面涂层配方；最后制造生产，选用锆刚玉磨料和高温煅烧棕刚玉磨料，采用锆刚玉和棕刚玉以7∶3的比例进行锆刚玉静电植砂和重力植砂；采用第一次、第二次复胶。
2、根据权利要求1所述的锆刚玉超涂层砂布，其特征在于所述的第一次轧浆配方为：轧浆酚醛树脂KP-8510：20份；水：80份；消泡剂NX2：0.4份；渗透剂LX113：0.4份；第二次轧浆配方为：25％PVA217：238份；KP-8510：45份；水：170；消泡剂NX2：0.4；渗透剂LX113：0.4份。
3、根据权利要求1所述的锆刚玉超涂层砂布，其特征在于所述的所述的正面涂层的配方为：酚醛树脂KP-60：87份；PVA-205(25％)：12份；S-20：0.2份；CaCo3：50份；NX2：0.4份；KM-550结合剂：0.6份；背面涂层的配方为：酚醛树脂KP-8501：69份；CaCo3：38份；丁苯332：60份；S-20：0.4份；NX2：0.2份。
4、根据权利要求1所述的锆刚玉超涂层砂布，其特征在于所述的值砂配方为：KP-75：100份；CaCo3：80份；S-20：0.8份；EC冰(1∶1)适量。
5、根据权利要求1所述的锆刚玉超涂层砂布，其特征在于所述的第一次复胶配方为：KP-75：80份；耐热性冰晶石：70份；EC冰(1∶2)适量；所述的第二次复胶配方：KBF4：141份；钛白粉：2份；环氧树脂：8份；环氧固化剂：6份；硅藻土：0.75份；EC冰(1∶1)适量。