CN101514028A - 一种片状重质碳酸钙粉体的制备方法 - Google Patents
一种片状重质碳酸钙粉体的制备方法 Download PDFInfo
- Publication number
- CN101514028A CN101514028A CNA2009100613599A CN200910061359A CN101514028A CN 101514028 A CN101514028 A CN 101514028A CN A2009100613599 A CNA2009100613599 A CN A2009100613599A CN 200910061359 A CN200910061359 A CN 200910061359A CN 101514028 A CN101514028 A CN 101514028A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- carbonate powder
- ground calcium
- raw material
- flaky
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及干法制备片状重质碳酸钙粉体的方法，以伟晶方解石矿为原料，按照下列步骤进行制备：①将原料粉碎至5mm～10mm，②干法研磨：将粉碎后的原料用卧式球磨机进行研磨，研磨介质为氧化锆棒，棒直径30mm～50mm、棒长60mm～100mm，研磨时间为40分钟～60分钟；得到片状重质碳酸钙粉体。本发明制备的片状重质碳酸钙粉体，粒径小于8μm的含量为92％～96％，片状重质碳酸钙粉体的径厚比大于4∶1。本发明采用干法制备片状重质碳酸钙粉体，无需干燥即可获得片状重质碳酸钙干粉，生产成本更低。
Description
技术领域
本发明涉及碳酸钙粉体的制备方法，特别是涉及片状碳酸钙粉体的制备方法。
背景技术
碳酸钙粉体是用途广泛的无机盐功能填料之一，主要用于塑料、橡胶、涂料、密封剂、胶粘剂、造纸、印刷油墨、日用品、食品、保健品、药品等中填充剂、增强剂、改性剂、增白剂等。片状碳酸钙粉体能够使制品表面光泽度、平整度提高，增强效果更好。碳酸钙粉体按加工工艺的不同分为重质碳酸钙和轻质碳酸钙两类。重质碳酸钙是将优质天然碳酸钙经物理粉碎加工而成，轻质碳酸钙是石灰岩经煅烧→消化→碳化反应获得的沉淀碳酸钙。片状碳酸钙粉体也有片状重质碳酸钙和片状轻质碳酸钙两类。制备片状轻质碳酸钙最简便的方法是一步法，如日本专利平2-184519、中国专利CN1080909A，但都使用了有毒的晶形控制剂；中国专利CN1157444C公布了一种片状重质碳酸钙制备方法，其工艺过程是：1.原料干法，2.调浆，3.湿法超细研磨，4.超细研磨后处理(压滤成饼、干燥)，这是一种湿法制备片状重质碳酸钙的方法，其优点是粉体粒度细(小于2微米颗粒的含量大于90％)，缺点是需干燥后才能获得片状重质碳酸钙干粉。
发明内容
本发明的目的在于提供一种干法制备片状重质碳酸钙粉体的方法，该方法简单方便，生产成本更低。
为了实现上述目的，本发明提供的技术方案是：以伟晶方解石矿为原料，按照下列步骤进行制备：1.原料粉碎至5mm～10mm，2.干法研磨。在干法研磨过程中，采用卧式球磨机进行研磨，研磨介质为氧化锆棒，棒直径30mm～50mm、棒长60mm～100mm，研磨时间为40分钟～60分钟。
本发明制备的片状重质碳酸钙粉体，粒径小于8μm的含量为92％～96％，粉体的径厚比大于4∶1。
本发明的技术特点
本发明采用干法制备片状重质碳酸钙粉体，无需干燥即可获得干粉，简单方便，生产成本更低。另外，本发明采用氧化锆棒作为研磨介质，研磨效果好，而且不产生污染。
具体实施方式
下面的实施例用于进一步说明本发明，而不能视作对本发明的限制。
实施例1：
以伟晶方解石矿为原料。
将原料粉碎至10mm。
将粉碎后的原料，在卧式球磨机进行研磨，研磨介质为氧化锆棒，棒直径40mm、棒长80mm。干法研磨50分钟后，获得的片状重质碳酸钙粉体粒径小于8μm的含量为93％，粉体的径厚比大于5∶1。
实施例2：
以伟晶方解石矿为原料。
将原料粉碎至5mm。
将粉碎后的原料，在卧式球磨机进行研磨，研磨介质为氧化锆棒，棒直径40mm、棒长80mm。干法研磨60分钟后，获得的片状重质碳酸钙粉体粒径小于8μm的含量为96％，粉体的径厚比大于6∶1。
Claims (1)
1.一种片状重质碳酸钙粉体的制备方法，以伟晶方解石矿为原料，按照下列步骤进行制备：①将原料粉碎至5mm～10mm，②干法研磨：将粉碎后的原料用卧式球磨机进行研磨，研磨介质为氧化锆棒，棒直径30mm～50mm、棒长60mm～100mm，研磨时间为40分钟～60分钟；得到片状重质碳酸钙粉体，粉体的径厚比大于4∶1。