CN101463235A - 一种高伸长率丙烯酸酯胶粘剂 - Google Patents
一种高伸长率丙烯酸酯胶粘剂 Download PDFInfo
- Publication number
- CN101463235A CN101463235A CNA2007101689859A CN200710168985A CN101463235A CN 101463235 A CN101463235 A CN 101463235A CN A2007101689859 A CNA2007101689859 A CN A2007101689859A CN 200710168985 A CN200710168985 A CN 200710168985A CN 101463235 A CN101463235 A CN 101463235A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic ester
- ester adhesive
- mixture
- adhesive according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明一种高伸长率丙烯酸酯胶粘剂是双组分胶粘剂。属于双组分丙烯酸酯胶粘剂技术领域。它主要是解决现有丙烯酸酯胶粘剂断裂伸长率较小，只有10～20％的问题。它的特征在于：(1)主剂组分：50～85份至少含有1个乙烯基的丙烯酸酯单体，0～25份甲基丙烯酸，5～30份弹性体，0.01～1份稳定剂，10～40份增韧树脂，0.5～5.5份引发剂；(2)固化剂组分：50～90份至少含有1个乙烯基的丙烯酸酯单体，1～10份促进剂，10～50份增韧树脂。本发明与现有丙烯酸酯胶粘剂比较，断裂伸长率具有显著提高，断裂伸长率可以达到100％以上，可用于多种材质的自粘和互粘，在机械制造和维修领域具有广泛的应用。
Description
技术领域
本发明属于双组分丙烯酸酯胶粘剂技术领域，具体涉及一种高伸长率丙烯酸酯胶粘剂。
背景技术
由于快固型丙烯酸酯结构胶粘剂具有室温快速固化、强度高、韧性好、可油面粘接、适应性强、工艺简便等显著特点，因此广泛用于宇航、航空、汽车、机械、舰船、电子、电器、仪表、建筑、家具、玩具、铁路车辆、土木工程、工艺美术等行业的结构粘接、小件装配、大件组装、应急修复、防渗堵漏、铭牌粘贴等。在尖端技术和高科技方面也得到了较好的应用。
一般来说，丙烯酸酯胶粘剂的脆性较大，断裂伸长率较小，只有10～20％。由于丙烯酸酯的脆性较大，影响了丙烯酸酯胶的应用范围。开发出一种高韧性、高断裂伸长率的产品就十分必要了。
发明内容
本发明针对上述不足之处而提供一种断裂伸长率可以达到100％以上的高伸长率丙烯酸酯胶粘剂。
本发明丙烯酸酯胶粘剂的技术解决方案是：一种高伸长率丙烯酸酯胶粘剂，包括主剂和固化剂两个组分，其特征在于：(1)主剂组分：50～85份至少含有1个乙烯基的丙烯酸酯单体，0～25份甲基丙烯酸，5～30份弹性体，0.01～1份稳定剂，10～40份增韧树脂，0.5～5.5份引发剂。(2)固化剂组分：50～90份至少含有1个乙烯基的丙烯酸酯单体，1～10份促进剂，10～50份增韧树脂。
本发明中技术解决方案所述的至少含有1个乙烯基的丙烯酸酯单体是单甲基丙烯酸酯单体、二甲基丙烯酸酯单体、多甲基丙烯酸酯单体或其混合物。
本发明中技术解决方案所述的引发剂是过氧化物。
本发明中技术解决方案所述的过氧化物是过氧化苯甲酰、叔丁基过氧化氢、异丙苯过氧化氢、过氧化甲乙酮、过氧化二异丙苯或其混合物。
本发明中技术解决方案所述的弹性体是氯磺化聚乙烯、丁腈橡胶、氯丁橡胶、丙烯酸酯橡胶、聚醚橡胶、SBS橡胶类弹性体或其混合物。
本发明中技术解决方案所述的稳定剂是酚类化合物、醌类化合物或其混合物。
本发明中技术解决方案所述的增韧树脂是ABS、MBS、MBAS工程塑料或其混合物。
本发明中技术解决方案所述的促进剂是胺类、硫脲类、醛胺缩合物或其混合物。
采用本发明方法制备的丙烯酸酯胶粘剂是一种高伸长率丙烯酸酯胶粘剂，与现有丙烯酸酯胶粘剂比较，断裂伸长率具有显著提高，断裂伸长率可以达到100％以上，可用于多种材质的自粘和互粘。在机械制造和维修领域具有广泛的应用。
本发明的高伸长率丙烯酸酯胶粘剂的相关性能测试，拉伸强度和断裂伸长率为胶粘剂固化物的物理性能，拉伸剪切强度所用试片均为铝试片。
具体实施方式
下列实施例将更详细介绍本发明，但本发明不局限于此。
实施例1：
配比 主剂 固化剂
甲基丙烯酸甲酯 56kg 71kg
MBS 14kg 23kg
甲基丙烯酸 14kg
氯丁橡胶 14kg
1、4-对苯二酚 1kg
异丙苯过氧化氢 1kg
醛胺缩合物 6kg
制备方法：
(1)主剂：将甲基丙烯酸甲酯单体和甲基丙烯酸投入反应釜中，加入氯丁橡胶弹性体，搅拌至氯丁橡胶弹性体完全溶解，加入1、4-对苯二酚稳定剂、MBS增韧树脂和异丙苯过氧化氢引发剂，搅拌均匀。(2)固化剂组分：将甲基丙烯酸甲酯单体、醛胺缩合物促进剂和MBS增韧树脂投入反应釜中搅拌均匀。
性能测试：
1、拉伸剪切强度按GB/T 7124-1986执行
2、拉伸强度按GB/T 528-92执行
3、断裂伸长率按GB/T 528-92执行
测试结果见表1。
实施例2：
配比 主剂 固化剂
甲基丙烯酸甲酯 56kg 37.4kg
甲基丙烯酸-2-羟乙酯 26kg
MBS 14kg 36kg
甲基丙烯酸 14kg
氯丁橡胶 14kg
1、4-对苯二酚 1kg
异丙苯过氧化氢 1kg
取代基硫脲 0.6kg
制备方法的条件同实施例1。
性能测试同实施例1。
测试结果见表1。
实施例3：
配比 主剂 固化剂
甲基丙烯酸甲酯 54kg 37.4kg
甲基丙烯酸-2-羟乙酯 26kg
MBS 12kg 36kg
甲基丙烯酸 14kg
氯丁橡胶 18kg
1、4-对苯二酚 1kg
异丙苯过氧化氢 1kg
取代基硫脲 0.6kg
制备方法的条件同实施例1。
性能测试同实施例1。
测试结果见表1。
实施例4：
配比 主剂 固化剂
甲基丙烯酸甲酯 56kg 37.9kg
甲基丙烯酸-2-羟乙酯 26kg
MBS 14kg 36kg
甲基丙烯酸 14kg
氯丁橡胶 14kg
1、4-对苯二酚 1kg
异丙苯过氧化氢 1kg
取代基硫脲 0.1kg
制备方法的条件同实施例1。
性能测试同实施例1。
测试结果见表1。
实施例5：
配比 主剂 固化剂
甲基丙烯酸甲酯 53kg 37.4kg
甲基丙烯酸-2-羟乙酯 26kg
MBS 12kg 33kg
甲基丙烯酸 14kg
氯丁橡胶 18kg
1、4-对苯二酚 1kg
异丙苯过氧化氢 2kg
三乙胺 3kg
取代基硫脲 0.6kg
制备方法的条件同实施例1。
性能测试同实施例1。
测试结果见表1。
实施例6：
配比 主剂 固化剂
甲基丙烯酸甲酯 53kg 37.4kg
甲基丙烯酸-2-羟乙酯 26kg
MBS 12kg 35kg
甲基丙烯酸 14kg
氯丁橡胶 18kg
1、4-对苯二酚 1kg
异丙苯过氧化氢 2kg
N，N-二甲基对甲苯胺 1kg
取代基硫脲 0.6kg
制备方法的条件同实施例1。
性能测试同实施例1。
测试结果见表1。
表1
| 实施例 | 拉伸剪切强度，MPa | 拉伸强度，MPa | 断裂伸长率，％ |
| 实施例1 | 8.5 | 3.1 | 103 |
| 实施例2 | 5.2 | 2.9 | 210 |
| 实施例3 | 5.4 | 2.9 | 245 |
| 实施例4 | 2.6 | 1.2 | 158 |
| 实施例5 | 15.2 | 15.0 | 196 |
| 实施例6 | 12.8 | 6.9 | 152 |
Claims (8)
1、一种高伸长率丙烯酸酯胶粘剂是双组分胶粘剂，包括主剂和固化剂两个组分，其特征在于：
(1)主剂组分：50～85份至少含有1个乙烯基的丙烯酸酯单体，025份甲基丙烯酸，5～30份弹性体，0.01～1份稳定剂，10～40份增韧树脂，0.5～5.5份引发剂；
(2)固化剂组分：50～90份至少含有1个乙烯基的丙烯酸酯单体，1～10份促进剂，10～50份增韧树脂。
2、根据权利要求1所述的丙烯酸酯胶粘剂，其特征在于：所述的至少含有1个乙烯基的丙烯酸酯单体是单甲基丙烯酸酯单体、二甲基丙烯酸酯单体、多甲基丙烯酸酯单体或其混合物。
3、根据权利要求1所述的丙烯酸酯胶粘剂，其特征在于：所述的引发剂是过氧化物。
4、根据权利要求3所述的丙烯酸酯胶粘剂，其特征在于：所述的过氧化物是过氧化苯甲酰、叔丁基过氧化氢、异丙苯过氧化氢、过氧化甲乙酮、过氧化二异丙苯或其混合物。
5、根据权利要求1所述的丙烯酸酯构胶粘剂，其特征在于：所述的弹性体是氯磺化聚乙烯、丁腈橡胶、氯丁橡胶、丙烯酸酯橡胶、聚醚橡胶、SBS橡胶类弹性体或其混合物。
6、根据权利要求1所述的丙烯酸酯胶粘剂，其特征在于：所述的稳定剂是酚类化合物、醌类化合物或其混合物。
7、根据权利要求1所述的丙烯酸酯胶粘剂，其特征在于：所述的增韧树脂是ABS、MBS、MBAS工程塑料或其混合物。
8、根据权利要求1所述的丙烯酸酯胶粘剂，其特征在于：所述的促进剂是胺类、硫脲类、醛胺缩合物或其混合物。