CN101407961A - Moisture absorption quick-drying fabric and producing method thereof - Google Patents
Moisture absorption quick-drying fabric and producing method thereof Download PDFInfo
- Publication number
- CN101407961A CN101407961A CNA2008101220395A CN200810122039A CN101407961A CN 101407961 A CN101407961 A CN 101407961A CN A2008101220395 A CNA2008101220395 A CN A2008101220395A CN 200810122039 A CN200810122039 A CN 200810122039A CN 101407961 A CN101407961 A CN 101407961A
- Authority
- CN
- China
- Prior art keywords
- fabric
- hydroscopic fast
- drying shell
- shell fabric
- fluorine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fabric with the capacity of moisture absorption and fast drying, and a production method thereof, belonging to the technical field of textile printing and dyeing. The moisture absorption and sweating effects of the fabric are improved by an inner-layer printing technology used in the fabric; a printing sizing agent containing a fluorine-containing water repellent is specially prepared and a printing plate with rice-shaped patterns is collocated so as to cause the fabric to have siphon effect and realize the purposes of adsorbing sweat and sweating; and a constant-temperature drying technology after printing and before setting effectively improves the sweat absorption effect and washing-resistant effect of the fabric.
Description
Technical field
The present invention relates to a kind of weaving face fabric,, belong to technical field of textile printing in particular to a kind of hydroscopic fast-drying shell fabric and production method thereof of making sportswear that be mainly used in.
Background technology
At present, people are after wearing sportswear and having moved, reason owing to garment material, as adopt terylene goods or the relatively poor fibre of other hydrophobicitys, hygroscopicity of fabric is relatively poor, sweat can not be discharged timely and effectively, after sweat gathers, makes the people produce feeling of oppression and heat, and easy breed bacteria, produce so-called movement syndrome, therefore, be used for the lining of sportswear, requirement has higher hygroscopicity and antibiotic property, at present, more hydroscopic fast-drying on the market and antibiotic facing material adopt and change raw material and constitute, and add antiseptic and wait and realize, on the one hand, its hygroscopicity and antibiotic property promote limited, on the other hand, seek hygroscopicity and the better hydrophobic fibre of antibiotic property production cost has also been increased.
Summary of the invention
For solving the problems referred to above of prior art, main purpose of the present invention is the raw material of existing hydroscopic fast-drying shell fabric is constituted and the production method further investigation, provides a kind of moisture sorption effect good hydroscopic fast-drying shell fabric.
The technical scheme that the present invention takes for achieving the above object is that a kind of hydroscopic fast-drying shell fabric is characterized in that: be printed with the concentrator that contains waterproofing agent that is grain of rice shape flower type on the internal layer of lining.
The further setting of the present invention is as follows:
Among the present invention, the indication skin is the outer surface of fabric, and internal layer is the contact-making surface of fabric and skin.
Hydroscopic fast-drying shell fabric of the present invention adopts 100% cotton, or 70～80% cotton and 20～30% terylene mixing are weaved and formed.
Concentrator of the present invention is composed as follows by ratio of weight and the number of copies:
Thickener 2～5
Fluorine-containing water repellent 1～3
Water 100
Described thickener is a kind of colorless and odorless, be used for increasing the viscosity and the intensity of concentrator, the preferred polyacrylic thickener that adopts, as homemade FS-200, external Clariant 2710 etc., for increasing the thickener effect, can drip certain amount of ammonia water (concentration is 15～25%) according to the thickness of fabric, be generally 1 ammoniacal liquor of adding in 10 kilograms of slurries.
Described fluorine-containing water repellent is a kind of nontoxic waterproofing agent that contains fluorine element, as AG-XF fluorine-containing water repellent, D-320 fluorine-containing water repellent, Clariant Nuva HPU etc.
Secondary objective of the present invention provides a kind of production method of above-mentioned hydroscopic fast-drying shell fabric, comprises and weaving---and steps such as finished product inspection is characterized in that stamp---typing---:
1, stamp flower type design: in order to guarantee that lining is not when influencing fabric moisture quick-drying energy, water repellent area with maximum overlay capacity, the present invention has designed a kind of special stamp flower type of grain of rice shape, and special one have the grain of rice type stamp space of a whole page, adopt a kind of concentrator that contains the durable waterproof agent will spend type to be printed on the internal layer of fabric, like this, owing to can form very slight gap in the middle of grain of rice shape (class grain of rice shape) the stamp type, this fine gap can have siphonic effect, thereby the sweat that inner textile layer absorbed is drawn onto outer the discharge rapidly, make internal layer keep clean salubrious, can improve the hydrofuge performance of fabric effectively, reduce the chance of sweat and contact skin.
2, concentrator configuration: be the hydrofuge performance that increases fabric, the present invention is special a kind of concentrator with good absorbing sweat effect, composed as follows by ratio of weight and the number of copies:
Thickener 2～5
Fluorine-containing water repellent 1～3
Water 100
3, stamp: stamp carries out on plain net, rotary screen printing machines or coating machine, and printing speed 25～40m/min guarantees that slurry is imprinted on inner textile layer in the printing process and not to exosmosis.In addition, because concentrator is transparent, therefore, preferably in concentrator, be added with fluorescent whitening agent, so that under ultraviolet light, carry out the examination and test of products.
4, back arrangement typing: grey cloth is after producing colored type through printing technology, and constant temperature was placed 1～3 hour down for 80～120 ℃ in drying room, preferably placed 1.5 hours down at 100 ℃, went up setting machine arrangement typing then.This procedure is very crucial to the present invention, and by the arrangement typing, the absorbing sweat effect and the washing-resistant effect of product are improved greatly.
5, the product after arrangement typing carries out the examination and test of products under ultraviolet light, can the clot warehouse-in after qualified.
Beneficial effect of the present invention is: 1, adopt the internal layer printing technology at fabric, improve the moisture absorbing and sweat releasing effect of fabric; 2, special concentrator with fluorine-containing water repellent, and the printing plate of configuration grain of rice shape flower type make fabric have siphon effect, really realize the purpose of quick absorbing sweat perspire; 3, behind the stamp, before the typing, constant temperature drying technology has strengthened the absorbing sweat effect and the washing-resistant effect of fabric, effectively through washing the moisture absorbing and sweat releasing effect that also can have after 20 times about 85%.
The invention will be further described below in conjunction with the drawings and specific embodiments.
Description of drawings
Fig. 1 is the grain of rice shape stamp flower type figure of hydroscopic fast-drying shell fabric internal layer of the present invention.
The specific embodiment
Weave according to the present invention that---production method of stamp---typing---finished product inspection gets following specific embodiment.
Embodiment 1
1, weave:
Raw material: adopt 40S half combed cotton/40S polyester-cotton blend combing
Density: 180～250g/m
2
The door width of cloth: 150～180 centimetres
Weaving speed: 250kg/ platform
2, stamp
Following composition preparation concentrator by ratio of weight and the number of copies:
Clariant 2710 22g
Clariant Nuva HPU 12g
Water 1000g
After above-mentioned batching and water mixed, stir back dropping ammonia, fluorescent whitening agent stirred then to evenly getting final product.Adopt grain of rice type print edition to look like shown in Figure 1, on plain net or rotary screen printing machines, concentrator is printed on the internal layer of fabric, the stamp process should guarantee that slurry is not to exosmosis, adopt the stamp flower type of this grain of rice shape or class grain of rice shape, the centre can form very slight gap, and this fine gap can have siphonic effect, thereby the sweat that inner textile layer absorbed is drawn onto outer the discharge rapidly, makes internal layer keep clean salubrious.
3, typing arrangement
With the fabric that produces behind the colored type, constant temperature was placed 1.5 hours down for 100 ℃ in drying room, went up the setting machine arrangement then and finalized the design.
4, the product after arrangement typing carries out the examination and test of products under ultraviolet light, can the clot warehouse-in after qualified.
5, check warehouse-in: the product after the typing arrangement, under ultraviolet light, carry out the examination and test of products, can the clot warehouse-in after qualified.
Embodiment 2
Production method is with embodiment 1, and difference is following composition preparation concentrator by ratio of weight and the number of copies:
Clariant 2710 50g
Clariant Nuva HPU 30g
Water 1000g
Embodiment 3
Production method is with embodiment 1, and when difference was the typing arrangement, with the fabric that produces behind the colored type, constant temperature was placed 1 hour down for 120 ℃ in drying room, went up the setting machine arrangement then and finalized the design.
The hydroscopic fast-drying shell fabric that the present invention produces detects through national departments concerned, product quality moisture absorption lining more in the past improves a lot, wherein, and through washing the moisture absorbing and sweat releasing effect that also can have after 20 times about 85%, and domestic equivalents only is about 15～20%, and is specifically as shown in table 1.
Table 1 hydroscopic fast-drying shell fabric quality testing table
Claims (7)
1, a kind of hydroscopic fast-drying shell fabric is characterized in that: be printed with the concentrator that contains waterproofing agent that is grain of rice shape flower type on the internal layer of lining.
2, a kind of hydroscopic fast-drying shell fabric as claimed in claim 1, it is characterized in that: described concentrator is composed as follows by ratio of weight and the number of copies:
Thickener 2～5
Fluorine-containing water repellent 1～3
Water 100.
3, a kind of hydroscopic fast-drying shell fabric as claimed in claim 2 is characterized in that: described thickener is selected from any one of FS-200, Clariant 2710 etc.
4, a kind of hydroscopic fast-drying shell fabric as claimed in claim 3 is characterized in that: also be added with ammoniacal liquor in described thickener, the ammoniacal liquor addition is to add 1 ammoniacal liquor in 10 kilograms of slurries.
5, a kind of hydroscopic fast-drying shell fabric as claimed in claim 2 is characterized in that: described fluorine-containing water repellent is selected from any one of AG-XF fluorine-containing water repellent, D-320 fluorine-containing water repellent, Clariant Nuva HPU etc.
6, a kind of production method as hydroscopic fast-drying shell fabric as described in the claim 1～5 comprises and weaving---steps such as finished product inspection is characterized in that stamp---typing---:
Stamp: the cotton that will weave or polyester-cotton fabric, adopt the grain of rice type stamp space of a whole page, on plain net or rotary screen printing machines, concentrator is printed on the internal layer of fabric;
Back arrangement typing: fabric is after printing technology produces colored type, and constant temperature was placed 1～3 hour down for 80～120 ℃ in drying room, went up setting machine arrangement typing then.
7, a kind of hydroscopic fast-drying shell fabric as claimed in claim 6 is characterized in that: fabric after printing technology produces colored type in drying room 100 ℃ of constant temperature placed 1.5 hours down.