CN103255546A - Machining method for composite fabric - Google Patents
Machining method for composite fabric Download PDFInfo
- Publication number
- CN103255546A CN103255546A CN201310186086.7A CN201310186086A CN103255546A CN 103255546 A CN103255546 A CN 103255546A CN 201310186086 A CN201310186086 A CN 201310186086A CN 103255546 A CN103255546 A CN 103255546A
- Authority
- CN
- China
- Prior art keywords
- yarns
- weft
- yarn
- composite material
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a machining method for a composite fabric. The method includes a first step of selecting raw materials, a second step of taking Dacron interlaced yarns as warp yarns, taking low stretch yarns as first weft yarns, taking the composite yarns, formed by covering spandex with cotton yarns, as second weft yarns and taking the first weft yarns and the second weft yarns as face weft yarns and back weft yarns respectively, a third step of knitting fabric patterns according to a set organization structure thread count and obtaining a gray fabric, a fourth step of immersing the gray fabric into dye liquor to conduct dyeing, enabling the dyeing temperature to be 230 DEG C and enabling the heat preservation time to be 55 minutes, a fifth step of conducting cooling for 20 minutes to 30 minutes until the temperature is lowered to 10 DEG C after dyeing and heat preserving, and a sixth step of conducting management and sizing. The machining method for the composite fabric is few in process step and simple and easy to achieve in production process, and has ideal windproof performance, waterproof performance and laundering durability.
Description
Technical field
The present invention relates to a kind of processing method of composite material, belong to the garment technology field.
Background technology
Raising day by day along with people's living standard, require also more and more higher to the fabric of making the clothes use, a lot of fabrics in the market all have only windproof or a kind of effect that wets thoroughly, under rainy day or burning sun, wearing the clothes that such fabric makes can make people not feel well, therefore, windproof performance and the water vapour permeability of fabric are had higher requirement, and easy fuzz balls.
For example Chinese utility model patent Granted publication number has been recommended a kind of outdoor exercises multifunctional water-proofing composite material of breathing freely for CN200997931Y, and the heat that sends when this patent is unfavorable for human motion sucks, the time wearer produce feeling of oppression and heat.
Summary of the invention
At the deficiency that prior art exists, the object of the invention provides a kind of processing method with composite material of desirable windproof performance and water vapour permeability.
To achieve these goals, the present invention realizes by the following technical solutions:
The present invention includes following step:
(1) selects raw material;
(2) with the terylene net-thread be warp thread, low-stretch yarn is first weft yarn, and the compound silk of cotton yarn coating spandex is second weft yarn, and described first weft yarn and the second dimension yarn are respectively table latitude and back weft;
(3) according to the institutional framework thread count establishment fabric pattern of setting, obtain grey cloth;
(4) grey cloth is immersed in the dye liquor dye, dyeing temperature is 230 ℃, temperature retention time 55 minutes;
(5) after the dyeing insulation, cooled off 20-30 minute to 10 ℃;
(6) put in order at last, finalize the design.
The table latitude is arranged according to 3 to 4 with back weft in the above-mentioned steps (2).
It is 7 to be woven into and to fly satin for 5 piece 6 and do the top layer that warp thread described in the above-mentioned steps (2) and table latitude fly number by eight times latitudes on five; It is 6 to be woven into and to fly satin for 9 piece 8 and make nexine that warp thread and back weft fly number by eight times latitudes on five.
Add in the dye liquor in the above-mentioned steps (4) DISPERSE DYES and auxiliary agent are arranged.
Above-mentioned auxiliary agent is the mixed liquor of glacial acetic acid 1.0g/L, high temperature levelling agent 2.2g/L and sodium acetate 0.8g/L.
Processing step of the present invention is few, production process is simple, and has desirable windproof, waterproof and washing resistance; Advantages such as the present invention is warp thread with the terylene net-thread, and low-stretch yarn is first weft yarn, and the compound silk of cotton yarn coating spandex is second weft yarn, makes the present invention can produce three-dimensional pattern, and rebound performance is good, soft, moisture absorption is ventilative.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with the specific embodiment, further set forth the present invention.
The present invention includes following step:
(1) selects raw material.
(2) with the terylene net-thread be warp thread, low-stretch yarn is first weft yarn, and the compound silk of cotton yarn coating spandex is second weft yarn, and described first weft yarn and the second dimension yarn are respectively table latitude and back weft.
The table latitude is arranged according to 3 to 4 with back weft.
It is 7 to be woven into and to fly satin for 5 piece 6 and do the top layer that warp thread and table latitude fly number by eight times latitudes on five; It is 6 to be woven into and to fly satin for 9 piece 8 and make nexine that warp thread and back weft fly number by eight times latitudes on five.
(3) according to the institutional framework thread count establishment fabric pattern of setting, obtain grey cloth.
(4) grey cloth is immersed in the dye liquor dye, dyeing temperature is 230 ℃, temperature retention time 55 minutes.
Add in the dye liquor DISPERSE DYES and auxiliary agent are arranged.
Auxiliary agent is the mixed liquor of glacial acetic acid 1.0g/L, high temperature levelling agent 2.2g/L and sodium acetate 0.8g/L.
(5) after the dyeing insulation, cooled off 20-30 minute to 10 ℃.
(6) put in order at last, finalize the design.
Processing step of the present invention is few, production process is simple, and has desirable windproof, waterproof and washing resistance; Advantages such as the present invention is warp thread with the terylene net-thread, and low-stretch yarn is first weft yarn, and the compound silk of cotton yarn coating spandex is second weft yarn, makes the present invention can produce three-dimensional pattern, and rebound performance is good, soft, moisture absorption is ventilative.
More than show and described basic principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and the specification just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof
Claims (5)
1. the processing method of a composite material is characterized in that, comprises following step:
(1) selects raw material;
(2) with the terylene net-thread be warp thread, low-stretch yarn is first weft yarn, and the compound silk of cotton yarn coating spandex is second weft yarn, and described first weft yarn and the second dimension yarn are respectively table latitude and back weft;
(3) according to the institutional framework thread count establishment fabric pattern of setting, obtain grey cloth;
(4) grey cloth is immersed in the dye liquor dye, dyeing temperature is 230 ℃, temperature retention time 55 minutes;
(5) after the dyeing insulation, cooled off 20-30 minute to 10 ℃;
(6) put in order at last, finalize the design.
2. the processing method of composite material according to claim 1 is characterized in that, the table latitude is arranged according to 3 to 4 with back weft in the described step (2).
3. the processing method of composite material according to claim 2 is characterized in that, it is 7 to be woven into and to fly satin for 5 piece 6 and do the top layer that warp thread described in the described step (2) and table latitude fly number by eight times latitudes on five;
It is 6 to be woven into and to fly satin for 9 piece 8 and make nexine that described warp thread and back weft fly number by eight times latitudes on five.
4. according to the processing method of any described composite material of claim 1 to 3, it is characterized in that adding in the dye liquor in the described step (4) has DISPERSE DYES and auxiliary agent.
5. the processing method of composite material according to claim 4 is characterized in that, described auxiliary agent is the mixed liquor of glacial acetic acid 1.0g/L, high temperature levelling agent 2.2g/L and sodium acetate 0.8g/L.